Antimicrobial activity on the copolymers of 2,4‐dichlorophenyl methacrylate with methyl methacrylate: Synthesis and characterization

Copolymers of monomers 2,4‐dichlorophenyl methacrylate (2,4‐DMA) and methyl methacrylate (MMA) were synthesized with different monomer feed ratios using toluene as a solvent and 2,2′‐azobisisobutyronitrile (AIBN) as an initiator at 70 °C. The copolymers were characterized by IR‐spectroscopy, and copolymer composition was determined with UV‐spectroscopy. The linearization method of Fineman–Ross was employed to obtain the monomer reactivity ratios. The molecular weights and polydispersity indexes were determined by gel permeation chromatography (GPC). Thermogravimetric analyses of polymers were carried out in nitrogen atmosphere. The homo‐ and copolymers were tested for their antimicrobial properties against selected microorganisms. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 5227–5234, 2004     

Tetrafunctional initiators for cationic polymerization of olefins

3,3′,5,5′‐Tetrakis(2‐chloro‐2‐propyl)biphenyl (biphenyl tetracumyl chloride, BPTCC) and 1,3‐bis[3,5‐bis(2‐chloro‐2‐propyl)phenoxy]propane (diphenoxypropane tetracumyl chloride, DPPTCC) were synthesized as initiators for quasiliving cationic polymerization of isobutylene (IB). In the synthesis of BPTCC, tetrafunctionality was achieved via the coupling of dimethyl 5‐bromoisophthalate (DMBI) using nickel dibromide bis(triphenylphosphine) and zinc in the presence of a base; in the synthesis of DPPTCC, two equivalents of dimethyl 5‐hydroxyisophthalate were linked via reaction with 1,3‐dibromopropane in the presence of potassium carbonate. Both initiators were used to initiate the polymerization of IB under quasiliving cationic polymerization conditions. PIB initiated from BPTCC revealed a chain end/molecule value (as determined by ¹H‐NMR) of 3.85, verifying the nearly exclusive production of 4‐arm polyisobutylene (PIB). GPC analysis revealed a narrow peak representing the target four‐arm PIB, with a slight shoulder at high elution volumes (low molecular weights). GPC analysis of the PIB initiated by DPPTCC revealed multimodal distributions, suggesting the formation of two‐, three‐, and four‐arm star polymers during the polymerization. This behavior was attributed to Friedel–Crafts alkylation of the initiator core after the addition of one IB unit, which was activated by the electron‐donating oxytrimethyleneoxy linking moiety. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 5942–5953, 2004     

Strain hardening of polycarbonate in the glassy state: Influence of temperature and molecular weight

This study is concerned with the temperature and molecular weight dependence of the strain-hardening behavior of polycarbonate. It is shown that the strain-hardening modulus reduces with increasing temperature and decreasing molecular weight. This result is interpreted in terms of temperature accelerated relaxation of the entanglement network. Moreover, it is shown that frozen-in orientations, induced by homogeneous deformations above the glass transition temperature, lead to anisotropic yield behavior that can be fully rationalized (and modelled) in terms of a superimposed stress contribution of the prestrained network. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 2041–2049, 2004     

Announcement of Proficiency Testing Schemes

Accreditation and Quality Assurance -     

Metallo‐supramolecular block copolymer micelles: Improved preparation and characterization

Micelles prepared from amphiphilic block copolymers in which a poly(styrene) segment is connected to a poly(ethylene oxide) block via a bis‐(2,2′:6′,2″‐terpyridine‐ruthenium) complex have been intensely studied. In most cases, the micelle populations were found to be strongly heterogeneous in size because of massive micelle/micelle aggregation. In the study reported in this article we tried to improve the homogeneity of the micelle population. The variant preparation procedure developed, which is described here, was used to prepare two “protomer”‐type micelles: PS₂₀‐[Ru]‐PEO₇₀ and PS₂₀‐[Ru]‐PEO₃₇₅. The dropwise addition of water to a solution of the compounds in dimethylformamide was replaced by the controlled addition of water by a syringe pump. The resulting micelles were characterized by sedimentation velocity and sedimentation equilibrium analyses in an analytical ultracentrifuge and by transmission electron microscopy of negatively stained samples. Sedimentation analysis showed virtually unimodal size distributions, in contrast to the findings on micelles prepared previously. PS₂₀‐[Ru]‐PEO₇₀ micelles were found to have an average molar mass of 318,000 g/mol (corresponding to 53 protomers per micelle, which is distinctly less than after micelle preparation by the standard method) and an average hydrodynamic diameter (d_h) of 18 nm. For PS₂₀‐[Ru]‐PEO₃₇₅ micelles, the corresponding values were M = 603,000 g/mol (31 protomers per micelle) and d_h = 34 nm. The latter particles were found to be identical to the “equilibrium” micelles prepared in pure water. Both micelle types had a very narrow molar mass distribution but a much broader distribution of s values and thus of hydrodynamic diameters. This indicates a conformational heterogeneity that is stable on the time scale of sedimentation velocity analysis. The findings from electron microscopy were in disagreement with those from the sedimentation analysis both in average micelle diameter and in the width of the distributions, apparently because of imperfections in the staining procedure. The preparation procedure described also may be useful in micelle formation from other types of protomers. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 4458–4465, 2004     

Completely biodegradable composites of poly(propylene carbonate) and short,lignocellulose fiber Hildegardia populifolia

The composites of biodegradable poly(propylene carbonate) (PPC) reinforced with short Hildegardia populifolia natural fiber were prepared by melt mixing followed by compression molding. The mechanical properties, thermal properties, and morphologies of the composites were studied via static and dynamic mechanical measurements, thermogravimetric analysis, and scanning electron microscopy (SEM) techniques, respectively. Static tensile tests showed that the stiffness and tensile strength of the composites increased with an increasing fiber content. However, the elongation at break and the energy to break decreased dramatically with the addition of short fiber. The relationship between the experimental results and the compatibility or interaction between the PPC matrix and fiber was correlated. SEM observations indicated good interfacial contact between the short fiber and PPC matrix. Thermogravimetric analysis revealed that the introduction of short Hildegardia populifolia fiber led to a slightly improved thermooxidative stability of PPC. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 666–675, 2004     

Fracture toughening of epoxy matrices with blends of resins of different molecular weights and other modifiers

The microstructure and fracture behavior of epoxy mixtures containing two monomers of different molecular weights were studied. The variation of the fracture toughness by the addition of other modifiers was also investigated. Several amounts of high‐molecular‐weight diglycidyl ether of bisphenol A (DGEBA) oligomer were added to a nearly pure DGEBA monomer. The mixtures were cured with an aromatic amine, showing phase separation after curing. The curing behavior of the epoxy mixtures was investigated with thermal measurements. A significant enhancement of the fracture toughness was accompanied by slight increases in both the rigidity and strength of the mixtures that corresponded to the content of the high‐molecular‐weight epoxy resin. Dynamic mechanical and atomic force microscopy measurements indicated that the generated two‐phase morphology was a function of the content of the epoxy resin added. The influence of the addition of an oligomer or a thermoplastic on the morphologies and mechanical properties of both epoxy‐containing mixtures was also investigated. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 3920–3933, 2004