Effect of MgO promoter on Ni-based SBA-15 catalysts for combined steam and carbon dioxide reforming of methane

A series of Ni/SBA-15 catalysts with Ni contents ranging from 5 wt% to 15 wt%, as well as another series of 10%Ni/MgO/SBA-15 catalysts, in which the range of the MgO content was from 1 wt% to 7 wt%, were prepared, and their catalytic performances for the reaction of combined steam and carbon dioxide reforming of methane were investigated in a continuous flow microreactor. The structures of the catalysts were characterized using the XRD, H2-TPR and CO2-TPD techniques. The results indicated that the CO selectivity for this reaction was very close to 100%, and the H2/CO ratio of the product gas could be controlled by changing the H2O/CO2 molar ratio of the feed gas. The simultaneous and plentiful existing of steam and CO2 had a significant influence on the catalytic performance of the 10%Ni/SBA-15 catalyst without modification. After reacting at 850 °C for 120 h over this catalyst, the CH4 conversion dropped from 98% to 85%, and the CO2 conversion decreased from 86% to 53%. However, the 10%Ni/3%MgO/SBA-15 catalyst exhibited a much better catalytic performance, and after reacting for 620 h, the CO2 conversion over this catalyst dropped from 92% to around 77%, while the CH4 conversion was not decreased. Oxidation of the Ni0 species as well as carbon deposition during the reaction were the main reasons for the deactivation of the catalyst without modification. On the other hand, modification by the MgO promoter improved the dispersion of the Ni0 species, and enhanced the CO2 adsorption affinity which in turn depressed the occurring of carbon deposition, and thus retarded the deactivation process.     

Catalytic steam reforming of biomass over Ni-based catalysts: Conversion from poplar leaves to hydrogen-rich syngas

A series of Ni/SBA-15 catalysts with Ni contents from 5 wt%–20 wt%and CaO-12.5%Ni/SBA-15 catalysts with CaO contents from 1.4 wt%–9.8 wt%have been prepared.The structure of the catalysts was characterized using X-ray diffraction(XRD),N2 adsorption-desorption,transmission electron microscopy(TEM)and X-ray photoelectron spectroscopy(XPS).The performance of catalytic steam reforming of the poplar leaves to the hydrogen-rich syngas was tested in a fixed-bed reactor.The results indicate that the 7.0wt%CaO-12.5wt%Ni/SBA-15 catalyst exhibits the best performance for the catalytic steam reforming of poplar leaves to hydrogen-rich syngas.The ratio of H2:CO can reach ca 5:1 in the hydrogen-rich syngas.The yield of H2 can reach 273.30 mL/g(poplar leaves).In the CaO-Ni/SBA-15 catalyst,Ni active component mainly fills the role of catalytic steam reforming of the poplar leaves,and CaO active component mainly plays the role as water-gas shift and CO2 sorbent.     

镧助剂对模拟生物沼气重整制备合成气中Ni/SBA-15催化剂结构和性能的影响

以介孔分子筛SBA-15为载体, 采用浸渍法制备了镍质量分数(w)为12.5%, 并且分别添加质量分数(w)为2.5%的镧、铈、镁、钙、锶等助剂的系列Ni基催化剂. 以CH4/CO2体积比为2:1的模拟生物沼气和适量氧气作为原料气, 在常压固定床反应器上评价了催化剂对模拟生物沼气重整制合成气的反应性能. 采用X射线粉末衍射(XRD)、N2吸附/脱附、透射电子显微镜(TEM)、X射线光电子能谱(XPS)及H2程序升温还原(H2-TPR)等对催化剂的结构进行了表征. 催化活性评价显示, 添加镧助剂的2.5%La/12.5%Ni/SBA-15催化剂比添加铈、镁、钙、锶等助剂的催化剂具有更高的催化活性, 并且具有很好的稳定性. 因此, 文中着重研究了镧助剂对催化剂结构和模拟生物沼气重整制合成气的反应性能的影响. 结果表明, 镧能明显提高Ni/SBA-15催化剂的表面镍含量, 同时还具有很好的抗积炭作用, 在850 ℃的温度下反应820 h没有发现积炭生成, 这些可能是提高催化剂性能和稳定性的重要因素.     

