数字微流控技术及其在生物分析中的应用

数字微流控技术是一种基于微电极阵列来实现离散液滴精确控制的新型液滴操纵技术。这种基于介电润湿现象实现的液滴电操纵体系,相比于传统微流控芯片具有自动化、可寻址、可动态配置、易集成等特点。该文介绍了数字微流控技术液滴驱动原理,总结了芯片的结构和常用的制作方法,举例阐述了现阶段该技术在生物分析化学领域的应用,并对其应用前景做了展望。     

Detection of new phenylpropanoids from Dendrobium chrysanthum

Herba Dendrobii has been documented in the Compendium of Materia Medica, with special efficacy in nourishing Yin and treating diabetes. However, the chemical profile of Dendrobium chrysanthum Lindl. has not been reported yet. The compositions were analysed with UPLC/Q-TOF-MS/MS. 53 compounds were tentatively characterised, and 14 compounds might be new compounds. Some novel lactones of poly-phenylpropanoids were firstly detected, and di-p-hydroxyphenylpropionic acidic p-coumaric acid lactone, a new compound of the first example, was obtained and identified. UPLC/Q-TOF-MS/MS was a feasible and efficient method to discover the unique compounds in complex matrices of D. chrysanthum.     

Mo掺杂Ce/石墨烯（GE）催化剂的制备及脱硝性能

采用浸渍法制备了不同负载量Mo掺杂Ce/GE催化剂,对其脱硝性能进行了测试,初步探明了Mo掺杂Ce/GE催化剂促进SCR活性增强的内在机制。结果表明,Mo的添加使nCe3+/(nCe3++nCe4+)比率增加、表面吸附氧(Oβ)含量增加及催化剂酸性位点增加,从而提高催化剂的脱硝活性。与5Ce/GE和5Mo/GE相比,5Ce-5Mo/GE催化剂脱硝性能更加优异。当Mo负载量为5%时,催化剂脱硝活性最好,在250℃时NOx转化率达到了99%。此外,5Ce-5Mo/GE催化剂具有较好的抗硫性能。     

新型BiOI/g-C3N4纳米片复合光催化剂的制备及其可见光催化活性增强

近年来, 石墨型氮化碳(g-C3N4)作为一种n型半导体光催化剂材料, 由于具有较好的热稳定性和化学稳定性, 同时具有可调的带隙结构和优异的表面性质而备受人们关注. 然而, 传统的g-C3N4块体材料存在比表面积小、光响应范围窄和光生载流子易复合等缺陷, 制约着其光催化活性的进一步提高. 因此, 人们开发了多种技术对块体状g-C3N4材料进行改性,其中构建基于g-C3N4纳米薄片的异质结复合光催化材料被认为是强化g-C3N4载流子分离效率, 进而提高其可见光催化活性的重要手段. BiOI作为一种窄带隙的p型半导体光催化剂, 具有强的可见光吸收能力和较高的光催化活性, 同时它与g-C3N4纳米薄片具有能级匹配的带隙结构. 因此, 基于以上两种半导体材料的特性, 构建新型的BiOI/g-C3N4纳米片复合光催化剂材料不仅能够有效提高g-C3N4的可见光利用率, 而且还可以在n型g-C3N4和p型BiOI界面间形成内建电场, 极大促进光生电子-空穴对的分离与迁移效率.为此, 本文通过简单的一步溶剂热法在g-C3N4纳米薄片表面原位生长BiOI纳米片材料, 成功制备了新型的BiOI/g-C3N4纳米片复合光催化剂. 利用X射线衍射仪(XRD), 场发射扫描电子显微镜(SEM)、透射电子显微镜(TEM)、紫外-可见漫反射光谱和瞬态光电流响应谱对所合成复合光催化剂的晶体结构、微观形貌、光吸收性能和电荷分离性能进行了表征测试. XRD, SEM和TEM结果显示, 结晶完好的BiOI呈小片状均匀分散在g-C3N4纳米薄片表面; 紫外漫反射光谱表明, 纳米片复合材料的吸光性能较g-C3N4薄片有显著提升; 瞬态光电流测试证明, 复合材料较单一材料有更好的电荷分离与迁移性能.在可见光催化降解RhB的测试中, BiOI/g-C3N4纳米片复合光催化剂显示出了优异的催化活性和稳定性, 其光降解活性分别为纯BiOI和g-C3N4的34.89和1.72倍; 自由基捕获实验发现, 反应过程中的主要活性物种为超氧自由基(·O2-), 即光生电子主导整个降解反应的发生. 由此可见, 强的可见光吸收能力和g-C3N4与BiOI界面处形成的内建电场协同促进了g-C3N4纳米薄片的电荷分离, 进而显著提高了该复合材料的可见光催化降解活性. 此外, 本文初步验证了在BiOI/g-C3N4纳米片复合光催化体系内光生电荷是依据"双向转移"机制进行分离和迁移的, 而非"Z型转移"机制.     

