Fluorescence spectrum,thermal properties,and continuous-wave laser performance of the mixed crystal Nd：Lu0.99La0.01 VO4

The fluorescence spectrum and thermal properties of the mixed crystal Nd：Luo.gvLa~.o1VO4 are determined. The strongest emission peak located at 1065.6 nm had a full width at half maximum （FWHM） of 2.1 nm. Continuous-wave （CW） laser performance is demonstrated by a compact planar planar cavity that is end- pumped by a diode laser. The laser output characteristics are investigated by using output couplers with different transmissions. A maximum CW output power of 8.09 W was obtained at an incident pump power of 19.4 W, which corresponds to an optical-to-optical conversion efficiency of 41.7% and a slope efficiency of 54.6%. The dependence of optimum transmission on pump power is calculated theoretically and is found to be consistent with experimental results.     

Yb3+:YVO4晶体的生长及光谱性能研究

采用提拉法生长出光学质量优良的Yb3+:YVO4晶体,研究生长过程中工艺参数的控制.测得掺杂浓度为18.1;Yb3+:YVO4晶体中Yb3+离子的有效分凝系数Keff为0.96.测定了不同Yb3+离子掺杂浓度晶体的吸收光谱和荧光光谱,并分别计算了不同掺杂浓度下Yb3+:YVO4晶体的光谱参数.本文总结和解释了掺杂浓度影响其性能的规律,讨论了Yb3+:YVO4晶体作为激光晶体的优点.     

用DSC法测定BBO、LBO和CLBO晶体的恒压比热容

本文用差示扫描量热法(DSC)测定了非线性光学晶体BBO、LBO和CLBO的恒压比热容,计算了在220～420K温度范围内每间隔10K的焓差值和熵差值.有关误差分析表明,该测试方法是有效的,并可用于其它晶体的恒压比热容的测量.     

戊二酸十八酯晶体的合成和结晶习性研究

本文合成了有机晶体材料戊二酸十八酯(OGO),对其样品进行了表征和鉴定.对OGO在多种有机溶剂中的结晶性能进行了研究,结果表明在实验的几种有机溶剂中OGO的成核趋势很强,在甲苯和苯中具有较好的结晶特性.苯和甲苯可作为晶体生长的溶剂,但不是理想的溶剂.测定了OGO在苯和甲苯中的溶解度曲线,讨论了OGO在甲苯中的晶体生长条件.     

四钼酸铵在过饱和溶液中的成核研究

本文根据经典均匀成核理论,分别研究了硝酸酸沉和盐酸酸沉制备的四钼酸铵过饱和溶液的成核过程,并讨论了过饱和比和温度对成核速率及成核机制的影响.研究结果表明,无论是硝酸酸沉还是盐酸酸沉,四钼酸铵过饱和溶液的成核速率均随过饱和比和温度的升高而增大;固液界面张力、临界半径及临界成核自由能均随温度的升高而减小.比较硝酸酸沉和盐酸酸沉四钼酸铵过饱和溶液的成核速率,发现后者的成核速率比前者大.     

Yb0.140Gd0.813La0.047VO4晶体的生长、光谱和激光损伤阈值

采用Czochralski方法生长出了Yb0.140Gd0.813La0.047VO4晶体,并测试了Yb3+与La3+在GdVO4晶体中的有效分凝系数.实验结果表明,掺入La3+可在一定程度上提高晶体的激光损伤阈值和晶体生长过程中的稳定性.此外,La3+的引入还有利于减缓高浓度Yb3+掺杂晶体中的荧光捕获效应和浓度猝灭效应的激光损伤阈值.Yb3+在该晶体中具有很宽的吸收半峰宽和荧光半峰宽,分别为26nm和47nm,具有较大的吸收截面和发射截面,分别为2.26×10-20cm2和0.96×10-20cm2,因此该晶体有望用作可调谐激光晶体和飞秒激光晶体.