Synthesis and luminescent properties of Eu<Superscript>3+</Superscript>- and Eu<Superscript>2+</Superscript>-activated sodium pyrophosphate Na<Subscript>4</Subscript>P<Subscript>2</Subscript>O<Subscript>7</Subscript>

The luminescent properties of Eu³⁺ and Eu²⁺ ions in sodium pyrophosphate, Na₄P₂O₇, have been studied. The excitation spectrum of the Eu³⁺ emission in Na₄P₂O₇ consists of several sets of bands in the range 280–535 nm due to 4f–4f transitions of Eu³⁺ ions and a broad band with a maximum at about 240 nm interpreted to be due to a charge transfer (CT) transition from oxygen 2p states to empty states of the Eu³⁺ 4f⁶-configuration. Although the CT band energy is large enough, the quantum efficiency (η) of the Eu³⁺ emission in Na₄P₂O₇ under CT excitation was estimated to be very low (η ≤ 0.01). In terms of a configurational coordinate model, this fact is interpreted as a result of the high efficiency of a radiationless relaxation from the CT state to the ⁷F₀ ground state of Eu³⁺ ions occupying sodium sites in Na₄P₂O₇. A strong reducing agent is required in order to stabilize Eu²⁺ ions in Na₄P₂O₇ during the synthesis. Several nonequivalent Eu²⁺ luminescence centers in Na₄P₂O₇ were found.     

On the Luminescence of Ce<Superscript>3+</Superscript>, Eu<Superscript>3+</Superscript>, and Tb<Superscript>3+</Superscript> in Novel Borate LiSr<Subscript>4</Subscript>(BO<Subscript>3</Subscript>)<Subscript>3</Subscript>

This paper reports on the photoluminescence (PL) and time-resolved properties of Ce³⁺, Eu³⁺, and Tb³⁺ in novel LiSr₄(BO₃)₃ powder phosphors. Ce³⁺ shows an emission band peaking at 420 nm under 350-nm UV excitation. Energy transfer from Ce³⁺ to Mn²⁺ takes place in the co-doped samples. Eu³⁺ shows red emission under near UV excitation. LiSr₄(BO₃)₃:Eu³⁺ phosphor could be a suitable candidate for phosphor-converted solid state lighting. The luminescence lifetime is 2.13 ms for Eu³⁺ in LiSr₄(BO₃)₃:0.001Eu³⁺. As Eu³⁺ concentration increasing, the decay curves deviate from exponential behavior. Tb³⁺ shows the strongest ⁵D₄→⁷ F₅ emission line at 540 nm. Decay curves of ⁵D₄→⁷ F₅ and ⁵D₃→⁷ F₅ emission with different Tb³⁺ concentrations were also measured. Cross-relaxation process is discussed based on the decay curves.     

Red,Yellow, Blue and Green Emission from Eu<Superscript>3+</Superscript>, Dy<Superscript>3+</Superscript> and Bi<Superscript>3+</Superscript> Doped Y<Subscript>2</Subscript>O<Subscript>3</Subscript>nano-Phosphors

Rare earth elements (RE = Eu³⁺& Dy³⁺)and Bi³⁺ doped Y₂O₃ nanoparticles were synthesized by urea hydrolysis method in ethylene glycol, which acts as reaction medium as well as a capping agent, at a low temperature of 140 °C,followed by calcination of the obtained product. Transmission electron microscope (TEM) images reveals that ovoid shaped Y₂O₃ nanoparticles of around 22–24 nm size range were obtained in this method. The respective RE and Bi³⁺ doped Y₂O₃ precursor nanoparticles when heated at 600 and 750 °C, retains the same shape as that of the as-synthesized Y₂O₃ precursor samples. From EDAX spectra, the incorporation of RE ions into the host has been studied. XRD pattern reveals the crystalline nature of the heated nanoparticles and indicate the absence of any impurity phase other than cubic Y₂O₃.However, the as-synthesized nanoparticles were highly amorphous without the presence of any sharp XRD peaks. Photoluminescence study suggests that the synthesized samples could be used as red (Eu³⁺), yellow (Dy³⁺), blue and green (Bi³⁺)emitting phosphors.     

