Hydrothermal Preparation and Characterization of TiO2/BiVO4 Composite Catalyst and its Photolysis of Water to Produce Hydrogen

In the present work, bismuth vanadate composited photocatalysts were synthesized and characterized. X‐ray diffractometry and Raman results showed that the particles were well crystallized, and formed by the complex of monoclinic BiVO₄ and TiO₂. On electron microscopy, the photocatalyst exhibited high crystallization, agglutination and irregular shape, and was surrounded by numerous TiO₂ particles. The study of surface areas showed that the specific surface area of 30‐BiVO₄/TiO₂ composited was 112 m²·g^?1, which was nearly 10 times that of pure BiVO₄. The ultraviolet–visible diffuse reflectance spectra indicated the composited photocatalyst were activated in visible light. The activity of photocatalytic water splitting was studied. The results showed that monomer BiVO₄ photocatalyst was not able to produce hydrogen under any light source. BiVO₄/TiO₂ composited photocatalysts, however, were capable of generating hydrogen. Under UV light irradiation for 120 min, 1 g catalyst dispersed in 50 mL deionized water produced almost 1 mL hydrogen, such that the productivity of hydrogen was higher than that of P25‐TiO₂. Photocatalytic decomposition of water under visible light also confirmed that the BiVO₄/TiO₂ composited photocatalyst had the ability of water splitting.     

Amperometric Determination of Maltol using a Cobalt Oxide-Assembled MCM-41 Composite-Modified Glassy Carbon Electrode

A sensitive and selective amperometric method for maltol is reported based on a nanostructural Co₃O₄-assembled Mobil composite material (MCM-41). The amperometric sensor was characterized by scanning electron microscopy, energy-dispersive X-ray spectrometry, cyclic voltammetry, electrochemical impedance spectroscopy, and ultraviolet–visible absorption spectroscopy. The obtained calibration curve showed that the oxidative peaks increased linearly with the maltol concentration from 1.66?×?10^?6?M to 1.15?×?10^?4?M with a detection limit of 0.42?µM. Furthermore, the mechanism of oxidation of the analyte on the modified electrode surface was investigated using electrochemical techniques. The modified electrode was used for the determination of maltol using the method of standard addition with satisfactory results.     

重力场流分离系统中载液及流速条件对分离的影响

重力场流分离作为最简单的一种场流分离技术,常用于分离微米级颗粒。选择两种不同粒径(20 μ m和6 μ m)的聚苯乙烯(PS)颗粒作为样品,通过改变载液中叠氮化钠浓度、混合表面活性剂的比例及载液流速,利用自行设计生产的重力场流分离(gravitational flow field-flow fractionation, GrFFF)仪器,对颗粒混合样品进行分离,得到了相关谱图与数据,考察了这3种因素对分离效果(保留比(R)、塔板高度(H))的影响。结果表明:20 μ m PS颗粒的R值均大于6 μ m PS颗粒的R值,H值均小于6 μ m颗粒的H值;PS颗粒的R值与H值均随着载液中叠氮化钠浓度的增加而增加;但随着载液流速的增加,R值增加,H值减小。该研究为GrFFF系统的开发及应用提供了重要的参考价值。     

Organized cryogel composites with 3D hierarchical porosity as an extraction adsorbent for nucleosides

Macroscopic monoliths are highly desirable in many fields of application. Herein, well organized organic–inorganic cryogel composite with a three‐dimensional hierarchical meso‐ and macroporous structure are presented, which were produced by in situ copolymerization of mesoporous multifunctional silica (size: 1–20 μm; pore: 2–20 nm mostly) and monomers (hydroxyethyl methacrylate and diallyldimethylammonium chloride) in water below the freezing point. This copolymerization method effectively adjusted the macropores of the basic cryogel, and the nanosilica was more homogeneously dispersed in the basic cryogel. The specific surface area of the cryogel composite was increased 17 times versus than that of the basic cryogel. The abundant meso‐ and macroporous pores on the cryogel composite provided sufficient reactive sites favorable for the efficient mass transport of target compounds. When the cryogel composite, as solid phase extraction adsorbent, was coupled with high‐performance liquid chromatography, an analytical tool, the nucleosides were quantified with good selectivity, lower detection limits (0.9–1.3 ng/mL) and satisfactory recoveries of greater than 80% from spiked human serum.     

Scandium Phosphonioketene: Synthesis,Bonding and Reactivity

Reaction of a scandium phosphoniomethylidene with carbon monoxide provides the first scandium phosphonioketene ( 1 ). X-ray diffraction analysis shows that the complex has a very short Sc−C bond (2.138(2) Å), and DFT calculations indicate that this unusual short bond length is due to the significant contribution of ionic coulomb interaction between carbon and scandium and the η²-O,C coordination fashion. Complex 1 is thermally stable, albeit shows high reactivity towards a series of unsaturated substrates, including carbon dioxide, ketone, imine, nitrile and isocyanide. In the reaction with tert-butyl isocyanide, not only an insertion of tert-butyl isocyanide into the Sc−C bond occur, but also a C−H activation on the phenyl ring. DFT calculations show that the reactivity of 1 operated by nucleophilic properties, and therefore the reaction mechanism favors the nucleophilic attack to isocyanide as a rate-determining step, followed by the stepwise C−H activation through an interesting C−H deprotonation.