Effect of annealing on structure and permeability of poly [(l-trimethylsilyl)-l-propyne]

The permeability of annealed poly (l-(trimethylsilyl)-l-propyne) was studied from the viewpoint of structural information obtained from x-ray diffraction and density. The sample cast from benzene solution had low density (0.82 g/cm³) and high permeability, whereas the annealed sample had a higher density (0.88 g/cm³) and permeability lower by two orders of magnitude. The smaller-angle x-ray diffraction peak for each sample, which was likely to reflect the distance between intermolecular chains, increased in intensity and shifted toward higher angle, corresponding to the change of the density with annealing. The logarithmic oxygen permeability was proportional to the density, namely the free volume fraction correlated with the diffusion coefficient and controlled by annealing and swelling by alcohols.     

Photo-Absorption and photochemical decomposition of copper and alkaline-earth ß-diketonates as source gases of high-Tc superconducting films

For low-temperature deposition of oxide films relating to Bi-Sr-Ca-Cu-O superconductors, photo-absorption and -decomposition properties were examined with respect to copper and alkaline-earth ß-diketonates. It was confirmed that all ß-diketonates examined were promising as source materials for photochemical vapour deposition (photo-CVD) using a low-pressure mercury lamp, in view of their large light absorption coefficients at wavelength 254 nm. The light irradiation was effective for the formation of highly crystalline oxide films at temperatures below 600 °C. By combining two sources, Ca₂CuO₃ and SrCuO₂ films were prepared. Photo-CVD of c-axis oriented Bi₂Sr₂CuO_x film was achieved by the irradiation of ternary sources of Bi(C₆H₅)₃ and strontium and copper ß-diketonates at 500 °C.     

Tristimulus colorimetry using a digital still camera and its application to determination of iron and residual chlorine in water samples.

Tristimulus colorimetry using a digital still camera (DSC) as a colorimeter has been developed. A photograph of a sample and standard solutions was taken simultaneously with the DSC, and it was transferred to a PC. On the PC, the colors of the sample and of the standard solutions were analyzed and L* (brightness), a* (red-green component), and b* (yellow-blue component) values were determined with laboratory-made software. A dedicated light-box containing white-color LEDs as light source was made of white acrylic to make constant exposure at each photograph. Various settings of the DSC, such as exposure mode, white balance, and so on, that affect analytical figures, were studied with determination of iron with 1,10-phenanthroline. This method was successfully applied to the determinations of iron in a river water sample and of residual chlorine in tap water samples with N,N-diethylphenylenediamine (DPD).     

Crystal and molecular structure of 6-0-acetylgrayanotoxin III

The crystal and molecular structure of a grayanotoxin III derivative, 6-0-acetylgrayanotoxin III is presented. The crystal is orthorhombic, space group P2₁2₁2₁, witha=15.582(3),b=21.304(3),c=6.339(3)Å,V=2104(1) ų Z=4. The structure was solved by direct methods and refined by full matrix least-squares methods to a finalR=0.047 for 1763 independent reflections withF ₀>3 (F ₀) The molecule is based on a tetracyclic structure consisting of two five-membered, one six-membered, and one seven-membered ring with various conformations.     

A regio- and stereoselective alpha-methylation of gamma,delta-epoxy-alpha,beta-unsaturated esters with a Me2Zn-CuCN reagent

A highly regio- and stereoselective alpha-methylation reaction of gamma,delta-epoxy-alpha,beta-unsaturated esters was achieved by using a Me2Zn-CuCN reagent.     

A novel scheme of heterogeneous polymerization of ethylene

The heterogeneous polymerization of ethylene initiated by radiation in tert-butyl alcohol was studied. The polymerization was carried out in a 100-ml reactor at 25–100°C and pressures of 200–300 kg/cm² in the presence of 50 ml of tert-butyl alcohol containing 7 wt-% water. The amounts of polymerized monomer, the average molecular weight of polymer formed, and the molecular weight distribution of polymer were measured at various stages of reaction and at various temperatures. The molecular weight distribution was found to be very much dependent on the reaction time and temperature. For the polymer formed at 50–60°C in the very early stages of reaction, the molecular weight distribution is unimodal, and in the intermediate stage a shoulder appears at a molecular weight higher than the first peak which increases as the polymerization proceeds; eventually a bimodal curve is formed. The bimodal distribution curves were analyzed to determine the fractions and average molecular weights of the each peak. On the basis of these data for the molecular weight distribution and kinetic behavior, a new scheme for the heterogeneous polymerization is proposed which indicates that the polymerization proceeds via propagating radicals in two different physical states, namely, loose and rigid states.     

Atomic absorption spectrometry of traces of tri- and hexavalent chromium

Summary Atomic absorption spectrometry combined with extraction is described for the determination of tri- and hexavalent chromium. The chromium diethyldithiocarbamate chelate was used for chromium (VI), whereas hydroxyquinolate or thenoyltrifluoroacetonate chelate for chromium(III). The method is rapid and precise.

---

Zusammenfassung Extraktion und darauffolgende Messung der Atomarabsorption wurden zur Bestimmung von drei- und sechswertigem Chrom verwendet. Die Chelatverbindung mit Diäthyldithiocarbamat wurde für Chrom(VI), der Chelatkomplex mit Hydroxychinolin oder Thenoyltrifluoraceton für Chrom(III) verwendet. Das Verfahren ist rasch und genau.

