Nitroxide‐mediated radical polymerization of 2‐(dimethylamino)ethyl acrylate and its sequential block copolymerization with styrene and N‐butyl acrylate

Nitroxide‐mediated radical polymerization (NMRP) of 2‐(dimethylamino)ethyl acrylate (DMAEA) was carried out at 100–120 °C, initiated by MONAMS, an alkoxyamine based on N‐tert‐butyl‐N‐(1‐diethyl phosphono‐2,2‐dimethylpropyl)nitroxide, SG1. Controlled polymerization can be achieved by the addition of free SG1 (the initial molar ratio of SG1 to MONAMS ranged from 0.06 to 0.12), giving a linear first‐order kinetic plot up to 55–70% conversion depending on the reaction conditions. The molecular weights show a near linear increase with conversion; however, they deviate to some extent with theoretical values. SG1‐mediated polymerization of DMAEA at 112 °C is also controlled in organic solvents (N,N‐dimethylformide, anisole, xylene). Polymerization rate increases with increasing solvent polarity. Chain transfer to polymer produces ～1 mol % branches in bulk and 1.2–1.9 mol % in organic solvents, typical of those for acrylates. From poly(styrene) (pS) and poly(n‐butyl acrylate) (pBA) macroinitiators, amphiphilic di‐ and triblock copolymers p(S‐b‐DMAEA), p(DMAEA‐b‐S‐b‐DMAEA), p(BA‐b‐DMAEA), and p(DMAEA‐b‐BA‐b‐DMAEA) were synthesized via NMRP at 110 °C. Polymers were characterized by GPC, NMR, surface tension measurements, and DSC. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 414–426, 2006     

Sulfonated poly(aryl ether ether ketone ketone)s containing fluorinated moieties as proton exchange membrane materials

A series of sulfonated poly(aryl ether ether ketone ketone)s statistical copolymers with high molecular weights were synthesized via an aromatic nucleophilic substitution polymerization. The sulfonation content (SC), defined as the number of sulfonic acid groups contained in an average repeat unit, could be controlled by the feed ratios of monomers. Flexible and strong membranes in sodium sulfonate form could be prepared by the solution casting method, and readily transformed to their proton forms by treating them in 2 N sulfuric acid. The polymers showed high T_gs, which increased with an increase in SC. Membranes prepared from the present sulfonated poly(ether ether ketone ketone) copolymers containing the hexafluoroisopropylidene moiety (SPEEKK‐6F) and copolymers containing the pendant 3,5‐ditrifluoromethylphenyl moiety (SPEEKK‐6FP) had lower water uptakes and lower swelling ratios in comparison with previously prepared copolymers containing 6F units. All of the polymers possessed proton conductivities higher than 1 × 10^?2 S/cm at room temperature, and proton conductivity values of several polymers were comparable to that of Nafion at high relative humidity. Their thermal stability, oxidative stability, and mechanical properties were also evaluated. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 2299–2310, 2006     

Quantum relativistic action at a distance

A well-known relativistic action at a distance interaction of two unequal masses is altered so as to yield purely Newtonian radial forces with fixed particle rest masses in the system center-of-momentum inertial frame. Although particle masses experience no kinematic mass increase in this frame, speeds are naturally restricted to less than the speed of light. We derive a relation between the center-of-momentum frame total Newtonian energy and the composite rest mass. In a new proper time quantum formalism, we obtain an L²(R⁴ R⁴, C) Hilbert space by varying individual particle rest masses. We propose the use of density operators, recognizing that the auxiliary proper time parameter is not an observable. The quantum formalism is applied to our altered version of the relativistic harmonic oscillator. Our generalized coherent states yield four-dimensional wave packets which follow the correct classical world lines. Appendices contain reviews of classical Hamiltonian reparametrization (incorporating our notion of manifest covariance), and a comparison of this work with the literature.     

