Asymptotic Analysis of the Current-Voltage Curve of a pnpn Semiconductor Device

We consider the one-dimensional steady-state semiconductor deviceequations modelling a pnpn device. There are two relevant scalingsof the equations corresponding to small and large applied voltages.In both scalings, the semiconductor equations can be consideredas singularly perturbed. It turns out that the small-voltagescaling breaks down for current values between two saturationcurrents. In that interval, the large-voltage scaling has tobe employed. For both scalings, we derive the first-order termsof an asymptotic expansion and show that the reduced problemhas a solution. An example verifies that the current-voltagecurves obtained have the expected qualitative structure.     

Electrical properties of neodymium doped CaBi4Ti4O15 ceramics

Neodymium doped bismuth layer structure ferroelectrics (BLSFs) ceramics CaBi_4−xNd_xTi₄O₁₅ (x=0, 0.25, 0.50, 0.75) were prepared by solid-state reaction method. X-ray diffraction pattern showed that single phase was formed when x=0-0.75. The refined lattice parameters showed that a (b) axes decrease at x=0.25 and increase with more Nd³⁺ dopant. The effects of Nd³⁺ doping on the dielectric and ferroelectric properties of CaBi₄Ti₄O₁₅ ceramics are studied. Nd³⁺ dopant decreased the Curie temperature linearly, and the dielectric loss, tan δ, as well. The remnant polarization of Nd³⁺ doped CaBi₄Ti₄O₁₅ ceramics was increased by 80% at x=0.25, while more Nd³⁺ dopant decreased the remnant polarization. CaBi_3.75Nd_0.25Ti₄O₁₅ ceramics had the largest piezoelectric constant d₃₃. The structure and properties of CaBi_4−xNd_xTi₄O₁₅ ceramics showed that Nd³⁺ may occupy different crystal locations when Nd³⁺ content x is less than 0.25 and more than 0.50.     

Low Cost, High Efficiency, Gain Flattened L Band EDFA Using FBGs as C Band Seed Generators

A low cost, coolerless 980nm diode pumped, gain flattened L band EDFA with fast transient control, high pump efficiency and gain clamping effect was realized by using FBGs as C band seed generators.     

Preparation and characterization of acrylic‐based black particles of poly(methyl methacrylate‐co‐ethylene glycol dimethacrylate) by dispersion polymerization for electrophoretic displays

Ultrafine black particles, ranging in diameter from 1 to 3 μm, were prepared by dispersion polymerization in a methanol/water mixture with vinyl monomers, nonpolymerizable Sudan black B dyes, and fluorescein isothiocyanate labeled charge control additives. Both the ratio of the methanol to the water dispersion medium and the polymeric stabilizer concentration had significant effects on the particle size. The important role of the stabilizer concentration lay in the particle formation step, during which it determined the particle stability and final particle size. These could affect the extent of the aggregation of nuclei by changing the adsorption rate of the stabilizer and the viscosity of the dispersion medium, resulting in smaller particles. The fluorescent‐labeled charge control additives strongly affected the electrophoretic mobility. A small concentration of fluorescent‐labeled charge control additives increased the electrophoretic mobility. However, a further addition reduced the electrophoretic mobility of the polymer particles. The concentration dependence of the fluorescent‐labeled charge control additives on the deposition behavior in the polymer particles was successfully imaged and thereafter quantified by image analysis. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 5608–5616, 2004     

Intramolecular energy transferable (2,2‐diphenylvinyl)phenyl substituted poly(p‐phenylenevinylene) derivative with efficient photoluminescence and electroluminescence

A poly(p‐phenylenevinylene) (PPV) derivative containing a bulky (2,2‐diphenylvinyl)phenyl group in the side chain, EHDVP‐PPV, was synthesized by Gilch route. The reduced tolane‐bisbenzyl (TBB) defects, as well as the structure of the polymer, was confirmed by various spectroscopic methods. The intramolecular energy transfer from the (2,2‐diphenylvinyl)phenyl side group to the PPV backbone was studied by UV‐vis and photoluminescence (PL) of the obtained polymer and model compound. The polymer film showed maximum absorption and emission peaks at 454 and 546 nm, respectively, and high PL efficiency of 57%. A yellow electroluminescence (λ_max = 548 nm) was obtained with intensities of 6479 cd/m² when the light‐emitting diodes of ITO/PEDOT/EHDVP‐PPV/LiF/Al were fabricated. The maximum power efficiency of the devices was 0.729 lm/W with a turn‐on voltage of 3.6 V. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 5636–5646, 2004     