luminescence of BaGa<Subscript>2</Subscript>Se<Subscript>4</Subscript> crystals activated by Eu<Superscript>2+</Superscript> and Ce<Superscript>3+</Superscript> ions

We have studied the effect of doping with Eu²⁺ and Ce³⁺ ions on the photoluminescence (PL) of BaGa₂Se₄ crystals in the temperature range 77–300 K. We have established that the broad bands with maxima at wavelengths 456 nm and 506 nm observed in the photoluminescence spectra of BaGa₂Se₄:Ce³⁺ crystals are due to intracenter transitions 5d → ²F_7/2 and 5d →²F_5/2 of the Ce³⁺ ions, while the broad photoluminescence band with maximum at 521 nm in the spectrum of BaGa₂Se₄:Eu²⁺ is associated with 4f⁶ 5d → 4f⁷ (⁸S_7/2) transitions of the Eu²⁺ ion. We show that in BaGa₂Se₄:Eu²⁺,Ce³⁺ crystals, excitation energy is transferred from the Ce³⁺ ions to the Eu²⁺ ions.     

Luminescence characteristics of energy transfer between Ce<Superscript>3+</Superscript> and Eu<Superscript>2+</Superscript> in NaMgPO<Subscript>4</Subscript> phosphor

Powder samples of NaMgPO₄ doped with Eu²⁺ and Ce³⁺ were prepared and their photoluminescence spectra were systemically studied. Energy transfer from Ce³⁺ to Eu²⁺ in NaMgPO₄ phosphor was observed by investigating the optical properties from photoluminescence spectra in Eu²⁺ or Ce³⁺ singly doped and Eu²⁺–Ce³⁺ codoped sodium magnesium orthophosphates, NaMgPO₄. The enhancement of UV excitation is attributed to energy transfer from Ce³⁺ to Eu²⁺, and Ce³⁺ plays a role as a sensitizer. Ce³⁺–Eu²⁺ codoped NaMgPO₄ phosphors in which Eu²⁺ can be efficiently excited by 390 nm are potential candidates for phosphor-converted LEDs.     

Luminescence in Dy<Superscript>3+</Superscript> and Eu<Superscript>3+</Superscript> Activated K<Subscript>3</Subscript>Al<Subscript>2</Subscript>(PO<Subscript>4</Subscript>)<Subscript>3</Subscript>

The Dy³⁺ and Eu³⁺ activated K₃Al₂ (PO₄)₃ phosphors were prepared by a combustion synthesis. From a powder X-ray diffraction (XRD) analysis the formation of K₃Al₂ (PO₄)₃ was confirmed. In the photoluminescence emission spectra, the K₃Al₂(PO₄)₃:Dy³⁺ phosphor emits two distinctive colors: blue and yellow whereas K₃Al₂(PO₄)₃:Eu³⁺ emits red color. Thus the combination of colors gives BYR (blue–yellow–red) emissions can produce white light. These phosphors exhibit a strong absorption between 340 and 400 nm which suggest that present phosphor is a promising candidate for producing white light-emitting diodes (LED).     

PL Properties of Sr<Subscript>2</Subscript>CeO<Subscript>4</Subscript> With Eu<Superscript>3+</Superscript> and Dy<Superscript>3+</Superscript> for Solid State Lighting Prepared by Precipitation Method

