Direct formation of thermally stabilized amorphous mesoporous Fe2O3/SiO2 nanocomposites by hydrolysis of aqueous iron III nitrate in sols of spherical silica particles

Nanocomposite materials containing 10% and 20% iron oxide/silica, Fe2O3/SiO2 (w/w), were prepared by direct hydrolysis of aqueous iron III nitrate solution in sols of freshly prepared spherical silica particles (St?ber particles) present in their mother liquors. This was followed by aging, drying, calcination up to 600 degrees C through two different ramp rates, and then isothermal calcinations at 600 degrees C for 3 h. The calcined and the uncalcined (dried at 120 degrees C) composites were characterized by thermogravimetric analysis, differential scanning calorimetry, Fourier transform infrared spectroscopy, X-ray diffraction (XRD), N2 adsorption/desorption techniques, and scanning electron microscopy as required. XRD patterns of the calcined composites showed no line broadening at any d-spacing positions of iron oxide phases, thereby reflecting the amorphous nature of Fe2O3 in the composite. The calcined composites showed nitrogen adsorption isotherms characterizing type IV isotherms with high surface area. Moreover, surface area increased with the increasing of the iron oxide ratio and lowering of the calcination ramp rate. Results indicated that iron oxide particles were dispersed on the exterior of silica particles as isolated and/or aggregated nanoparticles. The formation of the title composite was discussed in terms of the hydrolysis and condensation mechanisms of the inorganic FeIII precursor in the silica sols. Thereby, fast nucleation and limited growth of hydrous iron oxide led to the formation of nanoparticles that spread interactively on the hydroxylated surface of spherical silica particles. Therefore, a nanostructured composite of amorphous nanoparticles of iron oxide (as a shell) spreading on the surface of silica particles (as a core) was formed. This morphology limited the aggregation of Fe2O3 nanoparticles, prevented silica particle coalescence at high temperatures, and enhanced thermal stability.     

Surfactant templating effects on the encapsulation of iron oxide nanoparticles within silica microspheres

Hollow silica microspheres encapsulating ferromagnetic iron oxide nanoparticles were synthesized by a surfactant-aided aerosol process and subsequent treatment. The cationic surfactant cetyltrimethyl ammonium bromide (CTAB) played an essential role in directing the structure of the composite. Translation from mesoporous silica particles to hollow particles was a consequence of increased loading of ferric species in the precursor solution and the competitive partitioning of CTAB between silicate and ferric colloids. The hypothesis was that CTAB preferentially adsorbed onto more positively charged ferric colloids under acidic conditions. At a critical Fe/Si ratio, most of the CTAB was adsorbed onto ferric colloids and coagulated the colloids to form larger clusters. During the aerosol process, a silica shell was first formed due to the preferred silicate condensation on the gas-liquid interface of the aerosol droplet. Subsequent drying concentrated the ferric clusters inside the silica shell and resulted in a silica shell/ferric core particle. Thermal treatment of the core shell particle led to encapsulation of a single iron oxide nanoparticle inside each silica hollow microsphere.     

Modified reverse microemulsion synthesis for iron oxide/silica core–shell colloidal particles

Iron oxide/silica core–shell colloidal particles were prepared by basic reverse microemulsion (RM) method and two modified RM methods. By basic RM method, maximum particle size obtained was mere 40 nm. For building photonic crystals working in the visible range, the colloidal particles must be larger than 100 nm. Thus two modified RM methods were used. By alcohol modified RM method, short chain alcohols were used as co-surfactant. The particle size rose to near 100 nm, but the core–shell structure was comparatively poor. By emulsifier pair modified RM method, the particle size leapt to over 200 nm and a narrow growth window was found favorable to enhance the stability and rigidity of the surfactants layers. The core–shell mechanism was also discussed and a new four-step mechanism was proposed.     

