Kinetic and microstructure studies of poly(ethylene-co-p-methylstyrene) copolymers prepared by metallocene catalysts with constrained ligand geometry

This paper discusses the poly(ethylene-co-p-methylstyrene) copolymers prepared by metallocene catalysts, such as Et(Ind)₂ZrCl₂ and [C₅Me₄(SiMe₂N^tBu)]-TiCl₂, with constrained ligand geometry. The copolymerization reaction was examined by comonomer reactivity (reactivity ratio and comonomer conversion versus time), copolymer microstructure (DSC and ¹³C-NMR analyses) and the comparisons between p-methylstyrene and other styrene-derivatives (styrene, o-methylstyrene and m-methylstyrene). The combined experimental results clearly show that p-methylstyrene performs distinctively better than styrene and its derivatives, due to the cationic coordination mechanism and spatially opened catalytic site in metallocene catalysts with constrained ligand geometry. A broad composition range of random poly(ethylene-co-p-methylstyrene)copolymers were prepared with narrow molecular weight and composition distributions. With the increase of p-methylstyrene concentration, poly(ethylene-co-p-ethylstyrene)copolymer shows systematical decrease of melting point and crystallinity and increase of glass transition temperature. At above 10 mol % of p-methylstyrene, the crystallinity of copolymer almost completely disappears. © 1998 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 36: 1017–1029, 1998     

Synthesis of PP graft copolymers via anionic living graft-from reactions of polypropylene containing reactive p-methylstyrene units

In this article, we discuss a new chemical route for preparing polypropylene (PP) graft copolymers containing a PP backbone and several (polar and nonpolar) polymer side chains, including polybutadiene, polystyrene, poly(p-methylstyrene), poly(methyl methacrylate), and polyacrylonitrile. The new PP graft copolymers had a controlled molecular structure and a known PP molecular weight, graft density, graft length, and narrow molecular weight distribution of the side chains. The chemistry involves an intermediate poly(propylene-co-p-methylstyrene) copolymer containing few p-methylstyrene (p-MS) units. The methyl group in a p-MS unit could be lithiated selectively by alkylithium to form a stable benzylic anion. Because of the insolubility of the PP copolymer at room temperature, the excess alkylithium could be removed completely from the lithiated polymer. By the addition of the anionically polymerizable monomers, including polar and nonpolar monomers, the stable benzylic anions in PP initiated a living anionic graft-from polymerization at ambient temperature to produce PP graft copolymers without any significant side reactions. The side-chain length was basically proportional to the reaction time and monomer concentration. © 1999 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 37: 4176–4183, 1999     

Poly(ϵ‐caprolactone)‐b‐poly(ethylene glycol)‐b‐poly(ϵ‐caprolactone) triblock copolymers: Synthesis and self‐assembly in aqueous solutions

Nontoxic and biodegradable poly(?‐caprolactone)‐b‐poly(ethylene glycol)‐b‐poly(?‐caprolactone) triblock copolymers were synthesized by the solution polymerization of ?‐caprolactone in the presence of poly(ethylene glycol). The chemical structure of the resulting triblock copolymer was characterized with ¹H NMR and gel permeation chromatography. In aqueous solutions of the triblock copolymers, the micellization and sol–gel‐transition behaviors were investigated. The experimental results showed that the unimer‐to‐micelle transition did occur. In a sol–gel‐transition phase diagram obtained by the vial‐tilting method, the boundary curve shifted to the left, and the gel regions expanded with the increasing molecular weight of the poly(?‐caprolactone) block. In addition, the hydrodynamic diameters of the micelles were almost independent of the investigated temperature (25–55 °C). The atomic force microscopy results showed that spherical micelles formed at the copolymer concentration of 2.5 × 10^?4 g/mL, whereas necklace‐like and worm‐like shapes were adopted when the concentration was 0.25 g/mL, which was high enough to form a gel. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 605–613, 2007     

Novel synthesis of biodegradable poly(lactide-co-ethylene glycol) block copolymers

