Electrostatic multilayers of chitosan (CHI)/sodium alginate (SA) and CHI/poly(styrene sulfonate) sodium salt (PSS) were alternatively coated on electrospun cellulose acetate (CA) fiber mat. Morphologies of the composite membranes were characterized by scanning electron microscopy. The morphology of the CHI/SA-coated membrane was denser than the CHI/PSS-coated one. The top layers consisted of carboxyl and sulfonic functional groups for SA and PSS layers, respectively. Amino groups of CHI were only presented in slight quantity. X-ray photoelectron spectroscopy (XPS) confirmed the deposition of the amino groups of CHI on the multilayer membrane surface. These composite membranes were characterized for its water permeability where the water flux decreased with an increase in the number of the bilayers. The water flux was in the range of 60 and 40 L m−2 h−1 for 15 and 25 bilayered membranes, respectively. The sodium chloride (NaCl) solution flux was lower than the pure water flux due to the effect of osmotic pressure, and it decreased with an increase in the NaCl concentration. The rejection of NaCl increased substantially with the number of the bilayers of the polyelectrolytes multilayers. The level of NaCl rejection from this work was in the range of 6% and 15% for 15 and 25 bilayered membranes, respectively. 相似文献
2.
With the ability to form a submicron-sized fibrous structure with interconnected pores mimicking the extracellular matrix (ECM) for tissue formation, electrospinning was used to fabricate ultra-fine fiber mats of hexanoyl chitosan (H-chitosan) for potential use as skin tissue scaffolds. In the present communication, the in vitro biocompatibility of the electrospun fiber mats was evaluated. Indirect cytotoxicity evaluation of the fiber mats with mouse fibroblasts (L929) revealed that the materials were non-toxic and did not release substances harmful to living cells. The potential for use of the fiber mats as skin tissue scaffolds was further assessed in terms of the attachment and the proliferation of human keratinocytes (HaCaT) and human foreskin fibroblasts (HFF) that were seeded or cultured on the scaffolds at different times. The results showed that the electrospun fibrous scaffolds could support the attachment and the proliferation of both types of cells, especially for HaCaT. In addition, the cells cultured on the fibrous scaffolds exhibited normal cell shapes and integrated well with surrounding fibers. The obtained results confirmed the potential for use of the electrospun H-chitosan fiber mats as scaffolds for skin tissue engineering. 相似文献
3.
Thachapan Atchimarungsri Xinhua Gao Kangzhou Wang Qingxiang Ma Jianli Zhang Subing Fan Fugui He Jumei Tian Prasert Reubroycharoen Tiansheng Zhao 《Molecules (Basel, Switzerland)》2022,27(21)
Biodiesel is generally produced from vegetable oils and methanol, which also generates glycerol as byproduct. To improve the overall economic performance of the process, the selective formation of methanol from glycerol is important in biodiesel production. In the present study, a CaO modified HZSM-5 zeolite was prepared by an impregnation method and used for the conversion of glycerol to methanol. We found that the 10%CaO/HZSM-5 with Si/Al ratio of 38 exhibited highest selectivity to methanol of 70%, with a glycerol conversion of 100% under 340 ℃ and atmospheric pressure. The characterization results showed that the introduction of a small amount of CaO into the HZSM-5 did not affect the structure of zeolite. The incorporation of HZSM-5 as an acidic catalyst and CaO as a basic catalyst in a synergistic catalysis system led to higher conversion of glycerol and selectivity of methanol. 相似文献
4.
Wutticharoenmongkol P Sanchavanakit N Pavasant P Supaphol P 《Macromolecular bioscience》2006,6(1):70-77
Novel bone-scaffolding materials were successfully fabricated by electrospinning from polycaprolactone (PCL) solutions containing nanoparticles of calcium carbonate (CaCO(3)) or hydroxyapatite (HA). The diameters of the as-spun fibers were found to increase with the addition and increasing amounts of the nanoparticles. The observed increase in the diameters of the as-spun fibers with the addition and increasing amounts of the nanoparticulate fillers was responsible for the observed increase in the tensile strength of the obtained fiber mats. An increase in the concentration of the base PCL solution caused the average diameter of the as-spun PCL/HA composite fibers to increase. Increasing applied electrical potential also resulted in an increase in the diameters of the obtained PCL/HA composite fibers. Lastly, indirect cytotoxicity evaluation of the electrospun mats of PCL, PCL/CaCO(3), and PCL/HA fibers based on human osteoblasts (SaOS2) and mouse fibroblasts (L929) revealed that these as-spun mats posed no threat to the cells, a result that implied their potential for utilization as bone-scaffolding materials. 相似文献
5.
