Electrical and optical spectroscopy on ZnO:Co thin films

Magnetic oxide semiconductors, for example the highly transparent and intrinsically n-type conducting zinc oxide doped with the 3d transition metal Co (ZnO:Co), are promising for the emerging field of spintronics [1]. We investigated n-conducting ZnO:Co thin films with a Co content of nominal 0.02, 0.20, or 2.00 at. %. The substitution of Co cations in the tetrahedral sites of wurtzite ZnO with Zn was confirmed at low temperature by the 1.877 eV photoluminescence between crystal field split d-levels of Co²⁺ (d⁷) ions. Based on theoretical studies, it is predicted that the formation of electron levels with zinc interstitials (I_Zn) or hole levels with zinc vacancies (V_Zn) is necessary to induce ferromagnetism, whereas the formation of electron levels with oxygen vacancies (V_O) is detrimental for ferromagnetism in ZnO:Co [2]. Cobalt generates a hole level in ZnO [3]. We investigated the generation of electron levels in n-conducting ZnO:Co in dependence on the Co content by means of deep level transient spectroscopy (DLTS). However, because of the ambiguous categorization of deep defects in n-conducting ZnO (V_O, I_Zn), an optimization of defect-related ferromagnetism in ZnO:Co is not possible at the moment. PACS 78.30.Fs; 91.60.Ed; 91.60.Mk     

Mn和N共掺ZnO稀磁半导体薄膜的研究

使用对Zn₂N₃:Mn薄膜热氧化的方法成功制备了高含N量的Mn和N共掺ZnO的稀磁半导体薄膜.在没有N离子共掺的情况下,ZnO:Mn薄膜的铁磁性非常微弱;如果进行N离子的共掺杂,就会发现ZnO:Mn薄膜在室温下表现出非常明显的铁磁性,饱和离子磁矩为0.23 μ_B—0.61 μ_B.这说明N的共掺激发了ZnO:Mn薄膜中的室温铁磁性,也就是受主的共掺引起的空穴有利于ZnO中二价Mn离子的铁磁性耦合,这和最近的相关理论研究符合很好. 关键词： 磁性半导体 受主掺杂 空穴媒介的铁磁性     

Ferromagnetism of MnxLiyZn1−x−yO films

We had prepared Mn-doped ZnO and Li, Mn codoped-ZnO films with different concentrations using spin coating method. Crystal structure and magnetic measurements demonstrate that the impurity phases (ZnMnO₃) are not contributed to room temperature ferromagnetism and the ferromagnetism in Mn-doped ZnO film is intrinsic. Interesting, saturated magnetization decreases with Mn or Li concentration increase, showing that some antiferromagnetism exists in the samples with high Mn or Li concentration. In addition, Mn_0.05Zn_0.95O film annealed in vaccum shows larger ferromagnetism than the as-prepared sample and more oxygen vacancies induced by annealing in reducing atmosphere enhance ferromagnetism, which supports the bound magnetic polaron model on the origin of room temperature ferromagnetism.     

退火温度对N+注入ZnO:Mn薄膜结构及室温铁磁性的影响

采用射频磁控溅射法在石英玻璃衬底上制备了ZnO:Mn薄膜, 结合N⁺ 注入获得Mn-N共掺ZnO薄膜, 进而研究了退火温度对其结构及室温铁磁性的影响. 结果表明, 退火后ZnO:(Mn, N) 薄膜中Mn²⁺和N^3-均处于ZnO晶格位, 没有杂质相生成. 退火温度的升高 有助于修复N⁺注入引起的晶格损伤, 同时也会让N逸出薄膜, 导致受主(N_O)浓度降低. 室温铁磁性存在于ZnO:(Mn, N)薄膜中, 其强弱受N_O浓度的影响, 铁磁性起源可采用束缚磁极化子模型进行解释.     

Ferromagnetism induced by oxygen-vacancy complex in (Mn,in) codoped ZnO

Mn doped Zinc oxide (ZnO) thin films were prepared by metal organic chemical vapor deposition (MOCVD) technique. Structural characterizations by X-ray diffraction technique (XRD) and photoluminescence (PL) indicate the crystal quality of ZnO films. PL and Raman show a large fraction of oxygen vacancies (V_O²⁺) are generated by vacuum annealed the film. The enhancement of ferromagnetism in post-annealed (Mn, In) codoped ZnO could result from V_O²⁺ incorporation. The effect of V_O²⁺ on the magnetic properties of (Mn, In) codoped ZnO has been studied by first-principles calculations. It is found that only In donor cannot induce ferromagnetism (FM) in Mn-doped ZnO. Besides, the presence of V_O²⁺ makes the Mn empty 3d-t_2g minority state broadened, and a t_2g-V_O²⁺ hybrid level at the conduction band minimum forms. The presence of V_O²⁺ can lead to strong ferromagnetic coupling with the nearest neighboring Mn cation by BMP model based on defects reveal that the ferromagnetic exchange is mediated by the donor impurity state, which mainly consists of Mn 3d electrons trapped in oxygen vacancies.     