Polystyrene‐Core–Silica‐Shell Hybrid Particles Containing Gold and Magnetic Nanoparticles

Polystyrene‐core–silica‐shell hybrid particles were synthesized by combining the self‐assembly of nanoparticles and the polymer with a silica coating strategy. The core–shell hybrid particles are composed of gold‐nanoparticle‐decorated polystyrene (PS‐AuNP) colloids as the core and silica particles as the shell. PS‐AuNP colloids were generated by the self‐assembly of the PS‐grafted AuNPs. The silica coating improved the thermal stability and dispersibility of the AuNPs. By removing the “free” PS of the core, hollow particles with a hydrophobic cage having a AuNP corona and an inert silica shell were obtained. Also, Fe₃O₄ nanoparticles were encapsulated in the core, which resulted in magnetic core–shell hybrid particles by the same strategy. These particles have potential applications in biomolecular separation and high‐temperature catalysis and as nanoreactors.     

Combined muta- and semisynthesis: a powerful synthetic hybrid approach to access target specific antitumor agents based on ansamitocin P3

Access of four new tumor specific folic acid/ansamitocin conjugates is reported that relies on a synthetic strategy based on the combination of mutasynthesis and semisynthesis. Two bromo‐ansamitocin derivatives were prepared by mutasynthesis or by a modified fermentation protocol, respectively, that served as starting point for the semisynthetic introduction of an allyl amine linker under Stille conditions. A sequence of standard coupling steps introduced the pteroic acid/glutamic acid/cysteine unit to the modified ansamitocins. All new derivatives, including those that are expected to be generated after internalization of the folic acid/ansamitocin conjugates into the cancer cell and reductive cleavage of the disulfide linkage showed good to strong antiproliferative activity (IC₅₀ <10 nM ) for different cancer cell lines. Finally, the four conjugates were exposed to two cancer cell lines [cervix carcinoma, KB‐3‐1 (FR+) and lung carcinoma, A‐459 (FR?)], the latter devoid of the membrane‐bound folic acid receptor (FR?). All four conjugates showed strong antiproliferative activity for the FR+ cancer cell line but were inactive against the FR? cell line. The synthetic strategy pursued is based on the combination of mutasynthesis and semisynthesis and proved to be powerful for accessing new ansamitocin derivatives that are difficult to prepare by total synthesis.     

Core–Shell Hollow Microspheres of Magnetic Iron Oxide@Amorphous Calcium Phosphate: Synthesis Using Adenosine 5′‐Triphosphate and Application in pH‐Responsive Drug Delivery

Drug nanocarriers with magnetic targeting and pH‐responsive drug‐release behavior are promising for applications in controlled drug delivery. Magnetic iron oxides show excellent magnetism, but their application in drug delivery is limited by low drug‐loading capacity and poor control over drug release. Herein, core–shell hollow microspheres of magnetic iron oxide@amorphous calcium phosphate (MIO@ACP) were prepared and investigated as magnetic, pH‐responsive drug nanocarriers. Hollow microspheres of magnetic iron oxide (HMIOs) were prepared by etching solid MIO microspheres in hydrochloric acid/ethanol solution. After loading a drug into the HMIOs, the drug‐loaded HMIOs were coated with a protective layer of ACP by using adenosine 5′‐triphosphate (ATP) disodium salt (Na₂ATP) as stabilizer, and drug‐loaded core–shell hollow microspheres of MIO@ACP (HMIOs/drug/ACP) were obtained. The as‐prepared HMIOs/drug/ACP drug‐delivery system exhibits superparamagnetism and pH‐responsive drug‐release behavior. In a medium with pH 7.4, drug release was slow, but it was significantly accelerated at pH 4.5 due to dissolution of the ACP shell. Docetaxel‐loaded core–shell hollow microspheres of MIO@ACP exhibited high anticancer activity.     

Inductive heating with magnetic materials inside flow reactors

Superparamagnetic nanoparticles coated with silica gel or alternatively steel beads are new fixed-bed materials for flow reactors that efficiently heat reaction mixtures in an inductive field under flow conditions. The scope and limitations of these novel heating materials are investigated in comparison with conventional and microwave heating. The results suggest that inductive heating can be compared to microwave heating with respect to rate acceleration. It is also demonstrated that a very large diversity of different reactions can be performed under flow conditions by using inductively heated flow reactors. These include transfer hydrogenations, heterocyclic condensations, pericyclic reactions, organometallic reactions, multicomponent reactions, reductive cyclizations, homogeneous and heterogeneous transition-metal catalysis. Silica-coated iron oxide nanoparticles are stable under many chemical conditions and the silica shell could be utilized for further functionalization with Pd nanoparticles, rendering catalytically active heatable iron oxide particles.     

