α-Al2O3单晶的热释光和光释光特性

研究了纯α-Al₂O₃单晶的热释光发光曲线和三维发光谱，以及光释光衰变曲线，对它们的发光机理和剂量学特性进行了分析和讨论.实验观察到α-Al₂O₃单晶β射线照射后立即测量的热释光发光曲线，有峰温为76℃和207℃两个发光峰.经γ射线照射数小时后测量的三维发光谱，只有峰温207℃波长为416 nm发光峰，它与α-Al₂O₃:C晶体的发光波长基本相同，是受热激发到导带的电子与F< 关键词： 2O₃')" href="#">α-Al₂O₃ 三维发光谱 TL/OSL剂量响应     

一个凸轮边缘曲线检验的数学模型

加强数学应用问题的教学已成为数学教学与研究的热门课题．解答数学应用问题的关键是建立数学模型．一个构建较好的数学模型，对学生的能力培养和智力开发具有十分重要的意义，一个来自生产第一线又符合学生数学知识水平的数学模型对学生的教益可能更大．为此，笔者提供一...     

Third-Order Optical Nonlinearity of a Novel Material：（Tetramethylammonium） bis （1,3-dithiole-2-thione-4,5-dithiolato） Copper

A novel dmit^2- salt： （tetramethylammonium）bis（1,3-dithiole-2-thione-4,5-dithiolato） copper, abbreviated as MECu, is synthesized and its third-order optical nonlinearity is characterized by Z-scan technique at a wavelength of 1064nm with laser duration of 30ps. Z-scan curves reveal a negative Kerr coefficient at 1064nm and no nonlinear absorption is observed. The nonlinear refraction coefficient n2 and the second hyperpolarizability γ have been determined to be as large as 2.15 × 10^-11 esu and 3.23 × 10^-31 esu, respectively, suggesting MECu is a potential material for optical device applications.     

SrSO4:Eu磷光体的光释光特性

研究了通过掺杂得到的SrSO4:Eu(0.1mol%)的粉末样品的光释光(OSL)特性.用90Sr的β射线辐照0.116-1.16kGy后,测定了恒定光源激发的光释光发光曲线(CW-OSL)和线性光源激发的光释光发光曲线(LW-OSL),对发光曲线分析均得到了四种陷阱成分.采用复合作用响应函数得到SrSO4:Eu辐射剂量响应为线性-亚线性.测量了温度对OSL信号的影响,结果表明OSL信号的温度稳定性很好,最灵敏读出温度约为180℃,说明这时OSL信号来自热激发和光激发的共同作用.用60Coγ辐照100Gy后,测量了热释光(TL)三维光谱,确定了发光波长主要位于375nm,可以确定这是来自于Eu2+能级跃迁的发光.     

补偿法在电磁学教学中的应用

在物理学习中，有些问题因为某些物理量分布的不对称，常使问题复杂化，直接应用某些公式或定理求解时遇到困难，本文介绍的“补偿法”，可将一些相关物理量不对称分布的问题巧妙地转化为在一定假设条件下的对称问题从而使复杂问题得以简化．下面就“补偿法”在电磁学计算方面的应用做一介绍．     

SrSO4:Eu磷光体的光释光特性

研究了通过掺杂得到的SrSO4:Eu(01mol%)的粉末样品的光释光(OSL)特性.用90Sr的β射线辐照0116—116kGy后，测定了恒定光源激发的光释光发光曲线(CW-OSL)和线性光源激发的光释光发光曲线(LW-OSL)，对发光曲线分析均得到了四种陷阱成分.采用复合作用响应函数得到SrSO4:Eu辐射剂量响应为线性-亚线性.测量了温度对OSL信号的影响，结果表明OSL信号的温度稳定性很好，最灵敏读出温度约为180℃，说明这时OSL信号来自热激发和光激发的共同作用.用60Coγ辐照100Gy后，测量了热释光(TL)三维光谱，确定了发光波长主要位于375nm，可以确定这是来自于Eu2+能级跃迁的发光. 关键词： 光释光 热释光 SrSO4:Eu     

A MICROSCOPIC MECHANISM OF LOW TEMPERATURE HELIUM RELEASE

⁴He ions of various energies and at various doses were implanted into three kinds of samples: TiH₂ films, high purity Ti pieces as-received and after hydrogenation. Thermal release of helium was monitored in situ by proton-enhanced backscattering. Low-temperature helium release was observed at T≤573K. Single jump model was used to calculate the active energies for the release. Based on the observations, a mechanism of helium cluster vacancy complex (He_mV_n-V_i) for low temperature helium release is proposed.     

α-Al2O3: Mn单晶的三维热释发光谱研究

测量了α-Al2O3: Mn单晶中子辐照前后的三维热释发光谱.观察到α-Al2O3: Mn:Mn单晶γ射线照射后测量的三维热释发光谱中，峰温在350℃波长为680nm处有一宽发光峰，这可能与Mn2+离子有关；波长为695nm峰温在170℃和350℃的线状光谱，叠加在680nm宽发光峰上，是Cr3+离子的发光谱线,其中可能有Mn4+离子的贡献.与纯α-Al2O3单晶的热释发光谱相比，掺入Mn杂质后，γ射线照射的三维热释发光谱中完全地抑制了波长为416nm的α-Al2O3的F心发光峰.经1017cm-2中子注量辐照和退火后，γ射线照射后测量的三维热释发光谱中，在150℃出现了波长为416和695nm的发光峰，以及在250℃波长为680和695nm的发光峰，其中695nm新发光峰的强度略超过了中子辐照前α-Al2O3:Mn在350℃波长为695nm的发光峰，说明中子辐照产生了大量浅陷阱能级和F心.然而，经1018cm-2中子注量辐照和退火后，γ射线照射后测量的三维热释发光谱中，出现了峰温150℃，190℃和250℃波长为520nm的Mn2+离子发光峰，以及300℃波长为680和695nm的Cr3+（或Mn4+）的发光峰，表明增高中子注量的辐照，产生了温度为190℃，250℃和300℃深陷阱能级和F心，并使Mn2+离子发光峰明显加强. 关键词： α-Al2O3:Mn 三维发光谱 缺陷结构 发光机理     

三聚氰胺对吖啶橙-茜素红体系的荧光猝灭效应及其在药物分析中的应用

研究发现,在p H 6.0酸性条件下,当茜素红和吖啶橙混合时,茜素红能使吖啶橙的荧光少量猝灭。加入适量三聚氰胺后,由于其分子是一个富电子的大π键结构,可与电子接受体的茜素红发生荷移反应形成络合物。该络合物与吖啶橙之间能够发生有效能量转移,从而使吖啶橙的荧光强度减弱更明显,且其荧光信号的减弱程度与三聚氰胺的加入量呈良好线性关系。据此建立了吖啶橙-茜素红体系荧光猝灭法测定三聚氰胺含量的新方法。在优化条件下,三聚氰胺的线性范围为3.38×10-7~2.40×10-4mol·L-1,检出限为1.02×10-7mol·L-1,方法精密度为1.1%。该方法用于市售牛奶及奶粉中三聚氰胺的测定,其回收率为97.7%~102%。该方法成本低、简单、快速、准确。同时,通过紫外可见光谱法对方法机理做了深入探讨。