Completely biodegradable composites of poly(propylene carbonate) and short,lignocellulose fiber Hildegardia populifolia

The composites of biodegradable poly(propylene carbonate) (PPC) reinforced with short Hildegardia populifolia natural fiber were prepared by melt mixing followed by compression molding. The mechanical properties, thermal properties, and morphologies of the composites were studied via static and dynamic mechanical measurements, thermogravimetric analysis, and scanning electron microscopy (SEM) techniques, respectively. Static tensile tests showed that the stiffness and tensile strength of the composites increased with an increasing fiber content. However, the elongation at break and the energy to break decreased dramatically with the addition of short fiber. The relationship between the experimental results and the compatibility or interaction between the PPC matrix and fiber was correlated. SEM observations indicated good interfacial contact between the short fiber and PPC matrix. Thermogravimetric analysis revealed that the introduction of short Hildegardia populifolia fiber led to a slightly improved thermooxidative stability of PPC. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 666–675, 2004     

Synthesis and characterization of polyaniline/graphite conducting nanocomposites

A new method for the synthesis of exfoliated graphite and polyaniline (PANI)/graphite nanocomposites was developed. Exfoliated graphite nanosheets were prepared through the microwave irradiation and sonication of synthesized expandable graphite. The nanocomposites were fabricated via the in situ polymerization of the monomer at the presence of graphite nanosheets. The as-synthesized graphite nanosheets and PANI/graphite nanocomposite materials were characterized with Fourier transform infrared spectroscopy, scanning electron microscopy, transmission electron microscopy, and thermogravimetric analysis (TGA). The conductivity of the PANI/graphite nanocomposites was dramatically increased over that of pure PANI. TGA indicated that the incorporation of graphite greatly improved the thermal stability of PANI. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 1972–1978, 2004     

Toughness mechanism in polypropylene composites: Polypropylene toughened with elastomer and calcium carbonate

Polypropylene (PP) was modified with elastomer or CaCO₃ particles of two different sizes (1 μm and 50 nm) in various volume fractions. The dispersion morphology and mechanical properties of the two systems were investigated as functions of the particle size and volume fraction of the modifier. The brittle‐to‐tough transition occurred when the matrix ligament thickness was less than the critical ligament thickness, which was about 0.1 μm for the PP used here, being independent of the type of modifier. At the same matrix ligament thickness, the improvement of the toughness was obviously higher with the elastomer rather than with CaCO₃, but adding CaCO₃ increased the modulus of PP. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 1656–1662, 2004     

强流四脉冲电子束源实验研究

 为了进行强流多电子束源研究，对现有2MeV LIA 注入器进行了四脉冲改造，二极管脉冲电压约500kV。实验研究了天鹅绒阴极在四脉冲条件下的发射能力、传导电流负载效应以及阴极等离子体运动对阴极电子发射和束能量的影响。利用空间电荷限制流模型推算出阴极等离子体膨胀速率在1 ~4cm/μs之间。     

Low-threshold interband cascade lasers operating above room temperature

Mid-IR type-II interband cascade lasers were demonstrated in pulsed mode at temperatures up to 325 K and in continuous mode up to 200 K. At 80 K, the threshold current density was 8.9 A/cm² and a continuous wave output power of 140 mW/facet was obtained.     

Synthesis and characterization of poly(arylene ether)s containing 6‐(4‐hydroxyphenyl)pyridazin‐3(2H)‐one or 6‐(4‐hydroxyphenyl)pyridazine moieties

