Preparation of thermoplastic elastomer from natural rubber grafted with polystyrene

Thermoplastic elastomer was prepared from deproteinized natural rubber (DPNR) by graft-copolymerization of styrene, which was performed onto rubber particles of about 1 μm in diameter in latex stage with tert-butyl hydroperoxide/tetraethylenepentamine as an initiator. Suitable initiator concentrations were determined to be 3.3 × 10⁻² and 20 × 10⁻² mol/kg-rubber for the graft-coplymerization of styrene of 1.5 and 5.5 mol/kg-rubber, respectively, in which conversion and grafting efficiency of styrene were more than 90 mol% and 80 mol%, respectively. The resulting polystyrene, grafted onto the rubber particles, was characterized by size exclusion chromatography after ozonolysis. Morphology of the DPNR grafted with polystyrene (DPNR-graft-PS) was observed by transmission electron microscopy (TEM). Change in morphology after processing the DPNR-graft-PS at 150 °C was associated with change in mechanical properties, i.e. stress at strain of 1 and stress at break. The outstanding mechanical properties, maintained even after processing, were assigned to the thermoplasticity of the DPNR-graft-PS, based on the high conversion and high grafting efficiency.     

Photoreactive nanomatrix structure formed by graft‐copolymerization of 1,9‐nonandiol dimethacrylate onto natural rubber

Formation of photoreactive nanomatrix structure was investigated by graft‐copolymerization of an inclusion complex of 1,9‐nonandiol dimethacrylate (NDMA) with β‐cyclodextrin (β‐CD) onto natural rubber particle using potassium persulfate (KPS), tert‐butyl hydroperoxide/tetraethylenepentamine (TBHPO/TEPA), cumene hydroperoxide/tetraethylenepentamine (CHPO/TEPA), and benzoyl peroxide (BPO) as an initiator. The graft copolymer was characterized by ¹H NMR and FTIR after coagulation. The conversion of NDMA and the amount of residual methacryloyl group were found to be 58.5 w/w % and 1.81 w/w %, respectively, under the suitable condition of the graft‐copolymerization. The morphology of the film specimen, prepared from the graft copolymer, was observed by transmission electron microscopy (TEM) after staining the film with OsO₄. Natural rubber particle of about 1.0 μm in diameter was dispersed in poly(NDMA) matrix of about 10 nm in thickness. © 2010 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 48: 2418–2424, 2010