Conductivity and dielectric properties of sol–gel derived porous zirconia

The 8-mol percentage Y₂O₃-stabilized Porous Zirconia was prepared using sol–gel method. Zirconium oxalate gel was prepared by the addition of appropriate amount of oxalic acid solution into the 1 M aqueous solution of zirconium-oxy chloride. A cubic phase zirconia powder was obtained by calcination and milling of the zirconium oxalate gel. Crystallization temperature was found about 450 °C from the Differential thermal analysis. The phase analysis by X-ray diffraction shows the presence of cubic phase. Pellets sintered at 1,350 °C were highly porous, and the electrical conductivity was found with lower value due to the porosity, and the hardness was about 8.0 GPa. Paper presented at the Third International Conference on Ionic Devices (ICID 2006), Chennai, Tamilnadu, India, Dec. 7–9, 2006.     

Microdrilling for fabricating micrometer-scale holes in soft matter

Probing the response of soft materials at small scales requires examining fundamental behaviors that are often distinct from large-scale interactions. In the development of micrometer- and nanometer-sized holes in soft materials, understanding failure modes becomes essential. We observe fracture behavior in a soft material through a novel method, which leads to the fabrication of small-scale holes in polydimethylsiloxane. We utilize an ultra-sharp tungsten needle to drill this soft elastomeric polymer; this results in controlled hole size and exhibits fracture characteristics observed in brittle materials at larger length scales. We also examine the macroscopic characteristics known to contribute to brittleness and hardness for this material’s response with respect to curing times. This understanding will contribute to many applications including the development of porous materials and DNA sequencing efforts. PACS 81.05.Lg; 81.40.Np; 82.35.Lr     

Influence of the defect structure on the electrical conductivity of Pb5Ge3O11 single crystals at high temperatures

The impedance spectra of Pb₅Ge₃O₁₁ single crystals are measured in the frequency range from 5 Hz to 13 MHz at temperatures of 600 to 800 K in dry air and in a dry or wet nitrogen gas. It is found that the temperature and the gas composition significantly affect the electrical properties of the compound. The data obtained are used to discuss the origin of crystal lattice defects and their influence on charge transfer. It is concluded that the conduction is mixed in character (p-type electronic and ionic due to oxygen ions). The proton conduction is shown experimentally to be feasible. The possible mechanisms of proton transport in Pb₅Ge₃O₁₁ are discussed.     

Air-activated carbons from almond tree pruning: Preparation and characterization

In this work the results obtained in the preparation and characterization of carbons made from almond tree pruning by non-catalytic and catalytic gasification (using K and Co) with air are analyzed and discussed. The main aim was to obtain high quality activated carbons at the lowest possible cost. The variables studied have been the temperature (190-260 °C) and the time (1-10 h) in non-catalytic gasification and the influence of the catalyst type (K and Co, 1 wt.% referred to cation, at 190 °C and 1 h) and the time (1-4 h) in catalytic gasification with Co at 190 °C. The air flow rate used in all the series was 167 cm³ min⁻¹. In non-catalytic gasification the reaction normalized rate versus the conversion degree was maintained until a conversion value of 10% for the experiment made at 260 °C since, at lower temperatures, this rate drops quickly for low conversion values. The N₂ adsorption isotherms for the carbons of this series resemble type I, although there is an increase of N₂ adsorbed volume at relatively high pressures. A temperature rise produced an increase of the carbon porosity and BET specific surface (116-469 m² g⁻¹). The activation time has a positive effect on the N₂ volume adsorbed by the carbons. The isotherms shapes were similar to those previously commented. A concentration equal to 1 wt.% was used to study the influence of the catalyst type. Under the studied experimental conditions, Co drives to a bigger porosity development than K, although with both catalysts a very similar pore size distribution is obtained. The activation time, in the gasifications catalyzed with Co, gives rise to a very important porosity development in the carbons. This produces a strong increase of the carbon specific surface area with very high values in the 4 h experiment, in which a BET specific surface of 959 m² g⁻¹ was obtained.     

Synthesis and magnetic properties of multilayer Ni/Cu and NiFe/Cu nanowires

Highly ordered composite nanowires with multilayer Ni/Cu and NiFe/Cu have been fabricated by pulsed electrodeposition into nanoporous alumina membrane. The diameter of wires can be easily varied by pore size of alumina, ranging from 30 to 100 nm. The applied potential and the duration of each potential square pulse determine the thickness of the metal layers. The nanowires have been characterized by transmission electron microscopy (TEM), magnetic force microscopy (MFM), and vibrating sample magnetometer (VSM) measurements. The MFM images indicate that every ferromagnetic layer separated by Cu layer was present as single isolated domain-like magnet. This technique has potential use in the measurement and application of magnetic nanodevices.     

Is life improbable?

E. P. Wigner's argument that the probability of the existence of self-reproducing units, e.g., organisms, is zero according to standard quantum theory is stated and analyzed. Theorems are presented which indicate that Wigner's mathematical result in fact should not be interpreted as asserting the improbability of self-reproducing units.     

Particle size analysis by sedimentation field flow fractionation. Performance and application

Recently commercial equipment using sedimentation field flow fractionation (SFFF) has become available for analysis of particulate materials in the sub-micron range. This paper describes the DuPont instrument and discusses its performance. A particular study is described on the comparison of the SFFF technique with that of quasi-elastic light scattering (QELS). The paper concludes that the instrument is capable of measuring particle size distributions with high resolution and precision, provided that no particles above the upper size limit — about 1 μm — are present.