A series of novel soluble pyridazinone‐ or pyridazine‐containing poly(arylene ether)s were prepared by a polycondensation reaction. The pyridazinone monomer, 6‐(4‐hydroxyphenyl)pyridazin‐3(2H)‐one ( 1 ), was synthesized from the corresponding acetophenone and glyoxylic acid in a simple one‐pot reaction. The pyridazinone monomer was successfully copolymerized with bisphenol A (BPA) or 1,2‐dihydro‐4‐(4‐hydroxyphenyl)phthalazin‐1(2H)‐one (DHPZ) and bis(4‐fluorophenyl)sulfone to form high‐molecular‐weight polymers. The copolymers had inherent viscosities of 0.5–0.9 dL/g. The glass‐transition temperatures (T_g's) of the copolymers synthesized with BPA increased with increasing content of the pyridazinone monomer. The T_g's of the copolymers synthesized from DHPZ with different pyridazinone contents were similar to those of the two homopolymers. The homopolymers showed T_g's from 202 to 291 °C by differential scanning calorimetry. The 5% weight loss temperatures in nitrogen measured by thermogravimetric analysis were in the range of 411–500 °C. 4‐(6‐Chloropyridazin‐3‐yl)phenol ( 2 ) was synthesized from 1 via a simple one‐pot reaction. 2 was copolymerized with 4,4′‐isopropylidenediphenol and bis(4‐fluorophenyl)sulfone to form high‐T_g polymers. The copolymers with less than 80 mol % pyridazinone or chloropyridazine monomers were soluble in chlorinated solvents such as chloroform. The copolymers with higher pyridazinone contents and homopolymers were not soluble in chlorinated solvents but were still soluble in dipolar aprotic solvents such as N‐methylpyrrolidinone. The soluble polymers could be cast into flexible films from solution. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 3328–3335, 2006     

Synthesis of TiO2–SiO2/polymer core–shell microspheres with a microphase‐inversion method

A novel microphase‐inversion method was proposed for the preparation of TiO₂–SiO₂/poly(methyl methacrylate) core–shell nanocomposite particles. The inorganic–polymer nanocomposites were first synthesized via a free‐radical copolymerization in a tetrahydrofuran solution, and the poor solvent was added slowly to induce the microphase separation of the nanocomposite and result in the formation of nanoparticles. The average particle sizes of the microspheres ranged from 70 to 1000 nm, depending on the reaction conditions. Transmission electron microscopy and scanning electron microscopy indicated a core–shell morphology for the obtained microspheres. Thermogravimetric analysis and X‐ray photoelectron spectroscopy measurements confirmed that the surface of the nanocomposite microspheres was polymer‐rich, and this was consistent with the core–shell morphology. The influence of the synthetic conditions, such as the inorganic composition and the content of the crosslinking monomer, on the particle properties was studied in detail. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 3911–3920, 2006     

Morphological effect on spectral property of poly(9,9-dihexylfluorene-alt-2,5-dihexyloxybenzene) films

In this study the optical property and film morphology of a conjugated polymer, poly(9,9-dihexylfluorene-alt-2,5-dihexyloxybenzene) (PF6OC6), are investigated. It is found that the intensity of the 0-1 emission relative to the 0-0 emission in the PL spectra and the full width at the half-maximum (fwhm) of PL spectra of the PF6OC6 films decrease firstly and then increase with increasing the annealing temperature. The polymer films also exhibit different morphological features after annealing at different temperatures. The optical and morphological results suggest that the vibronic structure of PF6OC6 is closely related to the film morphology, and its formation is enhanced in the amorphous (or less ordered) films and inhibited in the ordered films.     

拟薄水铝石/陶瓷胶态加工浆料的流变性能

用拟薄水铝石纳米胶粒分散微米二硼化钛形成固含量为60Wt%的稳定陶瓷浆料,实验考察了拟薄水铝石固含量、二硼化钛固含量、温度对浆料流变性、稳定性的影响,对纳米γ-AlOOH胶粒分散微米TiB2的机制进行了讨论.大小约20nm的γ-AlOOH颗粒相互网联,成为外加微米陶瓷颗粒的骨架.浆料粘度随二硼化钛固含量的增加而增大,温度升高有利于胶体中薄水铝胶团与二硼化钛颗粒的相互作用并促进分散.