Preparation of SiO2/PMMA composite particles via conventional emulsion polymerization

A series of SiO₂/PMMA composite particles with different morphologies were prepared by conventional emulsion polymerization by the aid of acid–base interaction between the silanol groups of unmodified silica particles and the amino groups of 4‐vinylpyridine. In this approach, no surface treatment for nanosilica particles was required. The morphologies of composite particles, for example, multicore–shell, raspberry‐like, and conventional core–shell, could be controlled by modulating emulsifier content, monomer/silica ratio, silica size, and monomer feed method. The possible particle formation mechanisms were discussed. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 3807–3816, 2006     

A Sub‐50‐nm Monosized Superparamagnetic Fe3O4@SiO2 T2‐Weighted MRI Contrast Agent: Highly Reproducible Synthesis of Uniform Single‐Loaded Core–Shell Nanostructures

Oleic acid stabilized superparamagnetic iron oxide nanoparticles (SPION) were selected as the cores for fabrication of sub‐50‐nm monodisperse single‐loaded SPION@SiO₂ core–shell nanostructures. Parameters that influence the formation of SPION@SiO₂ in the water‐in‐oil reverse microemulsion system have been systematically investigated. The sufficiently high concentration of well‐dispersed SPION, together with an appropriately low injection rate of tetraethoxysilane, were found to be the keys to efficiently prevent the homogeneous nucleation of silica and obtain a high‐quality single‐loaded core–shell nanocomposite. A more detailed mechanism for incorporating oleic acid capped inorganic functional nanoparticles into silica is proposed on the basis of previous reports and our new experimental results. Finally, the as‐synthesized SPION@SiO₂ nanospheres are exploited as an MRI‐enhanced contrast agent, and their contrast effect in solution is tested by using a clinical MRI instrument.     

Magnetic poly(glycidyl methacrylate) microspheres prepared by dispersion polymerization in the presence of electrostatically stabilized ferrofluids

Fine magnetite nanoparticles, both electrostatically stabilized and nonstabilized, were synthesized in situ by precipitation of Fe(II) and Fe(III) salts in alkaline medium. Magnetic poly(glycidyl methacrylate) (PGMA) microspheres with core‐shell structure, where Fe₃O₄ is the magnetic core and PGMA is the shell, were obtained by dispersion polymerization initiated with 2,2′‐azobisisobutyronitrile (AIBN), 4,4′‐azobis(4‐cyanovaleric acid) (ACVA), or ammonium persulfate (APS) in ethanol containing poly(vinylpyrrolidone) or ethylcellulose stabilizer in the presence of iron oxide ferrofluid. The average microsphere size ranged from 100 nm to 2 μm. The effects of the nature of ferrofluid, polymerization temperature, monomer, initiator, and stabilizer concentration on the PGMA particle size and polydispersity were studied. The particles contained 2–24 wt % of iron. AIBN produced larger microspheres than APS or ACVA. Polymers encapsulating electrostatically stabilized iron oxide particles contained lower amounts of oxirane groups compared with those obtained with untreated ferrofluid. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 5827–5837, 2004     

Immobilization of RAFT agents on silica nanoparticles utilizing an alternative functional group and subsequent surface‐initiated RAFT polymerization