Biodegradable and amphiphilic diblock copolymers [polylactide-block-poly(ethylene glycol)] and triblock copolymers [polylactide-block-poly(ethylene glycol)-block-polylactide] were synthesized by the anionic ring-opening polymerization of lactides in the presence of poly(ethylene glycol) methyl ether or poly(ethylene glycol) and potassium hexamethyldisilazide as a catalyst. The polymerization in toluene at room temperature was very fast, yielding copolymers of controlled molecular weights and tailored molecular architectures. The chemical structure of the copolymers was investigated with ¹H and ¹³C NMR. The formation of block copolymers was confirmed by ¹³C NMR and differential scanning calorimetry investigations. The monomodal profile of the molecular weight distribution by gel permeation chromatography provided further evidence of block copolymer formation as well as the absence of cyclic species. Additional confirmation of the block copolymers was obtained by the substitution of 2-butanol for poly(ethylene glycol); butyl groups were clearly identified by ¹H NMR as polymer chain end groups. The effects of the copolymer composition and lactide stereochemistry on the copolymer properties were examined. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 2235–2245, 2007     

Cationic grafting of olefins from PVC: The effect of reaction conditions

The cationic grafting of isobutylene, styrene, α-methylstyrene, and β-pinene from a poly(vinyl chloride) (PVC) backbone was investigated. Grafting-from was induced by Et₂AlCl in 1,2-dichloroethane and methylene dichloride solutions from 20 to −70 °C. The effects of temperature and proton trap [2,6-di-tert-butylpyridine (DtBP)] on grafting-from efficiency (G_eff), extent of grafting, branch length (molecular weight), and number of branches per PVC molecule were determined. Reducing the temperature invariably increased the G_eff and the molecular weight of polyisobutylene, polystyrene, poly(α-methylstyrene), and poly(β-pinene) branches attached to PVC. The magnitude of the effects was different with the various olefins and depended on the reaction conditions. The effect of DtBP was examined in the 5 × 10⁻⁴–4 × 10⁻³ mol/L range. By increasing the DtBP concentration the G_eff increased; however, the number-average molecular weight of the grafted branches decreased. The lengths of the grafted branches can be controlled, and G_eff's close to 100% were obtained. The fact that the proton trap reduced the molecular weights of grafted branches suggests that besides proton scavenging, DtBP may also abstract protons from the growing carbenium ion site. © 2001 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 39: 1675–1680, 2001     

Study of molecular motion of block copolymers in solution by high-resolution proton magnetic resonance

Molecular motions of hydrophobic–hydrophilic water-soluble block copolymers in solution were investigated by high-resolution proton magnetic resonance (NMR). Samples studied include block copolymers of polystyrene–poly(ethylene oxide), polybutadiene–poly(ethylene oxide), and poly(ethylene oxide)–poly(propylene oxide)–poly(ethylene oxide). NMR measurements were carried out varying molecular weight, temperature, and solvent composition. For AB copolymers of polystyrene and poly(ethylene oxide), two peaks caused by the phenyl protons of low-molecular-weight (M?_n = 3,300) copolymer were clearly resolved in D₂O at 100°C, but the phenyl proton peaks of high-molecular-weight (M?_n = 13,500 and 36,000) copolymers were too broad to observe in the same solvent, even at 100°C. It is concluded that polystyrene blocks are more mobile in low-molecular-weight copolymer in water than in high-molecular-weight copolymer in the same solvent because the molecular weight of the polystyrene block of the low-molecular-weight copolymer is itself small. In the mixed solvent D₂O and deuterated tetrahydrofuran (THF-d₈), two peaks caused by the phenyl protons of the high-molecular-weight (M?_n = 36,000) copolymer were clearly resolved at 67°C. It is thought that the molecular motions of the polystyrene blocks are activated by the interaction between these blocks and THF in the mixed solvent.     

