In situ observation of NaBi(WO4)2 dendrite growth and the study on microstructure of solidification

The dendrite growth process of transparent NaBi(WO4)2 with small prandtl and high melting point was studied by using the in-situ observation system. According to the dynamic images and detailed information, there are two kinds of restriction effect on the dendrite growth, the competition between arms and branches and the convection in the melt. The dendrite growth rate was time dependent, and the rate of arm growth reached the maximum 5.8 mm/s in the diffusive-advective region and rapidly decreased in the diffusive-convective region. The growth rate of branch had the same change trends as the arm's. Based on the EPMA-EDS data of solidification structure of quenched NaBi(WO4)2 melt, it was found that there were component differences from stoichiometric concentration in the melt near the interface during the growth process.     

新型脱硅剂水合碳铁酸钙合成过程的光谱学研究

亚熔盐溶出一水硬铝石型铝土矿过程中需在高浓介质条件下脱除二氧化硅杂质,研究采用合成水合碳铁酸钙做为脱硅剂;因水合碳铁酸钙合成过程中会有碳酸钙、氢氧化钙、铁酸钙等副产物,故合成条件对水合碳铁酸钙含量及脱硅效果有重要影响。为了探讨反应机理并优化合成参数, 研究采用傅里叶变换红外光谱(FTIR)、电感耦合等离子发射光谱(ICP-AES)分析对合成过程产物进行了物相分析和脱硅实验。FTIR和脱硅过程元素分析表明水合碳铁酸钙在水溶液中为介稳物质,反应温度和反应时间对水合碳铁酸钙的合成具有重要影响,随时间和温度增加水合碳铁酸钙含量先增加后减少;单因素条件下最优的合成条件为, 反应温度30 ℃,反应时间16 h,反应液固比20,搅拌强度500 r·min-1;对最优条件下合成水合碳铁酸钙的物相结构进行了研究,表明水合碳铁酸钙为斜方六面体晶体结构,其中存在结晶水、羟基、Fe—O特征峰。     

先天性白内障一家系的致病基因研究

目的 对一个来自浙江省杭州地区的三代先天性白内障家系进行常染色体显性遗传基因的突变分析,以寻找其可能的致病基因及突变位点。方法 该家系共10例成员,其中包括4例患者。10 例家系成员在浙江省人民医院眼科中心接受眼科专科检查及全身检查,以排除存在白内障以外的眼部及全身疾患。10例家系成员各抽取外周血5ml,提取基因组DNA。针对国内外文献报道的与常染色体显性遗传先天性白内障相关的18 个基因（CRYAA、CRYAB、CRYBA1、CRYBA2、CRYBA4、CRYBB1、CRYBB2、CRYGC、CRYGD、CRYGS、GJA3、GJA8、MIP、BFSP、HSF4、PITX3、EPHA2、PAX6）设计引物,进行PCR 扩增,对扩产物进行测序和序列分析,了解这10例家系成员的以上基因是否存在相应的序列。结果 临床眼科检查显示该家系先天性白内障类型为粉尘状白内障。候选基因序列测定显示在CRYAA 第1 个外显子中第6 位碱基发生C→T 置换,氨基酸同为天门冬氨酸。该家系中所有患者均有此改变,而所有的正常家系成员均无此改变。结论 CRYAA 第1个外显子中第6位碱基发生C→T的同义突变可能是导致该家系先天性白内障发生的致病原因。     

在线质谱仪检测植物排放的挥发性有机物

利用在线检测质谱仪(SPIMS-1000)分别对高温烘烤、长时间密封保存、机械损伤等处理过的松科松属马尾松(Pinus Massoniana L.)样品排放的挥发性有机物(VOCs)与新鲜样品进行对比检测。SPIMS-1000在线检测质谱仪能够检测出植物排放的异戊二烯(m/z 68)和单萜(m/z 136),及其它一些特异性组分,如(Z)-3-己烯醛(m/z 98)等。利用在线检测质谱仪实现敞开环境中原位植物排放气体的检测。实验表明,在线检测质谱仪被广泛应用于环境中VOCs的实时、在线、定性快速检测。     

含绿色荧光蛋白发色团双自由基分子的非线性光学性质

采用密度泛函理论(DFT)方法研究了系列含绿色荧光蛋白发色团双自由基分子光学异构体的几何结构、极化率(αs)和第一超极化率(βtot).结果表明,引入电子给受体取代基使分子的极化率增大,而对第一超极化率有不同影响.对于光照前的反式结构,引入电子受体βtot值增加,且βtot值随取代基吸电子能力的增强而增大;引入电子给体βtot值降低,且βtot值随取代基给电子能力的增强而减小.当分子变成相应的顺式结构时,其βtot值变化趋势与反式结构的结果正好相反.光异构化前后分子的βtot值变化不同,引入电子受体使顺式结构的βtot值比反式结构的小,其中―NO2使顺式结构的βtot值减小为反式结构的1/6;引入电子给体使反式结构的βtot值比顺式结构的小,其中―NH2使反式结构的βtot值减小为顺式结构的1/6.从而,光异构化起到调节非线性光学(NLO)响应的作用.     