Effect of Ni Loading and CexZr1-xO2 Promoter on Ni-Based SBA-15 Catalysts for Steam Reforming of Methane

A series of Ni/SBA-15 catalysts with Ni contents ranging from 5wt% to 20wt% as well as 10wt%Ni/10wt?xZn-xO2/SBA-15 (z=0, 0.5, 1) were prepared. The structures of the catalysts were characterized using XRD, TPR, TEM and BET techniques. The catalytic activities of the catalysts for steam reforming of methane were evaluated in a continuous flow microreactor. The results indicated that both the Ni/SBA-15 and the Ni/CexZr1-xO2/SBA-15 catalysts had good catalytic activities at atmospheric pressure. The 10wt%Ni/SBA-15 catalyst exhibited excellent stability at 800癈 for time on stream of 740 h. After the reaction, carbon deposits were not formed on the surface of the catalyst. There existed a regular hexagonal mesoporous structure in the Ni/SBA-15 and the Ni/CexZr1-xO2/SBA-15 catalysts. The nickel species and the CexZr1-xO2 component were all confined in the SBA-15 mesopores. The CexZr1-xO2 could promote dispersion of the nickel species in the Ni/CexZr1-xO2/SBA-15 catalysts.     

Al-Ni2P/SBA-15催化剂的制备、表征及加氢脱硫催化性能

以磷酸氢二铵为磷源,硝酸镍为镍源,硝酸铝为助剂铝源,制备了n_P/n_Ni=0.8,Al含量为1.06wt%~6.35wt%的一系列Al-Ni₂P/SBA-15催化剂。采用XRD、TEM和N₂吸脱附等技术对催化剂的结构进行了表征研究,以二苯并噻吩(DBT)作为模型化合物,在微型固定床反应器上对催化剂的加氢脱硫(HDS)性能进行了评价。结果表明,Al修饰的Al-Ni₂P/SBA-15催化剂仍然保持介孔结构,当Al含量低于5.29wt%时,催化剂的物相主要是Ni₂P,当Al含量在5.29wt%-6.35wt%之间时,催化剂的物相为Ni₂P和Ni₁₂P₅。Al含量为4.24wt%的3-Al-Ni₂P/SBA-15催化剂具有最好的二苯并噻吩加氢脱硫催化活性,在反应温度为360 ℃,反应压力为3.0 MP的条件下,3-Al-Ni₂P/SBA-15催化剂对二苯并噻吩的转化率可达99.0%。     

Co-Ni2P/SBA-15/Cordierite整体式催化剂的制备及其二苯并噻吩加氢脱硫性能

用共浸渍法制备了Co-Ni2P/SBA-15前躯体,将其调制成活性胶后均匀涂覆到预处理后的堇青石载体上,程序升温还原后制备了一系列Co-Ni2P/SBA-15/堇青石整体式催化剂。采用XRD、N2吸脱附和XPS等对催化剂进行了表征,以1 wt%二苯并噻吩(DBT)/十氢萘溶液为模型化合物,在微型固定床反应器上对催化剂的加氢脱硫(HDS)性能进行了评价。结果表明,不同Co含量的Co-Ni2P/SBA-15/堇青石整体式催化剂中都形成了Ni2P相。Co的加入提高Ni2P/SBA-15/堇青石催化剂的比表面积和孔体积。Co含量为0.55wt%的Co-Ni2P/SBA-15/堇青石整体式催化剂有最好的二苯并噻吩加氢脱硫活性,在380℃,二苯并噻吩转化率能够达到98.8%。Co的加入能够提高二苯并噻吩直接加氢脱硫产物联苯的选择性。     

