Yb:YAG晶体的晶胞参量及Yb3+分凝系数的研究

应用提拉法生长出不同Yb³⁺浓度的Yb_3xY_3(1-x)Al₅O₁₂晶体.Yb³⁺离子的分凝系数1是1.08±0.01,与Yb³⁺离子掺杂浓度无关.研究了Yb_3xY_3(1-x)Al₅O₁₂晶体的晶胞参量,推导出联系晶胞参量、密度与Yb³⁺离子掺杂浓度的关系方程式.     

毛细管区带电泳检测抗EGFR抗体的电荷异质性

建立了抗表皮生长因子受体(EGFR)抗体电荷异质性的检测方法。采用毛细管区带电泳(CZE)模式,考察了分离缓冲液浓度和p H值、添加剂、分离电压、毛细管温度对主峰与酸碱性变体分离度的影响。以380 mmol·L~(-1)6-氨基己酸(EACA,pH 6.0)为分离缓冲液,0.1%羟丙基甲基纤维素(HPMC)和1.9mmol·L~(-1)三亚乙基四胺(TETA)作为添加剂,分离电压25 k V,分离时间8 min,毛细管温度20℃条件下,电荷变体能够得到良好分离,且在0.1~1 mg·m L~(-1)范围内线性关系良好,相关系数均大于0.99,主成分、酸、碱变体1和碱变体2的定量下限(LOQ)分别为30.0,150.2,125.2,93.3μg·L~(-1),重复性和中间精密度RSD值小于2%,回收率为95.4%~105.4%。该方法简单、快速、成本低,可以满足抗EGFR抗体的电荷异质性检测要求。     

The effect of polymer-substrate interaction on the nucleation property: Comparing study of graphene and hexagonal boron nitride Nanosheets

Hexagonal boron nitride nanosheets (BNNSs) can work as a more efficient nucleating agent for two polyesters compared to graphene. Studies on the crystallization and dewetting processes of two polyesters, poly(butylene succinate) and poly(butylene adipate), on the two substrate surfaces prove that the interaction between BNNSs and the polyesters is stronger than that between graphene and the polyesters. This strong interaction induces the pre-ordered conformation of molten PBA which has been identified by the in situ FTIR spectra. Thus BNNSs possess higher nucleation property than graphene. Finally, a new polymer-substrate interaction induced nucleation mechanism was proposed to explain the nucleation efficiency difference between graphene and BNNSs.     

Gd3+/Y3+共掺对Nd:CaF2晶体光谱性能的影响

通过坩埚下降法生长了系列共掺Nd,Gd:CaF₂和Nd,Y:CaF₂晶体, 研究了Gd³⁺/Y³⁺共掺对Nd³⁺光谱性能以及Nd:CaF₂晶体晶胞参数的影响规律. 对于0.5 at.%Nd, x at.%Gd(x=2,5,8,10):CaF₂系列晶体, 当调控Gd³⁺掺杂浓度为2 at.%时, 具有最大的荧光寿命499 μs; 当Gd³⁺掺杂浓度为5 at.%时, 具有最大的吸收截面1.47×10^-20 cm², 最大的发射截面1.9×10^-20 cm²; 当Gd³⁺掺杂浓度为8 at.%时, 具有最佳的发射带宽29.03 nm. 对于0.6 at.%Nd, xat.%Y(x=2, 5, 8, 10):CaF₂系列晶体, Y³⁺掺杂浓度为5 at.%时, 有最大的吸收截面2.41×10^-20 cm², 最大的发射截面3.17×10^-20 cm²; 当Y³⁺掺杂浓度为10 at.%时, 具有最长的荧光寿命359.4 μs,并且具有最大发射带宽26 nm.     

