The influence of hard‐segments on two‐phase structure and shape memory properties of PCL‐based segmented polyurethanes

Poly(ε‐caprolactone)‐based segmented polyurethanes (PCLUs) were prepared from poly(ε‐caprolactone) diol, diisocyanates (DI), and 1,4‐butanediol. The DIs used were 4,4′‐diphenylmethane diisocyanate (MDI), 2,4‐toluenediisocyanate (TDI), isophorone diisocyanate (IPDI), and hexamethylene diisocyanate (HDI). Differential scanning calorimetry, small‐angle X‐ray scattering, and dynamic mechanical analysis were employed to characterize the two‐phase structures of all PCLUs. It was found that HDI‐ and MDI‐based PCLUs had higher degree of microphase separation than did IPDI‐ and TDI‐based PCLUs, which was primarily due to the crystallization of HDI‐ and MDI‐based hard‐segments. As a result, the HDI‐based PCLU exhibited the highest recovery force up to 6 MPa and slowest stress relaxation with increasing temperature. Besides, it was found that the partial damage in hard‐segment domains during the sample deformation was responsible for the incomplete shape‐recovery of PCLUs after the first deformation, but the damage did not develop during the subsequent deformation. © 2007 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 45: 557–570, 2007     

Bis[μ‐1‐(1,10‐phenanthrolin‐2‐yl)‐2‐pyridone]bis{aqua[1‐(1,10‐phenanthrolin‐2‐yl)‐2‐pyridone]cadmium(II)} tetrakis(perchlorate)

In the title centrosymmetric binuclear complex, [Cd₂(C₁₇H₁₁N₃O)₄(H₂O)₂](ClO₄)₄, the Cd^II ion assumes a distorted octahedral geometry. There are π–π stacking interactions between the pyridine and 1,10‐phenanthroline ring systems of adjacent ligands at the same Cd^II centre. Intermolecular hydrogen bonds between the coordinated aqua ligand and the O atom of a keto group connect adjacent complex cations into extended chains. Hydrogen bonds also exist between the complex cations and the perchlorate anions. Compared with the fluorescence spectrum of the organic ligand, the complex displays strong fluorescent emission and an ipsochromic shift of the emission peaks, which may be attributed to the structural character.     

Crystallographic report: Crystal structure of tetra(4‐methyl‐5‐imidazole‐carboxyaldehyde)zinc(II) diperchlorate

The central zinc(II) atom in the title complex is tetrahedrally coordinated by four nitrogen atoms derived from 4‐methyl‐5‐imidazolecarboxyaldehyde ligands with Zn? N in the range 2.007(3) to 2.026(4) Å. Copyright © 2003 John Wiley & Sons, Ltd.     

Synthesis and nuclear magnetic resonance analysis of starch‐g‐poly(1,4‐dioxan‐2‐one) copolymers

A new biodegradable starch graft copolymer, starch‐g‐poly(1,4‐dioxan‐2‐one), was synthesized through the ring‐opening graft polymerization of 1,4‐dioxan‐2‐one onto a starch backbone. The grafting reactions were conducted with various 1,4‐dioxan‐2‐one/starch feed ratios to obtain starch‐g‐poly(1,4‐dioxan‐2‐one) copolymers with various poly(1,4‐dioxan‐2‐one) graft structures. The microstructure of starch‐g‐poly(1,4‐dioxan‐2‐one) was characterized in detail with one‐ and two‐dimensional NMR spectroscopy. The effect of the feed composition on the resulting microstructure of starch‐g‐poly(1,4‐dioxan‐2‐one) was investigated. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 3417–3422, 2004     

WAXS studies on block copolymers of ethylene and propylene

Wide-angle X-ray scattering from presumed block copolymers of polypropylene (PP) and ethylene-propylene copolymer (EPR), i.e., PP-EPR and PP-EPR-PP, synthesized by sequential polymerization with δ-TiCl₃? Et₂AlCl, was examined and compared with WAXS of mechanical blends and chain-transfer mixtures of PP and EPR with comparable compositions. The peak at 2θ = 20° for both the copolymers and the mixtures was attributed to the γ modification of PP in EPR. A strong variation in the ratio of diffraction intensities I₀₄₀/I₁₁₀ of PP in block copolymers and mixtures was explained in terms of crystallite growth in different directions. Analysis of the patterns and calculation of crystallinity, crystallite size, and lattice parameters led to the conclusion that block structure existed in the prepared copolymers.     

Ethylene–propylene copolymerization with bis(β‐enaminoketonato) titanium complexes activated with modified methylaluminoxane

Ethylene–propylene copolymerization, using [(Ph)NC(R₂)CHC(R₁)O]₂TiCl₂ (R₁ = CF₃, Ph, or t‐Bu; R₂ = CH₃ or CF₃) titanium complexes activated with modified methylaluminoxane as a cocatalyst, was investigated. High‐molecular‐weight ethylene–propylene copolymers with relatively narrow molecular weight distributions and a broad range of chemical compositions were obtained. Substituents R₁ and R₂ influenced the copolymerization behavior, including the copolymerization activity, methylene sequence distribution, molecular weight, and polydispersity. With small steric hindrance at R₁ and R₂, one complex (R₁ = CF₃; R₂ = CH₃) displayed high catalytic activity and produced copolymers with high propylene incorporation but low molecular weight. The microstructures of the copolymers were analyzed with ¹³C NMR to determine the methylene sequence distribution and number‐average sequence lengths of uninterrupted methylene carbons. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 5846–5854, 2006     