Preparation,characterization and hydrodesulfurization performances of Co-Ni_2P/SBA-15 catalysts

A series of Co-Ni2P/SBA-15 catalysts with various Co contents, Ni2P contents and P/Ni molar ratios were prepared by impregnating nickel nitrate, diammonium hydrogen phosphate, and then cobalt nitrate into SBA-15 support followed by temperature-programmed reduction in a H2 flow. The catalyst structure was characterized by X-ray diffraction(XRD), high resolution-transmission electron microscopy(HR-TEM)and N2adsorption-desorption techniques and their catalytic performance of the hydrodesulfurization(HDS) of dibenzothiophene(DBT) was evaluated. The effects of Co contents, Ni2 P contents and P/Ni molar ratios on the catalyst structure and HDS of DBT over the Co-Ni2P/SBA-15 catalyst were investigated. The results indicated that the mesoporous structure was mainly maintained and the nickel phosphides were well dispersed in all of the characterized catalysts. The 4Co-25Ni2P/SBA-15(P/Ni = 0.8) catalyst with the Co and Ni2 P contents of 4 wt% and25 wt%, respectively, and the P/Ni molar ratio of 0.8 showed the highest catalytic performance for HDS of DBT. Under the reaction conditions of 380?C and 3.0 MPa, the DBT conversion can reach 99.62%. The HDS of DBT proceeded mainly via the direct desulfurization(DDS)pathway with biphenyl(BP) as the dominant product on all of the catalysts and the BP selectivity was slightly enhanced after the introduction of Co promoters.     

Effect of O2 and H2O on the tri-reforming of the simulated biogas to syngas over Ni-based SBA-15 catalysts

A series of Ni/SBA-15 catalysts with Ni contents from 7.5 wt% to 15 wt% were prepared by impregnation method. The effect of O2 and H2O on the combined reforming of the simulated biogas to syngas was investigated in a continuous flow fixed-bed micro-reactor. The stability of the catalyst was tested at 800 ℃. The results indicated that 10 wt%Ni/SBA-15 catalyst exhibited the highest catalytic activities for the combined reforming of the simulated biogas to syngas. Under the reaction conditions of the feed gas molar ratios CH4/CO2/O2/H2O = 2/1/0.6/0.6, GHSV = 24000 ml•g{cat}-1\cdoth-1 and the reaction temperatureT = 800 ℃, the conversions of CH4 and CO2 were 92.8% and 76.3%, respectively, and the yields of CO and H2 were 99.0% and 82.0%, respectively. The catalytic activities of the catalyst did not decrease obviously after 100 h reaction time on stream.     

Effect of O_2 and H_2O on the tri-reforming of the simulated biogas to syngas over Ni-based SBA-15 catalysts

A series of Ni/SBA-15 catalysts with Ni contents from 7.5 wt% to 15 wt% were prepared by impregnation method.The effect of O2 and H2O on the combined reforming of the simulated biogas to syngas was investigated in a continuous flow fixed-bed micro-reactor.The stability of the catalyst was tested at 800 ?C.The results indicated that 10wt%Ni/SBA-15 catalyst exhibited the highest catalytic activities for the combined reforming of the simulated biogas to syngas.Under the reaction conditions of the feed gas molar ratios CH4/CO2/O2/H2O = 2/1/0.6/0.6,GHSV = 24000 ml gc?a1t h?1 and the reaction temperature T = 800 ?C,the conversions of CH4 and CO2 were 92.8% and 76.3%,respectively,and the yields of CO and H2 were 99.0% and 82.0%,respectively.The catalytic activities of the catalyst did not decrease obviously after 100 h reaction time on stream.     