微波辅助合成石墨烯/氧化镍复合材料及其表征

本文通过微波辅助的方法,快速而有效地在热膨胀石墨烯(RG)的缺陷上原位合成氧化镍纳米颗粒,形成石墨烯/氧化镍复合材料(RG/NiO)。利用X-射线衍射(XRD),拉曼光谱(Raman),傅里叶变换红外(FTIR),扫描电镜(SEM),透射电镜(TEM),热重-差热(TGA-DSC)对所制备样品的结构、形貌和NiO含量在复合材料中的含量进行表征。结果表明,热膨胀石墨烯层数约7~8层,层间距约为0.35nm,缺陷多,在水热和微波处理后抗氧化性明显变差。复合材料中氧化镍颗粒平均粒径为25nm,均匀而密集地分散在石墨烯平面上,同时在复合材料中的含量为19.8%。     

β-PbO2/TiO2纳米管电极的制备及其电催化降解苯酚

采用阳极氧化法和脉冲电沉积制备出β-PbO2改性TiO2纳米管(β-PbO2/TiO2-NTs)电极,通过扫描电子显微镜(SEM)、X射线衍射(XRD)和X射线光电子能谱(XPS)等技术手段对制备的β-PbO2/TiO2-NTs电极的表面形貌和结构进行了表征。结果表明,该方法成功地将β-PbO2纳米颗粒分散在TiO2纳米管中,通过电催化降解苯酚评价了β-PbO2/TiO2-NTs电极的电催化活性,实验结果表明,在TiO2-NTs中电沉积β-PbO2提高了电极的电催化活性,对苯酚的降解达到83%。     

BiOI/Bi_2WO_6对甲基橙和苯酚的光催化降解及光催化机理(英文)

采用简单的沉积方法制备了不同碘化氧铋含量的BiOI/Bi2WO6光催化剂,通过X射线衍射(XRD)、扫描电子显微镜(SEM)、高分辨透射电子显微镜(HR-TEM)、紫外-可见漫反射光谱(UV-Vis DRS)和BET比表面积测量对其进行了表征。在紫外和可见光的照射下,使用甲基橙和苯酚的光催化降解评价了BiOI/Bi2WO6催化剂的光催化性能。结果表明:与商业P25和纯Bi2WO6相比,13.2%BiOI/Bi2WO6光催化剂具有更高的紫外和可见光催化性能。这明显增加的光催化活性主要归功于光生电子和空穴在Bi2WO6和BiOI界面上的有效转移,降低了电子-空穴对的复合。基于BiOI和Bi2WO6的能带结构,提出了光生载流子的一种转移过程。自由基清除剂的实验表明,·OH,h+,·O2-和H2O2,特别是h+,共同支配了甲基橙和苯酚的光催化降解过程。     

基于石墨烯和金纳米笼修饰的无标记型微囊藻毒素免疫传感器的研制

利用石墨烯及中空结构的金纳米笼构建了无标记型电化学免疫传感器,并用于微囊藻毒素的检测。利用多元醇还原法合成制备了导电性好、催化性强、生物相容性好的金纳米笼;再利用高分散的石墨烯将其固定于玻碳电极表面,进一步吸附固定微囊藻毒素抗体。在无微囊藻毒素存在时,电化学探针[Fe(CN)6]3!/4!在传感器界面上能获得较高的电流响应信号。当培育了微囊藻毒素后,抗体与微囊藻毒素形成免疫结合物,增加了电极表面的电荷密度和传质阻力,阻碍[Fe(CN)6]3!/4!扩散到电极表面,导致[Fe(CN)6]3!/4!的电流响应信号明显降低,电流减小的程度间接地与微囊藻毒素的浓度成比例,可实现对微囊藻毒素的检测。实验考察了抗原培育时间,抗体浓度等条件对该传感器响应性能的影响。结果表明,此传感器对微囊藻毒素的线性响应范围为0.05~1000μg/L,检出限为0.017μg/L,优于文献报道。此传感器操作简单,并且具有良好的稳定性,将其用于实际水样中微囊藻毒素的检测,平均加标回收率为94.1%。     

Synthesis and Crystal Structure of a New Pr(Ⅲ)–K(Ⅰ) Heterometallic Oxalate Coordination Polymer

A new 3D heterometallic coordination polymer, namely [K2Pr2(C2O4)4·H2O]n(1), has been successfully synthesized under hydrothermal conditions. X-ray single-crystal diffraction determination reveals that 1 crystallizes in monoclinic system, space group P21/n with a = 12.060(4), b = 8.493(3), c = 15.776(5)(A), β = 93.235(3)°, V = 1613.4(9) 3, Z = 4, Mr = 730.12, Dc = 3.006 Mg/m3, μ = 6.581 mm-1, F(000) = 1368, the final R = 0.0283 and w R = 0.0866 for 2939 observed reflections with I 2σ(I). Complex 1 features an unusual 3D heterometallic coordination framework, in which oxalates exhibit three different coordination behaviours. Moreover, powder X-ray diffraction and thermal properties for 1 have also been investigated.