4-Amino-imidazole durchThorpe-Cyclisierung

The alkylation of arylaminomethylenecyanamides1 or cyano-imidothiocarbamates2 with -halogen carbonyl compounds followed by base catalysed cyclization yields substituted 4-amino-imidazoles4. Imidazo[4,5-d]pyrimidones5, 6 and imidazo[4,5-b]pyridines7 can be obtained from4.     

The electrocapillarity of polyacrylates

Summary The electrocapillary properties of polyacrylic acid have been studied by two methods. Exploratory measurements have been made of the effect of the polymer on the differential capacity of a mercury drop in 0.1 m sodium perchlorate. They showed that the polymer was strongly adsorbed over a wide range of potentials but that it did not appear to form a monolayer. The surface excess of polymer obtained from drop weight data showed a maximum at very low concentrations and then a decline at higher concentrations. The bulk of the work was carried out by making surface tension measurements, using a sessile mercury drop, in solutions of a fraction of polyacrylic acid (mol. wt. 7.02×10⁴) in potassium chloride at 0.01, 0.1, 0.2, and 0.5 m at 25°C.The data have been used to evaluate the surface excesses of the polymer and of the inorganic ions. The distribution of K⁺ and Cl^– in the electrical double layer and the contact adsorption of Cl^– on the mercury were very little affected by the presence of the polymer. The surface excess of polymer was always found to be greatest at low concentrations, to decrease steeply at first as the concentration was increased and then to decrease more slowly at higher concentrations.Possible explanations of this behaviour are discussed and it is concluded that the rapid decrease is a consequence of molecular weight dispersion and the stronger adsorption of high molecular weight polymer. The slow decrease in surface excess at higher concentrations may be a result of configurational changes of the polymer molecules.Surface pressure data show that, despite this decrease in the surface excess, the surface coverage reaches a high level at very low polymer concentrations and then continues to increase slowly as the concentration of polymer is increased. This apparent contradiction is due to changes in configuration of the adsorbed polymer molecules. At higher bulk concentrations the chain configurations are more compact and each adsorbed molecule makes more contacts with and so occupies a greater area of the mercury surface than at low concentrations.The conclusion is reached that the surface excess of polymer is mostly contained in a layer probably more than 1000 Å thick. It consists of a concentrated and entangled mass of polymer chains. Relatively few of these chains are in contact with the mercury at any istant. The concentration in this surface layer decreases steadily with increasing distance from the mercury surface and it merges without discontinuity into the bulk solution.With 10 figures in 22 details     

Zur Katalysierten Verflüchtigung von rotem Phosphor und von Claudetit

The Catalysed Volatilization of Red Phosphorus and of Claudetite The catalysis of the volatilization of P_red (as P₄) by AlCl_3,g, and of the volatilization of claudetite (as As₄O₆) by I_2,g is observed by mass spectrometry.     

Stereochemie von Metallocenen, 40. Mitt.

Starting from optically active methylferrocene-- and--carboxylic acids (1 a and1 b) of known absolute configuration and enantiomeric purity about 15 chiral ferrocenes (of each isomeric series— and ) were obtained by suitable ligand transformations. Thereby (almost) all possible chiral combinations of the ligands CH₃, COOH (COO^–), COOCH₃, CN and NH₂ (NH₃ ⁺) were accessible which are necessary for a potential test of approximations of chirality functions for compounds with basic symmetry C_5v. The chiroptical properties of these disubstituted ferrocenes are recorded.Preliminary tests using a shortened Ansatz revealed large discrepancies between calculated () and found [M]_D-values. Possible reasons for this failure are discussed.

---

---

61. Mitt. über Ferrocenderivate

---

39. Mitt.:A. Meyer, H. Neudeck undK. Schlögl, Chem. Ber.110, 1403 (1977).

---

60. Mitt.:V. Rapi, K. Schlögl undB. Steinitz, J. Organometal. Chem.94, 87 (1975).