A series of PCL/MDI/BDO segmented polyurethanes have been synthesized by two-step method in solution.The hard segment content ranges from 10% to 48% by weight, and the molecular weight of PCL diols is 1500. Hard segment spherulites have been observed in compression molded specimens of all of the samples except the one of the lowest hard segment content. The difficulty in sphernlite formation was explained as only in a small temperature range,the microphase separation rate may be faster than the crystallization rate and all these processes are very slow due to the hydrogen bonding between hard and soft segments and the interactions between hard segments themselves. PCL soft segments of molecular weight 1500 is still crystallizable and may form different crystalline superstructures. 相似文献
2.
研究了羟丙基纤维素和羟丙基醋酸纤维素的合成。制备羟丙基纤维素的较佳反应温度为40℃左右和2小时或稍长,羟丙基含量随环氧丙烷浓度的增加而增加。在制备羟丙基醋酸纤维素时,随羟丙基含量的增加,所需醋化和水解的时间减少。以甘油-正丙醇或磷酸为添加剂,丙酮为溶剂经30~60s蒸发后制得了羟丙基醋酸纤维素反渗透膜。后者在20kg/cm~2下对氯化钠脱盐率可达95~98%,水通量1.0~2.1mL/cm~2·h,其使用温度上限比醋酸纤维素反渗透膜提高10℃以上。 相似文献
3.
用溴化钾-溴酸钾滴定法测定双键含量,元素分析法测定共聚物组成。讨论了HEMA-NVP-St三元共聚体系在不同反应程度时共聚物组成的变化,以及在此三元共聚体系中引入均化剂后,少量均化剂对共聚体系组成均一性的影响。发现在HEMA-NVP-St三元共聚体系中加入均化剂,对共聚反应的反应动力学影响不大,但对共聚物的组成均一性有较大影响。它的加入使三元共聚物中的链节比分布(即不同反应程度时,产物的累积平均组成)向较均一的方向发展。结合红外光谱、电子显微镜等实验证据,从微观结构上探讨了约化剂的作用。阐明均化剂改善了反应体系的相容性,从而得到组成分布较为均一的共聚产物。 相似文献
4.
羟丙基醋酸纤维素反渗透膜 总被引:1,自引:0,他引:1
研究了羟丙基醋酸纤维素反渗透膜的制膜工艺和膜性能。实验表明,以甘油—正丙醇或磷酸为添加剂,蒸发时间30—60s,预热处理温度70℃,时间3—5min,可得到在2MPa操作压力下,氯化钠脱除率95—98%,水通量1.0~2.1ml/cm~2·h的反渗透膜。羟丙基醋酸纤维素膜具有一定的耐热性,其使用温度上限比醋酸纤维素膜至少提高了10℃以上。羟丙基醋酸纤维素的溶解性能与醋酸纤维素相似。X射线衍射和热重分析显示羟丙基醋酸纤维素具有与醋酸纤维素相似的聚集态结构。 相似文献
5.