Synthesis of β-Ga2O3 nanowires through microwave plasma chemical vapor deposition

In this study, we demonstrate the large-scale synthesis of beta gallium oxide (β-Ga₂O₃) nanowires through microwave plasma chemical vapor deposition (MPCVD) of a Ga droplet in the H₂O and Ar atmosphere at 600 W. Unlike the commonly used MPCVD method, the H₂O, not mixture of gas, was employed to synthesize the nanowires. The ultra-long β-Ga₂O₃ nanowires with diameters of about 20-30 nm were several tens of micrometers long. The morphology and structure of products were analyzed by scanning electron microscopy (SEM), X-ray diffraction (XRD), transmission electron microscopy (TEM) and high-resolution transmission electron microscope (HRTEM). The growth of β-Ga₂O₃ nanowires was controlled by vapor-solid (VS) crystal growth mechanism.     

Structural, microstructural and magnetic properties of NiFe2O4, CoFe2O4 and MnFe2O4 nanoferrite thin films

The structural, microstructural and magnetic properties of nanoferrite NiFe₂O₄ (NF), CoFe₂O₄ (CF) and MnFe₂O₄ (MF) thin films have been studied. The coating solution of these ferrite films was prepared by a chemical synthesis route called sol-gel combined metallo-organic decomposition method. The solution was coated on Si substrate by spin coating and annealed at 700 °C for 3 h. X-ray diffraction pattern has been used to analyze the phase structure and lattice parameters. The scanning electron microscopy (SEM) and atomic force microscopy (AFM) have been used to show the nanostructural behavior of these ferrites. The values of average grain's size from SEM are 44, 60 and 74 nm, and from AFM are 46, 61 and 75 nm, respectively, measured for NF, CF and MF ferrites. At room temperature, the values of saturation magnetization, M_s∼50.60, 33.52 and 5.40 emu/cc, and remanent magnetization, M_r∼14.33, 15.50 and 1.10 emu/cc, respectively, are observed for NF, CF and MF. At low temperature measurements of 10 K, the anisotropy of ferromagnetism is observed in these ferrite films. The superparamagnetic/paramagnetic behavior is also confirmed by χ′(T) curves of AC susceptibility by applying DC magnetizing field of 3 Oe. The temperature dependent magnetization measurements show the magnetic phase transition temperature.     

Non-isothermal decomposition of NiC2O4-FeC2O4 mixture aiming at the production of NiFe2O4

The non-isothermal decomposition of NiC₂O₄·2H₂O-FeC₂O₄·2H₂O (1:2 mole ratio) mixture was studied on heating to the formation of NiO-Fe₂O₃ mixture at 350 °C in air atmosphere using thermogravimetry. Kinetic analysis of data according to the integral composite method showed that the oxidative decomposition of FeC₂O₄ and NiC₂O₄ are best described by the three-dimensional phase boundary model. The activation parameters were calculated and discussed. The solid products at different decomposition stages were identified using XRD, Mössbauer and FT-IR spectroscopic techniques. Some characteristic XRD lines of NiFe₂O₄ start to appear at 800 °C beside the characteristic lines of NiO and Fe₂O₃, whereas at 1000 °C, only the characteristic lines of single phase cubic NiFe₂O₄ appeared. The Mössbauer spectrum at 1000 °C fitted into two Zeeman sextets characteristic of Fe³⁺ on the tetrahedral (A) and octahedral (B) sites of NiFe₂O₄ inverse spinel. Consistent results were obtained using FT-IR where the absorption bands appeared at 602 and 407 cm⁻¹ for the mixture calcined at 1000 °C. These can be assigned to the intrinsic vibrations of tetrahedral and octahedral sites of NiFe₂O₄, respectively.     