CeO_2/Ni/Mo/SBA-15甲烷二氧化碳重整催化剂的表征和催化性能(英文)

考察了CeO2修饰及未修饰的Ni/Mo/SBA-15催化剂在CH4-CO2重整上的催化性能并采用N2吸脱附、CO2程序升温脱附、H2程序升温还原、傅里叶红外光谱、X射线衍射、扫描电子显微镜和X射线光电子能谱对催化剂进行了表征.结果表明,在常压,800oC条件下,经过100h在线评价后,Ni/Mo/SBA-15和CeO2/Ni/Mo/SBA-15催化剂仍具有高的反应活性和规整的六方介孔结构,其中CeO2修饰的CeO2/Ni/Mo/SBA-15催化剂表面没有积炭形成,表明CeO2的加入促进了Ni物种在SBA-15介孔分子筛表面的分散,从而阻止了Ce/Ni/Mo/SBA-15催化剂上Ni的烧结和积炭.     

柠檬酸络合法制备Ni2P/SBA-15催化剂及加氢脱硫性能

以介孔分子筛SBA-15为载体,Ni组分采用柠檬酸(CA)配合法,制备了Ni2P质量含量为25%～45%、P/Ni为0.8、CA/Ni为0～1.5的一系列CA-Ni2P/SBA-15催化剂.利用XRD和N2吸脱附表征了催化剂结构,以二苯并噻吩(DBT)为模型硫合物,对催化剂加氢脱硫(HDS)性能进行了评价,考察了CA/Ni比对催化剂结构和反应性能的影响.结果表明,催化剂仍然保持有介孔结构,催化活性物相为Ni2P.反应温度为300～340℃时,Ni2P含量和CA/Ni比都对催化剂的性能有一定的影响,反应温度在360℃以上时,Ni2P含量和CA/Ni比对催化剂性能的影响不明显.Ni2P含量为35%、CA/Ni比为1.0的催化剂具有最好的HDS活性,DBT的转化率可达98%.     

由不同镍盐前体制备高分散Ni/SBA-15催化剂：活化氛围的影响

以硝酸镍和乙酸镍为镍前体,用浸渍法分别在空气和氢气氛围活化制得系列Ni/SBA-15催化剂,通过XRD、H₂-TPD、N₂物理吸附和在线质谱等物理化学手段对催化剂进行了表征,并结合微型高压反应釜萘加氢反应,评价了催化剂的加氢性能。结果表明,氢气氛围活化对硝酸镍为镍前体所制Ni/SBA-15催化剂的镍分散度和活性有显著促进作用,而空气氛围活化对乙酸镍为镍前体所制催化剂有明显促进作用。根据催化剂前体在不同氛围活化时的热分解产物,提出了活化氛围对不同镍前体制得Ni/SBA-15催化剂所产生的作用机理。     

Cr-free Co-Cu/SBA-15 catalysts for hydrogenation of biomass-derivedα-,β-unsaturated aldehyde to alcohol

Cr-free bi-metallic SBA-15-supported Co–Cu catalysts were examined in the conversion of bio-mass-derived α-, β-unsaturated aldehyde (furfural) to value-added chemical furfuryl alcohol (FOL). Co–Cu/SBA-15 catalysts with a fixed Cu loading of 10 wt% and varying Co loadings (2.5, 5, and 10 wt%) were prepared by the impregnation method. The catalysts were characterized by X-ray dif-fraction, N2 sorption, H2 temperature-programmed reduction, scanning electron microscopy, ener-gy-dispersive X-ray spectroscopy, high-resolution transmission electron microscopy, CO chemi-sorption, and inductively coupled plasma mass spectrometry. The influence of different reaction parameters such as temperature, pressure, catalyst dosage, and furfural concentration on the cata-lyst performance was evaluated. Relative to catalysts supported on amorphous silica, the current SBA-15-supported Co–Cu catalysts displayed higher performance, attaining a furfural conversion of 99% and furfuryl alcohol selectivity of 80%. The catalytic reactions were conducted in a 100-mL autoclave at 170 °C and 2 MPa H2 pressure for 4 h.     