     

Mechanism of charge–transfer polymerization. II. Propagation mechanism of the polymerization of N-vinylcarbazole with organic electron acceptors

Copolymerizations of N-vinylcarbazole with both isobutyl vinyl ether and N-vinyl-pyrrolidone initiated by some organic electron acceptors have been investigated for the purpose of elucidating the propagation mechanism in the charge-transfer polymerization. Copolymerizations of the same system catalyzed by authentic cationic catalysts have also been made for comparison. The results indicate that the propagation mechanism of the charge-transfer polymerization studied is catio ie.     

Partialsynthese der Grandidone A, 7-Epi-A,B, 7-Epi-B,C, D und 7-Epi-D aus 14-Hydroxytaxodion

Partial Synthesis of Grandidones A, 7-Epi-A, B, 7-Epi-B, C, D and 7-Epi-D, from 14-Hydroxytaxodione Oxydative addition of coleon U ( 6 ) to 14-hydroxytaxodione ( 5 ) in the presence of Fétizon's reagent mainly leads to grandidone A ( 1a ) and 7-epigrandidone A ( 1b ) (ca. 15:1), whereas coleon V ( 7 ) and 5 under the same conditions yield grandidone B ( 2a ) and 7-epigrandidone B ( 2b ) (ca. 3:1). Dimerization of 14-hydroxytaxodione ( 5 ) gives grandidone C ( 3 ; ca. 40%), grandidone D ( 4a ; ca. 50%) and 7-epigrandidone D ( 4b ; ca. 10%). All these compounds obtained by partial synthesis are in every respect identical with the natural products, thus establishing their absolute configurations. The thermal transformation of grandidone C ( 3 ) to grandidone D ( 4a )/7-epigrandidone D ( 4b ) and interconversions of 4a and 4b were achieved. Oxydative addition of coleon U ( 6 ) to 14-hydroxytaxodione ( 5 ) in the presence of Fétizon's reagent mainly leads to grandidone A ( 1a ) and 7-epigrandidone A ( 1b ) (ca. 15:1), whereas coleon V ( 7 ) and 5 under the same conditions yield grandidone B ( 2a ) and 7-epigrandidone B ( 2b ) (ca. 3:1). Dimerization of 14-hydroxytaxodione ( 5 ) gives grandidone C ( 3 ; ca. 40%), grandidone D ( 4a ; ca. 50%) and 7-epigrandidone D ( 4b ; ca. 10%). All these compounds obtained by partial synthesis are in every respect identical with the natural products, thus establishing their absolute configurations. The thermal transformation of grandidone C ( 3 ) to grandidone D ( 4a )/7-epigrandidone D ( 4b ) and interconversions of 4a and 4b were achieved. Oxydative addition of coleon U ( 6 ) to 14-hydroxytaxodione ( 5 ) in the presence of Fétizon's reagent mainly leads to grandidone A ( 1a ) and 7-epigrandidone A ( 1b ) (ca. 15:1), whereas coleon V ( 7 ) and 5 under the same conditions yield grandidone B ( 2a ) and 7-epigrandidone B ( 2b ) (ca. 3:1). Dimerization of 14-hydroxytaxodione ( 5 ) gives grandidone C ( 3 ; ca. 40%), grandidone D ( 4a ; ca. 50%) and 7-epigrandidone D ( 4b ; ca. 10%). All these compounds obtained by partial synthesis are in every respect identical with the natural products, thus establishing their absolute configurations. The thermal transformation of grandidone C ( 3 ) to grandidone D ( 4a )/7-epigrandidone D ( 4b ) and interconversions of 4a and 4b were achieved. Oxydative addition of coleon U ( 6 ) to 14-hydroxytaxodione ( 5 ) in the presence of Fétizon's reagent mainly leads to grandidone A ( 1a ) and 7-epigrandidone A ( 1b ) (ca. 15:1), whereas coleon V ( 7 ) and 5 under the same conditions yield grandidone B ( 2a ) and 7-epigrandidone B ( 2b ) (ca. 3:1). Dimerization of 14-hydroxytaxodione ( 5 ) gives grandidone C ( 3 ; ca. 40%), grandidone D ( 4a ; ca. 50%) and 7-epigrandidone D ( 4b ; ca. 10%). All these compounds obtained by partial synthesis are in every respect identical with the natural products, thus establishing their absolute configurations. The thermal transformation of grandidone C ( 3 ) to grandidone D ( 4a )/7-epigrandidone D ( 4b ) and interconversions of 4a and 4b were achieved.     

Effect of dose rate on the radiation-induced polymerization of ethylene in tert-butyl alcohol

The dependence of the dose rate on the rate of radiation-induced polymerization of ethylene in tert-butyl alcohol containing 5 vol-% water was studied. The reaction was carried out by use of a reactor with a capacity of 100 ml under the following conditions: pressure, 200 kg/cm²; temperature, 24 ± 3°C; dose rate, 3.7 × 10⁴?1.6 × 10⁵ rad/hr; amount of medium, 70 ml. The dose rate exponents for rate of the polymerization, the molecular weight, and the number of polymer chain were found to be about 0.8, ?0.1, and 0.9, respectively. These results were well explained with kinetic results (obtained by a novel analytical method) for the polymerization which contain both first-order and second-order terminations for the concentrations of propagating radical. The individual values of the rate constants in each elementary reaction were also obtained.