The interaction between C60's in solid C60 has been calculated by (exp-6-1) potential, and the cause and the controlled factor of the high rapid rotations of C60 's were discussed. In order to describe the disordered degree of C60 rotation, an equivalent M is introduced. The phase transitions at the ~260 K and at the ~90 K are studied from the viewpoint of C60 rotation. The potential barriers of the ordered rotation below the ~260 K and the disordered rotation above the ~260 K have been given, and the effect of the external pressure on the temperature of phase transition has also been given.     

Density of supercritical CO_2-tetrahydrofuran binary mixture and the partial molar volume of the cosolvent

The densities of supercritical CO2-tetrahydrofuran (cosolvent) binary mixture weremeasured at temperatures in range of 308.15 to 323.15 K and at pressure up to 16.5 MPa.The concentrations of tetrahydrofuran were from 0 to 0.57 mol/L.The partial molar volume of tetrahydrofuran was calculated based on the relationship between the density of the mixture and the concentration of the cosolvent.It is observed that the partial molar volume of the cosolvent is negative and the absolute value decreases with increasing pressure and the concentration of the cosolvent.     

载银磷酸活化剑麻基活性炭纤维的抗菌性能研究

本文利用磷酸化方法，制备各种剑麻基活性炭纤维，并利用活性炭纤维的氧化还原特性及吸附性能，在其上负载金属银，研究并比较了这些载银活性炭纤维对大肠杆菌和金黄色葡萄球菌的杀灭作用，结果表明，磷酸浓度，活化方法，活化时间，纤维的比表面积等因素的均对材料的抗菌性能有一定的影响，磷酸活化的活性炭纤维表现出强的抗菌杀菌能力，高浓度磷酸活化后的纤维抗菌能力有所提高，并且抗菌能力随活化时间的延长而增加，抗菌前后纤维上负载的银未曾大量脱落，经5次抗菌试验后材料仍显示出很强的抗菌能力。     

二甲胺修饰戊二醛交联壳聚糖树脂的制备及性能

研究了在均匀水相介质条件下，采用戊二醛稀溶液制备交联壳聚糖树脂的方法，并以三聚氯氰为活化剂，合成了二甲胺修饰戊二醛交联壳聚糖树脂．研究了该树脂的红外光谱及吸附性能．该树脂对铜(Ⅱ)和牛血清白蛋白(BSA)的吸附容量分别为42mg／g(干)和940mg／g(干)，其吸附行为均符合Freundlich等温吸附模型．该树脂制备工艺简单，机械强度较好，可作为金属离子或蛋白质分离纯化的吸附剂和色谱填料．     

聚合物驱蚊剂的慢释放研究

本文研究了丙烯酸酯共聚物载体对驱蚊剂N,N-二乙基间甲苯酰胺(DETA)慢释放行为的控制,探讨了单体配比、共聚物分子量以及DETA含量对释放速率的影响。结果表明。增加亲水性单体丙烯酸(AA),可提高DETA的释放速率;降低共聚物数均分子量,会减少DETA的释放量;剂型中DETA含量与释放量存在线性正比关系,但DETA的含量增加并不导致释放有效时间的线性增加。本文还就共聚物膜的透湿性和碱溶性作了研究,亲水性单体AA的增加同样导致透湿性和碱溶性的增加。制备的聚合物驱蚊剂经现场应用试验,表明具有良好的长效驱蚊特性。     

FFC-1离子交换纤维物理化学性能的研究

利用扫描电镜、热失重-红外、元素分析、低温氮吸附等技术和化学手段对聚羧酸基FFC-1离子交换纤维的结构与性能特点等进行了系统研究．结果表明：FFC-1离子交换纤维为含适量酰肼类交联键的聚羧酸(钠)型离子交换材料，外比表面积大和传质距离短是其反应动力学性能优异的主要原因，FFC-1纤维具有良好的化学与热稳定性。在5mol/L硫酸、硝酸、盐酸和2mol／L氢氧化钠溶液中浸泡，交换容量未见明显降低。但过氧化氢溶液对其功能基有明显破坏，CO2为FFC-1纤维在高温区间(300℃～350℃)的主要分解产物。     

酚醛树脂固化过程的红外光谱分析

利用红外光谱(IR)及其变温样品池、定量分析程序对酚醛树脂固化过程中的结构变化进行了研究,它对于酚醛树脂固化过程的质量控制具有重要意义。     

毛细管气相色谱法测定果蔬中α—萘乙酸残留量

用530μm大口径毛细管柱为分离柱,GC-FID法测定水果和蔬菜中的α一萘乙酸残留量。方法检测限为10~(-7),回收率和相对标准偏差分别为99.5%和3.0%。     

Photoinduced self-substitution of haloquinones

A series of novel oligo(halobenzoquinoid) compounds have been obtained from the photoinduced self-substitution of 2,5-dibromo-1,4-benzoquinone (1a), 2,6-dibromo-1,4-benzoquinone (1b), 2-chloro-1,4-benzoquinone (1c), 2-bromo-5-chloro-1,4-benzoquinone (1d), 2,3,5,6-tetrachloro-1,4-benzoquinone (1e) and 1,4-benzoquinone (1f) in the presence of N,N-dimethyl-t-butylamine (2) in acetonitrile. Dimers, trimers and/or pentamers of these haloquinones were found to be the major products.     

FFC-1离子交换纤维对酸碱有害气体吸附性能的研究

系统考察了不同直径及反离子形式的FFC-1聚羧酸离子交换纤维对酸碱有害气体的穿透吸附,各种温、湿度条件下的吸水率,以及作为有害气体吸附滤除材料的重复使用与再生性能。研究表明:FFC-1纤维直径的减小有利于提高对有害气体的动态吸附容量。在体系温度、相对湿度分别为15℃、50%时,以3D腈纶为起始原料的钠型FFC-1离子交换纤维的吸水率≥350mg/g.纤维;对SO2的穿透吸附容量可达200mg/g.纤维。FFC-1离子交换纤维具有良好的重复使用与再生能力,经20次再生循环使用后,纤维交换容量未见明显变化。