Magnetic,structural and electrical properties of ordered and disordered Co50Fe50 films

Co₅₀Fe₅₀ films with thickness varying from 100 to 500 Å were deposited on a glass substrate by sputtering process, respectively. Two kinds of CoFe films were studied: one was the as-deposited film, and the other the annealed film. The annealing procedure was to keep the films at 400 °C for 5 h in a vacuum of 5×10⁻⁶ mbar. From the X-ray study, we find that the as-deposited film prefers the CoFe(1 1 0) orientation. Moreover, the body-centered cubic (bcc) CoFe(1 1 0) line is split into two peaks: one corresponding to the ordered body-centered tetragonal (bct) phase, and the other, the disordered bcc phase. After annealing, the peak intensity of the ordered bct phase becomes much stronger, while that of the disordered bcc phase disappears. The annealing has also caused the ordered CoFe(2 0 0) line to appear. When the amount of the ordered bct phase in Co₅₀Fe₅₀ is increased, the saturation magnetization (M_s) and coercivity (H_c) become larger, but the electrical resistivity (ρ) decreases. From the temperature coefficient of resistance (TCR) measurement, we learn that the bct grains in the CoFe film start to grow at temperature 82 °C.     

Crystal-Orientation Dependent Evolution of Edge Dislocations from a Void in Single Crystal Cu

The micro-void growth by dislocation emission under tensile loading is explored with focus on the influence of crystal orientations. Based on the elastic theory, a dislocation emission criterion is formulated. It is predicted that the preferential location of dislocation nucleation and its threshold stress are dependent on the crystal orientation. Large-scale molecular dynamics （MD） simulations are also performed for single crystal copper to illustrate the dislocation evolution pattern associated with a nano-void growth. The results are in line with those given by the theoretical prediction. As revealed by MD simulations, the characteristics of void growth at micro-scale depend greatly on the crystal-orientation.     

等离子体中Langmuir波、横波和离子声波相互作用过程的孤立子行为

我们用Zakharov方程描述等离子体中Langmuir波、横波和离子声波的非线性相互作用,通过研究系统稳态的Sagdeev势的性质,讨论了该系统中孤立子可能存在的条件;同时和体系的极小能量状态相联系,构造了体系的Liapunov泛函,研究了孤立子的Liapunov稳定性。我们所采用的方法是完全非线性的,得到的稳定性判据在横波和Langmuir波解耦情况下退化为文献[8]的结果。 关键词：     

波长检测技术在温度测量中的应用

提出一种波长检测技术实现温度测量的方法,利用FBG传感器对温度等物理量实施监测,具有测试精度高,应用场合不受限制等特点,当环境参数发生变化时,光纤光栅的有效折射率和光栅周期会受到影响,将引起光纤光栅峰值波长的偏移,依据反射光谱结构的变化,可知道其温度的变化趋势。实验测试结果表明,在温度变化0.1°,波长变化1pm,温度和波长具有良好的线性关系。     

水下光通信PPM数字接收机的DSP实现

水下光通信充分利用了海水对激光的衰减窗口效应,具有隐蔽、安全、非接触和快速机动等特性,兼具无线通信和光纤通信的优点,其关键技术在于光收发端机的研制;PPM(Pulse Position Modulation)数字脉冲位置调制具有低平均功率和高峰值功率等特性,特别适合用于无线数字光通信。两者性能的融合需要高灵敏度数字光接收机的实现。利用阵列光电检测接收、高速A/D转换和信号处理等相关技术,采用DSP处理器,高灵敏度的数字光PPM接收机得以实现,实验和测试表明它大大降低了接收机对于整个系统信噪比的要求,获得了较好的性能。     

26Al的加速器质谱测量及其应用

26Al是一个在多个学科都非常有意义的放射性核素。主要介绍了国内外在利用加速器质谱技术测量26Al时所开展的各种测量方法、各自的优缺点和测量灵敏度，并介绍了目前利用^26Al在地球科学、生物医学、核物理以及天体物理等诸多方面的应用研究工作。     

单脉冲和多脉冲飞秒激光对单层光学薄膜的损伤

 利用掺钛的蓝宝石飞秒激光系统输出的单脉冲和多脉冲飞秒激光(中心波长800 nm，脉宽50 fs，靶面聚焦直径Ф 40 μm)，分别对BK7玻璃基底上厚约500 nm的单层HfO₂和单层ZrO₂薄膜进行辐照，得到了这两种薄膜在1-on-1和1 000-on-1测试方法下的激光损伤阈值。实验发现，两种方法下HfO₂单层膜的阈值均比ZrO₂单层膜的阈值高。从简化的Keldysh多光子离化理论出发，认为HfO₂薄膜材料的带比ZrO₂的宽是导致上述结果的主要原因。同时，同一种薄膜的多脉冲下的阈值比单脉冲下的低，原因是多脉冲下，飞秒激光对光学薄膜的损伤存在累积效应。     

SiO2-羟基表面上金属原子的第一性原理研究

采用第一性原理方法研究了SiO2-羟基表面上几种金属原子的吸附性质,发现In和Ga在SiO2-羟基表面上的结合很弱,而Fe,Co,Ni在该表面上与Si,O形成强的化学键.等势能面和扩散势垒计算表明In(Ga)的扩散激活能只有0.1-0.3 eV,表明这两种原子容易在表面上扩散.这些结果可以定性地解释纳米合成中的一些实验现象.     

各向同性湍流中颗粒引起湍流变动的直接模拟

本文通过直接数值模拟对均匀各向同性湍流中颗粒对湍流的变动作用进行了研究.颗粒相的体积分数很小而质量载荷足够大,以至于颗粒之间的相互作用可以忽略不计,而重点考虑颗粒与湍流间能量的交换。颗粒对湍流的反向作用使得湍动能的耗散率增强,以至于湍动能的衰减速率增大.湍动能的衰减速率随颗粒惯性的增大而增大。三维湍动能谱显示,颗粒对湍动能的影响在不同的尺度上是不均匀的。在低波数段,流体带动颗粒,而高波数段则相反.     

磁场对四端量子波导中电子输运性质的影响

采用模匹配方法，研究了非均匀磁场下开放的四端量子波导中的电子输运性质. 结果表明，从一端入射的电子可以透射到两个与之垂直的输出端和一个与之平行的输出端. 在没有外加磁场的情况下，两个垂直输出端的输运概率是相同的，但垂直端与水平端的输运概率不同；在外加磁场下，由于磁边缘态效应，两个垂直输出端的输运概率也有着相当大的差别. 通过施加不同的磁场，我们能获得丰富的电子输运结构，如台阶，宽谷，尖峰等；通过调节磁场的大小和比例以及结构参数可控制该量子结构在各输出端的输运概率. 关键词： 电子输运 介观体系 磁效应