介绍了垂直沉降法和旋涂法制备SiO2胶体晶体,并对两种方法制备的胶体晶体在宏观形貌、微观结构及光子带隙性质进行了比较。采用改进的Stober法在乙醇介质中合成粒径不同、单分散性较好的SiO2微球,用垂直沉积法和旋涂法制备出有序性较好的密排结构的SiO2胶体晶体。宏观照片表明,用旋涂法制备的SiO2胶体晶体经白光照射出现的光柱呈6次对称,而垂直沉降法制备的胶体晶体表面出现条纹。SEM分析表明,选用不同溶剂在同等旋涂工艺下制备SiO2胶体晶体,用乙醇和乙二醇混合溶液作溶剂制备出的SiO2胶体晶体质量最好。透射光谱表明,垂直沉降法所制备的胶体晶体在(111)方向具有明显的光子带隙性质,而旋涂法制备的胶体晶体则不明显。 相似文献
62.
采用3维时域有限差分方法和完全匹配吸收层,模拟了长方体缺陷在熔石英前后表面时对入射激光为TM波的调制作用,绘出了截面上的电场强度分布及最大电场强度随熔石英深度变化的曲线,并进行了比较和分析。结果表明:缺陷在前表面上时,后表面附近的最大电场强度2.522 41 V/m大于缺陷附近的1958 83 V/m;缺陷在后表面上时,材料中的最大电场强度为2.799 38 V/m,且出现在后表面附近。无论该缺陷在前表面还是在后表面,最大电场强度都是出现在后表面附近,表明光学材料的后表面在一定程度上更容易被损伤。 相似文献
63.
Incident laser modulation of a repaired damage site with a rim in fused silica rear subsurface 下载免费PDF全文
Local CO2 laser treatment has proved to be an effective method to prevent the 351-nm laser-induced damage sites in a fused silica surface from exponentially growing, which is responsible for limiting the lifetime of optics in high fluence laser systems. However, the CO2 laser induced ablation crater is often surrounded by a raised rim at the edge, which can also result in the intensification of transmitted ultraviolet light that may damage the downstream optics. In this work, the three-dimensional finite-difference time-domain method is developed to simulate the distribution of electrical field intensity in the vicinity of the CO2 laser mitigated damage site located in the exit subsurface of fused silica. The simulated results show that the repaired damage sites with raised rims cause more notable modulation to the incident laser than those without rims. Specifically, we present a theoretical model of using dimpled patterning to control the rim structure around the edge of repaired damage sites to avoid damage to downstream optics. The calculated results accord well with previous experimental results and the underlying physical mechanism is analysed in detail. 相似文献
64.
Surface defects,stress evolution,and laser damage enhancement mechanism of fused silica under oxygen-enriched condition 下载免费PDF全文
Wei-Yuan Luo 《中国物理 B》2022,31(5):54214-054214
Oxygen ions (O+) were implanted into fused silica at a fixed fluence of 1×1017 ions/cm2 with different ion energies ranging from 10 keV to 60 keV. The surface roughness, optical properties, mechanical properties and laser damage performance of fused silica were investigated to understand the effect of oxygen ion implantation on laser damage resistance of fused silica. The ion implantation accompanied with sputtering effect can passivate the sub-/surface defects to reduce the surface roughness and improve the surface quality slightly. The implanted oxygen ions can combine with the structural defects (ODCs and E' centers) to reduce the defect densities and compensate the loss of oxygen in fused silica surface under laser irradiation. Furthermore, oxygen ion implantation can reduce the Si-O-Si bond angle and densify the surface structure, thus introducing compressive stress in the surface to strengthen the surface of fused silica. Therefore, the laser induced damage threshold of fused silica increases and the damage growth coefficient decreases when ion energy up to 30 keV. However, at higher ion energy, the sputtering effect is weakened and implantation becomes dominant, which leads to the surface roughness increase slightly. In addition, excessive energy aggravates the breaking of Si-O bonds. At the same time, the density of structural defects increases and the compressive stress decreases. These will degrade the laser laser-damage resistance of fused silica. The results indicate that oxygen ion implantation with appropriate ion energy is helpful to improve the damage resistance capability of fused silica components. 相似文献
65.
66.
67.
68.
69.
70.
针对短脉冲激光打靶用溅射防护聚合物薄膜做了初步研究。研究了氟化乙丙共聚物(FEP)、全氟烷氧基共聚物和乙烯-四氟乙烯共聚物三种厚度均为25μm的聚合物薄膜的透过率,结果表明FEP薄膜在355nm处光透过率达93%,有望用于激光打靶的溅射防护。进一步对FEP聚合物薄膜的波前畸变、激光损伤阈值进行了研究,结果表明φ80mm的聚合物薄膜在632.8nm处的透射波前畸变的峰谷值(PV值)为波长的1.006倍;在采用输出波长355nm,脉冲宽度9.3ns的Nd:YAG激光为照射光源波长处,薄膜零损伤概率时的最高激光能量密度为10.35J/cm2,100%损伤概率时的最低激光能量密度为11.48J/cm2。 相似文献