Using the reversible addition–fragmentation chain transfer process to synthesize core‐crosslinked micelles

Poly(2‐hydroxyethyl acrylate)–poly(n‐butyl acrylate) block copolymers were synthesized with the reversible addition–fragmentation chain transfer (RAFT) process. The block copolymers were synthesized successfully with either poly(2‐hydroxyethyl acrylate) or poly(n‐butyl acrylate) macro‐RAFT agents. The resulting block copolymers had narrow molecular weight distributions (polydispersity index = 1.3–1.4). Copolymer self‐aggregation in water yielded micelles, with the hydrodynamic diameter (D_h) values of the aggregates dependent on the length of both blocks according to D_h ～ N_BA^1.17N_HEA^0.57, where N_BA is the number of repeating units of n‐butyl acrylate and N_HEA is the number of repeating units of 2‐hydroxyethyl acrylate. The micelles were subsequently stabilized via chain extension of the block copolymer with a crosslinking agent. The successful chain extension in a micellar system was confirmed by an increase in the molecular weight, which was detected with membrane osmometry. The crosslinked particles showed noticeably different aggregation behavior in diverse solvent systems. The uncrosslinked micelles formed by the block copolymer (N_HEA = 260, N_BA = 75) displayed a definite critical micelle concentration at 5.4 × 10^?4 g L^?1 in aqueous solutions. However, upon crosslinking, the critical micelle concentration transition became obscure. © 2006Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 2177–2194, 2006     

Living Cationic Polymerization of α-Methylstyrene. 2. Synthesis of Block and Random Copolymers with 2-Chloroethyl Vinyl Ether and End-Functionauzed Polymers†

Abstract

Both AB and BA block copolymers of α-methylstyrene (αMeSt) and 2-chloroethyl vinyl ether (CEVE) were synthesized by the sequential living cationic polymerization initiated with the HCl-CEVE adduct (1a)/SnBr₄ system in CH₂Cl₂ at -78°C. αMeSt-CEVE (AB) block copolymers with narrow molecular weight distributions ([Mbar]_w/[Mbar]_n ～ 1.15) were obtained when αMeSt was polymerized first, followed by addition of CEVE to the resulting αMeSt living polymer solution. The reverse order of monomer addition, from CEVE to αMeSt, also led to a BA-type block copolymer. In the polymerization of a mixture of the two monomers, almost random copolymers were obtained. Living polymerizations of αMeSt were also induced with functional initiating systems, HCl-functionalized vinyl ether adducts (1b-1d)/SnBr₄, to give end-function-alized poly(αMeSt)s with a methacrylate, an acetate, or a phthalimide terminal.     

Effect of zinc salts on the spontaneous copolymerization of 4-vinylpyridine with various electron-rich vinyl monomers

The spontaneous copolymerization of 4-vinylpyridine (4-VP) complexed with three different zinc salts (chloride, acetate, and triflate) with various electron-rich vinyl monomers (p-methoxystyrene, MeOSt; p-methylstyrene, MeSt; α-methylstyrene, α-MeSt; p-tert-butylstyrene, BuSt; styrene, St) was investigated in methanol at 75°C. Increasing the zinc salt concentration or the nucleophilicity of the electron-rich monomer increased the copolymer yields. All obtained copolymers are characterized by high molecular weight (10⁵) and broad molecular weight distribution. Both ¹H-NMR and elemental analyses confirmed the almost 1 : 1 copolymer structure. Changing the anion of the zinc salt does not have a considerable effect either on the copolymerization rate or on the molecular weight. The proposed mechanism exhibits the formation of a σ-bond between the β-carbons of the two donor–acceptor monomers. This creates the 1,4-tetramethylene biradical intermediate which can initiate the copolymerization reaction. © 1997 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 35 : 2787–2792, 1997     