Effect of annealing temperature on the decomposition of reactively sputtered Ag2Cu2O3 films

Ag₂Cu₂O₃ films were deposited on glass substrates by reactive sputtering of a composite silver-copper target. The deposited films were annealed in air at 100, 200 and 300 °C. The structure of the films was studied using X-ray diffraction (XRD), their surface morphology was characterised using scanning electron microscopy (SEM) and their electrical resistivity at room temperature was measured using the four point probe method. The 100 °C annealing did not modify either the film structure or the film morphology. On the other hand, Ag₂Cu₂O₃ films were partially decomposed into Ag and CuO after a 200 °C annealing. The decomposition was complete for a 300 °C annealing. The evolution of the film surface morphology as a function of the annealing temperature was discussed in connection to the evolution of the molar volume of the phases constituting the films.     

Synthesis and characterization of Co3O4 nanorods by thermal decomposition of cobalt oxalate

Cobalt oxalate was used as a precursor to prepare Co₃O₄ nanorods by thermal decomposition. The combinations of triphenylphosphine and oleylamine were added as surfactants to control the morphology of the particles. The products were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), Fourier transform infrared (FT-IR) spectroscopy and X-ray photoelectron spectroscopy (XPS). The diameters of Co₃O₄ nanorods are 20 nm and the average lengths are around 500 nm. The hysteresis loops of the obtained samples reveal the ferromagnetic behaviors, the enhanced coercivity (H_c) and decreased saturation magnetization (M_s) in contrast to their respective bulk materials. The study provides a simple and efficient route to synthesize Co₃O₄ nanorods at low temperature.     

Microwave assisted combustion synthesis of CdFe2O4: Magnetic and electrical properties

CdFe₂O₄ particles were synthesized by the microwave assisted combustion method using two different fuels—glycine and urea. Microwave heating provides higher chemical yield within a minute. The synthesized particles were characterized by X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), scanning electron microscope (SEM), ac impedance spectroscopy, vibrating sample magnetometry (VSM) and electron spin resonance (ESR) methods. XRD analysis shows the cubic structure of CdFe₂O₄. The high and low frequency absorption bands of CdFe₂O₄ were found using FTIR analysis. Spherical morphology was revealed from the SEM images. ESR and VSM measurements reveal the antiferromagnetic behavior of CdFe₂O₄. The electrical conductivities of CdFe₂O₄ synthesized using glycine and urea are 6.5×10⁻⁷ S cm⁻¹ and 4.7×10⁻⁸ S cm⁻¹ respectively at 240 ^oC. At elevated temperatures an occurrence of increase in conductivity was observed, which indicates the semiconducting behavior of CdFe₂O₄. The dielectric spectral analysis reveals that dielectric constant of CdFe₂O₄ decreases with frequency and increases with temperature.     

Chemical synthesis of spinel nickel ferrite (NiFe2O4) nano-sheets

The present investigation is related to the deposition of single-phase nano-sheets spinel nickel ferrite (NiFe₂O₄) thin films onto glass substrates using a chemical method. Nano-sheets nickel ferrite films were deposited from an alkaline bath containing Ni²⁺ and Fe²⁺ ions. The films were characterized for their structural, surface morphological and electrical properties by means of X-ray diffraction (XRD), transmission electron microscope (TEM), Fourier transform infrared spectroscopy (FT-IR), scanning electron microscopy (SEM), and two-point probe electrical resistivity techniques. The X-ray diffraction pattern showed that NiFe₂O₄ nano-sheets are oriented along (3 1 1) plane. The FT-IR spectra of NiFe₂O₄ films showed strong absorption peaks around 600 and 400 cm⁻¹ which are typical for cubic spinel crystal structure. Microstructural study of NiFe₂O₄ film revealed nano-sheet like morphology with average sheet thickness of 30 nm. The room temperature electrical resistivity of the NiFe₂O₄ nano-sheets was 10⁷ Ω cm.     

