1.
制备了新型掺Er3+铋铅锶玻璃,研究了玻璃的吸收光谱和上转换光谱性质,应用Judd-Ofelt理论计算了铋铅锶玻璃的3个强度参量Ωt(t=2,4,6),分别为Ω2=3·27×10-20cm2,Ω4=1.15×10-20cm2,Ω6=0.38×10-20cm2。计算了Er3+离子的振子强度、自发辐射跃迁几率、荧光分支比和辐射寿命等光谱参数。研究了上转换发光强度随泵浦激光功率的变化,上转换荧光525,546和657nm曲线的斜率分别为1·86,1·88和1·85,表明红、绿光发射均为双光子吸收过程。 相似文献
2.
Er~(3+)-doped fluoride lanthanum aluminosilicate glasses with compositions of (65-x/2)SiO_2·(25-x/2)Al_2O_3·xAlF_3·9.1La_2O_3·0.6Er_2O_3·0.3Yb_2O_3(x=4, 8, 12, 20, 30) (mol%) were prepared and their glass transition temperatures and spectroscopic properties were investigated.The Ω_2, Ω_4, and Ω_6 intensity parameters of glasses were calculated by Judd-Ofelt theory from absorption curves. It was found that glasses transition temperature and melting temperature decreased with the increase of fluoride content in glass,Ω_2 decreased gradually with the increase of AlF_3 content,but both Ω_4 and Ω_6 did not increase until AlF_3 content increased to 30 mol%.The quantum efficiency of ~4I_(13/2) to ~4I_(15/2) transition of Er~(3+) ions increases with the increase of AlF_3 content in glass.Fluorescent lifetime is longer in glass containing more AlF_3 content. 相似文献
3.
New chemically stable Er_(3+)-Yb_(3+) co-doped phosphate glass for optical waveguide lasers and amplifiers 总被引:3,自引:0,他引:3
A set of phosphate glasses with different amounts of Al2O3, Na2O, La2O3 and AlF3 contents were prepared to search for a phosphate glass which is suitable for ion-exchange process. Based on chemical durability test results and spectroscopic properties, a glass with excellent chemical durability and good spectroscopic properties is developed for ion-exchange process. The emission cross section of Er3+ in this glass is calculated to be 0.72×10~20 cm2 by McCumber theory. The planar waveguide with three modes at 632.8 nm and one mode at 1540 nm can be realized by 335℃ 3 hours ion-exchange in 5%AgNO3+95%KNO3 molten salt. 相似文献
4.
5.
Er3+-doped fluoride lanthanum aluminosilicate glasses with compositions of (65- x/2)SiO2 · (25 -and their glass transition temperatures and spectroscopic properties were investigated. The Ω2, Ω4, and Ω6 intensity parameters of glasses were calculated by Judd-Ofelt theory from absorption curves. It was found that glasses transition temperature and melting temperature decreased with the increase of fluoride content in glass, Ω2 decreased gradually with the increase of AlF3 content, but both Ω4 and Ω6 did not increase until AlF3 content increased to 30 mol%. The quantum efficiency of 4I13/2 to 4I15/2 transition of Er3+ ions increases with the increase of AlF3 content in glass. Fluorescent lifetime is longer in glass containing more AlFa content. 相似文献
6.
研究了退火和二次离子交换对Er3+/Yb3+共掺的磷酸盐玻璃平面光波导传输特性的影响。在退火过程中,由于热效应和波导层Ag+离子的浓度差使得Ag+离子重新分布;随着退火时间的延长和温度的升高,光波导模式数目逐渐增加,波导层深度加深,且波导表面折射率与玻璃基质折射率差减小,退火扩散深度与退火时间的平方根成正比。电子探针结果显示在二次离子交换后形成了掩埋式的光波导,Ag+离子浓度接近二次方分布,而掩埋式的光波导有助于降低光波导的传输损耗。 相似文献
7.
In recent years, because of the use of wavelength divi- sion multiplexing (WDM) technology and the related increase in the complexity of optical networks, there has been a growing interest in integrated photonic de- vices. Er3+-doped glass waveguide devices are suitable for the manufacture of hybrid integrated optical circuit, allowing integration with other optoelectronic devices. Different technologies such as ion-exchange[1], radio fre- quency (RF) sputtering[2] have been proved valid for… 相似文献
8.
Intense frequency upconversion fluorescence of Er~(3+)/Yb~(3+) co-doped lithium-strontium-lead-bismuth glasses 总被引:2,自引:0,他引:2
Infrared-to-visible upconversion fluorescence of Er3+/Yb3+ co-doped lithium-strontium-lead-bismuth (LSPB) glasses for developing potential upconversion lasers has been studied under 975-nm excitation. Based on the results of energy transfer efficiency and upconversion spectra, the optimal Yb3+-Er3+ concentration ratio is found to be 5:1. Intense green and red emissions centered at 525, 546, and 657 nm, corresponding to the transitions 2H11/2→4 I15/2, 4S3/2→4 I15/2, and 4F9/2→4 I15/2, respectively, were observed. The quadratic dependence of the 525-, 546-, and 657-nm emissions on excitation power indicates that a two-photon absorption process occurs under 975-nm excitation. The high-populated 4I11/2 level is supposed to serve as the intermediate state responsible for the upconversion processes. The intense upconversion luminescence of Er3+ /Yb3+ co-doped LSPB glasses may be a potentially useful material for developing upconversion optical devices. 相似文献
9.
新型掺铒铋酸盐玻璃上转换发光研究 总被引:2,自引:0,他引:2
制备了新型掺Er3 铋铅锶玻璃,研究了玻璃的吸收光谱和上转换光谱性质,应用Judd-Ofelt理论计算了铋铅锶玻璃的3个强度参量Ωt(t=2,4,6),分别为Ω2=3.27×10-20 cm2,Ω4=1.15×10-20cm2,Ω6=0.38×10-20 cm2.计算了Er3 离子的振子强度、自发辐射跃迁几率、荧光分支比和辐射寿命等光谱参数.研究了上转换发光强度随泵浦激光功率的变化,上转换荧光525,546和657 nm曲线的斜率分别为1.86,1.88和1.85,表明红、绿光发射均为双光子吸收过程. 相似文献
10.
制备了用于离子交换法制备光波导器件的掺铒碲-钨-钠玻璃基质。应用扎得-奥菲而特(Judd—Ofelt)理论计算了玻璃样品的三个强度参量,由强度参量计算了Er^3 离子的自发跃迁几率、荧光分支比等光谱参量;应用麦克库玻(McCumber)理论,计算了Er^3 离子在1.5μm的受激发射截面,荧光测试发现Er^3 离子的荧光半峰全宽可达65nm。比较了Er^3 离子在不同玻璃基质中的光谱特性。结果表明,Er^3 离子在碲-钨-钠玻璃中具有较高的受激发射截面和较宽的荧光半峰全宽,可以用于宽带光波导器件的制备。 相似文献