应用化学"113"人才培养体系的探索

In order to bridge the gap between the supply and the demand of talent cultivation, the existing talent cultivation system of applied chemistry specialty is reformed and a new "113" talent cultivation system is guided by Outcome-Based Education (OBE) education. The advanced engineering education mode is adopted to provide students with an engineering education based on the background environment of the conceptual-design-implementation-operation (CDIO) process. The characteristic "three modernizations" education mechanism, namely, cooperative education, family training and personalized guidance, are implemented. By building a new system of "113" talents training, an engineering talent training environment is formed, which takes the family as a unit, the enterprise as the background, and the project as the carrier. The problem of separating the supply from the demand of talents training for applied chemistry specialty will be fundamentally solved.     

生物活性复合材料在生物矿化过程中的微观形貌与离子浓度变化

采用3-羟基丁酸酯-3-羟基戊酸酯的共聚物(PHBV)与磷酸三钙(TCP)、羟基磷灰石(HA)、生物活性玻璃(BG)等进行复合,获得了性能优良的生物活性骨组织工程支架材料和骨修复材料.研究和比较了3种复合材料在体外模拟生理环境中发生的生物矿化反应,对比了反应前后因矿化物的形成导致的表面微观形貌的变化,通过检测反应液离子浓度的变化对不同材料的矿化过程和生物活性进行了定量表征.研究结果表明,3种复合材料在模拟生理溶液中发生生物矿化的过程和程度不同,其中PHBV/BG的生物活性反应最为明显.     

聚合物基纳米复合材料性能及理论研究

对近些年来国内外聚合物／MMT纳米复合材料(polymer montmorillonite nanocomposites,PMN)的研究进行了归纳总结,详细讨论了该类材料结晶、流变和力学性能,阐述了合成过程中的热力学、动力学理论和平均场理论,最后对该类材料的制备方法提出展望。     

热塑性淀粉/蒙脱石复合材料性能研究

用柠檬酸活化蒙脱石(CMMT),用尿素和甲酰胺塑化热塑性淀粉(UFTPS),制备了热塑性淀粉/蒙脱石(UFTPS/CMMT)复合材料.广角X-ray衍射(WAXD)、透射电子显微镜(TEM)表明,UFTPS和CMMT形成复合材料.CMMT质量分数2%~10%时,将复合材料在相对湿度50%(RH=50%)的环境下保存10 d,力学测试得出,复合材料的最大拉伸应力达到24.86 MPa,应变为134.50%,杨氏模量和断裂活化能分别由UFTPS的87.25MPa,1.87 N.m上升到复合材料625.25 MPa,2.45 N.m;可以看出,和纯UFTPS相比,复合材料强度明显提高;流变行为研究得出,通过改变加工温度和螺杆挤出机速度可以调整复合材料的流变行为;与传统的甘油体系相比,复合材料很好的抑制了材料长时间放置的结晶行为;并且该材料比纯UFTPS具有很好的耐水性能和热稳定性.     

钇对掺饵多孔硅体系1.54μm发光的增强作用

首次报道了用恒电位电解法将饵、钇共掺入多孔硅（porous silicons, PS） 中，经高温退火处理后，观察到了在近红外区（1.54 μm）室温下较强的光致发光 （photoluminescence, PL），并与掺饵多孔硅（erbium-doped porous silicon, PS:Er）做了比较，发现钇的共掺入对掺饵多孔硅体系1.54 μm发射起了增强作用 。研究了饵、钇共掺杂多孔硅（erbium and yttrium co-doped porous silicon, PS:Er, Y）光致发光强度随温度的变化，发现PS:Er与Si:Er材料相似，有较强的 温度猝灭效应，而PS:Er，Y体系的PL强度随温度升高趋于平稳，且有增强的趋势， 受温度影响不明显，并初步探讨了其发光机制。     

对固体圆二色光谱测试方法的再认识——兼谈“浓度效应”