Kodchakon Kun-asa Prof. Prasert Reubroycharoen Dr. Kiyoyuki Yamazaki Dr. Naoki Mimura Dr. Osamu Sato Dr. Aritomo Yamaguchi 《ChemistryOpen》2021,10(3):308-315
Although chitin, an N-acetyl-D-glucosamine polysaccharide, can be converted to valuable products by means of homogeneous catalysis, most of the chitin generated by food processing is treated as industrial waste. Thus, a method for converting this abundant source of biomass to useful chemicals, such as lactic acid, would be beneficial. In this study, we determined the catalytic activities of various metal oxides for chitin conversion at 533 K and found that MgO showed the highest activity for lactic acid production. X-ray diffraction analysis and thermogravimetry-differential thermal analysis showed that the MgO was transformed to Mg(OH)2 during chitin conversion. The highest yield of lactic acid (10.8 %) was obtained when the reaction was carried out for 6 h with 0.5 g of the MgO catalyst. The catalyst could be recovered as a solid residue after the reaction and reused twice with no decrease in the lactic acid yield. 相似文献
6.
7.
Wongpanit P Sanchavanakit N Pavasant P Supaphol P Tokura S Rujiravanit R 《Macromolecular bioscience》2005,5(10):1001-1012
CM-chitin and CM-chitosan films were successfully crosslinked by microwave treatment. Crosslinking of the microwave-treated CM-chitin films involved mainly the carboxylate and the secondary alcohol groups, while crosslinking of microwave-treated CM-chitosan films involved the carboxylate and the amino groups. In addition, the crystallinity of CM-chitin increased with increasing microwave treatment time, whereas an increase in the crystallinity of the microwave-treated CM-chitosan films was not observed. At a similar percentage of weight loss, the crosslinking of either CM-chitin or CM-chitosan films by microwave treatment required much less stringent condition when compared with the crosslinking by autoclave treatment. Based on both direct and indirect cytotoxicity assays, the cytotoxicity of the microwave-treated CM-chitin films was negative, while that of the microwave-treated CM-chitosan films was positive. Human fibroblasts adhered on the surface of microwave-treated CM-chitosan films much better than on the surface of microwave-treated CM-chitin films. 相似文献
8.
For highly porous form such as sponges or scaffolds, the induction of the β-sheet formation of silk fibroin to make the water-stable materials usually results in their high shrinkage leading to a difficulty in controlling shape and size of materials. Thus, the objective of this study was to improve dimensional stability of silk fibroin sponge by incorporating chitin whiskers as nanofiller. Chitin whiskers exhibited the average length and width of 427 and 43 nm, respectively. Nanocomposite sponges at chitin whiskers to silk fibroin weight ratio (C/S ratio) of 0, 1/8, 2/8, or 4/8 were prepared by using a freeze-drying technique. The dispersion of chitin whiskers embedded in the silk fibroin matrix was found to be homogeneous. The presence of chitin whiskers embedded into silk fibroin sponge not only improved its dimensional stability but also enhanced its compression strength. Regardless of the chitin whisker content, SEM micrographs showed that all samples possessed an interconnected pore network with an average pore size of 150 μm. To investigate the feasibility of the nanocomposites for tissue engineering applications, L929 cells were seeded onto their surfaces, the results indicated that silk fibroin sponges both with and without chitin whiskers were cytocompatible. Moreover, when compared to the neat silk fibroin sponge, the incorporation of chitin whiskers into the silk fibroin matrix was found to promote cell spreading. 相似文献
9.
10.
K-hasuwan PR Pavasant P Supaphol P 《Langmuir : the ACS journal of surfaces and colloids》2011,27(17):10938-10946
The use of electrospun fibrous matrices as substrates for cell/tissue culture has usually been confined to those consisting of smooth fibers. Here, we demonstrated that in vitro responses of mouse-calvaria-derived preosteoblastic cells (MC3T3-E1) that had been cultured on electrospun fibrous substrates made from blend solutions of 50/50 w/w poly(ε-caprolactone) (PCL) and poly(3-hydroxybutyrate-co-3-hydroxyvalerate) (PHBV) of varying concentrations, ranging from 4 to 14 wt %, depended strongly on the topography of the individual fibers. As the concentration of the blend solutions increased from 4 to 14 wt %, the topography of the individual fibers changed from discrete beads/smooth fibers to beaded fibers/smooth fibers and finally to smooth fibers, and the average diameter of the individual, smooth fibers increased from ~0.4 to ~1.8 μm. The results clearly showed that MC3T3-E1 preferred the smooth hydrophilic surface of the fibrous substrate from 10 wt % PCL/PHBV solution because the cells appeared to attach, proliferate, and differentiate on the surface of this substrate particularly well. 相似文献