Temperature dependence of aluminum nitride reflectance spectra in vacuum ultraviolet region

Temperature dependence of optical reflectance spectra in vacuum ultraviolet region for aluminum nitride has been measured on high-quality single crystal with synchrotron radiation. The dominant structure due to the interband transition is observed at photon energy around 7.7 eV. With decreasing temperature, the energy position of the dominant structure in the reflectance spectra shifts towards higher energy. The experimental data has been fitted to the Bose-Einstein expression and the obtained parameter related to the strength of the electron-phonon interactions is much smaller than that for the peak at 6.2 eV, suggesting that the higher-lying interband transition energy decreases more slowly with increasing temperature in aluminum nitride (AlN).     

Permeability,permselectivity, and penetrant‐induced plasticization in fluorinated polyimides studied by positron lifetime measurements

The ortho‐positronium (o‐Ps) lifetime τ₃ and its intensity I₃ in various fluorinated polyimides were determined by the positron annihilation technique and were studied with the spin–lattice relaxation time T₁ and the propylene permeability, solubility, diffusivity, and permselectivity for propylene/propane in them. τ₃, I₃, and the distribution of τ₃ changed when the bulky moieties in the polyimides were changed. The polyimides, having both large τ₃ and I₃ values, exhibited a short T₁ and a high permeability with a low permselectivity. The propylene permeability and diffusivity were exponentially correlated with the product of I₃ and the average free‐volume hole size estimated from τ₃. In highly plasticized states induced by the sorption of propylene, the permeability increased with the propylene pressure in excellent agreement with the change in the free‐volume hole properties probed by o‐Ps. The large and broad distribution of the free‐volume holes and increased local chain mobility for the 2,2‐bis(3,4‐decarboxyphenyl) hexafluoropropane dianhydride‐based polyimides are thought to be important physical properties for promoting penetrant‐induced plasticization. These results suggest that o‐Ps is a powerful probe of not only the free‐volume holes but also the corresponding permeation mechanism and penetrant‐induced plasticization phenomenon. © 2003 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 41: 308–318, 2003     

Synthesis and characterization of model 3‐miktoarm star copolymers of poly(dimethylsiloxane) and poly(2‐vinylpyridine)

3‐Miktoarm star copolymers, 3μ‐D₂V, with two poly(dimethylsiloxane) (PDMS) and one poly(2‐vinylpyridine) (P2VP) arm, were synthesized by using anionic polymerization–high vacuum techniques and (chloromethylphenylethyl)methyl dichlorosilane, heterofunctional linking agent, with two SiCl groups and one CH₂Cl group. The synthetic strategy involves the selective reaction of the two ? SiCl groups with PDMSOLi living chains, followed by reaction of the remaining chloromethyl group with P2VPLi. Combined molecular characterization results (size exclusion chromatography, membrane osmometry, and ¹H NMR spectroscopy) revealed a high degree of structural and compositional homogeneity. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 614–619, 2006     

Lithographic design of photosensitive polyarylates based on reaction development patterning

The factors affecting pattern‐forming properties in reaction development patterning were examined with polyarylates with various bisphenol moieties. The developability of the photosensitive polyarylates was dependent on the properties of the subtituent (R) in the bisphenol moieties. The development time decreased in the following order: R?C(CH₃)₂ > fluorenyl unit ? phenolphthalein unit > C(CF₃)₂ > SO₂. This order agreed with that of the reactivity between the polyarylates and ethanolamine, and these orders can be explained by pK_a of the bisphenol used to prepare the polyarylates. The development with NH₂? R′? OH resulted in successful positive‐tone pattern formation. However, pattern formation with the developers containing NH₂? R′? OCH₃ was unsuccessful. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 2694–2706, 2006     

Preparation and certification of the new reference materials; plastics (disk form, JSAC 0621-0625) for determination of mercury using x-ray fluorescent analysis.

The Japan Society for Analytical Chemistry has developed some new plastic certified reference materials (CRMs) for the analysis of mercury in polyester disks using XRF analysis. These CRMs (named as JSAC 0621-0625) were prepared by casting polyesters including a toluene solution of organometallic compounds as a standard. Concentrations of the five levels of mercury ranged from 0 to 250 mg/kg. Homogeneity tests of prepared disks had shown excellent results. Interlaboratory comparison study for the certification was performed by 15 laboratory participants. The z-scores in robust statistical method was applied for the evaluation of outliers. The certified values were assigned after discarding outliers. The uncertainties of certified values were determined as the confidence levels of 95%.     

Synthesis of aromatic polyamides by 1-hydroxybenzotriazole-catalyzed polycondensation of active aromatic diesters with aromatic diamines

Catalytic actions of various additives were studied in the polycondensation of di(4-nitrophenyl) isophthalate with bis(4-aminophenyl) ether in N-methyl-2-pyrrolidone, and 1-hydroxybenzotriazole (HOBt) was found to be a highly effective catalyst that yielded high-molecular-weight polyamide. In addition to the polycondensation of the 4-nitrophenyl ester, the polymerization of negatively substituted phenyl esters like di(2,4,5-trichlorophenyl) isophthalate was also accelerated by HOBt. For the HOBt-catalyzed aminolysis of esters a bifunctional concerted mechanism that involves an eight-membered transition state was proposed.