Temperature-programmed desorption and adsorption of hydrogen on Mo2N

Hydrogen adsorption-desorption over Mo₂N has been studied using a temperature-programmed technique. It is revealed that hydrogen on Mo₂N exhibits very high mobility leading to migration of the surface hydrogen into the sublayer and bulk of the sample or the reverse. The surface hydrogen species are preferentially formed when adsorption is carried out below 573 K. On increasing the adsorption temperature to above 573 K, the quantity of hydrogen species located in the sublayer or/and bulk of the Mo₂N sample increases significantly.     

Detection of metal ions using ion-channel sensor based on self-assembled monolayer of thioctic acid

Gold electrodes were chemically modified with thioctic acid monolayer designed to mimic biological ion-channel membranes. The technique was then used in the determination of alkali, alkaline earth, thallium(I), and lanthanum metal cations as analytes. Cyclic voltammograms (CV) of [Fe(CN)6]³⁻ an electroactive marker, were measured in the presence of the various types of analyte cations. In the absence of the analyte cation, electrostatic repulsion between the marker anions and the carboxylate groups of the receptor monolayer hindered the approach of the marker anion to the electrode surface and hence hindered its reduction. The modified electrodes responded well to the metal cations except the alkali metal cations. The sensors could detect the trivalent cation La³⁺ at concentrations as low as 10⁻⁸ M. The response of the sensor to the metal cations increase in the order alkali metal3+ can be discriminated in the ratio 1:100. This makes it possible to determine the trivalent ion in a sample matrix containing monovalent and divalent cations. Thallium(I) ion showed marked deviation in its response as compared to monovalent ions of the alkali metals. The ion-channel sensor based on self-assembled monolayer of thioctic acid therefore offers a potential alternative technique for the selective determination of metal ions.     

Mg改性对Co/γ-Al2O3-TiO2催化燃烧丙烷性能影响

采用分步浸渍法制备了系列Mg改性的Co/γ-Al_2O_3-TiO_2催化剂,通过X射线衍射(XRD)、紫外可见漫反射光谱(DR-UV-vis)、N_2吸附-脱附(BET)、X射线光电子能谱(XPS)和H_2程序升温还原(H_2-TPR)等技术对催化剂进行表征,并考察了其对丙烷燃烧的催化性能。结果表明,Co在原始γ-Al_2O_3-TiO_2载体和Mg改性MgO/γ-Al_2O_3-TiO_2载体上均以Co_3O_4的形式存在;Mg掺入后与Al_2O_3作用形成MgAl_2O_4尖晶石,改善了载体的织构性质,提升了Co_3O_4在催化剂载体表面的暴露数量和分散程度。此外,MgAl_2O_4与Co_3O_4相互作用提升了Co_3O_4颗粒表面Co~(3+)/Co~(2+)和O_(ads)/O_(latt)的比例,并削弱了Co-O键键能,从而提升了其对丙烷的催化燃烧活性。当Mg负载量为15%(质量分数)时,在Co/MgO(15%)/γ-Al_2O_3-TiO_2催化剂上进行丙烷燃烧,丙烷90%转化率的温度比无Mg掺杂的Co/γ-Al_2O_3-TiO_2催化剂的降低了45℃,并且连续反应40 h其活性保持稳定。     

破碎-絮凝法分离细长碳纳米管与碳纤维

根据碳纤维与细长碳纳米管耐磨性能与絮凝沉降性能的差异，提出了一种有效分离细长碳纳米管与碳纤维的物理方法——破碎-絮凝法.该方法包括研磨破碎、液相分散、絮凝沉降、过滤分离等步骤，可高效去除混杂于细长碳纳米管样品中的碳纤维，同时还可去除螺旋状碳纤维及细小碳颗粒等易悬浮杂质.纯化过程对细长碳纳米管无损伤.用电子显微镜和热重分析表征了纯化效果，并初步分析了纯化机理.     

A 3-D noninterpenetrating diamondoid network of a decanuclear copper(I) complex

The solvothermal reaction of CuCl(2).2H(2)O with pyridine-4-thiol and ethanol yielded a novel photoluminescent 3-D polymeric complex with an interesting decorated diamondoid network that is constructed of decanuclear copper(I) cluster units and mu(4)-Cl ligands. The in situ generation of CuSO(4).5H(2)O implies the spontaneous occurrence of desulfurization and redox reactions in the present system.     

