Simple fabrication of Cu~(2+) doped calcium alginate hydrogel filtration membrane with excellent anti-fouling and antibacterial properties

Herein,copper ion doped calcium alginate(Cu~(2+)/CaAlg) composite hydrogel filtration membranes were prepared by using natural polymer sodium alginate(NaAlg) as raw material.The thermal stability and structure of the composite membranes were characterized by thermogravimetric analysis and infrared spectroscopy.The mechanical strength,anti-fouling performance,hydrophilicity and filtration performance of the membrane were studied.The results show that Cu~(2+)/CaAlg hydrogel membrane has excelle nt mechanical properties and thermal stability.The anti-swelling ability of the membrane was greatly enhanced by doping Cu~(2+).After three alternate filtration cycles,the flux recovery rate of Cu~(2+)/CaAlg hydrogel membrane can still reach 85%,indicating that the membrane has good antipollution performance.When the operation pressure was 0.1 MPa,the rejection of coomassie brilliant blue G250 reached 99.8% with a flux of 46.3 L m ~2 h ~1,while the Na_2 SO_4 rejection was less than 10.0%.The Cu~(2+)/CaAlg membrane was recycled after 24 h in the filtration process,and its flux and rejection rate did not decrease significantly,indicating that the hydrogel membrane has long-term application potential.The Cu~(2+)/CaAlg membrane has a wide range of applications prospect in dye desalination,fine separation and biopharmaceutical technology fields.     

高力学强度细菌纤维素气凝胶纤维的连续化制备

气凝胶纤维因其高外表面积和高柔韧性在能量管理系统中具有潜在应用而引起了广泛关注.但是,目前制备的气凝胶纤维力学强度较低,限制了其实际应用.为提高气凝胶纤维力学性能,在始终保持细菌纤维素(BC)纳米纤维处于湿态下,利用NaOH/尿素/硫脲复合溶剂直接低温溶解原生BC,获得透明的BC纺丝原液;通过湿法纺丝制备了BC水凝胶纤维,经过水洗和冷冻干燥后处理,制得BC气凝胶纤维.采用偏光显微镜(POM)、13C核磁共振(13C-NMR)和高级旋转流变仪研究BC在复合溶剂中的溶解过程与状态;利用全反射傅里叶变换红外吸收光谱(ATR-FTIR)、X射线衍射(XRD)和热失重(TG)研究BC溶解前后结构与性能变化;利用场发射扫描电镜(FESEM)、全自动比表面积和孔径分布分析仪、单丝强力仪对获得的BC气凝胶纤维结构与性能进行表征.结果表明,复合溶剂在?15℃条件下可以直接溶解原生湿态BC,最高溶解浓度为3 wt%;采用湿法纺丝制得高度多孔的连续BC气凝胶纤维,比表面积高达192 m^2/g且具有优异的力学性能,断裂强度和杨氏模量高达(9.36±1.68)MPa和(176±17.55)MPa,如0.4 mg BC气凝胶纤维可以支撑高于其本身质量5×10^4倍的重物.     

金属锂负极的成核机制与载体修饰

金属锂具有电位低、比容量高等突出优点,是极具吸引力的下一代高能量密度电池的负极材料,然而存在枝晶、死锂、副反应严重、库伦效率低、循环稳定性差等问题,限制了其实际应用。金属锂负极的成核是电化学沉积过程中的重要步骤,锂在集流体或导电载体上的均匀成核和稳定生长对于抑制枝晶死锂、提高充放电效率和循环性能具有关键作用。本文从成核机制与载体效应的角度概述了锂金属负极的研究进展,介绍了锂成核驱动力、异相成核模型、空间电荷模型等内容,分析了锂核尺寸及分布与过电位和电流密度的关系,并通过三维载体分散电流密度、异相晶核/电场诱导成核、晶格匹配等方面的研究实例讨论了载体修饰对锂负极的性能提升。     

Recent advances in bismuth vanadate-based photocatalysts for photoelectrochemical water splitting