对近期发展的固体圆二色(CD)光谱测试方法进行了概述、评价和比较, 着重探讨了“浓度效应”的存在使固体CD光谱失真的原因. 通过对本课题组和其他作者已报道的四种化合物的固体CD谱再测试的反思, 强调了依手性化合物的手性光谱学性质不同, 根据浓度梯度实验选择其合适测试浓度的必要性. 对固有手性的阻转异构化合物(S)-1,1'-联二萘酚(S-BINOL)进行了成膜法固体CD谱浓度梯度测试, 发现所得固体薄膜CD谱中也存在着“浓度效应”     

N-芳亚甲基-4-(4-甲氧基苯基)-5-(1H-1,2,4-三唑-1-基)-1,3-噻唑-2-胺的合成与生物活性

通过2-氨基-4-(4-甲氧基苯基)-5-(1H-1,2,4-三唑-1-基)-1,3-噻唑与取代苯甲醛发生缩合,合成了一系列新型含三唑环的噻唑席夫碱类化合物.利用1H NMR和元素分析对所有化合物进行了结构表征.初步的毒性试验表明,部分标题化合物具有一定的抗肿瘤活性.     

利用糖芯片研究半乳寡糖与蓖麻凝集素和鸡冠刺桐凝集素间的相互作用

建立了用糖芯片技术研究寡糖与凝集素相互作用的方法.以新乳糖-N-四糖(LNnT)、乳糖-N-四糖(LNT)、λ-卡拉胶四糖(L4)和琼胶五糖(A5)为原料,经还原胺化法分别将其与1,2-十六烷基磷脂酰乙醇胺偶联得到拟糖脂,再将其与卵磷脂和胆固醇按4∶2∶5比例混合制备成脂质体后,用全自动芯片点样仪将其点印在硝酸纤维素膜包被的玻片上制成糖芯片,并进行寡糖与凝集素的结合实验.结果表明,蓖麻凝集素(Rieinus communis agglutinin 120,RCA120)特异性识别非还原端糖残基为Galβ(1 →4)的寡糖,而鸡冠刺桐凝集素(Erythrina cristagalli lectin,ECL)特异性识别非还原端糖残基为Galβ(1→4)GlcNAc的LNnT.采用接触式芯片点样仪制备糖芯片,并用荧光扫描仪对糖与凝集素结合信号进行检测,增加了灵敏度和准确性.本方法不仅适合于糖与蛋白相互作用的研究,也有助于加快糖类药物的发现.     

“化学一步法”制备电磁功能化聚吡咯/γ-Fe2O3复合物纳米球及结构表征

在不添加掺杂剂的条件下, 以吡咯为单体, 三氯化铁为氧化剂, 采用"化学一步法"合成了电磁功能化的聚吡咯/γ-Fe2O3 复合物纳米结构. 研究了不同氯化亚铁用量对聚吡咯/γ-Fe2O3 复合物形貌、 电学性能以及磁学性能的影响. 结果表明, 氯化亚铁的用量对聚吡咯/γ-Fe2O3复合物的形貌影响不大, 都得到了聚吡咯/γ-Fe2O3复合物纳米球; 然而, 聚吡咯/γ-Fe2O3复合物纳米球的电学和磁学性能却明显受到氯化亚铁用量的影响. 聚吡咯/γ-Fe2O3复合物纳米球的电导率和最大饱和磁化强度随着氯化亚铁用量的增加而增大, 并在氯化亚铁用量增加到150 mg时达到最大值, 分别为72.1 S/cm和10.07 A·m2/kg, 实现了高电学性能和高磁学性能兼顾的电磁功能化导电聚合物纳米结构的制备.     

铑配合物催化丁烯氢甲酰化性能的研究

制备了一系列铑配合物,并对其催化丁烯氢甲酰化的催化性能进行了研究.在1-丁烯的反应中,RhCl(PPh3)3和trans-RhCl(CO)(PPh3)2的反应速度很慢,而RhH(CO)(PPh3)3、Rh(CO)2(acac)和 Rh(CO)(acac)(PPh3)三者反应速度都很快.而不同丁烯原料氢甲酰化的反应速度也各不相同,反应速度依次为1-丁烯》2-丁烯》异丁烯.