方酸染料在远红光区／近红外区对纳米晶二氧化钛电极的高效敏化作用

Four para-dialkylaminophenyl （PDAAP1-PDAAP4） bearing carboxyl groups were studied for application to the dye-sensitized solar cells （DSC）. It was found the short spacer CH2 between carboxyl and dialkylaminophenyl chromophore in PDAAP3 and PDAAP4 led to highly efficient monochromatic incident photon-to-current conversion efficiencies （IPCE）, however the long alkyl group C4H9 attached on aniline moieties in PDAAP2 and PDAAP4 favored improvement of open-circuit photovoltage. Thus, the solar cell sensitized by PDAAP4, having both short carboxyl groups CH2COOH and long alkyl groups C4H9, exhibited the IPCE maximum of 73% at 670 nm and overall energy conversion efficiency η of 3.06%, representing the highest IPCE and η values so far in dialkylaminophenyl-based organic dye-sensitized semiconductor solar cells. Taking advantage of the highly efficient sensitizing ability of PDAAP4 in far-red region, the data of IPCE above 630 nm of the solar cells were improved greatly by cosensitization with both N3 and PDAAP4. The influences of the TiO2 film thickness and the concentration of 4-tert-butylpyridine （TBP） in electrolyte were also investigated.     

四核钼簇合物Mo4S4（μ—OAc）2（dtp）4在一些非水溶剂中的电化学研究

利用循环伏安法测定了四核钼簇合物Ｍｏ４Ｓ４（μ－ＯＡｃ）２（ｄｔｐ）４在ＣＨ４ＣＮ，ＤＭＦ，ＤＭＳＯ等溶剂中的氧化还原半波电位（Ｅ１／２），对其氧化还原进行了归属，结果表明在ＣＨ３ＣＮ中存在一个单电子的氧化过程和二个单电子的还原过程，而在ＤＭＦ和ＤＭＳＯ中只存二个单电子的还原过程，同时还探讨了溶剂的ＤＮ数对该簇合物电化学性质的影响。     

阳光络合催化分解水制氢研究的进展

引言 能源问题关系到人类的生存、发展和前途,其重要性不言而喻.随着传统的化石燃料资源的逐渐消耗,特别是石油和天然气的日益枯竭,以及人们对环境保护和生态平衡的密切关注,新能源的开发已成为当前急待解决的重大研究课题.有人估计,到2050年世界的能源结构将从现在的以石油和天然气为主转变为50％煤和49％核能与太阳能.当然这种转变应该是逐步的.因为这不单单取决于技术经济的成熟程度,而且必须设法解决煤     

气相色谱-质谱联用测定苯乙烯中的阻聚剂对叔丁基邻苯二酚

 建立了气相 质谱联用 (GC/MS)测定苯乙烯中阻聚剂对叔丁基邻苯二酚含量的方法。苯乙烯样品直接进样 ,通过毛细管柱 (HP 1,30m× 0 32mmi.d .× 0 2 5 μm)分离 ,由电子轰击 (EI)源于选择离子监测 (SIM)模式下进行检测。结果表明 ,对叔丁基邻苯二酚含量在 5mg/kg～ 5 0mg/kg时线性关系良好 (r2 =0 9987) ,回收率高 ;与美国材料测试标准ASTMD4 5 90中的分光光度测量法比较具有操作简捷、准确度高的特点。     

^1H弛豫研究具有表面活性的探针: 2-氯-N-十二烷基吡啶盐碘化 物(CDPI)在不 同集合体内的动态行为

本文报道具有表面活性的探针---2-氯-N-十二烷基吡啶盐碘化物(CDPI)的疏水碳氢链在几种包结体(胶束、包结在环糊精(β-CD)中以及包结在甲基直链淀粉(MA))中的^1H核磁弛豫时间。通过比较CDPI中碳氢链的CH~3、(CH~2)~9的T~1及T~1(CH~3)/T~1(CH~2)~9的变化,发现CDPI的运动自由度按下列次序降低:游离态、包结在β-CD中、胶束状态、包结在MA中,顺磁离子Mn^2^+对CDPI内各种质子的T~1的影响随其所处之包结体不同而变化。在胶束和甲基直链淀粉体系中,烷链的T~1几乎均不受Mn^2^+的影响,说明水合Mn^2^+不能进入CDPI胶束或甲基直链淀粉的螺旋内穴。     

