喷雾干燥-高温固相法制备纳米LiFePO4与LiFePO4/C材料及性能研究

采用喷雾干燥-高温固相法制备纳米LiFePO₄与LiFePO₄/C正极材料，用X-射线衍射，扫描电镜等对合成材料进行了表征，并对以LiFePO₄为正极的电池进行了电化学性能测试。结果表明:材料合成最佳煅烧温度为600 ℃;合成过程中由于碳对LiFePO₄晶型的生长有一定的抑制作用，相对于纯LiFePO₄材料，LiFePO₄/C材料粒径更小;并且，在此最佳合成温度下合成的LiF     

一维螺旋状3，6-哒嗪二甲酸镉(Ⅱ)配位聚合物的合成与结构

Using the ligand pyridazine-3，6-dicarboxylate (H₂pzdc)， a coordination polymer [Cd₂(pzdc)₂(H₂O)₄] was synthesized and characterized by elemental analysis， thermal analysis， IR and single-crystal X-ray diffraction. The complex crystallizes in the tetragonal system with space group I4₁/a. The crystallographic data are: a=1.470 6(4) nm， c=1.489 8(6) nm， V=3.222 0(19) nm³， Z=16， μ=2.725 mm^-1， D_c=2.594 g·cm^-3， R₁=0.017 8， wR₂=0.044 6. In the complex， the cadmium(Ⅱ) ions with the eight-coordinated dodecahedral geometry are linked by the pzdc ligands to generate one-dimensional chains， which are associated into the three-dimensional architecture via O-H…O hydrogen bonding. CCDC: 658853.     

水溶性席夫碱型锰配合物的合成、表征及其模拟超氧化物歧化酶活性研究

以水杨醛为母体, 与胺类化合物缩合形成席夫碱配体, 用分子自组装法合成了一系列水溶性席夫碱型金属锰单核、双核配合物. 通过元素分析、红外光谱对配合物进行了表征, 采用邻苯三酚自氧化法测定了配合物的超氧化物歧化酶(SOD)活性. 结果表明, 这些水溶性锰配合物具有良好的SOD活性.     

聚苯并咪唑金属复合物的X-射线光电子能谱(XPS)研究

本文报道以聚苯并咪唑(PBI)与某些过渡金属卤化物所形成的金属复合物的XPS研究,由反映在金属复合物N_(1s)和C_(1s)振起(Shake-up)伴峰的消失,反映在PBI中N_(1s)双峰变为复合物中的具有高结合能的单峰以及与其复合金属离子结合能的降低,这就从施受两个侧面确证金属复合物的形成。XPS结果也说明在金属复合物的制备中,不同溶剂条件所制得的复合物在硅氢加成中活性丧失归结於溶剂导致的金属离子的还原。     

3,3,6,6-四甲基-9-邻氯苯基-1,8-二氧代-3,4,5,6,7,9-六氧化氧杂蒽的合成和晶体结构

标题化合物C23H25对O3Cl是由邻氯苯甲醛与5，5-二甲基1，3-环己二酮在N，N-二甲基甲酸腹中反应而得。结构通过单晶X-射线衍射法确定，其晶体属于单科晶系，空间群=1632。晶体结构用直接法解出，使用全矩阵最小二乘法对原子参数进行修正，最后的偏离因子为R=0．054，Rw一0．063。在晶体结构中，吡喃环与苯环之间的两面角为92．43°。     

Semiconducting organic polymer from polyacrylamide–Cu++ chelate and iodine

Semiconducting organic polymer was obtained by the modification of polyacrylamide (PAAm)–Cu⁺⁺ chelate with iodine in acetone. Favorable conditions for preparing the chelate effective for the conduction were investigated. Surface resistivities were affected by the amounts of cupric salts and iodine, satisfactory results being given by about 25 wt % of the salts based on PAAm and more than 1 wt % of iodine on the chelate. The conductivity was also varied with the degree of neutralization of the chelate in solution, and optimal values were obtained by addition of about an equimolar amount of potassium hydroxide to cupric salts. Effective structures of the polymer chelate in solution were assumed on the basis of the visible and the NMR spectra and potentiometric titration.     

阿托伐他汀钙与β-环糊精相互作用的研究及应用

采用线性扫描伏安法和循环伏安法并结合紫外分光光度法研究了新型抗血脂紊乱药物阿托伐他汀钙(AC)与β-环糊精(-βCD)的相互作用.探讨了-βCD对AC的峰电流及AC对-βCD吸附峰电流的影响,测得在0.06mol/LKH2PO4-Na2HPO4(pH=7.17)缓冲溶液中,AC与-βCD包结比为1:1,用电流法测得包结物的形成常数为9.09×104L/mol.根据碱性介质条件下β-CD分子与AC形成包结物而使β-CD吸附峰电流减小的特性,建立了一种利用β-CD间接测定AC的伏安方法.     

用ATRP法构筑核壳型梯度极性的多羟基多臂星状超支化聚合物及聚合物刷——双层聚合物刷的合成与表征

设计并通过原子转移自由基聚合方法 (ATRP)合成了核壳型多羟基多臂星状超支化聚合物刷 .以 2 溴异丁基酰溴封端的超支化聚 (3 乙基 3 羟甲基氧杂环丁烷 ) (HP Br)作为大分子引发剂 ,采用Cu(I)Br和N ,N ,N′ ,N′ ,N″ 五甲基二乙基三胺 (PMDETA)催化体系 ,在丁酮与丙醇的混和溶液中 ,通过甲基丙烯酸羟乙酯(HEMA)的ATRP溶液聚合 ,得到了一系列含有大量羟基的多臂星状超支化聚合物刷 (HP g PHEMA) ,并考察了其羟基的活性 ,发现羟基还可以与苯甲酰氯发生反应 .产物的结构和热性能用1 H NMR、FTIR、GPC、TGA、DSC等进行了表征和测试 .     

氰根桥连的异金属配位聚合物{[Ni(pn)2][Fe(CN)4(bipy)]}2·3H2O(pn=1,3-丙二胺,bipy=2,2′-联吡啶)的合成与结构

以[Fe(CN)₄(bipy)]^2-为建筑块和[Ni(pn)₂]²⁺在水溶液中反应,合成了{[Ni(pn)₂][Fe(CN)₄(bipy)]}₂·3H₂O(pn=1,3-丙二胺)。通过X-射线单晶衍射确定了其晶体结构。该配合物属单斜晶系,P2₁/n空间群,晶胞参数为:a