Effect of EVA copolymer containing different VA content on the thermal and rheological properties of bio-based high-density polyethylene/ethylene vinyl acetate blends

The effect of ethylene vinyl acetate (EVA) concentration and vinyl acetate (VA) content of EVA on the mechanical, morphological, and rheological properties of bio-based high-density polyethylene (BioPE)/EVA blends was investigated. The blends were characterized by X-ray diffraction, differential scanning calorimetry, scanning electron microscopy, and rheological measurements under oscillatory shear flow. The degree of crystallinity of BioPE decreased with the increase in the EVA concentration and was unaffected with the increase in the VA content. DMTA results showed a decrease in the storage modulus (E′) with the increase in EVA content and that the BioPE/EVA19 blends showed higher E′ values than BioPE/EVA28 blend. The impact strength substantially increased with the addition of EVA concentration above 5 mass% and was higher for the blends containing the highest VA content. The blends containing a higher content of VA exhibited the higher EVA dispersed phase domain size, which increased with the increase in EVA concentration. The complex viscosity increased with the increase in the EVA content, being higher for the BioPE/EVA blends containing higher VA content. The storage modulus increased, at low frequencies, with the increase in the EVA content and can be ascribed to the increase in the EVA dispersed phase domain size.

     

Energetics of cation mixing in urania-ceria solid solutions with stoichiometric oxygen concentrations

Cation mixing energetics in urania-ceria solid solutions with stoichiometric oxygen concentrations (U(1-y)Ce(y)O(2)) have been measured by high-temperature oxide-melt drop-solution calorimetry. Measurements have been performed on eight samples with compositions spanning y = 0.119 to y = 0.815. The measured mixing enthalpies (ΔH(mix)) range from -0.6 ± 3.3 to 3.9 ± 3.0 kJ mol(-1). These values are discussed in the context of results from atomistic modeling which take into consideration the possibility of charge transfer between uranium and cerium cations to form solid solutions with mixed charge states. A comparison between measured and calculated results for ΔH(mix) suggests that such charge transfer takes place to a limited extent in the most concentrated mixtures studied.