水菱钇型碳酸钕的形成及聚甘油脂肪酸酯对结晶的影响

Amorphous Neodymium carbonate was prepared by the precipitation reaction of neodymium chloride with ammonium bicarbonate in solution, and then aged at 60 ℃ to form crystalline neodymium carbonate. The feed molar ratio of n_(NH4HCO3)/n_(NdCl3 was 2.5, and the precipitation was carried out with or without addition of polyglyceryl fatty acid ester (PGFAE). The phase type and morphology of crystalline neodymium carbonates were examined by XRD and SEM, and the effect of PGFAE on the crystallization speed was investigated by volume change in deposit layer and in situ pH determination. The content of neodymium and chloride in crystals was analyzed, and the crystallization reaction or crystal growth characteristics were discussed. It was found that all the crystalline neodymium carbonates were tengerite type, and contained less crystalline water and chloride than that of lanthanite type neodymium carbonate crystallized at room temperature, which is beneficial to the production of neodymium carbonate with higher neodymium and lower chloride content. The addition of PGFAE not only could eliminate the foam formed during precipitation, but also could shorten crystallization time, and form large radiative-like shape conglomeration by the irregulative linkage of one dimension needle crystals. It is also suggested that the morphology and the chloride content of neodymium carbonate were dependent on the structure and crystal growth characteristics.     

离子吸附型稀土高效提取和分离技术进展

离子吸附型稀土资源(或称风化壳淋积型稀土资源)由于中重稀土含量高而得到国内外的广泛重视。对该类资源的开采和分离加工技术以及相关的环境保护问题进行了述评和讨论,包括矿山提取技术、萃取分离技术、沉淀结晶分离技术、材料前躯体制备技术和环境水处理技术。针对矿山开采中的主要问题,提出了该类稀土实现资源与环境保护性开采的环境工程模式及其对应的技术内涵;根据稀土市场和环境保护要求,讨论了离子吸附型稀土开发过程中今后需要开展的研究工作。     

5-4-(1H-四唑基)苯氧基-间苯二甲酸构筑的镉配位聚合物的合成、晶体结构及荧光性质

以柔性配体为原料,在水热条件下合成了1个新的三维镉配位聚合物{[Cd₂L（OH）（H₂O）]·2H₂O}_n（1）（H₃L=5-4-（1H-四唑基）苯氧基-间苯二甲酸）,并对其进行了元素分析、红外、紫外、热重、荧光以及单晶X-衍射表征及研究。单晶衍射结果表明,配合物结晶于三斜晶系P1空间群。配合物中,相邻的Cd（1）和Cd（2）原子通过μ₃-桥联的羟基形成1个四核镉簇单元。相邻的四核簇二级构筑单元通过5-4-（1H-四唑基）苯氧基-间苯二甲酸连接形成三维结构。配合物1的荧光测试表明该化合物是1个潜在的蓝色发光材料。     

基于浸取pH依赖性的离子吸附型稀土分类及高效浸取方法

研究了稀土及主要杂质离子被硫酸铵浸出的pH依赖性。结果证明稀土和钙镁等离子的浸取率在低酸度范围内随酸度增大有明显提高,继续提高酸度并不会进一步提高浸取率,而铝、铁、钪等易水解金属离子的浸取率随酸度增大而持续增加。据此,基于离子吸附型稀土的定义及浸取所需pH值的范围,将离子吸附型稀土进一步区分为易浸稀土和难浸稀土,其中难浸稀土是需要在弱酸性条件（pH≤4）下才能浸取的被胶体等强吸附剂吸附的稀土离子。由于在不同地区和不同矿层及不同粒级的样品中所含强吸附剂的量以及磨蚀pH（pH_d）和交换pH（pH_t）的不同,这两类离子吸附型稀土的比例不同。对于pH_d和pH_t值较高的矿样,适当提高浸取酸度可以显著提高稀土浸取率。为此,提出了分阶段浸取稀土并增加石灰水护尾工序来保证稀土浸取率和尾矿安全稳定性的原则流程。     

Gd2(CO3)3:Eu@SiO2@APTES 磁性-荧光双功能核壳微球的制备与性能

采用尿素均相沉淀法和Stöber法制备了氨基化SiO₂修饰Gd₂(CO₃)₃:Eu顺磁性-荧光双功能微球.用扫描电镜(SEM)、红外光谱(IR)、X-射线粉末衍射(XRD)等测试手段对微球的结构和颗粒特征进行了分析.结果表明:微球为核壳结构,其Gd₂(CO₃)₃:Eu核平均直径为150 nm左右,SiO₂壳层的厚度大约为30 nm,分散性良好.磁性测试显示微球拥有良好的顺磁性,荧光光谱表明,在396 nm紫外光激发下,微球在613 nm发射较强荧光,属于Eu³⁺的特征发射,同时微球能成功标记NCIH460肺癌细胞,MTT毒性测试表明该法制备的双功能微球在100~400 μg·mL^-1的浓度范围内无毒,表明其在生物应用方面的潜在应用价值.     

