Electromagnetic interference shielding and radiation absorption in thin polypyrrole films

Results of permittivity measurements, electromagnetic interference shielding effectiveness, and heat generation due to microwave absorption in conducting polymer coated textiles are reported and discussed. The intrinsically conducting polymer, polypyrrole, doped with anthraquinone-2-sulfonic acid (AQSA) or para-toluene-2-sulfonic acid (pTSA) was applied on textile substrates and the resulting materials were investigated in the frequency range 1-18 GHz. The 0.54 mm thick conducting textile/polypyrrole composites absorbed up to 49.5% of the incident 30-35 W microwave radiation. A thermography station was used to monitor the temperature of these composites during the irradiation process, where absorption was confirmed via visible heat losses. Samples with lower conductivity showed larger temperature increases caused by microwave absorption compared to samples with higher conductivity. A sample with an average sheet resistivity of 150 Ω/sq. showed a maximum temperature increase of 5.27 °C, whilst a sample with a lower resistivity (105 Ω/sq.) rose by 3.85 °C.     

Surface thermodynamic functions of dilute solutions of methylcyclohexanols in ethylene glycol

Surface thermodynamic functions (surface entropy, surface enthalpy, and surface composition) of dilute solutions of 2-, 3-, and 4-methylcyclohexanol in ethylene glycol were obtained using surface tension measurements at various temperatures. Surface excess values and surface mole fractions were obtained from Gibbs equation and extended Langmuir model respectively. The results show that all methylcyclohexanols are surface active in ethylene glycol. The lyophobicity of solutes decreases with increasing temperature. The presence of a maximum point in the surface entropy diagram in all systems is explained by the formation of clathrate-like solvates at the surface of these systems.     

Mutual Separation and Determination of Th(IV) and U(VI) Using Arsenazo III as a Dye Collector Reagent by Flotation‐Spectrophotometric Method

This paper reports a simple and highly selective method for the separation, preconcentration, and determination of trace amounts of thorium and uranium in some complex samples via staircase flotation. The method is based on the initial flotation of the Th(IV)‐arsenazo III complex in the presence of U(VI) from a solution of 5 mol dm^?3 HCl, then reduction of U(VI) to U(IV) and repetition of the flotation step. In both steps, the floated complex was dissolved in a 5‐mL portion of methanol and its absorbance was measured at 655 nm, spectrophotometrically. For a 30‐mL portion of the sample, Beer's law was obeyed over the concentration ranges of 3.40 × 10^?7to 3.06 × 10^?6 mol dm^?3 for Th(IV) and3.40 × 10^?7 to 3.40 × 10^?6 mol dm^?3 for U(IV) with the apparent molar absorptivity of 4.20 × 10⁵ dm³ mol^?1 cm^?1 and 3.59 × 10⁵ dm³ mol^?1 cm^?1, respectively. The RSDs (n = 7) corresponding to 1.7 × 10^?6 mol dm^?3 of Th(IV) and U(IV) were obtained as 1.7% and 1.87%. The detection limits (7 blanks) for both the metal ions were found to be 1.7 × 10^?7 mol dm^?3. The important benefit of the method is that the determinations are free from the interference of almost all cations and anions found in the complex matrixes, such as seawater samples. The proposed method was also applied to reference materials, and the determinations were shown to have good agreement with the certified values.     

Reducing Occupational Noise Propagated from Centrifugal Fan through Dissipative Silencers: A Field Study

Acoustic performance of dissipative silencer was evaluated to determine the effectiveness of perforated duct porosity and absorbent material density in reducing occupational noise exposure propagated from centrifugal fan. Design charts were applied to predict noise reduction and length of a dissipative silencer. Dissipative silencers with various punched duct porosity (14%, 30% and 40%) and sound absorbent density (80 Kg/m³, 120 Kg/m³, and 140 Kg/m³) were designed and fabricated. According to ISO9612 and ISO11820, noise level was measured before and after installing all nine test silencers at fixed workstations around the discharge side of a centrifugal fan in a manufacturing plant. On average, the noise level at the discharge side of a fan without silencer was measured to be 93.6 dBA, whereas it was significantly mitigated by 67.4 dBA to 70.1 dBA after installing all silencers. Dynamic insertion loss for a dissipative silencer with 100 cm length was predicted to be 27.9 dB, which was in agreement with experimental ones. Although, there was no significant differences between insertion loss of silencers, the one with 30% porosity and 120 Kg/m³ rock wool density had the highest insertion loss of 26.2 dBA. Dissipative silencers noticeably reduced centrifugal fan noise exposures. Increasing sound absorbent density and duct porosity up to a certain limit could probably be effective in noise reduction of dissipative silencers.     

Catalytic study of the copper-based magnetic nanocatalyst on the aerobic oxidation of alcohols in water

A copper-based magnetic nanocatalyst has been prepared by co-precipitation method and characterized by FESEM, EDS, TEM, XRD, XRF, ICP–OES, FTIR, and BET analysis. This new nanocatalyst displays a good activity toward the aerobic oxidation of a wide range of alcohols in water. Moreover, it is recyclable up to five following runs by simple filtration without any significant loss of its catalytic activity.

     

Influence of imide functionalized organo‐modified Mg‐Al layered double hydroxide on the thermal and mechanical properties of new aliphatic‐aromatic poly (amide‐imide)

A new dicarboxylic acid modified Mg‐Al LDH (DLDH) containing imide groups was prepared and its effects on the thermal and mechanical properties of the new synthesized aliphatic‐aromatic poly (amide‐imide) (PAI) were investigated via preparation of PAI/nanocomposite films by solution casting method. The results of X‐ray diffraction (XRD), field emission‐scanning electron microscopy (FE‐SEM) and transmission electron microscopy (TEM) showed a uniform dispersion for LDH layers into the PAI matrix. For comparison, the effects of polyacrylic acid‐co‐poly‐2‐acrylamido‐ 2‐methylpropanesulfonic acid (PAMPS‐co‐PAA) modified Mg‐Al LDH (ALDH) on the PAI properties were also studied. The thermogravimetric analysis (TGA) results exhibited that the temperature at 5 mass% loss (T₅) increased from 277 °C to 310 °C for nanocomposite containing 2 mass% of DLDH, while T₅ for nanocomposite containing 2 mass% of ALDH increased to 320 °C, along with the more enhancement of char residue compared to the neat PAI. According to the tensile test results, with 5 mass% DLDH loading in the PAI matrix, the tensile strength increased from 51.6 to 70.8 MPa along with an increase in Young's modulus. Also the Young's modulus of PAI nanocomposite containing 5 mass% ALDH reduced from 1.95 to 0.81 GPa.