Biodegradable and stimuli sensitive amphiphilic graft copolymers and their sol–gel phase transition behavior

pH and temperature‐sensitive biodegradable poly(β‐aminoester)‐graft‐poly(ε‐caprolactone)‐block‐methoxy poly(ethylene glycol) (PBAE‐g‐PCL‐b‐mPEG) amphiphilic graft copolymers with different molecular weights were synthesized. The structure of these copolymers was adjusted by varying the feed ratios of ε‐caprolactone to methoxy poly(ethylene glycol)s (mPEG), amine and diacrylate monomer amounts and the molecular weight of mPEG. Aqueous solutions of these copolymers formed micelles at lower concentrations; however, the concentrated solutions showed a reversible sol–gel transition property depending on both pH and temperature changes under representative physiological conditions (pH 7.4, 37°C). The effects of the molecular weight of pH‐sensitive poly(β‐aminoester) block and mPEG group, the hydrophobic to hydrophilic block ratio (PCL/mPEG) and the concentration of the copolymer on the sol–gel transition were investigated. Proton nuclear magnetic resonance (¹H NMR) and gel permeation chromatography measurements were used to characterize the structure of the synthesized copolymers. The self‐assemble behavior and critical micelle concentration of the amphiphilic copolymers were estimated in phosphate buffer solution using fluorescence spectroscopy. The gelling behavior was measured by using tube inversion method. At pH 7.4, all copolymer solutions prepared 20 wt% concentration indicated sol–gel transition with increasing temperature. In vitro degradation experiments displayed that the synthesized graft copolymers mostly degraded hydrolytically within 20 days under physiological conditions. In order to investigate the potential application of synthesized hydrogels in drug delivery, Methylene Blue was used and approximately 70% of the loaded amount was released in 120 hr. The findings indicate that obtained graft copolymers can be used as injectable biodegradable carriers for pharmaceutical drugs. Copyright © 2015 John Wiley & Sons, Ltd.     

Temperature dependence of unperturbed dimensions for stereoirregular 1,4-polybutadiene and poly(α-methylstyrene)

The temperature coefficient of chain dimensions, d ln〈r²〉₀/dT, was determined for stereoirregular 1,4-polybutadiene and poly(α-methylstyrene) via dilute solution viscometry. The 1,4-polybutadiene was examined in oligomeric 1,4-polybutadiene (an athermal solvent), and poly(α-methylstyrene) was evaluated under near-theta conditions using 1-chloro-n-alkanes as solvents. Both approaches minimize the potential for influence by specific solvent effects. The resulting temperature coefficients, ?0.1₀ × 10^?3 deg^?1 for 1,4-polybutadiene and ?0.3₀ × 10^?3 deg^?1 for poly(α-methylstyrene) are in excellent agreement with rotational isomeric state calculations.     

Synthesis and characterization of block copolymers from 2‐vinylnaphthalene by anionic polymerization

The anionic polymerization of 2‐vinylnaphthalene (2VN) has been studied in tetrahydrofuran (THF) at ?78 °C and in toluene at 40 °C. 2VN polymerization in THF, toluene, or toluene/THF (99:1 v/v) initiated by sec‐butyllithium (sBuLi) indicates living characteristics, affording polymers with predefined molecular weights and narrow molecular weight distributions. Block copolymers of 2VN with methyl methacrylate (MMA) and tert‐butyl acrylate (tBA) have been synthesized successfully by sequential monomer addition in THF at ?78 °C initiated by an adduct of sBuLi–LiCl. The crossover propagation from poly(2‐vinylnaphthyllithium) (P2VN) macroanions to MMA and tBA appears to be living, the molecular weight and composition can be predicted, and the molecular weight distribution of the resulting block copolymer is narrow (weight‐average molecular/number‐average molecular weight < 1.3). Block copolymers with different chain lengths for the P2VN segment can easily be prepared by variations in the monomer ratios. The block copolymerization of 2VN with hexamethylcyclotrisiloxane also results in a block copolymer of P2VN and poly(dimethylsiloxane) (PDMS) contaminated with a significant amount of homo‐PDMS. Poly(2VN‐b‐nBA) (where nBA is n‐butyl acrylate) has also been prepared by the transesterification reaction of the poly(2VN‐b‐tBA) block copolymer. Size exclusion chromatography, Fourier transform infrared, and ¹H NMR measurements indicate that the resulting polymers have the required architecture. The corresponding amphiphilic block copolymer of poly(2VN‐b‐AA) (where AA is acrylic acid) has been synthesized by acidic hydrolysis of the ester group of tert‐butyl from the poly(2VN‐b‐tBA) copolymer. © 2002 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 40: 4387–4397, 2002     

