Mechanistic Aspects of a Highly Active Dinuclear Zinc Catalyst for the Co‐polymerization of Epoxides and CO2

The dinuclear zinc complex reported by us is to date the most active zinc catalyst for the co‐polymerization of cyclohexene oxide (CHO) and carbon dioxide. However, co‐polymerization experiments with propylene oxide (PO) and CO₂ revealed surprisingly low conversions. Within this work, we focused on clarification of this behavior through experimental results and quantum chemical studies. The combination of both results indicated the formation of an energetically highly stable intermediate in the presence of propylene oxide and carbon dioxide. A similar species in the case of cyclohexene oxide/CO₂ co‐polymerization was not stable enough to deactivate the catalyst due to steric repulsion.     

Anisotropic Elastic-Viscoplastic Properties at Finite Strains of Injection-Moulded Low-Density Polyethylene

Injection-moulding is one of the most common manufacturing processes used for polymers. In many applications, the mechanical properties of the product is of great importance. Injection-moulding of thin-walled polymer products tends to leave the polymer structure in a state where the mechanical properties are anisotropic, due to alignment of polymer chains along the melt flow direction. The anisotropic elastic-viscoplastic properties of low-density polyethylene, that has undergone an injection-moulding process, are therefore examined in the present work. Test specimens were punched out from injection-moulded plates and tested in uniaxial tension. Three in-plane material directions were investigated. Because of the small thickness of the plates, only the in-plane properties could be determined. Tensile tests with both monotonic and cyclic loading were performed, and the local strains on the surface of the test specimens were measured using image analysis. True stress vs. true strain diagrams were constructed, and the material response was evaluated using an elastic-viscoplasticity law. The components of the anisotropic compliance matrix were determined together with the direction-specific plastic hardening parameters.     

Synthesis of Polyol Tetrabromophthalate and Its Use as a Component for Preparing Foamed Polyurethanes of Reduced Flammability

A procedure was suggested for preparing brominated polyols of reduced viscosity for the synthesis of foamed polyurethanes of reduced flammability. The flame-retarding action of the synthesized polyol tetrabromophthalate in polyurethane was studied in comparison with that of other widely used flame retardants. Evaluation of the effect exerted on the flammability of the polurethane compound by the polyol tetrabromophthalate synthesized, melamine, and aluminum hydroxide shows that all the samples containing flame retardants are self-extinguishing. The shortest combustion time was observed for the sample containing 6% polyol tetrabromophthalate synthesized. The sample containing as a flame retardant additive solely the synthesized polyole tetrabromophthalate also exhibits the highest performance as a heat-insulating material from the viewpoint of thermal conductivity.

     

Formation and pharmacological activity of silicon—chitosan-containing glycerohydrogels obtained by biomimetic mineralization

The biomimetic sol—gel synthesis of silicon—chitosan-containing glycerohydrogels was carried out using silicon tetraglycerolate as a precursor. It was found that chitosan accelerates gel formation in weakly acidic media. In more acidic media, the kinetics of the process changes according to the curve with a maximum, which can be attributed to different mechanisms of silanol condensation before and after the isoelectric point. The investigated silicon—chitosan-containing glycerohydrogels exhibit antibacterial, anti-inflammatory, and wound healing activity. The synthesized hybrid glycerohydrogels are promising materials for biomedical applications.