Natural rubber nanocomposites with SiC nanoparticles and carbon nanotubes

Single-walled carbon nanotubes (SWNTs) and SiC nanoparticles were dispersed in natural rubber (NR) polymer solution and subsequently evaporated the solvent to prepare NR nanocomposites. Using this technique, nanoparticles can be better dispersed in the NR matrix. The influence of nano-fillers on the mechanical properties of the resulting nanocomposites was quantified.Mechanical test results show an increase in the initial modulus with nanoscale reinforcements for up to 50% strain compared to pure NR. The modulus and strength of natural rubber with 1.5% SiC nanoparticles appear to be superior to those of SWNTs with the same filler content. In addition to mechanical testing, these nanocomposites were studied using the SEM and Raman spectroscopy techniques in order to understand the morphology of the resulting system and the load transfer mechanism, respectively. The Raman spectrum of the SWNT/NR system is characterized by a strong band at 1595 cm⁻¹ (G mode—C-C stretching) and other two bands at 1300 cm⁻¹ (D mode-disorder induced) and 2590 cm⁻¹ (D* band). A shift of the 2590 cm⁻¹ Raman band to the lower wavenumber was observed after subjecting SWNT/NR sample to cyclic stress testing. Ageing SWNT/NR specimen in distilled water for 30 days also provided a similar result. The Raman shift in aged samples indicates internal stress transfer from the natural rubber matrix to the SWNTs implying the existence of bonding at the interface.