Metallic nickel supported on mesoporous silica as catalyst for hydrodeoxygenation: effect of pore size and structure

Catalytic hydrodeoxygenation (HDO) of anisole, a methoxy-rich lignin-derived bio-oil model compound, was carried out over a series of Ni-containing (5, 10, 20, and 30 wt%) catalysts with commercial silica and ordered mesoporous silica SBA-15 as support. Both supports and catalysts were characterized by N₂ adsorption–desorption isotherms, X-ray diffraction, CO chemisorption, and transmission electron microscopy (TEM). Catalytic reaction was performed at 250 °C and 10 bar H₂ pressure. Depending on the catalyst support used and the content of active metal, the catalytic activity and product distribution changed drastically. Increase of the nickel loading resulted in increased anisole conversion and C₆ hydrocarbon (benzene and cyclohexane) yield. However, loading more Ni than 20 wt% resulted in a decrease of both conversion and C₆ yield due to agglomeration of Ni particles. In addition, Ni/SBA-15 samples exhibited much stronger catalytic activity and selectivity toward C₆ hydrocarbon products compared with Ni/silica catalysts. The differences in catalytic activity among these catalysts can be attributed to the effect of the pore size and pore structure of mesoporous SBA-15. SBA-15 can accommodate more Ni species inside channels than conventional silica due to its high pore volume with uniform pore structure, leading to high HDO catalytic activity.     

SBA-15负载钒氧化物催化剂上甲烷选择氧化反应

对SBA-15负载的钒、钼、钨氧化物催化的甲烷选择氧化反应性能进行了比较,发现VO_x/SBA-15催化剂优于MoOx/SBA-15和WOx/SBA-15催化剂.针对钒氧化物催化剂,考察了不同钒源、不同载体以及少量P元素的添加对催化性能的影响,结果表明以SBA-15为载体的催化剂的性能好于MCM-41和Cab-O-Sil为载体的催化剂;与V₂O₅,VO(C₂O₄)相比,NH₄VO₃是制备性能良好的VO_x/SBA-15的钒源;在VO_x/SBA-15中,添加少量P元素后,HCHO的选择性有一定程度的提高.XRD,N₂物理吸附、UN-Raman和H₂-TPR表征结果表明,负载量低于3 wt%时,钒组分可能主要以高分散的单核的VO_x物种存在,我们推测该物种对甲烷选择氧化制甲醛起关键作用.     

Ni2P/SBA-15催化剂的结构及加氢脱硫性能

以硝酸镍为镍源, 磷酸氢二铵为磷源, 介孔分子筛SBA-15为载体, 用共浸渍法制备了含磷化镍前驱体的样品, 然后在氢气流中采用程序升温还原法, 制备了Ni2P质量分数为5%-40%的Ni2P/SBA-15催化剂. 用X射线衍射(XRD)、N2吸附脱附、透射电子显微镜(TEM)、傅立叶变换红外光谱(FTIR)等分析测试技术对催化剂的结构进行了表征, 以噻吩和二苯并噻吩(DBT)为模型化合物, 在微型固定床反应器上对催化剂的加氢脱硫(HDS)性能进行了评价. 结果表明, Ni2P/SBA-15催化剂中SBA-15 的介孔结构依然存在, 活性组分Ni2P具有良好的分散性, 但随Ni2P含量的增加, 催化剂的比表面积、孔容和孔径均有明显减小. 当反应温度为320 ℃时, Ni2P含量为15%-25%(w)的催化剂就具有很好的加氢脱硫催化性能; 反应温度在360 ℃以上时, 所有催化剂都具有优异的深度脱硫催化性能. Ni2P/SBA-15催化剂对二苯并噻吩的加氢脱硫(HDS)主要以直接脱硫机理(DDS)进行.     

