Cyclolinear polysiloxanes. II. Crosslinking and characterization

The synthesis and characterization of two groups of novel networks prepared from cyclolinear polysiloxanes are described. The first group of networks from cyclolinear polysiloxanes (N‐CLPSs) was synthesized by the hydrosilation of vinyl‐terminated cyclolinear polyorganosiloxanes [prepared from diacetoxydiethyltetramethylcyclotetrasiloxane (D₄Et₂OAc₂) or diacetoxytriethylpentamethylcyclopentasiloxane (D₅Et₃OAc₂)] with a copolymer of dimethylsiloxane and methylhydrosiloxane as the crosslinking agent. Hydrosilation was effected with a platinum carbonyl catalyst with a cyclovinylsiloxane moderator. The second group of networks (N‐eCLPSs) was prepared similarly with extended cyclolinear polysiloxanes. The mechanical properties of the novel networks were comparable to those of polydimethylsiloxane networks (N‐PDMS). The oxygen permeabilities were similar to or slightly higher than that of N‐PDMS. The glass‐transition temperatures of D₄Et₂OAc₂‐ and D₅Et₃OAc₂‐based N‐CLPSs were ?67.8 and ?90.8 °C, respectively, whereas the incorporation of polydimethylsiloxane spacers into similar N‐eCLPSs lowered their glass‐transition temperatures to ?109.7 and ?115.0 °C. Upon heating to 800 °C in air, N‐CLPSs yielded more residue than N‐eCLPSs, which in turn yielded more residue than N‐PDMS. These results may have been due to the presence of T units in the cyclic siloxane units, which may have inhibited chain degradation or the formation of volatile products. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 4053–4062, 2006     

Synthesis and cationic photopolymerization of new fluorinated,polyfunctional propenyl ether oligomers

New fluorinated, polyfunctional propenyl ether functionalized resins were synthesized, and their behavior in cationic photopolymerization was investigated. The photopolymerization proceeded efficiently with a high double‐bond conversion (>90%), giving rise to UV‐cured coatings characterized by low glass‐transition temperatures (?33 °C ≤ glass‐transition temperature ≤ ?15 °C) and hydrophobic surface properties. A fluorinated additive was also employed as a reactive additive in the cationic photopolymerization of trimethylolpropane tripropenyl ether, increasing the double‐bond conversion, polymer network flexibility, thermal stability, and surface hydrophobicity. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 6943–6951, 2006     

Practical syntheses of [1,3,5]‐triazine dendritic molecules on solid supports

A practical and divergent synthesis of supported [1,3,5]‐triazine dendritic molecules on Wang resin, PEGA resin, SynPhase? Lanterns, and silica gel is described. The alkylamine linkers used allow derivatization with functionality for both synthetic (e.g., supported reagent and scavenger activity) and chemical biology applications. The use of supported intermediates allows differentiation of symmetric linkers without the need for protecting group chemistry. The synthetic route uses inexpensive, readily available starting materials in a straightforward and scaleable strategy. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 2248–2259, 2006     

Synthesis and characterization of poly(dimethylsiloxane‐urethane) elastomers: Effect of hard segments of polyurethane on morphological and mechanical properties

A series of poly(dimethylsiloxane‐urethane) elastomers based on hexamethylenediisocyanate, toluenediisocyanate, or 4,4′‐methylenediphenyldiisocyanate hard segment and polydimethylsiloxane (PDMS) soft segment were synthesized. In this study, a new type of soft‐segmented PDMS crosslinker was synthesized by hydrosilylation reaction of 2‐allyloxyethanol with polyhydromethylsiloxane, using Karstedt's catalyst. The synthesized soft‐segmented crosslinker was characterized by FT‐IR, ¹H, and ¹³C NMR spectroscopic techniques. The mechanical and thermal properties of elastomers were characterized using tensile testing, thermogravimetric analysis, differential scanning calorimetry (DSC), and dynamical mechanical analysis measurements. The molecular structure of poly(dimethylsiloxane‐urethane) membranes was characterized by ATR‐FTIR spectroscopic techniques. Infrared spectra indicated the formation of urethane/urea aggregates and hydrogen bonding between the hard and soft domains. Better mechanical and thermal properties of the elastomers were observed. The restriction of chain mobility has been shown by the formation of hydrogen bonding in the soft and hard segment domains, resulting in the increase in the glass‐transition temperature of soft segments. DSC analysis indicates the phase separation of the hard and soft domains. The storage modulus (E′) of the elastomers was increasing with increase in the number of urethane connections between the hard and soft segments. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 2980–2989, 2006     