Amphiphilic block and statistical copolymers with pendant glucose residues: Controlled synthesis by living cationic polymerization and the effect of copolymer architecture on their properties

Amphiphilic block and statistical copolymers of vinyl ethers (VEs) with pendant glucose residues were synthesized by the living cationic polymerization of isobutyl VE (IBVE) and a VE carrying 1,2:5,6‐di‐O‐isopropylidene‐D ‐glucose (IpGlcVE), followed by deprotection. The block copolymer was prepared by a two‐stage sequential block copolymerization, whereas the statistical copolymer was obtained by the copolymerization of a mixture of the two monomers. The monomer reactivity ratios estimated with the statistical copolymerization were r₁ (IBVE) = 1.65 and r₂ (IpGlcVE) = 1.15. The obtained statistical copolymers were nearly uniform with the comonomer composition along the main chain. Both the block and statistical copolymers had narrow molecular weight distributions (weight‐average molecular weight/number‐average molecular weight ∼ 1.1). Gel permeation chromatography, static light scattering, and spin–lattice relaxation time measurements in a selective solvent revealed that the block copolymer formed multimolecular micelles, possibly with a hydrophobic poly(IBVE) core and a glucose‐carrying poly(VE) shell, whereas the statistical copolymer with nearly the same molecular weight and segment composition was molecularly dispersed in solution. The surface properties of the solvent‐cast films of the block and statistical copolymer were also investigated with the contact‐angle measurement. © 2001 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 39: 459–467, 2001     

Synthesis and thermal,mechanical, and optical properties of A–B–A or A–B block copolymers containing poly(norbornene‐co‐1‐octene)

A–B–A block copolymers which consist of poly(norbornene‐co‐1‐octene) and atactic polypropylene (PP) segments were synthesized by using ansa‐fluorenylamidotitanium complex as a catalyst varying the ratio of norbornene, 1‐octene, and propylene. The copolymer was obtained quantitatively with high molecular weight (>100,000) and narrow molecular weight distribution (polydispersity index, <1.5). A–B block copolymers of poly(norbornene‐co‐1‐octene) and poly(methyl methacrylate) (PMMA) was also obtained by the same procedure. Mechanical and optical properties of these copolymer films, which were obtained by solution casting process, were also investigated. Introduction of PP soft segment greatly improved mechanical properties, keeping their high transparency. Introduction of PMMA block also increased the tensile strength. © 2013 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2014 , 52, 267–271     

Novel synthesis of biodegradable linear and star block copolymers based on ε‐caprolactone and lactides using potassium‐based catalyst

Biodegradable, triblock poly(lactide)‐block‐poly(ε‐caprolactone)‐block‐poly(lactide) (PLA‐b‐PCL‐b‐PLA) copolymers and 3‐star‐(PCL‐b‐PLA) block copolymers were synthesized by ring opening polymerization of lactides in the presence of poly(ε‐caprolactone) diol or 3‐star‐poly(ε‐caprolactone) triol as macroinitiator and potassium hexamethyldisilazide as a catalyst. Polymerizations were carried out in toluene at room temperature to yield monomodal polymers of controlled molecular weight. The chemical structure of the copolymers was investigated by ¹H and ¹³C‐NMR. The formation of block copolymers was confirmed by NMR and DSC investigations. The effects of copolymer composition and molecular structure on the physical properties were investigated by GPC and DSC. © 2008 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 46: 5363–5370, 2008     

Supramolecular complexes of poly(3‐Hexylthiophene)‐block (and random)‐poly[3‐(2‐(6‐carboxyhexyl)methyl)thiophene] copolymers with perylene bisimide

