Desorption behavior of a surfactant in a linear low‐density polyethylene blend at elevated temperatures

The desorption behavior of a surfactant in a linear low‐density polyethylene (LLDPE) blend at elevated temperatures of 50, 70, and 80 °C was studied with Fourier transform infrared spectroscopy. The composition of the LLDPE blend was 70:30 LLDPE/low‐density polyethylene. Three different specimens (II, III, and IV) were prepared with various compositions of a small molecular penetrant, sorbitan palmitate (SPAN‐40), and a migration controller, poly(ethylene acrylic acid) (EAA), in the LLDPE blend. The calculated diffusion coefficient (D) of SPAN‐40 in specimens II, III, and IV, between 50 and 80 °C, varied from 1.74 × 10^?11 to 6.79 × 10^?11 cm²/s, from 1.10 × 10^?11 to 5.75 × 10^?11 cm²/s, and from 0.58 × 10^?11 to 4.75 × 10^?11 cm²/s, respectively. In addition, the calculated activation energies (E_D) of specimens II, III, and IV, from the plotting of ln D versus 1/T between 50 and 80 °C, were 42.9, 52.7, and 65.6 kJ/mol, respectively. These values were different from those obtained between 25 and 50 °C and were believed to have been influenced by the interference of Tinuvin (a UV stabilizer) at elevated temperatures higher than 50 °C. Although the desorption rate of SPAN‐40 increased with the temperature and decreased with the EAA content, the observed spectral behavior did not depend on the temperature and time. For all specimens stored over 50 °C, the peak at 1739 cm^?1 decreased in a few days and subsequently increased with a peak shift toward 1730 cm^?1. This arose from the carbonyl stretching vibration of Tinuvin, possibly because of oxidation or degradation at elevated temperatures. In addition, the incorporation of EAA into the LLDPE blend suppressed the desorption rate of SPAN‐40 and retarded the appearance of the 1730 cm^?1 peak. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 1114–1126, 2004     

Novel fixed‐site–carrier polyvinylamine membrane for carbon dioxide capture

Fixed‐site–carrier membranes were prepared for the facilitated transport of CO₂ by casting polyvinylamine (PVAm) on various supports, such as poly(ether sulfone) (PES), polyacrylonitrile (PAN), cellulose acetate (CA), and polysulfone (PSO). The cast PVAm on the support was crosslinked by various methods with glutaraldehyde, hydrochloric acid, sulfuric acid, and ammonium fluoride. Among the membranes tested, the PVAm cast on polysulfone and crosslinked by ammonium fluoride showed the highest selectivity of CO₂ over CH₄ (>1000). The permeance of CO₂ was then measured to be 0.014 m³ (STP)/(m² bar h) for a 20 μm thick membrane. The effect of the molecular weight of PVAm and feed pressure on the permeance was also investigated. The selectivity increased remarkably with increasing molecular weight and decreased slightly with increased pressure in the range of 1 to 4 bar. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 4326–4336, 2004     

Pressure and temperature dependence of the gas‐transport properties of dense poly[2,6‐toluene‐2,2‐bis(3,4‐dicarboxylphenyl)hexafluoropropane diimide] membranes

The gas‐transport properties of poly[2,6‐toluene‐2,2‐bis(3,4‐dicarboxylphenyl)hexafluoropropane diimide] (6FDA‐2,6‐DAT) have been investigated. The sorption behavior of dense 6FDA‐2,6‐DAT membranes is well described by the dual‐mode sorption model and has certain relationships with the critical temperatures of the penetrants. The solubility coefficient decreases with an increase in either the pressure or temperature. The temperature dependence of the diffusivity coefficient increases with an increase in the penetrant size, as the order of the activation energy for the diffusion jump is CH₄ > N₂ > O₂ > CO₂. Also, the average diffusion coefficient increases with increasing pressure for all the gases tested. As a combined contribution from sorption and diffusion, permeability decreases with increases in the pressure and the kinetic diameter of the penetrant molecules. Even up to 32.7 atm, no plasticization phenomenon can be observed on flat dense 6FDA‐2,6‐DAT membranes from their permeability–pressure curves. However, just as for other gases, the absolute value of the heat of sorption of CO₂ decreases with increasing pressure at a low‐pressure range, but the trend changes when the feed pressure is greater than 10 atm. This implies that CO₂‐induced plasticization may occur and reduce the positive enthalpy required to create a site into which a penetrant can be sorbed. Therefore, a better diagnosis of the inherent threshold pressure for the plasticization of a glassy polymer membrane may involve examining the absolute value of the heat of sorption as a function of pressure and identifying the turning point at which the gradient of the absolute value of the heat of sorption against pressure turns from a negative value to a positive one. © 2003 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 354–364, 2004     

Bio‐based nanocomposites from functionalized plant oils and layered silicate

Some discovery work was done on the synthesis of clay nanocomposites based on renewable plant oils. Functionalized triglycerides, such as acrylated epoxidized soybean oil, maleinized acrylated epoxidized soybean oil, and soybean oil pentaerythritol maleates, combined with styrene were used as the polymer matrix. The miscibility of these monomers and clay organomodifier was assessed by solubility parameters. The formation of nanocomposites was confirmed by both X‐ray data and transmission electron microscopy. The morphology showed a mix of intercalated and partially exfoliated sheets. The flexural modulus increased 30% at only 4 vol % clay content, but there was no significant effect on flexural strength, glass‐transition temperature, and thermal stability. Property enhancement was related to the degree of exfoliation that depends on both the polarity and flexibility of the monomers. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 1441–1450, 2004     

Relationship between the dynamic softening transition and wet sliding friction of elastomer compounds