Random multiblock poly(ester amide)s containing poly(L‐lactide) and cycloaliphatic amide segments: Synthesis and biodegradation studies

Novel multiblock poly(ester amide)s containing poly(L ‐lactide) and cycloaliphatic amide segments were synthesized from telechelic oligomer of α,ω‐hydroxyl terminated poly(L ‐lactide), 1,3‐cyclohexylbis(methylamine), and sebacoylchloride by the “two‐step” interfacial polycondensation method. The blocky nature of PEAs was established by FTIR and ¹H NMR spectroscopies. The effect of relative content of ester and amide segments on the crystallization nature of PEAs was investigated by WAXD and DSC analyses. PEAs having lower content of PLLA, PEA 1 and PEA 2, showed a crystallization pattern analogous to polyamides, whereas PEA 3, having higher content of PLLA, showed two crystalline phases characterized by polyester and polyamide segments. Random nature of PEAs was observed from single T_g values. Biodegradation studies using the enzyme lipase from Candida Cylindracea showed higher degradation rate for PEA 3 than that for PEA 1 and PEA 2. FTIR, ¹H NMR, and DSC analyses of the degraded products indicated the involvement of ester linkages in the degradation process. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 3250–3260, 2006     

Evaluation of piezoelectric PVDF polymers for use in space environments. III. Comparison of the effects of vacuum UV and gamma radiation

Films of piezoelectric PVDF and P(VDF‐TrFE) were exposed to vacuum UV (115–300 nm VUV) and γ‐radiation to investigate how these two forms of radiation affect the chemical, morphological, and piezoelectric properties of the polymers. The extent of crosslinking was almost identical in both polymers after γ‐irradiation, but surprisingly, was significantly higher for the TrFE copolymer after VUV‐irradiation. Changes in the melting behavior were also more significant in the TrFE copolymer after VUV‐irradiation due to both surface and bulk crosslinking, compared with only surface crosslinking for the PVDF films. The piezoelectric properties (measured using d₃₃ piezoelectric coefficients and D‐E hysteresis loops) were unchanged in the PVDF homopolymer, while the TrFE copolymer exhibited more narrow D‐E loops after exposure to either γ‐ or VUV‐radiation. The more severe damage to the TrFE copolymer in comparison with the PVDF homopolymer after VUV‐irradiation is explained by different energy deposition characteristics. The short wavelength, highly energetic photons are undoubtedly absorbed in the surface layers of both polymers, and we propose that while the longer wavelength components of the VUV‐radiation are absorbed by the bulk of the TrFE copolymer causing crosslinking, they are transmitted harmlessly in the PVDF homopolymer. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 3253–3264, 2006     

Encapsulation of ZnS:Mn2+ nanocrystals with diblock copolymers

The encapsulation of the nanocrystalline manganese‐doped zinc sulfide (ZnS:Mn) in poly(styrene‐b‐2vinylpyridine) (PS‐PVP) diblock copolymers is reported. Below the critical micelle concentration in the absence of nanocrystals (NCs), inverse micelles of PS‐PVP were induced by adding ZnS:Mn NCs, the presence of which was confirmed by scanning force microscope and dynamic light scattering. In toluene, a PS‐selective solvent, the less‐soluble PVP blocks preferentially surround the ligand‐coated ZnS:Mn NCs. For PS‐PVP encapsulated ZnS:Mn NCs, the ratio of blue emission to orange emission of ZnS:Mn NCs is dependent on both the concentration of PS‐PVP and the solvent quality. The pyridine of PVP blocks form complexes with the Zn atoms via the nitrogen lone pair and thus the sulfur vacancies are passivated. As a result, the defect‐related blue emission is selectively quenched even when the micelles are not formed. As the concentration of PS‐PVP encapsulating the ZnS:Mn NCs increases, the intensity of blue emission decreases. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 3227–3233, 2006     