Highly soluble and optically transparent poly (ether imide)s based on 2,6‐ or 2,7‐bis(3,4‐dicarboxyphenoxy)naphthalene dianhydride and aromatic bis(ether amine)s bearing trifluoromethyl groups

Two series of novel fluorinated poly(ether imide)s (coded IIIA and IIIB ) were prepared from 2,6‐bis(3,4‐dicarboxyphenoxy)naphthalene dianhydride and 2,7‐bis(3,4‐dicarboxyphenoxy)naphthalene dianhydride, respectively, with various trifluoromethyl‐substituted aromatic bis(ether amine)s by a standard two‐step process with thermal or chemical imidization of the poly(amic acid) precursors. These fluorinated poly(ether imide)s showed good solubility in many organic solvents and could be solution‐cast into transparent, flexible, and tough films. These films were nearly colorless, with an ultraviolet–visible absorption edge of 364–386 nm. They also showed good thermal stability with glass‐transition temperatures of 221–298 °C, 10% weight loss temperatures in excess of 489 °C, and char yields at 800 °C in nitrogen greater than 50%. The 2,7‐substituted IIIB series also showed better solubility and higher transparency than the isomeric 2,6‐substituted IIIA series. In comparison with nonfluorinated poly (ether imide)s, the fluorinated IIIA and IIIB series showed better solubility, higher transparency, and lower dielectric constants and water absorption. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 5909–5922, 2006     

Synthesis and characterization of novel perfluorinated polyimides with 3D‐controlled structures for photonic applications

We have designed and synthesized novel perfluorinated polyimides with 3D controlled structure. At first, we successfully developed the new synthetic routes to diamines with pendant bulky perfluorinated aromatic units in a multi‐step synthetic procedure. Novel perfluorinated polyimides were prepared in a two‐step reaction in N‐methyl‐2‐pyrrolidinone (NMP) solution: The first step was for the synthesis of polyamic acids (PAAs) and the second reaction was for the imidization of PAA. The polymer yield was over 89% and the inherent viscosity of PAAs was in the range of 0.24–0.36 dL/g. The thin films were prepared by spin‐coating the PAA solution in NMP onto various substrates such as a Si wafer or a KBr pellet, dried at 80 °C and further cured at 230 °C. The resultant polyimides are thermally stable over 400 °C. The refractive index and birefringence of the resultant polyimides are 1.5858–1.6452 and 0.01–0.005, respectively. The refractive index of polyimide decreases with increasing the fluorine content. The copolymerization and the ether linkages into the backbone reduce the birefringence of polyimides. Surprisingly, the pendant ether linkage is not a crucial factor in reducing the polyimide birefringence. Their birefringence is comparatively very low, compared with that of previous polyimides. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 1326–1342, 2006     

Crystal structure and morphology of phenyl‐capped tetraaniline in the leucoemeraldine oxidation state

A series of crystals of phenyl‐capped tetraaniline in the leucoemeraldine oxidation state were obtained at different isothermal temperatures and were observed directly under transmission electron microscope. The crystals obtained at higher temperatures exhibit more perfect structures than those obtained at lower temperatures. Both the lamella thickness and the crystal size increase with crystallization temperature. The tetraaniline is apt to form larger scale crystals under lower degree of supercooling. However, their crystal structures keep steady with the crystallization temperature. The tetramer was found to adopt a monoclinic lattice with unit cell parameter of a = 13.93 Å, b = 8.82 Å, c = 23.20 Å, and β = 95.03°, as determined using electron diffraction tilting method combined with wide‐angle X‐ray diffraction experiment. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 764–769, 2006     

Melting behaviors,crystallization kinetics,and spherulitic morphologies of poly(butylene succinate) and its copolyester modified with rosin maleopimaric acid anhydride

This article investigated the melting behaviors, crystallization kinetics, and spherulitic morphologies of poly(butylene succinate) (PBS) and its copolyester (PBSR) modified with rosin maleopimaric acid anhydride, using wide‐angle X‐ray diffraction, differential scanning calorimeter (DSC), and polarized optical microscope. Subsequent DSC scans of isothermally crystallized PBS and PBSR exhibited two melting endotherms, respectively, which was due to the melt‐recrystallization process occurring during the DSC scans. The equilibrium melting point of PBSR (125.9 °C) was lower than that of PBS (139 °C). The commonly used Avrami equation was used to describe the isothermal crystallization kinetics. For nonisothermal crystallization studies, the model combining Avrami equation and Ozawa equation was employed. The result showed a consistent trend in the crystallization process. The crystallization rate was decreased, the perfection of crystals was decreased, the recrystallization was reduced, and the spherulitic morphologies were changed when the huge hydrogenated phenanthrene ring was added into the chain of PBS. The activation energy (ΔE) for the isothermal crystallization process determined by Arrhenius method was 255.9 kJ/mol for PBS and 345.7 kJ/mol for PBSR. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 900–913, 2006