101.
研究了一种新型掺Er3+碲酸盐玻璃的光谱性质;应用Judd-Ofelt理论计算了碲 酸盐玻璃中Er3+离子的强度参数Ω(Ω2=479×10-20 cm2,Ω4= 152×10-20cm2,Ω6=066×10-20cm2),计算了离子的自发跃迁概 率,荧光分支比;应用McCumber理论计算了Er3+的受激发射截面(σe=1040×1 0-21cm2),Er3+离子4I13/ 2→4I15/2发射谱的 荧光半高宽(FWHM=655nm)及各能级的荧光寿命(4I13/2 能级为τrad =399ms);比较了不同基质玻璃以及不同类型碲酸盐玻璃中Er3+离子的光谱 特性, 结果表明该掺铒碲酸盐玻璃具有更好的光谱性能,更适合于掺Er3+光纤放大 器实现宽带和高增益放大.
关键词:
碲酸盐玻璃
光谱性质
Judd-Ofelt理论 相似文献
102.
103.
测试了不同掺杂浓度和不同厚度下Yb3+ 磷酸盐玻璃的吸收光谱、荧光光谱和荧光寿命 ,计算了积分吸收截面、吸收截面、受激发射截面、自发辐射寿命以及荧光有效线宽等光谱参数 ,讨论了荧光俘获效应对Yb3+ 磷酸盐玻璃光谱性质的影响 .结果表明荧光俘获效应随样品厚度和掺杂浓度的增加而增大 .由于荧光俘获效应的存在使得测量的Yb3+ 磷酸盐玻璃荧光寿命明显长于计算的荧光寿命 ,在 0 2mol%Yb2 O3低掺杂浓度下采用不同厚度 ( <4mm)的样品测量的荧光寿命之间误差为 3 0 %左右 ,高浓度 ( 6mol%Yb2 O3)掺杂下误差可达 43 % .荧光俘获还造成荧光谱线加宽 ,导致荧光有效线宽在低浓度 ( 0 2mol%Yb2 O3)时增加 14% ,在高掺杂浓度 ( 6mol%Yb2 O3)下增加 3 0 %以上 相似文献
104.
Er^{3+}-doped lead chloride tellurite glasses were prepared using the conventional melting and quenching method. The absorption spectra were measured and the Judd-Ofelt analysis was performed. The spectroscopic parameters such as the intensity parameters, transition probabilities, radiative lifetimes, and branching ratios were obtained. Intense infrared emission and visible upconversion luminescence under 976 nm excitation were observed. For the 1.55μm emission, the full width at half maximum and the emission cross sections are more than 50 nm and 8×10^{- 20}cm^2, respectively. Three efficient visible luminescences centred at 525, 547, and 658nm are assigned to the transitions from the excited states {}^{2}H_{11/2}, {}^{4}S_{3/2}, and {}^{4}F_{9/2} to the ground state {}^{4}I_{15/2}, respectively. The upconversion mechanisms and the power-dependent intensities are also discussed and evaluated. 相似文献
105.
106.
OH~-对磷酸盐铒玻璃光谱性质的影响 总被引:1,自引:1,他引:0
本文系统研究了 Yb3 + 、Er3 + 共掺磷酸盐铒玻璃中 OH- 含量与铒玻璃荧光寿命和光谱性质的关系 .结果表明 OH- 基团的存在使得 Er3 + 离子的荧光强度显著降低 ,荧光寿命大大缩短 .比较了三种不同 Al2 O3 含量 ( 5mol% ,8mol%和 1 3 mol% )的铒玻璃在 2 .9μm波长处的红外吸收系数与铒离子荧光寿命的关系 ,发现玻璃中 OH- 在 2 .9μm的吸收系数和 Er3 +的4 I13 / 2 能级离子衰减速率成线性关系 ,不同 Al2 O3 含量的玻璃具有不同 Er3 + 和 OH- 基团的相互作用参量和不同的荧光寿命值及量子效率 .并从玻璃结构上解释了 Al2 O3 含量对除水机制和光谱性质的影响 .经过充分除水后的铒玻璃荧光寿命可达到 9.1 ms 相似文献
107.
Structural and Upconversion Fluorescence Properties of Er^3+/Yb^3+-Codoped Lead-Free Germanium-Bismuth Glass 下载免费PDF全文
We study the structural and infrared-to-visible upconversion fluorescence properties of Er^3 /yb^3 -codoped leadfree germanium-bismuth glass. The structure of lead-free germanium-bismuth-lanthanum glass is investigated by peak-deconvolution of F~aman spectroscopy. Intense green and red emissions centred at 525, 546, and 657nm,corresponding to the transitions ^2H11/2 → 4I15/2, ^4S3/2 → 4I15/2, and 4F9/2 → 4I15/2, respectively, are observed at room temperature. The quadratic dependence of the 525, 546, and 657nm emissions on excitation power indicates that a two-photon absorption process occurs under 975nm excitation. 相似文献
108.
Laser Characteristics of Cladding-Pumped Short Er^3+/yb^3+ Codoped Single Mode Phosphate Glass Fibre 下载免费PDF全文
We experimentally investigate the laser characteristics of a series of short pieces of newly-developed Er^3+/ Yb^3+ codoped single mode phosphate glass fibres via the cladding pump of a 976nm multimode laser diode. A stable continuous-wave single transverse mode laser with over 85 m W at 1553nm is generated from a 5.5-em-long active fibre. Single mode laser output power per unit length is up to 15 mW/cm. Moreover, the slope efficiency is 11.8% when the pump power is below 940mW and the 3dB linewidth is 0.06nm at the maximum pump power. The numerical simulation results show that the laser emission slope efficiency can exceed 20% by means of increasing the coupling efficiency of the pump to the fibre core further. 相似文献
109.
110.
Erbium-doped glass showing the wider 1.5-/μm emission band is reported in a novel oxide system TeO2-WO3-Nb2O5 and their thermal stability and optical properties such as absorption,emission spectra,cross-sections and fluorescence lifetime were investigated.Compared with other glass hosts,the gain bandwidthproperties of Er3+ in TWN glass is close to that of bismuth glasses,and larger than those of tellurite,germanatc,silicate and phosphate glasses.The broad and flat 4I13/2 → 4I15/2 emission and the largestimulated emission cross-section of Er3+ ions around 1.5 μm can be used as host material for potentialbroadband optical amplifier in the wavelength-division-multiplexing(WDM)network system. 相似文献