Measurement and prediction of solubilities and diffusion coefficients of carbon dioxide in starch–water mixtures at elevated pressures

The solubility and diffusion coefficient of carbon dioxide in intermediate‐moisture starch–water mixtures were determined both experimentally and theoretically at elevated pressures up to 16 MPa at 50 °C. A high‐pressure decay sorption system was assembled to measure the equilibrium CO₂ mass uptake by the starch–water system. The experimentally measured solubilities accounted for the estimated swollen volume by Sanchez–Lacombe equation of state (S‐L EOS) were found to increase almost linearly with pressure, yielding 4.0 g CO₂/g starch–water system at 16 MPa. Moreover, CO₂ solubilities above 5 MPa displayed a solubility increase, which was not contributed by the water fraction in the starch–water mixture. The solubilities, however, showed no dependence on the degree of gelatinization (DG) of starch. The diffusion coefficient of CO₂ was found to increase with concentration of dissolved CO₂, which is pressure‐dependent, and decrease with increasing DG in the range of 50–100%. A free‐volume‐based diffusion model proposed by Areerat was employed to predict the CO₂ diffusivity in terms of pressure, temperature, and the concentration of dissolved CO₂. S‐L EOS was once more used to determine the specific free volume of the mixture system. The predicted diffusion coefficients showed to correlate well with the measured values for all starch–water mixtures. © 2005 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 607–621, 2006     

Probing the use of small‐angle light scattering for characterizing structure of titanium dioxide/low‐density polyethylene nanocomposites

Small‐angle light scattering (SALS) measurements were used to study the structure of titanium dioxide (TiO₂)/low‐density polyethylene (LDPE) nanocomposites. The results showed that the scattering from LDPE crystalline structures and the scattering from TiO₂ nanoparticles can be resolved and separated. It is shown that the independent effects of crystallization conditions and the presence of nanoparticle aggregates on the spherulitic structure of the LDPE matrix can be determined by analyzing the scattering patterns using the methods proposed. From the SALS results, we conclude that the nanoparticle surface chemistry affects both nucleation of spherulites and their structure particularly under rapid cooling conditions. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 1084–1095, 2006     

Acrylic acid level and adhesive performance and peel master‐curves of acrylic pressure‐sensitive adhesives

Three series of pressure‐sensitive adhesives were prepared with constant glass‐transition temperature, using emulsion polymerization. The monomers chosen were butyl acrylate, 2‐ethylhexyl acrylate (EHA), methyl methacrylate (MMA), and acrylic acid (AA). Within each polymer series, the proportion of AA monomer was held constant for each polymer preparation but acrylic ester monomer levels were varied. Adhesion performance was assessed by measurement of loop tack, static shear resistance, and through the construction of peel master‐curves. Peel master‐curves were generated through peel tests conducted over a range of temperatures and peel rates and through application of the time–temperature superposition principle. Bulk effects dominated by polymer zero shear viscosity change as AA and EHA levels were varied were attributed to the observed effect on static shear resistance and the horizontal displacements of peel master‐curves. Static shear resistance was found to strongly correlate with log(a_C), a parameter introduced to horizontally shift peel master‐curves to form a superposed, “super master‐curve”. An interfacial interaction was proposed to account for deviations observed when loop tack was correlated with log(a_C). Surface rearrangements via hydrogen bonding with the test substrate were suggested as responsible for the interfacial interaction. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 1237–1252, 2006