Block and random copolymers of poly(3‐hexylthiophene) and poly[3‐(2‐(6‐carboxyhexyl)methyl)thiophene] with side‐chain carboxylic functionality ((P3HT‐b‐P3COOH) and (P3HT‐r‐P3COOH) were developed by Grignard Metathesis (GRIM) polymerization. The carboxylic functionality was introduced in the side chain via the oxazoline route. Both the block and random polythiophene copolymers were complexed with pyridine functionalized perylene bisimide to obtain supramolecular block and random polymer complexes. The complex formation in both systems was confirmed by ¹H NMR, WXRD and SAXS studies. An expansion of d spacing upon complex formation was observed in both the block and random copolymer, which could be traced by WXRD. Hole and electron mobilities measured for the supramolecular complexes indicated values which were higher by an order of magnitude for the supramolecular block complex (μ_h ≈ 2.9 × 10⁻⁴ cm²/Vs; μ_e ≈ 3.1 × 10⁻⁶ cm²/Vs) as compared to the random (μ_h ≈ 1.4 × 10⁻⁵ cm²/Vs; μ_e ≈ 4.7 × 10⁻⁷ cm²/Vs) copolymer. These results are indicative of the higher degree of disorder prevailing in the films of random copolymer system compared to the block copolymer. © 2018 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2018 , 56, 1574–1583     

Amphiphilic diblock,triblock, and star block copolymers by living radical polymerization: Synthesis and aggregation behavior

Copper(I)‐mediated living radical polymerization was used to synthesize amphiphilic block copolymers of poly(n‐butyl methacrylate) [P(n‐BMA)] and poly[(2‐dimethylamino)ethyl methacrylate] (PDMAEMA). Functionalized bromo P(n‐BMA) macroinitiators were prepared from monofunctional, difunctional, and trifunctional initiators: 2‐bromo‐2‐methylpropionic acid 4‐methoxyphenyl ester, 1,4‐(2′‐bromo‐2′‐methyl‐propionate)benzene, and 1,3,5‐(2′‐bromo‐2′‐methylpropionato)benzene. The living nature of the polymerizations involved was investigated in each case, leading to narrow‐polydispersity polymers for which the number‐average molecular weight increased fairly linearly with time with good first‐order kinetics in the monomer. These macroinitiators were subsequently used for the polymerization of (2‐dimethylamino)ethyl methacrylate to obtain well‐defined [P(n‐BMA)_x‐b‐PDMAEMA_y]_z diblock (15,900; polydispersity index = 1.60), triblock (23,200; polydispersity index = 1.24), and star block copolymers (50,700; polydispersity index = 1.46). Amphiphilic block copolymers contained between 60 and 80 mol % hydrophilic PDMAEMA blocks to solubilize them in water. The polymers were quaternized with methyl iodide to render them even more hydrophilic. The aggregation behavior of these copolymers was investigated with fluorescence spectroscopy and dynamic light scattering. For blocks of similar comonomer compositions, the apparent critical aggregation concentration (cac = 3.22–7.13 × 10^?3 g L^?1) and the aggregate size (ca. 65 nm) were both dependent on the copolymer architecture. However, for the same copolymer structure, increasing the hydrophilic PDMAEMA block length had little effect on the cac but resulted in a change in the aggregate size. © 2002 John Wiley & Sons, Inc. J Polym Sci Part A: Polym Chem 40: 439–450, 2002; DOI 10.1002/pola.10122     

Synthesis of four‐armed poly(ε‐caprolactone)‐block‐poly(ethylene oxide) by diethylzinc catalyst