For properly chosen elastomer compounds, thermorheological characterization is combined with an examination of the variation of the wet sliding friction with temperature. A conceptual argument leads to the assumption that the wet sliding friction should maximize at the energy dissipation peak associated with the dynamic softening transition at a characteristic frequency determined by the sliding speed and the effective smallest surface asperity scale. The dynamic softening transition is characterized with the peak in tan δ/G′ⁿ, where tan δ is the loss tangent, G′ is the elastic modulus, and n is a constant between 0 and 1. The William–Landel–Ferry transform is uncritically applied for extrapolating the position of the peak in tan δ/G′ⁿ at high frequencies. Even based on the criterion of tan δ, the results obtained on a concrete surface indicate that the effective smallest asperity scale is of order of 100 μm. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 2467–2478, 2004     

Differential scanning calorimetry and thermogravimetric analysis investigation of the thermal properties and degradation of some radiation‐grafted films and membranes

The influence of irradiation and grafting on the crystallinity of three base polymers has been investigated with differential scanning calorimetry. Grafting has the largest effect on the base polymer crystallinity and results in a reduction of the crystallinity. The thermal degradation of the base polymers and grafted films has been investigated with thermogravimetric analysis. The extent of the fluorination of the base polymer, the irradiation method, and the graft level all influence the thermal degradation and its activation energy. It is proposed that the variation of the chain lengths of the grafted polystyrene chains is actually a primary underlying factor responsible for the influence of these various parameters on the degradation process. The first results of a comparative thermal analysis of some fuel‐cell membranes are also presented, and the promise and shortcomings of this method are discussed. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 2612–2624, 2004     

Colorimetric recognition of different enzymology-concerning transition metals based on a hybrid cluster complex.

A hybrid cluster complex, formed by chelating a chromogenic ligand to a [2Fe-2S] cluster, sensitively exhibited differential colorimetric responses towards Hg2+, Cd2+, Cr3+, Pb2, Sn2+, Cu2+, Zn2+, Fe3+ and Co2+ in water at physiological pH. Speciation of some of these metal elements, such as Cr(III) and Sn(IV), was also studied by UV/Vis absorption.     

波段三维ESR成像系统的研制（Ⅴ）——灵敏度与分辨率实验及系统总性能指标

实验确定了自行研制的L波段三维电子自旋共振成像（3D-ESRI）系统的检测灵敏度及成像分辨率指标. 用Tempo水溶液模型测量灵敏度结果表明： 样品体积为10 mm, 高30 mm，测量浓度1×10^-4 mol/L水溶液的信噪比为S/N=4∶1；加梯度磁场后，样品浓度需>5×10^-4 mol/L，样品体积为19 mm, 高30 mm时，获得的投影谱的信噪比可满足图像重建的需要. 用DPPH固体样品确定的成像分辨率结果<1 mm. 文中还对ESRI系统的
各项总体性能做了归纳总结.     

Zn(BTZ)2白色有机电致发光材料的合成及其器件制备

以PCl₃为脱水剂,将邻氨基硫酚与水杨酸脱水环化合成出2-(2-羟基苯基)苯并噻唑,并进一步将所得产物与乙酸锌反应合成出2-(2-羟基苯基)苯并噻唑螯合锌(Zn(BTZ)₂)材料。以该配合物作为发光层制备出结构为ITO/PVK:TPD/Zn(BTZ)₂/Al近白色电致发光器件,其色坐标位于白场之内(x=0.242,y=0.359),在驱动电压为16V时,亮度达3200cdm²,对应的量子效率为0.32%。进一步在Zn(BTZ)₂中掺入橙红色染料Rubrene,制成ITO/PVK:TPD/Zn(BTZ)₂:Rubrene/Al结构器件,实现了纯白色发光(色坐标值:x=0.324,y=0.343),非常接近于白色等能点,且量子效率达0.47%。最后对上述器件的发光和电学性能进行了深入的研究和探讨。     

Synthesis of Cationic PEM Emulsion and Application in Waste Water Treatment

Cationic polymer as a kind of flocculant is widely applied in purification treatment of waste water. Because it has positive charge group, it is able to connect strongly the suspended matters, short cellulose and other microparticles. The research on synthesis of cationic polymer and application in treatment of waste water is very universal abroad. But domestic research on those is not general. The technology of synthesis of PEM is simple, and the production cost is low. It is easy to apply in treatment of waste water.Synthesis of PEM Emulsion FlocculantSome distilled water, PVA(poly(vinyl alcohol)), EA(ethyl acrylate), and K2S2O8(potassium persulfate) were put into reaction vessel. Kept stirring up under nitrogen. When heated the solution to 40℃, dropped the water solution of MTA[(2-methacryloxylethyl)trimethyl ammonium].Maintained the temperature at 70℃, reacted about 7-8 hours. Then got the PEM emulsion. Changed the ratio of EA and MTA. Obtained a series of PEM emulsions.Stability and Convertibility of PEM EmulsionThe test results showed that when the EA/MTA was 85/15, the PEM emulsion was most stable.When the total monomer quantity was 35%, the convertibility of PEM emulsion was the highest,i.e.98.6%.The MTA Copolymerization Ratio and Morphology of PEM EmulsionWhen the monomers EA/MTA=85/15 and total monomer quantity was 35%, the MTA copolymerization ratio of PEM emulsion was 95.15%(the highest), and the PEM emulsion was some microspheres with 100-180nm of diameter.The Test Results of PEM Emulsion in Treatment of Waste Water The PEM emulsion flocculant was applied in treatment of waste water of paper mill, and measured the precipitation time(t) and transmittancy(T). The test results were showed in table 1. The optimum value of PEM which was able to make the waste water of paper mill into clear water was 0.008%.