Photoluminescence studies of pure and Dy³⁺, Eu³⁺ doped Sr₂CeO₄ compounds are presented by oxalate precipitation method for solid state lighting. The prepared samples also characterized by XRD, SEM (EDS) and FTIR spectroscopy. The pure Sr₂CeO₄ compound displays a broad band in its emission spectrum when excited with 280 nm wavelength, which peaks centered at 488 nm, which is due to the energy transfer between the molecular orbital of the ligand and charge transfer state of the Ce⁴⁺ ions. Emission spectra of Sr₂CeO₄ with different concentration of Dy³⁺ ions under near UV radiation excitation, shows that intensity of luminescence spectra is found to be affected by Dy³⁺ ions, and it increases with adding some percentages of Dy³⁺ ions. The maximum doping concentration for quenching is found to be Dy³⁺?=?0.2 mol % to Sr²⁺ions. The observed broad spectrum from 400 to 560 nm is mainly due to CT transitions in Sr₂CeO₄ matrix and some fractional contribution of transitions between ⁴F_9/2 → ⁶H_15/2 of Dy³⁺ ions. Secondly the effect of Eu³⁺ doping at the Sr²⁺ site in Sr₂CeO₄, have been studied. The results obtained by doping Eu³⁺ concentrations (0.2 mol% to 1.5 mol%), the observed excitation and emission spectra reveal excellent energy transfer between Ce⁴⁺ and Eu³⁺. The phenomena of concentration quenching are explained on the basis of electron phonon coupling and multipolar interaction. This energy transfer generates white light with a color tuning from blue to red, the tuning being dependent on the Eu³⁺ concentration. The results establish that the compound Sr₂CeO₄ with Eu³⁺?=?1 mol% is an efficient “single host lattice” for the generation of white lights under near UV-LED and blue LED irradiation. The commission internationale de I’Eclairage (CIE) coordinates were calculated by Spectrophotometric method using the spectral energy distribution of prepared phosphors.     

Possibility of adjusting photoluminescence spectra of Ca scheelites (CaMoO<Subscript>4</Subscript>: Eu<Superscript>3+</Superscript> and CaWO<Subscript>4</Subscript>: Eu<Superscript>3+</Superscript>) to the emission spectrum of incandescent lamps

The peculiarities of the photoluminescence of compounds CaMoO₄: Eu³⁺ and CaWO₄: Eu³⁺ with the scheelite structure associated with a change in the short- and long-range orders of the crystal lattice upon a change in the activator (Eu³⁺) of the photoluminescence range in the interval 1–4 mol %, in which the photoluminescence of the matrix is preserved in the range 484–557 nm, are investigated using X-ray phase analysis as well as photoluminescence, Raman, and diffuse reflection spectroscopies. The introduction of Eu³⁺ ions leads to the reconstruction of the lattice so that up to 10% of these ions stimulate the formation of centrosymmetric localization upon the substitution of Ca²⁺ ions in the noncentrosymmetric positions. It is found that the spectral radiant emittance of the more effective luminophore CaMoO₄: Eu³⁺ can be adjusted to this parameter for an incandescent lamp for the Eu³⁺ concentration of 1–2 mol %.     

Spectral-luminescent properties of Eu<Superscript>3+</Superscript> ions in inorganic D<Subscript>2</Subscript>O and POCl<Subscript>3</Subscript>-SnCl<Subscript>4</Subscript> solvents

Absorption and luminescence spectra of Eu³⁺ ions in D₂O and POCl₃-SnCl₄ inorganic solvents were measured. Oscillator strengths and spontaneous radiation transition probabilities for the most intense electron transitions in Eu³⁺ were calculated. Judd-Ofelt parameters, the radiative lifetime of the ⁵ D ₀ metastable level of Eu³⁺ in D₂O-Eu³⁺ and POCl₃-SnCl₄-Eu³⁺ solutions, and matrix elements for radiative transitions from the ⁵ D ₀ level were determined. The luminescence lifetime of the ⁵ D ₀ level of Eu³⁺ in these solutions was measured. The photoluminescence quantum yield for transitions from the ⁵ D ₀ level of Eu³⁺ in ⁵ D ₀ and POCl₃-SnCl₄-Eu³⁺ solutions was found to be 0.32 and 0.88, respectively.     

Luminescent properties of SrMg<Subscript>2</Subscript>(PO<Subscript>4</Subscript>)<Subscript>2</Subscript>:Eu<Superscript>2+</Superscript>, and Mn<Superscript>2+</Superscript> as a potential phosphor for ultraviolet light-emitting diodes

Eu²⁺ and Mn²⁺ co-doped SrMg₂(PO₄)₂ phosphors with blue and red two emission bands were prepared by the high temperature solid state method and their luminescent properties have been investigated as a function of activator and co-activator concentrations. Resonance-type energy transfers from Eu²⁺ to Mn²⁺ were discovered by directly overlapping the Eu²⁺ emission spectrum and the excitation spectrum of Mn²⁺. Efficiencies of energy transfer were also calculated according to the changes of relative intensities of Eu²⁺ and Mn²⁺ emission. According to the principle of energy transfer, we demonstrated that the phosphor SrMg₂(PO₄)₂:Eu²⁺,Mn²⁺ with double emission bands exhibited a great potential as a phosphor for ultraviolet light-emitting diodes and the relative intensities of blue and red emission could be tuned by adjusting the contents of Eu²⁺ and Mn²⁺. PACS 78.55.-m     