Concerning the cation distribution in MnFe2O4 synthesized through the thermal decomposition of oxalates

A single phase manganese ferrite powder have been synthesized through the thermal decomposition reaction of MnC₂O₄·2H₂O-FeC₂O₄·2H₂O (1:2 mole ratio) mixture in air. DTA-TG, XRD, Mössbauer spectroscopy, FT-IR and SEM techniques were used to investigate the effect of calcination temperature on the mixture. Firing of the mixture in the range 300-500 °C produce ultra-fine particles of α-Fe₂O₃ having paramagnetic properties. XRD, Mössbauer spectroscopy as well as SEM experiments showed the progressive increase in the particle size of α-Fe₂O₃ up to 500 °C. DTA study reveals an exothermic phase transition at 550 °C attributed to the formation of a Fe₂O₃-Mn₂O₃ solid solution which persists to appear up to 1000 °C. At 1100 °C, the single phase MnFe₂O₄ with a cubic structure predominated. The Mössbauer effect spectrum of the produced ferrite exhibits normal Zeeman split sextets due to Fe³⁺ions at tetrahedral (A) and octahedral (B) sites. The obtained cation distribution from Mössbauer spectroscopy is (Fe_0.92Mn_0.08)[Fe_1.08Mn_0.92]O₄.     

Influence of Lu2O3 on electrical and microstructural properties of CaCu3Ti4O12 ceramics

In this work, the influence of Lu₂O₃ doped on the dielectric and electrical properties of CaCu₃Ti₄O₁₂ was reported. Lu₂O₃-doped CCTO was prepared by a conventional solid state technique using CuO, TiO₂, and CaCO₃ as starting materials. The samples were studied by X-ray diffraction (XRD) and scanning electron microscopy (SEM); dielectric measurements were measured in the 10² Hz–10⁷ Hz frequency range at room temperature; and the nonlinear behavior of all samples was measured. The doping of Lu₂O₃ resulted in an increase in the dielectric constant of CCTO, but decreased the stability of the frequency dependence. Increasing concentrations of Lu₂O₃ resulted in decreasing nonlinear coefficients.     

Microstructure and interfacial properties of HfO2-Al2O3 nanolaminate films

High-k HfO₂-Al₂O₃ composite gate dielectric thin films on Si(1 0 0) have been deposited by means of magnetron sputtering. The microstructure and interfacial characteristics of the HfO₂-Al₂O₃ films have been investigated by using X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR) and spectroscopic ellipsometry (SE). Analysis by XRD has confirmed that an amorphous structure of the HfO₂-Al₂O₃ composite films is maintained up to an annealing temperature of 800 °C, which is much higher than that of pure HfO₂ thin films. FTIR characterization indicates that the growth of the interfacial SiO₂ layer is effectively suppressed when the annealing temperature is as low as 800 °C, which is also confirmed by spectroscopy ellipsometry measurement. These results clearly show that the crystallization temperature of the nanolaminate HfO₂-Al₂O₃ composite films has been increased compared to pure HfO₂ films. Al₂O₃ as a passivation barrier for HfO₂ high-k dielectrics prevents oxygen diffusion and the interfacial layer growth effectively.     

Growth and characterization of Y2O3 thin films

Y₂O₃ thin films were grown on silicon (1 0 0) substrates by pulsed-laser deposition at different substrate temperatures and O₂ pressures. The structure and composition of films are studied by using X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS). The Y₂O₃ thin films deposited in vacuum strongly oriented their [1 1 1] axis of the cubic structure and the film quality depended on the substrate temperature. The magnitude of O₂ pressure obviously influences the film structure and quality. Due to the silicon diffusion and interface reaction during the deposition, yttrium silicate and SiO₂ were formed. The strong relationship between composition and growth condition was discussed.     