Preparation,Structure, Fluorescence,Semiconductor Properties and TDDFT Calculation of a Mononuclear Zinc Complex with Mixed Ligands

A novel zinc complex[ZnL(bipy)(H2O)]×H2O with mixed ligands of 3-hydroxy-2-methylquinoline-4-carboxylic acid(HL)and bipy(bipy=2,2'-bipyridine)was synthesized by solvothermal reaction and its crystal structure was determined by single-crystal X-ray diffraction technique.The title compound crystallizes in the orthorhombic system of Pbca space group,and exists as an isolated mononuclear complex.The intermolecular hydrogen bonds and strongπ…πstacking interactions form a three-dimensional(3-D)supramolecular network.Solid-state photoluminescence spectrum reveals that it shows an emission in the blue region of the light spectrum.Time-dependent density functional theory(TDDFT)calculations reveal that this emission can be attributed to ligand-to-ligand charge transfer(LLCT).Solid-state diffuse reflectance data show that there is a narrow optical band gap of 1.83 eV.     

碳酸铈的相态转变及其对物性化学指标的调谐

为了获得同时具有高堆密度、低氯根和细颗粒特征的CeO_2,研究了在碱性热水溶液中镧石型碳酸铈向碱式碳酸铈相态转变的条件和特点。结果表明:在95℃下,随着溶液pH值的提高和反应时间的延长,相态转化越彻底,所得产物的颗粒大小和分布范围均减小,堆密度增大,氯根含量降低。当溶液pH在12～13时,经4 h的陈化可以得到纯的碱式碳酸铈。原始碳酸铈的颗粒度为22.3μm,氯根含量为1814 mg·kg~(-1),堆密度为0.55 kg·L~(-1),相态转化后的颗粒度下降到1～2μm,氯根含量降低到100 mg·kg~(-1)以下,堆密度上升到1 kg·L~(-1)以上。与此同时,碱的加入可以促进相态转化速度和程度,减少气泡产生。据此,确定了碱的加量。工业应用结果证明,采用该方法可以制备D_(50)为1～2μm,氯根含量小于100 mg·kg~(-1),堆密度介于1.1～1.2 kg·L~(-1)的CeO_2产品。     

Gd2(CO3)3:Eu@SiO2@APTES磁性-荧光双功能核壳微球的制备与性能

采用尿素均相沉淀法和Stöber法制备了氨基化SiO₂修饰的Gd₂(CO₃)₃:Eu顺磁性-荧光双功能微球。用扫描电镜(SEM)、红外光谱(IR)、X-射线粉末衍射(XRD)等测试手段对微球的结构和颗粒特征进行了分析。结果表明:微球为核壳结构,其Gd₂(CO₃)₃:Eu核平均直径为150nm左右,SiO₂壳层的厚度大约为30nm,分散性良好。磁性测试显示微球拥有良好的顺磁性,荧光光谱表明,在396nm紫外光激发下,微球在613nm发射较强荧光,属于Eu³⁺的特征发射,同时微球能成功标记NCIH460肺癌细胞,MTT毒性测试表明该法制备的双功能微球在100~400μg·mL^-1的浓度范围内无毒,表明其在生物应用方面的潜在应用价值。     

镧石型碳酸镨钕向碱式碳酸镨钕的相转变反应特征及其应用

镧石型碳酸镨钕[(PrNd)2(CO3)3·8H2O,LPN]在95℃的不同起始pH值的溶液中陈化不同时间所得样品的XRD衍射图证明了LPN向碱式碳酸镨钕[(PrNd)(OH)(CO3),BPN]的相态转变。为此,详细研究了这一相态转变的反应条件以及粒子特征变化。结果表明:LPN是由片状或条状结晶连生而成的聚集体,具有大的粒度和小的堆密度。当在热的水溶液中陈化时,由于水解反应而发生由LPN向BPN的相转变。这一相转变可以在95℃下pH=7以上的溶液中发生,其转化率随起始溶液pH值的升高和陈化时间的延长而增大。随着相转变的进行,溶液的pH值开始下降明显,而后趋于平缓。相应地,大的团聚体颗粒解散成小的单个粒子,导致粒度减小,分布变窄,氯根含量降低和堆密度的增大。而且,这些变化直接与溶液pH值和陈化时间相关。据此,发展了一种新的制备具有高堆密度、低氯根含量、细粒度和窄分布的新方法,而且通过改变相转变条件可以方便地调谐颗粒特征。     

5-4-(1H-四唑基)苯氧基-间苯二甲酸构筑的镉配位聚合物的合成、晶体结构及荧光性质(英文)

以柔性配体为原料,在水热条件下合成了1个新的三维镉配位聚合物{[Cd2L(OH)(H2O)]·2H2O}n(1)(H3L=5-4-(1H-四唑基)苯氧基-间苯二甲酸),并对其进行了元素分析、红外、热重、荧光以及单晶X-衍射表征及研究。单晶衍射结果表明,配合物结晶于三斜晶系P1空间群。配合物中,相邻的Cd(1)和Cd(2)原子通过μ3-桥联的羟基形成1个四核镉簇单元。相邻的四核簇二级构筑单元通过5-4-(1H-四唑基)苯氧基-间苯二甲酸连接形成三维结构。配合物1的荧光测试表明该化合物是1个潜在的蓝色发光材料。