Synthesis and Optical Properties of Novel Red-Emitting PbNb<Subscript>2</Subscript>O<Subscript>6</Subscript>: Eu<Superscript>3+</Superscript> Phosphors

Undoped and PbNb₂O_6:Eu³⁺ (1.0 ≤ x ≤ 6.0 mol%) phosphors were synthesized at 1100 °C for 3.5 h by the conventional solid state reaction method. Synthesized PbNb₂O₆:Eu³⁺ phosphors were characterized by X-ray diffraction (XRD), Scanning electron microscopy (SEM), Energy dispersive spectroscopy (EDS) and Photoluminescence (PL) analyses. The PL spectra showed series of excitation peaks between 350 and 430 nm due to the 4f–4f transitions of Eu³⁺. For 395.0 nm excitation, emission spectra of Eu³⁺ doped samples were observed at 591 nm (orange) and 614 nm (red) due to the ⁵D₀ → ⁷F₁ transitions and ⁵D₀ → ⁷F₂ transitions, respectively. PL analysis results also showed that the emission intensity increased by increasing Eu³⁺ ion content. No concentration quenching effect was observed. The CIE chromaticity color coordinates (x,y) of the PbNb₂O₆:Eu³⁺ phosphors were found to be in the red region of the chromaticity diagram.     

Synthesis and Optical Characterization of Red-Emitting BaTa<Subscript>2</Subscript>O<Subscript>6</Subscript>:Eu<Superscript>3+</Superscript> Phosphors

Undoped and Eu³⁺ doped BaTa₂O₆ phosphors were synthesized via solid state reaction method and characterized by using XRD, SEM-EDS and photoluminescence (PL) analyses. The XRD results revealed that the crystal structure of BaTa₂O₆ allowed up to 10 mol% levels of Eu³⁺ ions due to the TTB characteristic network of adjacent octahedrals. SEM-EDS analyses confirmed the formation of BaTa₂O₆ structure and EuTaO₄ secondary phase. BaTa₂O_6:Eu³⁺ phosphors exhibited orange and red emissions at 592.2 nm and 615.7 nm in the visible region respectively. The Commission Internationale d’Eclairage (CIE) chromaticity coordinates of the BaTa₂O_6:Eu³⁺ phosphors that excited at λ _ex = 400 nm ranged from orangish-red to pinkish-red depending on increasing Eu³⁺ concentration.     

Enhanced photoluminescence of Ca<Subscript>2</Subscript>Al<Subscript>2</Subscript>SiO<Subscript>7</Subscript>:Eu<Superscript>3+</Superscript> by charge compensation method

The effect of compensator on optical properties of Ca₂Al₂SiO₇:Eu³⁺ is systematically investigated by the X-ray powder diffraction, photo-luminescence (PL) properties and lifetime. It is obviously observed that the PL intensity of Eu³⁺ under 394 nm excitation increases in the order of Ca_1.86Eu_0.14Al₂SiO₇ (CAS), Ca_1.72Na_0.14Eu_0.14Al₂SiO₇ (CASNa) and Ca_1.86Eu_0.14Al_2.14Si_0.86O₇ (CASAl), the intensity of Eu³⁺ are 100%, 134%, 184%, and the lifetime of Eu³⁺ are 0.75 ms, 1.28 ms and 1.39 ms, respectively. A charge compensation model is proposed to explain the changes in the emission intensity and lifetime of Eu³⁺ in Ca₂Al₂SiO₇ with different compensation methods. PACS 78.55.-m; 61.72.Ji; 61.43.Gt; 42.70.-a; 74.62.Dh     

Phase transition induced formation of hollow structures in colloidal lanthanide-doped NaYF<Subscript>4</Subscript> nanocrystals

