一维链状的3-羧基苯氧乙酸铜配位聚合物[Cu(3-cpoa)(phen)(H2O)]n的合成与晶体结构

A novel coordination polymer [Cu(3-cpoa)(phen)(H₂O)]_n(3-cpoa^2-=3-carboxylphenoxyacetate, phen=1,10-phenanthroline) was synthesized and characterized by elemental analysis, IR spectra and single crystal X-ray diffraction. Crystallographic facts are as follows: monoclinic crystal system, space group P2₁/n， a=0.688 96(14) nm， b=1.652 3(3) nm， c=1.651 1(3) nm， β=95.20(3)°, V=1.871 9(6) nm³, Z=4, D_c=1.618 g·cm^-3， F(000)=932， μ=1.211 mm^-1，R=0.048 2 and wR=0.062 2. The copper atom exhibits a distorted square pyramidal coordination geometry, involving two oxygen atoms of different 3-cpoa^2- ligands, two nitrogen atoms of 1,10-phen ligand and one coordinated water molecule. The copper atoms are bridged by 3-cpoa^2- ligand, forming a one-dimensional chain along c axis. The distance of adjacent Cu…Cu is 0.916 6(4) nm. A three-dimensional network structure is constructed by the intermolecular hydrogen bond and π-stacking interactions. CCDC: 219724.     

一维链状配位聚合物[Ni(p-CPOA)(2,2′-bipy)(H2O)]n的合成与晶体结构

合成了一个新的配位聚合物[Ni(p-CPOA)(2,2′-bipy)(H2O)]n(p-CPOA2-= 4-羧基苯氧乙酸根,2,2′-bipy= 2,2′-联吡啶),并对其进行了元素分析、红外和单晶X-射线的表征.结果表明:配合物的化学式为C19H16N2O6Ni,晶体属单斜晶系,空间群为C2/c,晶胞参数a = 14.254(3),b = 13.085(3),c = 19.372(4)A,β = 104.89(3)°,V = 3491.8(12)A3,Z = 8,Mr = 427.05,Dc = 1.625 g/cm3,μ = 1.153mm－1,F(000) = 1760,最终R = 0.0345,wR = 0.0565。Ni原子为扭曲的六配位八面体构型,每个p-CPOA2－配体桥联2个Ni原子形成一维折叠链状结构,Ni…Ni原子之间的距离为9.675A,且通过分子间氢键将一维链连接成双链结构.     

2，2’-二硫代二苯甲酸、2，2’-二羧苯基硫醚及含氮配体构筑的2个配合物的合成、结构与热稳定性研究

使用2,2’-二硫代二苯甲酸和2,2’-联吡啶（2,2’-bipy）、硝酸铜在水热条件下发生的原位反应合成了一个铜配合物,即[Cu₂（C₁₄H₈O₄S）₂（C₁₀H₈N₂）₂]（1）（C₁₄H₈O₄S=2,2’-二羧苯基硫醚,C₁₀H₈N₂=2,2’-联吡啶）;然后又利用2,2’-二硫代二苯甲酸和菲咯啉（phen）、氯化钙在水溶液中合成了一个钙配合物,即{[Ca（C₁₄H₈O₄S₂）（C₁₂H₈N₂）₂]·（H₂O）₂}_n（2）（C₁₄H₈O₄S=2,2’-二硫代二苯甲酸根,C₁₂H₈N₂=菲咯啉）,并对它们分别进行了元素分析、红外光谱、热稳定性、X射线粉末衍射和X射线单晶衍射的表征。结果表明：配合物1由2,2’-二羧苯基硫醚配体连接形成了一个双核的化合物,通过氢键和氮杂环之间的π…π作用形成三维超分子网络结构。配合物2由二硫代二苯甲酸配体桥联形成了一个一维链状结构,通过氢键和氮杂环之间的π…π作用也形成三维超分子网络结构。并且,对这2个配合物的热稳定性分别进行了研究。     

2，5-二烷基-1，4-苯二酚类衍生物的新合成方法

研究了合成2，5-二烷基-1，4-苯二酚衍生物的新方法，该方法是以2-取代烷 基1，4-环已二酮为原料，在LiCl催化下，与各种醛缩合反应就得2，5-二烷基-1， 4-苯二酚衍生物，是一种由非芳香环化合物合成2，5-二烷基-1，4-苯二酚衍生物 的新方法。应用该方法简便地合成了天然化合物η-生育酚。     

聚氯乙烯／热塑性弹性体共混增韧的研究进展

聚氯乙烯（PVC）是一种性能优良,价格低廉的通用树脂,但其脆性大、热稳定性差、加工性能不佳等,需要进行改性。通过用热塑性弹性体（TPE）对PVC进行共混增韧改性,可得到高性能的PVC复合材料。共混改性为PVC增韧改性的最简单易行的有效方法。本文概述了聚氯乙烯／热塑性弹性体共混体系的种类和制备方法,同时对影响热塑性弹性体...     