Silica–polystyrene core‐shell particles were successfully prepared by surface‐mediated reversible addition fragmentation chain transfer (RAFT) polymerization of styrene monomer from the surfaces of the silica‐supported RAFT agents. Initially, macro‐RAFT agents were synthesized by RAFT polymerization of γ‐methacryloxypropyltrimethoxysilane (MPS) in the presence of chain transfer agents (CTAs). Immobilization of CTAs onto the silica surfaces was then performed by reacting silica with macro‐RAFT agents via a silane coupling. Grafting of polymer onto silica forms core‐shell nanostructures and shows a sharp contrast between silica core and polymer shell in the phase composition. The thickness of grafted‐polymer shell and the diameter of core‐shell particles increase with the increasing ratio of monomer to silica. A control experiment was carried out by conventional free radical emulsion copolymerization of MPS‐grafted silica and styrene under comparable conditions. The resulting data provide further insight into the chemical composition of grafted‐polymers that are grown from the silica surface through RAFT process. © 2008 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 47: 467–484, 2009     

Multi-component hybrid inorganic–organic–inorganic particles with various metal oxide outer shells

Non-agglomerated hybrid particles of 200 nm diameter with an outer metal oxide shell were prepared by reacting the COOH groups of poly((S)-N-dicarbazolyl-lysine)-covered silica particles with metal alkoxides, such as titanium, zirconium and aluminum alkoxides, followed by sol–gel processing. With tetraethoxysilane (Si(OEt)₄), the silica particle core was growing rather than forming an external metal oxide shell, as observed for the other tested metal alkoxides.     

Preparation of hexagonal platy particles of nanoporous silica using hydrotalcite as morphology template

Hexagonal platy composite particles with a hydrotalcite core and a nanoporous silica shell with a thickness of ca. 100 nm were synthesized by the reaction of a Mg-Al hydrotalcite with a homogeneous aqueous solution containing tetraethoxysilane, hexadecyltrimethylammonium chloride, ammonia and methanol at 3 degrees C. The calcination of the products at 500 degrees C in air led to the composite particle with a Mg/Al mixed oxide core and a nanoporous silica shell. Hexagonal platy particles of nanoporous silica with a pore diameter of 2.3 nm and BET surface area of 700 m(2) (g of silica)(-1) were obtained by removing the Mg/Al mixed oxide core.     

Reversible Modulation of Surface Plasmons in Gold Nanoparticles Enabled by Surface Redox Chemistry

Switchable surface redox chemistry is demonstrated in gold@iron/iron oxide core–shell nanoparticles with ambient oxidation and plasmon‐mediated reduction to modulate the oxidation state of shell layers. The iron shell can be oxidized to iron oxide through ambient oxidation, leading to an enhancement and red‐shift of the gold surface plasmon resonance (SPR). This enhanced gold SPR can drive reduction of the iron oxide shell under broadband illumination to reversibly blue‐shift and significantly dampen gold SPR absorption. The observed phenomena provide a unique mechanism for controlling the plasmonic properties and surface chemistry of small metal nanoparticles.     

Selected‐Control Fabrication of Multifunctional Fluorescent–Magnetic Core–Shell and Yolk–Shell Hybrid Nanostructures

The selected‐control preparation of uniform core–shell and yolk–shell architectures, which combine the multiple functions of a superparamagnetic iron oxide (SPIO) core and europium‐doped yttrium oxide (Y₂O₃:Eu) shell in a single material with tunable fluorescence and magnetic properties, has been successfully achieved by controlling the heat‐treatment conditions. Furthermore, the shell thickness and interior cavity of SPIO@Y₂O₃:Eu core–shell and yolk–shell nanostructures can be precisely tuned. Importantly, as‐prepared SPIO@Y₂O₃:Eu yolk–shell nanocapsules (NCs) modified with amino groups as cancer‐cell fluorescence imaging agents are also demonstrated. To the best of our knowledge, this is the first report on the selected‐control fabrication of uniform SPIO@Y₂O₃:Eu core–shell nanoparticles and yolk–shell NCs. The combined magnetic manipulation and optical monitoring of magnetic–fluorescent SPIO@Y₂O₃:Eu yolk–shell NCs will open up many exciting opportunities in dual imaging for targeted delivery and thermal therapy.     