ZrO2在Cu-ZnO-ZrO2甲醇水蒸汽重整制氢催化剂中的作用

通过对一系列Cu-ZnO-ZrO2甲醇水蒸汽重整(SRM)催化剂的XRD、TEM和BET表征及催化性能测定,研究催化剂中ZrO2对催化剂粒径、比表面以及对SRM反应性能的影响.结果表明,ZrO2的加入,使催化剂的粒径从15 nm降至10 nm（其中CuO和ZnO的平均粒径分别从7.7和10.4 nm降至3.9和8.7 nm）,BET比表面从60 m2•g－1增至78 m2•g－1.随着催化剂含ZrO2量不同,甲醇的转化率和H2、CO2的选择性均产生变化,当催化剂中Zr含量为24.0％(w),反应温度为220 ℃,水、醇摩尔比为1.3时,甲醇的转化率达到51.6％, H2和CO2的选择性达到100％(CO和CH4在产物气体中的体积分数小于10－4),这一结果对甲醇燃料电池甲醇重整器的应用具有重要的意义.     

含环氧端基酚酞聚芳醚酮E-PEK的合成及表征

由酚酞和4,4′-二氯二苯酮经亲核缩聚制得了一系列不同分子量的含—OK端基的聚醚酮低聚物,将其与环氧氯丙烷反应得到了分子量为1000～8000的含环氧端基聚芳醚酮(E-PEK)。用IR和~1H NMR表征了E-PEK的分子链结构,测定了T_g、溶解性和熔融粘度。研究了E-PEK/DDE体系的固化,固化后树脂的T_(g∞)=183～215℃,与低聚物的初始分子量有关。     

α—溴代萘的无保护性介质流体室温磷光特性

含α－溴代萘（α－ＢｒＮｐ）的水溶液仅以Ｎａ２ＳＯ３作化学除氧剂，在仪器光源的照射下，即能很快触发α－ＢｒＮｐ或而稳定的室温磷光（ＲＴＰ）信号。体系ＲＴＰ性质和所需光诱导的时间对有机试剂的存在及其种类和用量极为敏感。０．５％（Ｖ／Ｖ）乙腈或丙酮的存在所需光照时间短，ＲＩＰ强度高。α－ＢｒＮｐ浓度分别在１．０×１０＾－６￣２．４×１０＾－５ｍｏｌ／Ｌ和４．０×１０＾－７￣２．０×１０＾－５ｍｏｌ／Ｌ     

Development of an RPLC-based Method for Measurement of Indoprofen Stability and Validation of the Method

A method for quantitative measurement of the photochemical decomposition of the anti-inflammatory agent, indoprofen （INP） is descriped. An RPLC-based assay that could determine the extent of degradation of INP in a rapid, sensitive, and accurate manner was developed. The method was validated under photoirradiation. Quantitation was monitored with an Inertsil ODS-3V column using a mobile phase of acetonitril and 1% HOAc solution in deionized H2O. Statistics relevant to the system criteria, peak integrity and resolution among the parent drug and its degradation products were performed. From the intra- and inter-day tests, the coefficients of variation were found to range from 0.59% to 4.25% for the former and from 0.71% to 4.86% for the latter. The good selectivity and specificity of this RPLC-based procedure render it suitable for measurements of INP stability.     

溶胶凝胶法制氧化铝负载铜基超细粒子催化剂的研究

采用溶胶凝胶法制氧化铝负载铜基超细粒子催化剂的制备了氧化铝负载的铜基超细粒子催化剂，用ＴＧ－ＤＴＡ，ＸＲＤ，ＢＥＴ以及ＴＥＭ等技术手段，对催化剂的物相结构，表面孔结构，粒子形貌以及催化性能等进行了研究。结果表明，利用溶胶凝胶法，可以直接帛备出高比表面积，低堆积密度的纤维状纳米级负载型Ｃｕ／Ａｌ２Ｏ３超细粒子；活性组分以远低于纳米级的微晶粒子簇状态，均匀地分散在纳米级氧化铝载体表面上，而且在低于５０