Formation of colloidal hollow structures in NaYF₄ nanocrystals (NCs) with and without lanthanide ion doping has been observed and investigated via the co-thermolysis of a mixture of trifluoroacetate precursors in trioctylphosphine oxide. The Kirkendall effect in this one-step reaction is driven by the monomer diffusion and crystal phase transition. It is found that three kinetic stages which include rapid precipitation of cubic phase NCs, cubic to hexagonal phase transition concurrent with an inward transport of NaF species, and vacancy diffusion are attributed to the hollow structure formation. X-ray energy dispersive spectroscopy (XEDS) point analysis is applied to examine the ions distribution and crystalline components in the lanthanides (Yb and Er)-doped NaYF₄ up-conversion nanophosphors (UCNPs). The hollow structures increase the surface-to-volume of a single NC and thus have a significant effect on the photoluminescence of the lanthanide-doped NPs and provide synthetic applications for achieving novel NaYF₄-based NCs.     

Photolumiscent Properties of Nanorods and Nanoplates Y<Subscript>2</Subscript>O<Subscript>3</Subscript>:Eu<Superscript>3+</Superscript>

Nanorods and nanoplates of Y₂O₃:Eu³⁺ powders were synthesized through the thermal decomposition of the Y(OH)₃ precursors using a microwave-hydrothermal method in a very short reaction time. These powders were analyzed by X-ray diffraction, field emission scanning electron microscopy, Fourrier transform Raman, as well as photoluminescence measurements. Based on these results, these materials presented nanoplates and nanorods morphologies. The broad emission band between 300 and 440 nm ascribed to the photoluminescence of Y₂O₃ matrix shifts as the procedure used in the microwave-hydrothermal assisted method changes in the Y₂O₃:Eu³⁺ samples. The presence of Eu³⁺ and the hydrothermal treatment time are responsible for the band shifts in Y₂O₃:Eu³⁺ powders, since in the pure Y₂O₃ matrix this behavior was not observed. Y₂O₃:Eu³⁺ powders also show the characteristic Eu³⁺ emission lines at 580, 591, 610, 651 and 695 nm, when excited at 393 nm. The most intense band at 610 nm is responsible for the Eu³⁺ red emission in these materials, and the Eu³⁺ lifetime for this transition presented a slight increase as the time used in the microwave-hydrothermal assisted method increases.     

Luminescence and energy transfer mechanism in Eu<Superscript>3+</Superscript>/Tb<Superscript>3+</Superscript>-co-doped ZrO<Subscript>2</Subscript> nanocrystal rods

Nanocrystal rods of Eu³⁺/Tb³⁺-co-doped ZrO₂ were synthesized using a simple chemical precipitation technique. Both ions were successfully doped into the Zr⁴⁺ ion site in a mixed structure containing both monoclinic and tetragonal phases. The Eu³⁺ or Tb³⁺ singly doped zirconia produced red and green luminescence which are characteristics of Eu³⁺ and Tb³⁺ ions, respectively. The co-doped zirconia samples produced blue emission from defect states transitions in the host ZrO₂, red and green luminescence from dopant ions giving cool to warm white light emissions. The phosphors were efficiently excited by ultraviolet and near-ultraviolet/blue radiations giving white and red light, respectively. The decay lifetime was found to increase with increasing donor ion concentration contrary to conventional observations reported by previous researchers. Weak quadrupole–quatdrupole multipolar process was responsible for energy transfer from Tb³⁺ (donor) ion to Eu³⁺ ion. No energy back-transfer from Eu³⁺ to Tb³⁺ ion was observed from the excitation spectra. Temperature-dependent photoluminescence shows the presence of defects at low temperature, but these defects vanished at room temperature and beyond. The Eu³⁺/Tb³⁺-co-doped ZrO₂ nanocrystal rod is a potential phosphor for white light application using UV as an excitation source. Thermoluminescence measurements show that the inclusion of Tb³⁺ ion increases trap depths in the host zirconia.     