Composite Silica Particles Using a Mixture of Organosilane Monomers

Composite silica particles were synthesized by a two-step (acid-base) process in an aqueous solution with a mixture of organoalkoxysilane monomers. The two-step process separates the hydrolysis and condensation procedures to easily control condensation rate. In this study, the silane monomers used were phenyltrimethoxysilane (PTMS), vinyltrimethoxysilane (VTMS), methyltrimethoxysilane (MTMS), and tetraethyl-orthosilicate (TEOS). The physical properties of the resultant composite particles were investigated with the change in the molar ratio of monomers. The size of the particles increased with increasing the molar ratio of R_aSi(OR)₃/R_bSi(OR)₃ or R_aSi(OR)₃/TEOS (R_a: phenyl; R_b: vinyl, methyl).     

Relationship between the dynamic softening transition and wet sliding friction of elastomer compounds

For properly chosen elastomer compounds, thermorheological characterization is combined with an examination of the variation of the wet sliding friction with temperature. A conceptual argument leads to the assumption that the wet sliding friction should maximize at the energy dissipation peak associated with the dynamic softening transition at a characteristic frequency determined by the sliding speed and the effective smallest surface asperity scale. The dynamic softening transition is characterized with the peak in tan δ/G′ⁿ, where tan δ is the loss tangent, G′ is the elastic modulus, and n is a constant between 0 and 1. The William–Landel–Ferry transform is uncritically applied for extrapolating the position of the peak in tan δ/G′ⁿ at high frequencies. Even based on the criterion of tan δ, the results obtained on a concrete surface indicate that the effective smallest asperity scale is of order of 100 μm. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 2467–2478, 2004     

Effects of poly[styrene‐b‐(ethylene‐co‐butylene)‐b‐styrene] on the charge distributions of low‐density polyethylene/polystyrene blends

The effect of the triblock copolymer poly[styrene‐b‐(ethylene‐co‐butylene)‐b‐styrene] (SEBS) on the formation of the space charge of immiscible low‐density polyethylene (LDPE)/polystyrene (PS) blends was investigated. Blends of 70/30 (wt %) LDPE/PS were prepared through melt blending in an internal mixer at a blend temperature of 220 °C. The amount of charge that accumulated in the 70% LDPE/30% PS blends decreased when the SEBS content increased up to 10 wt %. For compatibilized and uncompatibilized blends, no significant change in the degree of crystallinity of LDPE in the blends was observed, and so the effect of crystallization on the space charge distribution could be excluded. Morphological observations showed that the addition of SEBS resulted in a domain size reduction of the dispersed PS phase and better interfacial adhesion between the LDPE and PS phases. The location of SEBS at a domain interface enabled charges to migrate from one phase to the other via the domain interface and, therefore, resulted in a significant decrease in the amount of space charge for the LDPE/PS blends with SEBS. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 2813–2820, 2004     

Fabrication and Characteristics of Sol-Gel Derived Fluorinated Hybrid Material Films

Fluorinated inorganic-organic hybrid materials (HYBRIMER) were successfully prepared from fluoroalkylsilanes (FASs) containing fluoro-alkyl functions and methacryloxypropyltrimethoxysilane (MPTMS) through a sol-gel process. The influence of concentration and fluoro-alkyl chain lengths of FASs on the physical characteristics of the fluorinated HYBRIMER films was examined. Larger fluorine contents lowered the refractive index within a range, which was closely dependent on the fluoro-alkyl chain lengths of FASs. Thermo-optic coefficients (TOC) were negative values, and the values grew with increasing fluorine contents and fluoro-alkyl chain lengths. Also, the thermal stability is enhanced by addition of fluorine in the HYBRIMER.