Biodegradable, amphiphilic, four‐armed poly(?‐caprolactone)‐block‐poly(ethylene oxide) (PCL‐b‐PEO) copolymers were synthesized by ring‐opening polymerization of ethylene oxide in the presence of four‐armed poly(?‐caprolactone) (PCL) with terminal OH groups with diethylzinc (ZnEt₂) as a catalyst. The chemical structure of PCL‐b‐PEO copolymer was confirmed by ¹H NMR and ¹³C NMR. The hydroxyl end groups of the four‐armed PCL were successfully substituted by PEO blocks in the copolymer. The monomodal profile of molecular weight distribution by gel permeation chromatography provided further evidence for the four‐armed architecture of the copolymer. Physicochemical properties of the four‐armed block copolymers differed from their starting four‐armed PCL precursor. The melting points were between those of PCL precursor and linear poly(ethylene glycol). The length of the outer PEO blocks exhibited an obvious effect on the crystallizability of the block copolymer. The degree of swelling of the four‐armed block copolymer increased with PEO length and PEO content. The micelle formation of the four‐armed block copolymer was examined by a fluorescent probe technique, and the existence of the critical micelle concentration (cmc) confirmed the amphiphilic nature of the resulting copolymer. The cmc value increased with increasing PEO length. The absolute cmc values were higher than those for linear amphiphilic block copolymers. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 950–959, 2004     

Synthesis and characterization of biodegradable triblock copolymers based on bacterial poly[(R)‐3‐hydroxybutyrate] by atom transfer radical polymerization

Biodegradable poly(tert‐butyl acrylate)–poly[(R)‐3‐hydroxybutyrate]–poly (tert‐butyl acrylate) triblock copolymers based on bacterial poly[(R)‐3‐hydroxybutyrate] (PHB) were synthesized by atom transfer radical polymerization. The chain architectures of the triblock copolymers were confirmed by ¹H NMR and ¹³C NMR spectra. Gel permeation chromatography analysis was used to estimate the molecular weight characteristics and lengths of the PHB and poly(tert‐butyl acrylate) blocks of the copolymers. The thermal properties of the copolymers were studied by thermogravimetric analysis (TGA) and differential scanning calorimetry (DSC). TGA showed that the triblock copolymers underwent stepwise thermal degradation and had better thermal stability than their respective homopolymers, whereas DSC analyses showed that a microphase‐separation structure was formed only in the triblock copolymers with the longer PHB block. As a similar result, from wide‐angle X‐ray diffraction experimentation, the crystalline phase of PHB could not be seen evidently in the triblock copolymers with the shorter PHB block. The enzymatic hydrolysis of the copolymer films was carried at 37 °C and pH 7.4 in a potassium phosphate buffer with an extracellular PHB depolymerase from Penicillum sp. The biodegradability of the triblock copolymers increased with an increase in the PHB block content. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 43: 4857–4869, 2005     

Synthesis of poly(vinyl chloride)‐b‐poly(n‐butyl acrylate)‐b‐poly(vinyl chloride) by the competitive single‐electron‐transfer/degenerative‐chain‐transfer‐mediated living radical polymerization in water

The synthesis of a block copolymer poly(vinyl chloride)‐b‐poly(n‐butyl acrylate)‐b‐poly(vinyl chloride) is reported. This new material was synthesized by single‐electron‐transfer/degenerative‐chain‐transfer‐mediated living radical polymerization (SET‐DTLRP) in two steps. First, a bifunctional macroinitiator of α,ω‐di(iodo)poly (butyl acrylate) [α,ω‐di(iodo)PBA] was synthesized by SET‐DTLRP in water at 25 °C. The macroinitiator was further reinitiated by SET‐DTLRP, leading to the formation of the desired product. This ABA block copolymer was synthesized with high initiator efficiency. The kinetics of the copolymerization reaction was studied for two PBA macroinitiators with number–average molecular weight of 10 k and 20 k. The relationship between the conversion and the number–average molecular weight was found to be linear. The dynamic mechanical thermal analysis suggests just one phase, indicating that copolymer behaves as a single material with no phase separation. This methodology provides the access to several block copolymers and other complex architectures that result from combinations of thermoplastics (PVC) and elastomers (PBA). From industrial standpoint, this process is attractive, because of easy experimental setup and the environmental friendly reaction medium. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 3001–3008, 2006