21.
以硝酸锂、偏钒酸铵、硝酸钙、硝酸镁、正硅酸乙酯为原料,采用溶胶-凝胶法低温合成纳米CaMgSi2O6微波介质陶瓷粉体,研究了不同粒径粉体的烧结行为与微波介电性能。结果表明,通过在钙镁硅溶胶中引入锂钒烧结助剂可大大降低陶瓷粉体的晶相合成温度,干凝胶在750 ℃煅烧后可获得主晶相为CaMgSi2O6、分散性良好、粒径为78~98 nm的陶瓷粉体,可满足微型片式元器件用超薄陶瓷介质层的制备要求;该粉体在890 ℃烧结后获得致密结构的陶瓷,具有良好的微波介电性能:介电常数为7.68,品质因数为24 542 GHz,频率温度系数为-57.25×10-6 ℃-1。 相似文献
22.
制备了新型掺Er3+铋铅锶玻璃,研究了玻璃的吸收光谱和上转换光谱性质,应用Judd-Ofelt理论计算了铋铅锶玻璃的3个强度参量Ωt(t=2,4,6),分别为Ω2=3·27×10-20cm2,Ω4=1.15×10-20cm2,Ω6=0.38×10-20cm2。计算了Er3+离子的振子强度、自发辐射跃迁几率、荧光分支比和辐射寿命等光谱参数。研究了上转换发光强度随泵浦激光功率的变化,上转换荧光525,546和657nm曲线的斜率分别为1·86,1·88和1·85,表明红、绿光发射均为双光子吸收过程。 相似文献
23.
Infrared-to-visible upconverted luminescent spectra of Er3 t and La3 t codoped Y2O3 powders are investigated.By introducing La3 t ions, the upconversion green radiation is found to be greatly enhanced when compared with the powders with La3 t absent. Such enhancement can be attributed to the modification of the local symmetry surrounding the Er3 t ion, which benefits the intra-4f transitions of Er3 t ion, and the decreasing interaction between Er3 t ions, which suppresses the energy transfer process4F7∕2t 4I11∕2→ 4F9∕2t 4F9∕2. 相似文献
24.
研究了Yb2O3浓度对Tm3 /Yb3 共掺氧卤碲酸盐玻璃的上转换发光的影响,分析了上转换发光机理。结果发现,通过980 nm的激光二极管激发,在室温下同时观察到强烈的蓝光(475 nm)和微弱的红光(649 nm),分别是由于Tm3 离子1G4→3H6和1G4→3F4跃迁产生的;上转换机理分析表明,上转换蓝光和红光都是由于双光子吸收过程。随Yb2O3浓度增加,Yb3 离子寿命降低,Yb3 到Tm3 的能量转移效率增加,上转换蓝光和红光强度先增加,在Yb2O3摩尔比为3时达到最大,然后降低。分析认为,Yb3 的浓度猝灭主要是由于3H4(Tm3 )→2F5/2(Yb3 )反向能量转移的结果。结果表明Yb3 敏化Tm3 掺杂氧卤碲酸盐玻璃是一种上转换蓝光激光器的潜在基质材料。 相似文献
25.
26.
27.
Er^3 -doped strontium-lead-bismuth glasses for developing potential upconversion lasers have been fabricated and characterized. Under 975 nm excitation, intense green and red emissions centred at 525, 546, and 657nm,corresponding to the transitions ^2H11/2 → ^4I15/2, ^4S3/2 → ^4I15/2, and ^4F9/2 → ^4I15/2, respectively, were observed at room temperature. The upconversion mechanisms are discussed based on the energy matching and quadratic dependence on excitation power, and the dominant mechanisms are excited state absorption and energy transfer upconversion for 525 and 546nm emissions, and energy transfer upconversion for 657nm emission. 相似文献
28.
研究了Tm3+/Ho3+共掺TeO2-WO3-ZnO玻璃在808 nm激光二极管抽运下的2.0μm发光特性及Tm3+与Ho3+之间的能量传递.应用Judd-Ofelt理论计算了Ho3+在碲酸盐玻璃中的谱线强度参量Ωt(t=2,4,6)、自发辐射概率Ar、辐射寿命τr等.计算了Ho3+的吸收截面σa(λ)和受激发射截面σa(λ).结果表明:碲酸盐玻璃中Tm3+→Ho3+正向能量传递系数大约是Tm3+←Ho3+反向能量传递系数的18倍.Ho3+离子的5I7能级的寿命为3.9 ms,2.0 μm处的最大发射截面为9.15×10-21cm2.在O.5 mol%Tm2O3和0.15 mol%Ho2O3共掺的碲酸盐玻璃中能获得2.0μm的最大增益.通过比较氟化物、碲酸盐和镓铋酸盐重金属氧化物等玻璃中Ho3+的量子效率η,σe×τm值和增益系数G(λ)等,发现Tm3+/Ho3+共掺碲酸盐玻璃是一种理想的2.0μm激光器用基质玻璃. 相似文献
29.
Er^3+-doped phosphor-tellurite glass for broadband short-length Er^3+-doped fiber amplifier (EDFA) is fabricated and characterized. The differential value (AT) of onset crystalline temperature (Tx) and glass transition temperature (Tg) is 206 ℃. The stimulated emission cross section of Er^3+ is calculated from absorption spectrum by McCumber theory and is 0.87 × 10 ^-20 cm^2 at 1532 nm. A broad 1.5-μm fluorescence spectrum with 54-nm full-width at half maximum (FWHM) is demonstrated. Especially, the maximum phonon energy of undoped phosphor-tellurite glass is 1100 cm^- 1, which restricts the upconversion luminescence. It is possible to pump efficiently at 980 nm. These results indicate Er^3+-doped phosphor-tellurite glass is suitable for fabricating broadband short-length EDFA. 相似文献
30.
We have prepared Er^3 -doped borotellurite glasses using conventional melting and quenching method.The absorption spectrum analysis is performed on the basis of Judd-Ofelt theory.The effects of B2O3 on the spectroscopic parameters such as intersity parameters,line strengths of electric-dipole transitions,and sopontaneous emission probability are discussed. 相似文献