Direct kinetic correlation of carriers and ferromagnetism in Co2+: ZnO

The hypothesis that high-Curie-temperature ferromagnetism in cobalt-doped ZnO (Co2+: ZnO) is mediated by charge carriers was tested by controlled introduction and removal of the shallow donor interstitial zinc. Using oriented epitaxial Co2+: ZnO films grown by chemical vapor deposition, kinetics measurements demonstrate a direct correlation between the oxidative quenching of ferromagnetism and the diffusion and oxidation of interstitial zinc. These results demonstrate controlled systematic variation of a key parameter involved in the ferromagnetism of Co2+: ZnO and, in the process, unambiguously reveal this ferromagnetism to be dependent upon charge carriers. The distinction between defect-bound and free carriers in Co2+: ZnO is discussed.     

Ho3+掺杂对ZnO薄膜的微观结构和磁性的影响

研究Ho³⁺掺杂对氧化锌半导体材料的微结构和磁学性质影响. 利用热蒸发技术制备了一系列沉积在Si(100)衬底的Zn_1-xHo_xO(x=0.0、0.04、0.05）薄膜. X射线光谱、表面形貌以及磁性的实验结果表明,Ho³⁺掺杂对ZnO薄膜材料的性能影响很大. X射线衍射图显示峰位出现高角度转变并且趋向于(101)取向,在ZnO晶格显示Ho³⁺置换. 扫描电子显微镜和能谱仪对薄膜的表面形貌以及化学     

Co100-xMnx合金在GaAs(001)表面的生长结构和磁性的实验研究

对Co_100-xMn_x合金在GaAs(001)表面的分子束外延生长、晶体结构和磁学性质进行了研究.结果表明,当0100-xMn_x合金薄膜是体材料中不存在的体心立方(bcc)结构,并且具有较强的铁磁性,当44100-xMn_x合金薄膜最初为bcc结构,随着厚度的增加,逐渐从bcc向面心立方(fcc)结构转化,最后成为完全的fcc结构,薄膜具有较 关键词：     

Deep defects generated in n-conducting ZnO:TM thin films

The ferromagnetism in highly transparent and intrinsically n-type conducting zinc oxide doped with 3d transition metals (TM), is predicted to be defect mediated. We investigate the generation of deep defects in n-conducting 1 μm thick ZnO:TM films (TM=Co, Mn, Ti) with a nominal TM content of 0.02, 0.20 and 2.00 at.% grown by pulsed laser deposition on a-plane sapphire substrates using deep level transient spectroscopy. We find that a defect level is generated, independent of the TM content, located 0.31 and 0.27 eV below the conduction band minimum of ZnO:Mn and ZnO:Ti, respectively. Different defect levels are generated in dependence on the Co content in ZnO:Co. This work shows that an optimization of defect-related ferromagnetism in n-conducting ZnO:TM thin films will only be possible if the preparation sensitive formation of deep defects is controlled in the same time.     

Preparation, structure and ferromagnetic properties of the nanocrystalline Ti1-xMnxO2 thin films grown by radio frequency magnetron co-sputtering

This paper reported that the Mn-doped TiO2 films were prepared by radio frequency （RF） magnetron cosputtering. X-ray diffraction measurements indicate that the samples are easy to form the futile structure, and the sizes of the crystal grains grow big and big as the Mn concentration increases. X-ray photoemlssion spectroscopy measurements and high resolution transmission electron microscope photographs confirm that the manganese ions have been effectively doped into the TiO2 crystal when the Mn concentration is lower than 21%. The magnetic property measurements show that the Ti1-xMnxO2 （x = 0.21） films are ferromagnetic at room temperature, and the saturation magnetization, coercivity, and saturation field are 16.0 emu/cm^3, 167.5 × 80 A/m and 3740 × 80 A/m at room temperature, respectively. The room-temperature ferromagnetism of the films can be attributed to the new futile Ti1-xMnxO2 structure formed by the substitution of Mn^4＋ for Ti^4＋ into the TiO2 crystal .lattice, and could be explained by O vacancy （Vo）-enhanced ferromagnetism model.     