Green synthesis of soya bean sprouts-mediated superparamagnetic Fe3O4 nanoparticles

Superparamagnetic Fe₃O₄ nanoparticles were first synthesized via soya bean sprouts (SBS) templates under ambient temperature and normal atmosphere. The reaction process was simple, eco-friendly, and convenient to handle. The morphology and crystalline phase of the nanoparticles were determined from scanning electron microscopy (SEM), transmission electron microscopy (TEM), selected area electron diffraction (SAED), and X-ray diffraction (XRD) spectra. The effect of SBS template on the formation of Fe₃O₄ nanoparticles was investigated using X-ray photoemission spectroscopy (XPS) and Fourier-transform infrared spectroscopy (FT-IR). The results indicate that spherical Fe₃O₄ nanoparticles with an average diameter of 8 nm simultaneously formed on the epidermal surface and the interior stem wall of SBS. The SBS are responsible for size and morphology control during the whole formation of Fe₃O₄ nanoparticles. In addition, the superconducting quantum interference device (SQUID) results indicate the products are superparamagnetic at room temperature, with blocking temperature (T_B) of 150 K and saturation magnetization of 37.1 emu/g.     

Low-temperature sintering and microwave dielectric properties of Ca2Zn4Ti15O36 ceramics

The sintering behavior, microstructures, and microwave dielectric properties of Ca₂Zn₄Ti₁₅O₃₆ ceramics with B₂O₃ addition were investigated. The crystalline phases and microstructures of Ca₂Zn₄Ti₁₅O₃₆ ceramics with 0-10 wt% B₂O₃ addition were studied by X-ray diffraction (XRD), scanning electron microscopy (SEM), and energy-dispersive X-ray spectroscopy (EDS). The sintering temperature of Ca₂Zn₄Ti₁₅O₃₆ ceramic was lowered from 1170 to 930 °C by 10 wt% B₂O₃ addition. Ca₂Zn₄Ti₁₅O₃₆ ceramics with 8 wt% B₂O₃ addition sintered at 990 °C for 2 h exhibited good microwave dielectric properties, i.e., a quality factor (Qf) 11,400 GHz, a relative dielectric constant (ε_r) 41.5, and a temperature coefficient of resonant frequency (τ_f) 94.4 ppm/°C.     

Synthesis of In-doped Ga2O3 zigzag-shaped nanowires and optical properties

In-doped Ga₂O₃ zigzag-shaped nanowires and undoped Ga₂O₃ nanowires have been synthesized on Si substrate by thermal evaporation of mixed powders of Ga, In₂O₃ and graphite at 1000 °C without using any catalyst via a vapor-solid growth mechanism. The morphologies and microstructures of the products were characterized by field-emission scanning electron microscopy (FE-SEM), X-ray diffraction (XRD), transmission electron microscopy (TEM), energy-dispersive X-ray spectroscopy (EDS) and photoluminescence spectroscopy (PL). The nanowires range from 100 nm to several hundreds of nanometers in diameter and several tens of micrometers in length. A broad emission band from 400 to 700 nm is obtained in the PL spectrum of these nanowires at room temperature. There are two blue-emission peaks centering at 450 and 500 nm, which originate from the oxygen vacancies, gallium vacancies and gallium-oxygen vacancy pairs.     

Columnar-grown porous films of lithium manganese oxide spinel (LiMn2O4) prepared by ultrasonic spray deposition

Using LiNO₃ and Mn(Ac)₂ as raw materials, ultrasonic spray deposition (USD) technique was used to fabricate LiMn₂O₄ films on platinum substrate at different substrate temperatures from 310 to 390 °C. The prepared thick films were characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM). Electrochemical performance of the USD-derived films was also evaluated with LiMn₂O₄/Li cells. It is found that all of the LiMn₂O₄ films are porous and composed of orderly oriented columnar particles. The substrate temperature affects the fine microstructure of the columnar particles. The film prepared at 360 °C substrate temperature give rise to best electrochemical behavior.     

Fabrication of chain-like Mn2O3 nanostructures via thermal decomposition of manganese phthalate coordination polymers

A novel manganese coordination polymer [Mn(Pht)(H₂O)]_n as a precursor was obtained by chemical precipitation involving an aqueous solution of anhydrous manganese acetate and phthalate anion as a potential O-banded ligand. Fourier transform infrared (FT-IR) results proved that phthalate anions coordinate to metal cations as a chelating bidentate ligand, making polymeric structure. The Mn₂O₃ nanostructures have been prepared via thermal decomposition of as-prepared manganese phthalate polymers as precursor in the presence of oleic acid (OA) and triphenylphosphine (TPP) as a stabilizer and capping. Different approaches such as FT-IR, X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM) and transmission electron microscopy (TEM) were applied to characterize the products. TEM images and XRD analysis indicated that the as-synthesized chain-like Mn₂O₃ has a crystal phase of cubic syngony with a mean size of ∼40 nm.     