嫁接法制备Ni/SBA-15催化剂的催化氯苯加氢脱氯

SBA-15表面经嫁接方式引入氨基官能团,与Ni络合制备了SBA-15负载的Ni催化剂(Ni/SBA-15N)。同时,采用传统的浸渍法制备了具有相似Ni负载量的催化剂(Ni/SBA-15)。在负载量相近条件下,Ni/SBA-15N的Ni颗粒分散性均高于Ni/SBA-15。XRD和TPR结果表明,催化剂焙烧后,在氨化SBA-15表面,Ni以硅酸镍形式存在,而在SBA-15表面,Ni以NiO形式存在。Ni/SBA-15对氯苯催化加氢脱氯活性不随Ni负载量的变化而变化;而在Ni/SBA-15N中,Ni负载量增加,催化剂活性增加。     

Reductive amination of cyclohexanol/cyclohexanone to cyclohexylamine using SBA-15 supported copper catalysts

Amination of cyclohexanol was investigated in vapour phase over copper catalysts supported on mesoporous SBA-15. The different products identified during reductive amination of cyclohexanol reaction were cyclohexanone, cyclohexylamine, along with small amounts of N-Cyclohexylidinecyclohexylamine and dicyclohexylamine. Among several catalysts tested for the reductive amination, 5% Cu supported on SBA-15 exhibited better catalytic performance than other catalysts with 36% selectivity towards cylclohexylamine at 80% cyclohexanol conversion. The optimum reaction conditions employed to achieve the best catalyst performance were at 250 °C, 0.1 MPa of H₂/NH₃, TOS-10h. The active Cu sites, acidity of the catalyst, and effect of reaction parameters play a pivotal role in the reductive amination reaction. The prepared catalysts were characterized by XRD, BET, SEM, H₂-TPR and NH₃-TPD. The dispersion of Cu, particle size, and metal surface area (m²/g) calculated from pulse N₂O decomposition method. TPR findings reveal the presence of substantially dispersed copper oxide species at lower loadings which is easily reducible than the bulk copper oxide species found at higher Cu loadings. The acidity measurements by NH₃-TPD analysis suggest that the maximum acidic strength was obtained at 5 wt% copper on porous SBA-15, and decreased with Cu loadings. The catalytic properties are well in agreement with the findings of catalysts characterization.     

氮化SBA-16负载镍基催化剂的制备及其对甲烷二氧化碳重整反应的催化性能

通过软模板法合成了SBA-16分子筛,采用高温氨气氮化的方法使有序介孔硅材料中的氧原子部分被氮原子取代,得到氮化的SBA-16载体(SBA-16-N)。采用满孔浸渍法制备了镍基催化剂,并将制得的Ni/SBA-16和Ni/SBA-16-N催化剂用于甲烷二氧化碳重整反应。通过透射电镜、氮气物理吸附、X射线衍射、X射线光电子能谱和二氧化碳程序升温脱附等手段研究了载体和催化剂的结构,并利用热重分析对反应之后回收催化剂进行了表征。结果表明,高温氮化后的分子筛中掺入了氮元素,增加了载体的碱性,改善了载体对反应气体的吸附活化能力,增强了载体与金属之间的相互作用,从而提高了催化剂的活性和抗积炭性能。     

助剂对CH4,CO2和O2制合成气反应催化剂性能的影响

考察了NiCaO-Al2O3催化剂中添加碱金属、碱土金属、稀土金属氧化物、CuO助剂及CaO含量对催化剂性能的影响。结果表明,10Ni-2K-2Cu15CaO-Al2O3催化剂对CH4、CO2和O2制合成气反应具有较高的催化活性、选择性和较好的抗积炭性能。通过TPR、CO-TPD、XPS和XRD对催化剂进行表征,发现K2O、CuO和CaO的添加削弱了活性组分Ni与载体Al2O3间的相互作用,增加Ni的电子密度,加速了CO与H2的脱附,从而抑制了CH4深度裂解积炭和CO歧化积炭。此外,这些助剂的添加也提高了Ni的分散度,增强了催化剂的抗积炭能力。