Chemical manipulation of high-T(C) ferromagnetism in ZnO diluted magnetic semiconductors

We report the use of targeted p- and n-type chemical perturbations to manipulate high-T(C) ferromagnetism in Mn(2+):ZnO and Co(2+):ZnO in predictable and reproducible ways. We demonstrate a clear correlation between nitrogen and high-T(C) ferromagnetism for Mn(2+):ZnO and an inverse correlation for Co(2+):ZnO, both as predicted by recent theoretical models. These chemical perturbations reveal rich possibilities for exerting external control over high-T(C) spin ordering in diluted magnetic semiconductors.     

Room-temperature anomalous Hall effect and magnetroresistance in (Ga, Co)-codoped ZnO diluted magnetic semiconductor films

This paper reports that the(Ga,Co)-codoped ZnO thin films have been grown by inductively coupled plasma enhanced physical vapour deposition.Room-temperature ferromagnetism is observed for the as-grown thin films.The x-ray absorption fine structure characterization reveals that Co 2+ and Ga 3+ ions substitute for Zn 2+ ions in the ZnO lattice and exclude the possibility of extrinsic ferromagnetism origin.The ferromagnetic(Ga,Co)-codoped ZnO thin films exhibit carrier concentration dependent anomalous Hall effect and positive magnetoresistance at room temperature.The mechanism of anomalous Hall effect and magneto-transport in ferromagnetic ZnO-based diluted magnetic semiconductors is discussed.     

Raman scattering investigations on Co-doped ZnO epitaxial films: Local vibration modes and defect associated ferromagnetism

Raman scattering spectroscopy has been performed on high quality Co-doped ZnO epitaxial films, which were grown on Al₂O₃ (0001) by oxygen-plasma assisted molecular beam epitaxy. Raman measurements revealed two local vibration modes (LVMs) at 723 and 699 cm⁻¹ due to the substitution of Co²⁺ in wurtzite ZnO lattice. The LVM at 723 cm⁻¹ is found to be an elemental sensitive vibration mode for Co substitution. The LVM at 699 cm⁻¹ can be attributed to enrichment of Co²⁺ bound with oxygen vacancy, the cobalt–oxygen vacancy–cobalt complexes, in Zn_1−xCo_xO films associated with ferromagnetism. The intensity of LVM at 699 cm⁻¹, as well as saturated magnetization, enhanced after the vacuum annealing and depressed after oxygen annealing.     

Room-Temperature Ferromagnetism in Zn1-xMnxO Thin Films Deposited by Pulsed Laser Deposition

Zn1-xMnxO （x = O.Olq3.1） thin films with a Curie temperature above 300K are deposited on Al2O3 （0001） substrates by pulsed laser deposition. X-ray diffraction （XRD）, ultraviolet （UV）-visible transmission and Raman spectroscopy are employed to characterize the microstructural properties of these films. Room temperature ferromagnetism is observed by superconducting quantum interference device （SQUID）. The results indicate that Mn doping introduces the incorporation of Mn^2＋ ions into the ZnO host matrix and the insertion of Mn^2＋ ions increases the lattice defects, which is correlated with the ferromagnetism of the obtained films. The doping concentration is also proven to be a crucial factor for obtaining highly ferromagnetic Zn1-xMnxO films.     

Magnetic and optical properties of epitaxial n-type Cu-doped ZnO thin films deposited on sapphire substrates

In this paper, we report on pulsed laser deposition of n-type Cu-doped ZnO thin films on c-plane sapphire substrates at 700°C. XRD and HRTEM were employed to study the epitaxial growth relationship between the Zn_1−x Cu _x O film and sapphire substrate. Absorption measurements showed excitonic nature of the thin films and a decrease in the bandgap energy with increased Cu concentration was observed. Such as-deposited films showed room temperature ferromagnetism with Curie temperature (T _c ) at around 320 K. The moment per Cu atom decreases as the Cu concentration increases. The largest magnetic moment about 0.81μ _B /Cu atom was observed for Zn_0.95Cu_0.05O thin films. The presence of any magnetic second phase was ruled out and the ferromagnetism was attributed to Cu ions substituted directly into the ZnO lattice.     