稀土对Si3N4陶瓷力学性能和显微组织的影响

研究了Y2 O3,La2 O3,Nd2 O3等稀土氧化物对Si3N4 陶瓷力学性能和显微组织的影响。添加稀土氧化物的Si3N4 陶瓷可以获得较好的力学性能。添加复合稀土氧化物 (Y2 O3 La2 O3)后 ,断裂韧性达 7 8MPa·m1 2 ,抗弯强度达 962MPa,其性能提高的主要原因是稀土氧化物改善了材料的显微组织 ,提高了 β Si3N4 晶粒的长径比。     

Superconducting properties of the C15-type Laves phase ZrIr2 with an Ir-based kagome lattice

We report systematic studies on superconducting properties of the Laves phase superconductor ZrIr$_2$. It crystallizes in a C15-type (cubic MgCu$_2$-type, space group $Fd\overline{3}m$) structure in which the Ir atoms form a kagome lattice, with cell parameters $a=b=c=7.3596(1)$ Å. Resistivity and magnetic susceptibility measurements indicate that ZrIr$_2$ is a type-II superconductor with a transition temperature of 4.0 K. The estimated lower and upper critical fields are 12.8 mT and 4.78 T, respectively. Heat capacity measurements confirm the bulk superconductivity in ZrIr$_2$. ZrIr$_2$ is found to possibly host strong-coupled s-wave superconductivity with the normalized specific heat change $\Delta C_{\rm e}/\gamma T_{\rm c} \sim 1.86$ and the coupling strength $\Delta_0/k_{\rm B}T_{\rm c} \sim 1.92$. First-principles calculations suggest that ZrIr$_2$ has three-dimensional Fermi surfaces with simple topologies, and the states at Fermi level mainly originate from the Ir-5d and Zr-4d orbitals. Similar to SrIr$_2$ and ThIr$_2$, spin--orbit coupling has dramatic influences on the band structure in ZrIr$_2$.     

基于3-羟基-2-吡啶苯甲酸的铜(Ⅱ)配位聚合物的合成,晶体结构和光催化性能

以3-羟基-2-吡啶苯甲酸(H2L)和Cu(NO3)2·6H2O为原料,通过溶剂热反应得到了一个新的配位聚合物[Cu(HL)2·C2H5OH]n(1).通过X-射线单晶衍射、元素分析、红外光谱(FT-IR)、热重分析(TG-DTA)和固态漫反射光谱(UV-Vis)等实验手段对配合物进行了表征.结果表明,配合物1结晶于单斜晶系,P21/c空间群.最小结构单元中包含一个铜离子与四个有机配体,形成六配位模式,并进一步通过有机配体的羧基和羟基基团桥接,形成了二维平面结构.配合物1具有半导体性质,带隙能(Eg)为3.01 eV.光催化性能测试结果表明,配合物1对染料亚甲基蓝(MB)和甲基橙(MO)均具有催化降解效果,在紫外光照射下120 min和180 min内,对二者的降解率分别为92.6;和45.4;.配合物1还具有良好的循环再生性,重复使用5次后仍能保持对MB分子的光催化活性基本不变.     

变质量,变阻尼,变刚度结构系统的动力响应

本文首次提出了变质量、变阻尼、变刚度结构系统的动力响应问题，并根据抓斗卸船机的工作过程导出了结构系统的动力方程及解法。最后给出了工程实际算例。     

喷射成形粉末高温合金FGH4095M的制备及组织特征

喷射成形是一种近净成形的在粉末冶金气体雾化制粉技术基础上发展起来的快速凝固技术. 本文采用喷射成形技术制备成分优化后的FGH4095M合金, 研究了喷射成形FGH4095M合金沉积坯的致密度、显微组织特征, 特别是研究了喷射成形高温合金组织中特殊形貌的γ’相. 研究表明, 致密度与沉积坯部位有关, 底部致密度最高, 可达99.63%, 热等静压后的致密度可达100%. 喷射成形合金组织以均匀细小的等轴晶为主, 不存在原始颗粒边界; 一次γ’ 相尺寸约为0.6-0.8 μm, 二次γ’相尺寸约为0.1-0.5 μm, 在二次γ’相的间隙中有少量尺寸约为10-20 nm的三次γ’相. 喷射成形FGH4095M 合金中的二次 γ’相中出现特殊形貌的γ’相, 这是由单个γ’颗粒分裂形成, 与沉积过程的低冷却速度有关. 分裂过程是γ’颗粒总能量降低的过程, γ’颗粒间的弹性交互作用能起到主导作用. 对分裂γ’相的等效直径进行统计, 得到γ’ 相等效直径超过0.40 μm 后, 会出现分裂趋势. 合金具备优异的拉伸性能, 室温塑性得到显著提高, 出现γ’ 相分裂的特殊形貌组织是否对合金性能的提高产生直接影响仍需进行进一步的研究.