Thermal, thermomechanical, and caloric properties of commercial orthodontic wires (produced by Natural Orthodontics Corp., USA) with cylindrical and rectangular geometry were studied. Depending on the applied forces, there were identified the range of elasticity, the elasticity–viscoelasticity coexistence domain and the domain in which a maximum force of 18 N is applied, for the orthodontic wires. When increasing the thickness of orthodontic wires, deformation decreases. The Controlled Force Module, in the tension mode, was used for the determination of the orthodontic wires elongation at application of the stretching forces from 0 to 13 N, at 35 °C, maintaining each static force value for 3 min. The increase in the cross-sectional area of the orthodontic wires disfavors the process of elongation of the sample, at the same applied static force. Using the Multi-Frequency–Strain–Stress modulus, in the tension mode, DMA cyclic heating–cooling measurements were performed. The measured physical quantities for orthodontic wires were Storage Modulus, Loss Modulus, Tanδ and Stiffness, at heating and cooling. Thus, the characteristic temperatures of the phase transitions (As, Af, Ms, Mf), of all the studied orthodontic wires were identified. Also, the values of the elasticity modulus (Young’s Modulus) of the orthodontic wires were calculated at 35 °C. With the DSC Q200 device, using temperature-modulated differential scanning calorimetry method, a multi-step temperature variation program, was applied to a rectangular wire, in three stages (cooling–heating–cooling). Through the interpretation of heat fluxes (reversible, irreversible and total), the phase transitions in the formation of martensite, austenite, but also of the rombohedral phase (R-phase), were identified. Formations of austenite and martensite were also evidenced by the classical DSC method, but the classical DSC method also enabled the R-phase identification. The adherence of some food dyes on the orthodontic wires, as well as the modification of the surface roughness of the orthodontic wire after the deposition of the food dye, was also studied. By magnetic measurements, it was established that the orthodontic wires had paramagnetic properties at room temperature, and nitinol was a mixture of 49.2% austenite and 50.8% martensite.
Recently, esters have received much attention as transmetalation partners for cross‐coupling reactions. Herein, we report a systematic study of the reactivity of a series of esters and thioesters with [{(dtbpe)Ni}2(μ‐η2:η2‐C6H6)] (dtbpe=1,2‐bis(di‐tert‐butyl)phosphinoethane), which is a source of (dtbpe)nickel(0). Trifluoromethylthioesters were found to form η2‐carbonyl complexes. In contrast, acetylthioesters underwent rapid Cacyl?S bond cleavage followed by decarbonylation to generate methylnickel complexes. This decarbonylation could be pushed backwards by the addition of CO, allowing for regeneration of the thioester. Most of the thioester complexes were found to undergo stoichiometric cross‐coupling with phenylboronic acid to yield sulfides. While ethyl trifluoroacetate was also found to form an η2‐carbonyl complex, phenyl esters were found to predominantly undergo Caryl?O bond cleavage to yield arylnickel complexes. These could also undergo transmetalation to yield biaryls. Attempts to render the reactions catalytic were hindered by ligand scrambling to yield nickel bis(acetate) complexes, the formation of which was supported by independent syntheses. Finally, 2‐naphthyl acetate was also found to undergo clean Caryl?O bond cleavage, and although stoichiometric cross‐coupling with phenylboronic acid proceeded with good yield, catalytic turnover has so far proven elusive. 相似文献
Synthesis and studies of graphite oxide started more than 150 years ago and turned into a boom by the measurements of the outstanding physical properties of graphene. A series of preparation protocols emanated trying to optimize the synthesis of graphene oxide in order to obtain a less defective material, as source for graphene. However, over-oxidation of the carbon framework hampered establishing structure-property relationships. Here, the fact that two different synthetic methods for graphene oxide preparation lead to very similar types of graphene oxide with a preserved graphene lattice is demonstrated. Either sodium chlorate in nitric acid (similar to Brodie's method) or potassium permanganate in sulfuric acid (similar to Hummers’ method) treatment are possible; however, reaction conditions must be controlled. With a preserved carbon lattice analytical differences between the samples relate to the altered on-plane functionality. Consequently, terming preparation protocols “according to Brodie's/Hummers’ method” is not sufficient. 相似文献