Room-temperature ferromagnetism in N+-implanted ZnO:Mn thin films

Mn–N co-doped ZnO films with wurtzite structure were fabricated by RF magnetron sputtering together with the ion-implantation technique. Then a post-annealing at 650 °C for 10 min in a N₂ atmosphere was performed to activate the implanted N⁺ ions and recover the crystal quality, and a p-type ZnO:Mn–N film with a hole concentration of about 2.1×10¹⁶ cm^?3 was obtained. It is found that the Mn mono-doped ZnO film only exhibits paramagnetic behavior, while after N⁺-implantation, it shows ferromagnetism at 300 K, and the magnetization of the ZnO:Mn–N films can be further enhanced by thermal annealing due to the activation of the N acceptors. Our experimental results confirm that the codoping N acceptors are favorable for ferromagnetic ordering of Mn²⁺ ions in ZnO, which is consistent with the recent theoretical calculations.     

氮掺杂(1120) ZnO 薄膜磁性质研究

采用基于密度泛函理论(DFT)和局域密度近似(LDA)的第一性原理分析了氮掺杂(1120) ZnO 薄膜的磁性质.首先,研究了一个N原子掺杂ZnO薄膜的磁性质,结果表明N 2p,O 2p和Zn 3d 发生自发自旋极化.其次,研究了二个N原子掺杂ZnO薄膜的磁性质,9个不同几何结构的计算结果表明N原子之间具有FM耦合稳定性,而且具体分析了N掺杂ZnO铁磁稳定性的产生原因.最后,讨论了氮 关键词： 第一性原理 半导体 铁磁性     

Preparation and characterization of the ZnO:Al/Fe65Co35/ZnO:Al multifunctional films

The ferromagnetic transparent conducting film is a multifunctional film which has high visible transmittance, low resistivity and room-temperature ferromagnetism, simultaneously. In this article, ferromagnetic transparent conducting ZnO:Al/Fe₆₅Co₃₅/ZnO:Al multilayer films were fabricated by inserting a middle magnetic Fe₆₅Co₃₅ layer into aluminum-doped zinc oxide (ZnO:Al) matrix using a magnetron sputtering apparatus at substrate temperature ranging from room temperature (RT) to 400^∘C. The total film thickness was about 400 nm and the middle Fe₆₅Co₃₅ alloy layer was 4 nm. The influences of substrate temperature (T _s ) on the structural, electrical, optical and magnetic properties of the multilayer films were systemically investigated. The results showed that the microstructure and performance of the composite multilayer films strongly depended on the substrate temperature. The present results also showed that the inserted middle Fe₆₅Co₃₅ alloy thin layer played an important role in providing the RT ferromagnetism and decreasing the resistivity of the multilayer films. Therefore, it is possible to obtain a multifunctional film material with the combination of good optical transparency, high electrical conductivity and RT ferromagnetism.     

Structure and room-temperature ferromagnetism of Co-doped ZnO DMS films

Co-doped ZnO diluted magnetic semiconductor films were prepared on Si(100) substrates by magnetron sputtering system and the Co content varies from 0.01 to 0.15. The X-ray diffraction results showed ZnO of the wurtzite structure. The ferromagnetism was observed at room temperature. The X-ray near-edge absorption spectroscopy revealed that Co substitutes for Zn²⁺ ions in the valence of +2 state in the Co-doped ZnO films.     

Fe,Co共掺杂ZnO薄膜结构及发光特性研究

采用溶胶凝胶法在玻璃衬底上制备了Fe,Co共掺Zn0.9FexCo0.1-xO(x=0,0.03,0.05,0.07)系列薄膜.通过扫描电镜(SEM)、X射线衍射(XRD)、X射线光电子谱(XPS)和光致发光(PL)谱对薄膜样品的表面形貌、晶体结构、成分和光学性能进行了研究.XRD结果表明所有ZnO薄膜样品都呈六方纤锌矿结构,在样品中没有观察到与Fe和Co相关的团簇,氧化物及其他杂相的衍射峰,表明共掺杂改善了Fe或Co在ZnO的分散性.XPS测试结果揭示样品中Co离子的价态为+2价;Fe离子的价态为+2价和+3价共存,但Fe相对浓度的增大导致Fe3+含量增加.所有样品的室温光致发光谱(PL)均观察到紫外发光峰和蓝光双峰,其中Fe,Co共掺ZnO薄膜的紫外发光峰较本征ZnO出现蓝移,蓝光双峰峰位没有变化,但发光强度有所减弱;而掺杂ZnO薄膜的绿光发光峰几乎消失.最后,结合微结构和成分分析对薄膜样品的发光机理进行了讨论.