现场表面拉曼光谱研究Fe-Mo合金诱导共沉积

现场表面拉曼光谱结果显示，在0．2mol·L-1Na2MoO4,pH＝4．0的溶液中，电位正于0．5V（vsSCE）时只观察到多钼酸盐的拉曼峰（940、880和450cm-1）．负于-0．5V时，出现中心位于730cm-1的宽峰．同时电极表面有蓝色膜生成．表明混合氧化态（MO（Ⅳ），MO（Ⅴ））氧化膜的形成．730cm-1的峰在-1．9V时仍然存在，说明氧化膜没有被进一步还原．在钼酸钠溶液中同时含有0．1mol·L-1FeSO4和0．2mol·L-1柠檬酸时，中间态氧化膜的拉曼峰的中心移到740cm-1．且峰强度随着电位从-1．3V负移到-1．9V而逐渐减弱并最终消失．电极表面沉积层呈银白色，说明由于Fe2 的存在，钼的中间态氧化膜的结构发生了变化，能够被进一步还原形成Fe－Mo合金，表现出诱导共沉积的特征．     

（η^2—C60）[Pt（PPh3）2]8的合成与表征

C60是高度共轭的宠状结构碳素体．分子结构中六元环间的共价碳碳双键是富电子区，其反应性能与烯键类似，以碳碳双键与中心金属形成η2配位化合物．富勒烯η2配合物的合成及性能研究是当前研究热点之一[1~7]．本文在（η2-C60）［Pt（PPh3）2］n（n=1～6）系列研究[7]的基础上制备了（η2－C60）［Pt（PPh3）2］8，并用元素分析、红外光谱和光电子能谱进行鉴定和表征．1实验部分四（三苯基膦）合铂Pt（PPh3）4按文献[8]方法制备；C60纯度为99％；其余试剂均为分析纯．元素分析在ERLA－1106型元素分析仪上进行；光电子能谱在VGESCA…     

不同构象铂(Ⅱ)配合物与G-肌动蛋白作用的光谱研究

The cyclohexamethylene-diamine squaric acid platinum(Ⅱ) complexs(R,R, S,S) binding to G-actin and the consquence conformation change were studied by N-(1-pyrenyl) maleimide(NPM) labeled fluorescence and intrinsic fluorescence. The binding and chemical kinetics were determined by fluorometry. The results showed that when R (Pt/actin molar ratio) was lower than 30, the Pt binded to G-actin strong binding sites(-SH), when R was larger than 30, the Pt binded to G-actin weaker binding sites. The consquence conformation changes were determined by CD. The CD results showed that R was smaller than 60, G-actin α-helix contents decreased slowly, R was larger than 60, G-actin conformation changed obviously. The reaction of R,R complex of platinum(Ⅱ) S,S complex of platinum(Ⅱ) with G-actin was similar to that of with S,S complex of platinum(Ⅱ).     

ZrxTixAl1-2xO2的制备及其在三效催化剂上的应用

Zr_0.5Ti_0.5O₂(ZT) and Zr_0.25Ti_0.25Al_0.5O₂(ZTA) mixed oxides were prepared by co-precipitation method and characterized by low temperature adsorption-desorption， XRD and NH₃-TPD. The activity of Pt/Zr_0.5Ti_0.5O₂ and Pt/ Zr_0.5Ti_0.5Al_0.5O₂ catalysts was evaluated using the simulated gases. The results show that ZTA samples exhibit higher specific surface area， larger pore volume and proper surface acidic amount and acidity in comparison with ZT. The results of the catalytic test indicate that Pt/ZT and Pt/ZTA catalysts exhibit excellent low-temperature catalytic activity and lower light-off temperatures of hydrocarbon， carbon monoxide and nitrogen oxides， especially better conversion for nitrogen oxides (NO_x). The addition of Al₂O₃ into ZT enhanced the anti-aging property of Pt/ ZTA catalysts due to the excellent textural， structural， surface acidity and thermal stability.