Photoelectrochemical(PEC) technology is considered to be a promising approach for solar-driven hydrogen production with zero emissions. Bismuth vanadate(BiVO_4) is a kind of photocatalytic material with strong photoactivity in the visible light region and appropriate band gap for PEC water splitting.However, the solar-to-hydrogen efficiency(STH) of BiVO_4 is far away from the 10% target needed for practical application due to its poor charge separation ability. Therefore, this review attempts to summarize the strategies for improving the photocurrent density and especially hydrogen production of BiVO_4 materials through PEC techniques in the last three years, such as doping nonmetal and metal elements, depositing noble metals, constructing heterojunctions, coupling with carbon and metalorganic framework(MOF) materials to further enhance the PEC performance of BiVO_4 photoanode. This review aims to serve as a general guideline to fabricate highly efficient BiVO_4-based materials for PEC water splitting.     

Ruthenium(II)-catalyzed para-selective CH difluoroalkylation of aromatic aldehydes and ketones using transient directing groups

A Ru(II)-catalyzed para-difluoroalkylation of aromatic aldehydes and ketones with a transient directing group has been developed. It utilizes less expensive ruthenium catalysts and allows facile access to challenging difluoroalkylated aldehydes. The mechanism studies suggest that the distinct coordination mode of ruthenium complex with imine moieties is responsible for para-selectivity.     

Upgrade of beamline BL08B at Taiwan Light Source from a photon‐BPM to a double‐grating SGM beamline

During the last 20 years, beamline BL08B has been upgraded step by step from a photon beam‐position monitor (BPM) to a testing beamline and a single‐grating beamline that enables experiments to record X‐ray photo‐emission spectra (XPS) and X‐ray absorption spectra (XAS) for research in solar physics, organic semiconductor materials and spinel oxides, with soft X‐ray photon energies in the range 300–1000 eV. Demands for photon energy to extend to the extreme ultraviolet region for applications in nano‐fabrication and topological thin films are increasing. The basic spherical‐grating monochromator beamline was again upgraded by adding a second grating that delivers photons of energy from 80 to 420 eV. Four end‐stations were designed for experiments with XPS, XAS, interstellar photoprocess systems (IPS) and extreme‐ultraviolet lithography (EUVL) in the scheduled beam time. The data from these experiments show a large count rate in core levels probed and excellent statistics on background normalization in the L‐edge adsorption spectrum.     

Charge redistribution and a shortening of the Fe—As bond at the quantum critical point of SmO1–xFxFeAs

Many researchers have pointed out that there is a quantum critical point (QCP) in the F‐doped SmOFeAs system. In this paper, the electronic structure and local structure of the superconductive FeAs layer in SmO_1–xF_xFeAs as a function of the F‐doping concentration have been investigated using Fe and As K‐edge X‐ray absorption spectroscopy. Experiments performed on the X‐ray absorption near‐edge structure showed that in the vicinity of the QCP the intensity of the pre‐edge feature at the Fe‐edge decreases continuously, while there is a striking rise of the shoulder‐peak at the As edge, suggesting the occurrence of charge redistribution near the QCP. Further analysis on the As K‐edge extended X‐ray absorption fine structure demonstrated that the charge redistribution originates mostly from a shortening of the Fe—As bond at the QCP. An evident relationship between the mysterious QCP and the fundamental Fe—As bond was established, providing new insights on the interplay between QCP, charge dynamics and the local structural Fe—As bond in Fe‐based superconductors.     

氧化还原可逆Nb2TiO7复合阴极电解池高温水蒸气电解研究

系统地研究Nb₂TiO₇与Nb_1.33Ti_0.67O₄材料相互转变的氧化还原循环可逆性能,同时研究Nb2TiO7和Nb_1.33Ti_0.67O₄样品随温度和氧分压变化的电导率,并与复合电极对称电池和电解池的电化学性能相关联. 在830 oC下,对Nb_1.33Ti_0.67O₄复合电极电解池进行水蒸气的电解研究测试. 电流电压曲线和电解池短期性能测试表明在低电压下主要为电极的还原和活化过程;而在高电压下主要为水蒸气的电解. 当3%H₂O/Ar/4%H_{2气体通入阴极时电解池水蒸气电解的法拉第效率为98.9%;而当通入气体转换为3%H2O/Ar时效率为89%.}