类水滑石Mg3Al1-xFex负载Ir催化剂在肉桂醛加氢反应中的应用:Fe的促进作用

水滑石类化合物 (LDH) 的层板金属阳离子组成具有可调变性,通过将具有变价特性的过渡金属定量引入 LDH 层板,经热处理后可以得到具有高比表面积和层板金属原子级分散的混合金属氧化物,后者可广泛用作催化剂载体.如三元Mg-Al-Fe 类水滑石材料在光催化、H2S 选择性氧化和乙苯脱氢等反应中表现出较好的活性.Ir 催化剂在α,β-不饱和醛加氢反应中具有较好的活性,Fe 修饰 Ir 催化剂可提高不饱和醇选择性,但有关 Fe 的作用以及 Fe 与活性组分 Ir 间的相互作用本质还不是很清楚.本文以类水滑石材料 Mg3Al1–xFex为载体,采用等体积浸渍法制备了 Ir 催化剂,并用于肉桂醛加氢反应,通过考察 Fe的加入对 Ir 电子和几何结构的影响揭示了 Fe 的加入对活性和选择性的影响规律.结果表明,当 x 从 0 (Ir/Mg3Al) 增加到 1 (Ir/Mg3Fe) 时,肉桂醛加氢的反应速率在 x = 0.25 时达到最大值,肉桂醇选择性从 44.9% 增加到 80.3%,且不随肉桂醛转化率的增加而改变.透射电镜结果表明,Ir 纳米粒子的粒径随着 x 的增加未发生明显变化,均为 1.7±0.2 nm.H2程序升温还原结果发现 Ir 可以促进 Fe3+的还原且两者之间存在相互作用.X射线光电子能谱结果表明,Fe 的掺杂没有改变催化剂表面Ir0和 Ir4+含量的比值,但当 Fe 含量增加时,Fe2+2p3/2向高结合能方向偏移,且 Ir04f7/2向低结合能方向偏移,说明电子从 Fe2+转移到 Ir,形成了富电子的 Ir 物种和缺电子的 Fe 物种.富电子的 Ir 物种有利于肉桂醛分子中的 C=O 键在其表面吸附,并且和 Ir 相邻的 Fen+物种可以作为亲电位点吸附肉桂醛分子中氧,从而极化和活化 C=O 键,因而催化剂活性和选择性增大.采用吸附 CO 红外光谱表征了催化剂表面的几何结构,2058–2069 cm-1处出现了 CO 吸附峰,归属于 Ir0表面 CO 的线性吸附,高波数 2069 cm-1的吸附峰归属于 CO 在高配位 Ir 位点 (平台) 的吸附,低波数 2058 cm-1的吸附峰归属于 CO 在低配位Ir 位点 (台阶、角、楞) 的吸附.随着 Fe 含量的增加,CO 吸附峰蓝移 11 cm-1,表明 Fe 的加入改变了催化剂表面 Ir 的几何结构,低配位 Ir 位点减少,高配位 Ir 位点增多.高配位 Ir 位点 (平台) 有利于肉桂醛分子中 C=O 键的吸附,从而提高了肉桂醇的选择性.总之,Fe 的加入虽然没有明显改变 Ir 纳米粒子的粒径,但却改变了其电子和几何结构,从而提高了催化剂活性和选择性.     

铜催化芳香醛和酮的氢硼化转化合成苄基硼酸酯类化合物（英文）

有机硼化合物广泛应用于合成化学、药物化学以及材料化学等领域,开发新颖实用的方法合成有机硼化合物是重要的研究领域.在各种有机硼化合物中,苄基硼酸酯有着一些特有的性质,例如活性相对较高,可以有效地当作苄基化试剂使用.目前已有多种合成苄基硼酸酯的方法,主要集中在苄基格氏试剂或者锂试剂的硼化反应,但是该方法底物兼容性较差,而且苄基格氏试剂或者锂试剂的制备比较困难.随着催化反应的发展,过渡金属(如Pd,Cu,Ni,Fe)催化苄基卤代物的硼化反应及芳基卤代物和1,1-二硼类化合物的偶联反应能够有效地合成这类化合物.一级苄醇在钯或铜的催化作用下也可以转化为苄基硼酸酯.苄基C–H键的催化硼化是潜在的构建苄基硼酸酯的高原子经济性的方法,但目前其选择性和反应活性仍不高.在无金属催化的条件下,对甲苯磺酰腙类化合物与HBpin或B_(2pin_2)发生1,2-金属迁移是合成苄基硼酸酯的有效方法.到目前为止,虽然有很多种合成苄基硼酸酯的方法,但仍无法满足其合成需求,因此开发新型的方法合成苄基硼酸酯具有重要的意义.本文开发了一种新型的铜催化芳香醛/酮类化合物的脱氧氢硼化转化体系.使用廉价易得的铜作为催化剂,叔丁醇钠或者叔丁醇钾作为碱,醇质子作为氢源,在100℃的条件下,芳香醛和芳香酮可直接转化成一级和二级苄基硼酸酯类化合物,该反应操作简单,反应体系可以兼容多种官能团,分离产率在21%–77%之间.反应机理方面,该转化有两种可能的过程,(1)反应体系中首先生成1,1-偕二硼化合物,该化合物在碱和EtOH的作用下发生脱硼质子解,最终转化成苄基单硼化合物;(2)醇质子转化成负氢物种,并与体系中的冄-OBpin硼酸酯生成四配位硼,发生1,2-迁移后得到目标产物.为了验证上述两种反应途径的可行性,我们进行了一系列的控制试验.首先合成了苯乙酮的1,1-二硼化合物,在催化量碱与当量醇的作用下,以99%的收率得到了脱硼质子解的产物,说明1,1-二硼化合物可以在反应体系中转化成苄基单硼化合物.以苯甲醛作为原料合成了冄-OBpin硼酸酯,首先将其投入到甲醇、叔丁醇钠和B_(2pin_2)的体系中,最终得到了47%的苄基单硼;同时将冄-OBpin硼酸酯投入到HBpin与叔丁醇钠的体系中,得到了57%的苄基单硼化合物,说明第二种反应过程通过1,2-迁移得到目标产物也是可行的.在当前的实验条件下,两种反应路径都是可能的.     