High-power and wavelength tunable diode-pumped continuous wave Yb:SSO laser

A wavelength-tunable,efficient,and high-average power single diode-pumped continuons wave(CW) Yb:SSO laser is reported.A maximum output power of 8.8 W at 1 062.6 nm is obtained using the absorbed pump power of 11.7 W,which corresponds to a slope efficiency of 85.5% and an optical-to-optical conversion efficiency of 48.9%.The wavelength tuning of the Yb:SSO laser pumped by the 976-nm LD is also investigated.The results show the tuning range from 1 002.30 to 1 068.47 nm,which corresponds to a tunability range of 66.17 nm.     

多孔坩埚温度梯度法生长Ho,Y∶CaF2晶体及其光谱性能

采用自主设计改造的温梯炉,成功生长了不同浓度Ho³⁺、Y³⁺掺杂的CaF₂及Sr_xCa_1-xF₂晶体,晶体尺寸约为ϕ15 mm×55 mm,生长周期约为6 d,能够实现7种不同浓度晶体的同步生长,并选取其中的4%(原子数分数)Ho,4%Y∶CaF₂晶体进行分析,吸收测试表明,该晶体448 nm和643 nm处吸收峰的吸收截面分别是1.13×10^-20 cm²和0.84×10^-20 cm², J-O理论分析得到了晶场强度参数Ω_t(t=2、4、6)、辐射跃迁几率、荧光分支比和辐射寿命。在448 nm氙灯激发下,经计算得到该晶体在546 nm、650 nm 和752 nm处的发射截面分别为10.450×10^-21 cm²、8.737×10^-21 cm²和5.965×10^-21 cm²,测得⁵F₄和⁵F₅能级的寿命分别为33.5 μs和17.7 μs。在640 nm LD泵浦激发下,经计算得到该晶体2 031 nm处发射截面为5.375×10^-21 cm²,2 847 nm处发射截面为10.356×10^-21 cm²,测得⁵I₇和⁵I₆ 能级的寿命分别为4.37 ms 和1.85 ms。以上结果表明,多孔坩埚温梯法能够大大提高激光晶体稀土离子掺杂浓度筛选的效率,加快新型激光晶体材料的研发速度。     

Yb:Y3Al5O12晶体晶格振动光谱的研究

采用提拉法生长Y3Al5O12(YAG)晶体和Yb3 掺杂原子数分数分别为5%,10%,15%,20%,25%,50%和100%的Yb:Y3Al5O12(Yb:YAG)晶体.系统表征和分析了Yb3 掺杂浓度对拉曼光谱的影响.随着Yb3 掺杂浓度的增加,晶体的振动模式没有明显的变化,晶体结构没有改变;在370 cm-1和785 cm-1附近,振动吸收峰的半峰全宽逐渐增大.分析得出,Yb3 掺杂浓度对晶体的晶格、对称性、荧光寿命均有影响,从而可能影响到晶体的光谱和激光性能.     

气相平衡扩散法制备β-BBO薄膜

用气相平衡扩散(VTE)法在α-偏硼酸钡单晶衬底上成功地制备出β-偏硼酸钡薄膜.使用X射线衍射技术(XRD)测试了样品的衍射峰,并比较了不同温度、不同保温时间、不同衬底方向对薄膜的影响.     

溶胶-凝胶法制备MgxZn1-xO及其特性

采用溶胶-凝胶法制备了不同组分(x=0.1～0.3)的MgxZn1-xO前驱体,并对它进行不同温度的热处理(550℃～1000℃).X射线衍射(XRD)结果表明,Mg0.1Zn0.9O具有和ZnO一样的衍射谱,为六方纤锌矿结构,而且随着热处理温度的升高,ZnO衍射峰的强度逐渐增强,半高宽不断减小;Mg元素掺杂浓度增大后,出现了MgO的峰位.扫描电子显微镜(SEM)显示Mg0.1Zn0.9O晶粒粒径分布较均匀;热处理温度升高,晶粒的尺寸不断变大.用室温荧光光谱(PL)分析了经过550～1000℃热处理获得的Mg0.1Zn0.9O粉末,结果发现除了550℃下处理的样品,其它都有紫外发射峰(350nm左右),而且随着热处理温度的升高紫外峰有明显的蓝移现象.