Re-dispersible Li<Superscript>+</Superscript> and Eu<Superscript>3+</Superscript> co-doped CdS nanoparticles: Luminescence studies

Re-dispersible CdS, 5 at.% Eu³⁺-doped CdS, 2 at.% Li⁺ and 5 at.% Eu³⁺ co-doped CdS nanoparticles in organic solvent are prepared by urea hydrolysis in ethylene glycol medium at a low temperature of 170°C. CdS nanoparticles have spherical shape with a diameter of ∼80 nm. The asymmetric ratio (A ₂₁) of the integrated intensities of the electrical dipole transition to the magnetic dipole transition for 5 at.% Eu³⁺-doped CdS is found to be 3.8 and this ratio is significantly decreased for 2 at.% Li⁺ and 5 at.% Eu³⁺ co-doped CdS (A ₂₁ = 2.6). It establishes that the symmetry environment of Eu³⁺ ion is more favored by Li-doping. Extra peak at 550 nm (green emission) could be seen for 2 and 5 at.% Eu³⁺ co-doped CdS. Also, the significant energy transfer from host CdS to Eu³⁺ is found for 5 at.% Eu³⁺-doped CdS compared to that for 2 at.% Li⁺ and 5 at.% Eu³⁺ co-doped CdS.      

Synthesis and Luminescent Properties of M<Subscript>2</Subscript>V<Subscript>2</Subscript>O<Subscript>7</Subscript>: Eu (M=Sr,Ba) Nanophosphors

A solution combustion route for the synthesis of Eu³⁺-activated M₂V₂O₇ (M = Sr, Ba) and their luminescent properties have been investigated. Structure and luminescent characteristics of Sr₂V₂O₇:Eu³⁺ and Ba₂V₂O₇:Eu³⁺ nanophosphors have been studied by x-ray diffraction, scanning electron microscopy, transmission electron microscopy, fluorescence spectrometry and Fourier transform infra-red spectroscopy. The incorporation of Eu³⁺ activator in these nanoparticles has been checked by luminescence characteristics. These nanoparticles have displayed red color under a UV source which is due to characteristics transition of Eu³⁺ from ⁵D₀ → ⁷F₂ at 613 nm in both Sr₂V₂O₇:Eu³⁺ and Ba₂V₂O₇:Eu³⁺ nanophosphors. In addition, the optimal Eu³⁺ - doped contents of Sr_2(1-x)Eu_2xV₂O₇ and Ba_2(1-x)Eu_2xV₂O₇ nanophosphors for both were 4 mol%.     

Quantum cutting in Gd<Subscript>2</Subscript>SiO<Subscript>5</Subscript>: Eu<Superscript>3+</Superscript> by VUV excitation

The emission and excitation spectra of Gd₂SiO₅∶Eu³⁺ were investigated using the VUV beam line of the Beijing Synchrotron Radiation Facility (BSRF). The experimental results were discussed in the frame of visible quantum cutting process involved in Gd³⁺−Eu³⁺ system. Upon direct excitation into the⁶G _J states of Gd³⁺, two visible photon emissions from Eu³⁺ were observed. Cursory evaluation proved that Gd₂SiO₅∶Eu³⁺ is an efficient visible quantum cutter.     

Fabrication,structure, and properties of Fe<Subscript>3</Subscript>O<Subscript>4</Subscript>@C encapsulated with YVO<Subscript>4</Subscript>:Eu<Superscript>3+</Superscript> composites

The use of carbon shells offers many advantages in surface coating or surface modification due to their surface with activated carboxyl and carbonyl groups. In this study, the Fe₃O₄@C@YVO₄:Eu³⁺ composites were prepared through a simple sol–gel process. Reactive carbon interlayer was introduced as a key component, which separates lanthanide-based luminescent component from the magnetite, more importantly, it effectively prevent oxidation of the Fe₃O₄ core during the whole preparation process. The morphology, structure, magnetic, and luminescent properties of the composites were characterized by transmission electron microscopy (TEM), high-resolution TEM, X-ray diffraction, X-ray photoelectron spectra, VSM, and photoluminescent spectrophotometer. As a result, the Fe₃O₄@C/YVO₄:Eu³⁺ composites with well-crystallized and core–shell structure were prepared and the YVO₄:Eu³⁺ luminescent layer decorating the Fe₃O₄@C core–shell microspheres are about 10 nm. In addition, the Fe₃O₄@C@YVO₄:Eu³⁺ composites have the excellent magnetic and luminescent properties, which allow them great potential for bioapplications such as magnetic bioseparation, magnetic resonance imaging, and drug/gene delivery.