Flexible asymmetric supercapacitor based on MnO2 honeycomb structure

By controlling the electroplating time of solution containing Mn(Ac)₂, the MnO₂ nanosheets were self-assembled to the honeycomb structure and showed an excellent electrochemical performance in 1 mol/L Na₂SO₄ electrolyte. Via pairing with activated carbon as negative electrode, the capacitor could deliver a maximum energy density of 43.84 Wh/kg and a maximum power density of 6.62 kW/kg.     

Preparation of MnCo/MCM-41 catalysts with high performance for chlorobenzene combustion

MCM-41 was synthesized by a soft template technique. The specific surface area and pore volume of the MCM-41 were 805.9 m²/g and 0.795 cm³/g, respectively. MCM-41-supported manganese and cobalt oxide catalysts were prepared by an impregnation method. The energy dispersive X-ray spectroscopy clearly confirmed the existence of Mn, Co, and O, which indicated the successful loading of the active components on the surface of MCM-41. The structure and function of the catalysts were changed by modulating the molar ratio of manganese to cobalt. The 10%MnCo(6:1)/MCM-41 (Mn/Co molar ratio is 6:1) catalyst displayed the best catalytic activity according to the activity evaluation experiments, and chlorobenzene (1000 ppm) was totally decomposed at 270 °C. The high activity correlated with a high dispersion of the oxides and was attributed to the exposure of more active sites, which was demonstrated by X-ray diffraction and high-resolution transmission electron microscopy. The strong interactions between MnO₂, Co₃O₄, MnCoO_x, and MCM-41 indicated that cobalt promoted the redox cycles of the manganese system. The bimetal-oxide-based catalyst showed better catalytic activity than that of the single metal oxide catalysts, which was further confirmed by H₂ temperature-programmed reduction. Chlorobenzene temperature-programmed desorption results showed that 10%MnCo(6:1)/MCM-41 had higher adsorption strength for chlorobenzene than that of single metal catalysts. And stronger adsorption was beneficial for combustion of chlorobenzene. Furthermore, 10%MnCo(6:1)/MCM-41 was not deactivated during a continuous reaction for 1000 h at 260 °C and displayed good resistance to water and benzene, which indicated that the catalyst could be used in a wide range of applications.     

Acid‐treated g‐C3N4‐Cu2O composite catalyst with enhanced photocatalytic activity under visible‐light irradiation

Acid‐treated g‐C₃N₄‐Cu₂O was prepared by hydrothermal reduction followed by high temperature calcination and acid exfoliation. The structures and properties of as‐synthesized samples were characterized using a range of techniques, such as X‐ray photoelectron spectroscopy, scanning electron microscopy, Photoluminescence Spectroscopy and the Brunauer–Emmett–Teller (BET) theory. The photocatalytic activity was evaluated by measuring the photodegradation of methyl orange under visible‐light irradiation. Based on the results of TEM, XPS, EPR and other techniques, it was verified that a heterojunction was formed. The acid treatment process can increase the specific surface area to form abundant heterojunction interfaces as channels for photo‐generated carrier separation, thereby enhancing its light utilization and quantum efficiency. Results indicate that acid‐treated g‐C₃N₄‐Cu₂O possesses a large specific surface area, which provides plentiful activated sites for heterojunctions to form; in addition, it showed a high visible light effect and the minimum charge‐transfer resistance. Furthermore, the g‐C₃N₄‐Cu₂O material exhibits high levels of effectiveness and stability. Electron paramagnetic resonance and a series of radical trapping experiments demonstrate that the holes and ?O₂^? could be the main active species in methyl orange photodegradation. This work could provide new insights into the fabrication of composite materials as high‐performance photocatalysts, and facilitate their application in addressing environmental protection issues.