Mechanical stress in ALD-Al2O3 films

Mechanical stress in atomic-layer deposition (ALD)-Al₂O₃ films was investigated at room temperature and during thermal cycling up to 870 °C. The films were generally under tensile stress. Thicker films (25-60 nm) showed a sharp stress increase at about 780-790 °C. X-ray diffraction (XRD)-, X-ray reflectance (XRR)- and X-ray photoelectron spectroscopy (XPS)-measurements indicate an irreversible phase transition from amorphous AlO(OH) to a mixture of different crystalline Al₂O₃-phases. Annealing at higher temperatures leads to a stress reduction as a result of diffusion and recovery processes. The stress behaviour of thinner films (<20 nm) during thermal cycling is quite different. Tensile stress increases with increasing temperature and decreases to nearly the same value during cooling down. The process is continuous and reversible.     

Low-temperature synthesis and growth of superparamagnetic Zn0.5Ni0.5Fe2O4 nanosized particles

Mono-disperse spinel Ni_0.5Zn_0.5Fe₂O₄ nanosized particles have been synthesized via a hydrothermal method at low temperature. X-ray diffraction (XRD), transmission electron microscope (TEM) and high-resolution transmission electron microscope (HRTEM) analysis indicated that the synthesized nanocrystals were of pure cubic spinel structure with the size about 6-20 nm. The activation energy of grain growth is 35.06 kJ/mol experimented by the Arrhenius equation. A primary experimental model was put forward to shed light on the growth mechanism of crystallined spinel Ni-Zn ferrite nanosized particles under hydrothermal conditions. The magnetic measurements shows that the prepared Ni_0.5Zn_0.5Fe₂O₄ nanoparticle possess good superparamagnetic behavior.     

Facile synthesis and electrochemical properties of hierarchical MnO2 submicrospheres and LiMn2O4 microspheres

Hierarchical MnO₂ submicrospheres have been successfully synthesized by a wet chemical method. The as-prepared products were characterized by means of XRD, SEM, FTIR, TG, and TEM. With the as-prepared MnO₂ submicrospheres as precursors, LiMn₂O₄ microspheres were conveniently prepared by a simple solid-state reaction between MnO₂ and LiOH at a temperature as low as 600 °C. Electrochemical properties of the as-prepared MnO₂ submicrospheres and LiMn₂O₄ microspheres as cathode materials in lithium ion cells were investigated by galvanostatic charge/discharge tests.     

MAO-synthesized Al2O3-supported V2O5 nano-porous catalysts: Growth, characterization, and photoactivity

V₂O₅-loaded Al₂O₃ layers were successfully grown via micro-arc oxidation (MAO) process for the first time. Surface morphology and topography of the layers were investigated by scanning electron microscope (SEM) and atomic force microscope (AFM). It was found that the composite layers had a porous structure with a rough surface which is suitable for catalytic applications. X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and energy dispersive X-ray spectroscopy (EDS) techniques were also employed to study phase structure and chemical composition of the composite layers. The layers consisted of γ-alumina, α-alumina, and vanadium pentoxide phases in which their relative contents varied with the applied voltage. Meanwhile, optical properties of the composite layers were investigated using UV-vis spectrophotometry technique, and the band gap energy was calculated as 3.15 eV. Furthermore, photocatalytic performance of the synthesized composite layers was determined by measuring the decomposition rate of methylene blue solution, as a model compound, on the surface of the layers under ultra violet photo-irradiation. It was found that more than 91% of the methylene blue was degraded after 120 min with a rate constant of k = 0.0192 min⁻¹.