Core–shell column Tanaka characterization and additional tests using active pharmaceutical ingredients

In the last decade, core–shell particles have gained more and more attention in fast liquid chromatography separations due to their comparable performance with fully porous sub‐2 μm particles and their significantly lower back pressure. Core–shell particles are made of a solid core surrounded by a shell of classic fully porous material. To embrace the developed core–shell column market and use these columns in pharmaceutical analytical applications, 17 core–shell C₁₈ columns purchased from various vendors with various dimensions (50 mm × 2.1 mm to 100 mm × 3 mm) and particle sizes (1.6–2.7 μm) were characterized using Tanaka test protocols. Furthermore, four selected active pharmaceutical ingredients were chosen as test probes to investigate the batch to batch reproducibility for core–shell columns of particle size 2.6–2.7 μm, with dimension of 100 × 3 mm and columns of particle size 1.6 μm, with dimension 100 × 2.1 mm under isocratic elution. Columns of particle size 2.6–2.7 μm were also tested under gradient elution conditions. To confirm the claimed comparable efficiency of 2.6 μm core–shell particles as sub‐2 μm fully porous particles, column performances of the selected core–shell columns were compared with BEH C₁₈, 1.7 μm, a fully porous column material as well.     

Bioinspired Core–Shell Nanoparticles for Hydrophobic Drug Delivery

A large range of nanoparticles have been developed to encapsulate hydrophobic drugs. However, drug loading is usually less than 10 % or even 1 %. Now, core–shell nanoparticles are fabricated having exceptionally high drug loading up to 65 % (drug weight/the total weight of drug‐loaded nanoparticles) and high encapsulation efficiencies (>99 %) based on modular biomolecule templating. Bifunctional amphiphilic peptides are designed to not only stabilize hydrophobic drug nanoparticles but also induce biosilicification at the nanodrug particle surface thus forming drug‐core silica–shell nanocomposites. This platform technology is highly versatile for encapsulating various hydrophobic cargos. Furthermore, the high drug loading nanoparticles lead to better in vitro cytotoxic effects and in vivo suppression of tumor growth, highlighting the significance of using high drug‐loading nanoparticles.     

Superparamagnetic Fe3O4SiO2 nanocomposites: enabling the tuning of both the iron oxide load and the size of the nanoparticles

Using a water-in-oil microemulsion system, silica nanoparticles containing superparamagnetic iron oxide (SPIO) crystals have been prepared and characterized. With this method, the loading of iron oxide crystals, the thickness of the silica shells, and the overall particle sizes are tunable. Moving from low to high water concentration, within the microemulsion region, resulted in a gradual shift from larger particles, ca. 100 nm and fully loaded with SPIOs, to smaller particles, ca. 30 nm containing only one or a few SPIOs. By varying the amount of silica precursor, the thickness of the silica shell was altered. Field dependent magnetization measurements showed the magnetic properties of the SPIOs were preserved after the synthesis.     

Highly magnetic latexes from submicrometer oil in water ferrofluid emulsions

The synthesis of functionalized submicrometer magnetic latex particles is described as obtained from a preformed magnetic emulsion composed of organic ferrofluid droplets dispersed in water. Composite (polystyrene/γ‐Fe₂O₃) particles were prepared according to a two‐step procedure including the swelling of ferrofluid droplets with styrene and a crosslinking agent (divinyl benzene) followed by seeded emulsion polymerization with either an oil‐soluble [2,2′‐azobis(2‐isobutyronitrile)] or water‐soluble (potassium persulfate) initiator. Depending on the polymerization conditions, various particle morphologies were obtained, ranging from asymmetric structures, for which the polymer phase was separated from the inorganic magnetic phase, to regular core–shell morphologies showing a homogeneous encapsulation of the magnetic pigment by a crosslinked polymeric shell. The magnetic latexes were extensively characterized to determine their colloidal and magnetic properties. The desired core–shell structure was efficiently achieved with a given styrene/divinyl benzene ratio, potassium persulfate as the initiator, and an amphiphilic functional copolymer as the ferrofluid droplet stabilizer. Under these conditions, ferrofluid droplets were successfully turned into superparamagnetic polystyrene latex particles, about 200 nm in size, containing a large amount of iron oxide (60 wt %) and bearing carboxylic surface charges. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 2642–2656, 2006