High performance of interpenetrating polymer network hydrogels induced by frontal polymerization

We report the rapid synthesis of hydrogels with interpenetrating polymer networks (IPNs) by frontal polymerization (FP). Appropriate amounts of diacetone acrylamide (DAAM), N-methylolacrylamide (NMA), thermoplastic polyurethane (TPU), N,N′-methylenebisacrylamide (MBAA), and ammonium persulfate (APS)/N,N,N′,N′-tetramethylethylenediamine (TMEDA) were mixed together at ambient temperature. FP was initiated by transitorily heating the upper side of the reactants, and poly(DAAM-co-NMA)/TPU IPN hydrogels were obtained within minutes. The preparation parameters were thoroughly investigated. Moreover, we investigated the morphology, swelling capacity, chemical structure and the mechanical properties of poly(DAAM-co-NMA)/TPU IPN hydrogels, along with those of poly(DAAM-co-NMA) hydrogels without IPN structure for comparison. Interestingly, the mechanical strength of poly(DAAM-co-NMA)/TPU IPN hydrogels is notably improved in comparison with that of poly(DAAM-co-NMA) hydrogels. The results indicate that the IPN structure endows hydrogels with high mechanical strength, and FP can be applied as an alternative means for synthesis of IPN hydrogels with additional advantages of speed and efficiency.     

Thermo- and pH-sensitive comb-type grafted poly(N,N-diethylacrylamide-co-acrylic acid) hydrogels with rapid response behaviors

Poly(N,N-diethylacrylamide) with a terminal hydroxyl end group (PDEA-OH) was synthesized by radical telomerization of N,N-diethylacrylamide (DEA) monomer using 2-hydroxyethanethiol as a chain transfer agent. Macromonomer of thermo-sensitive PDEA was synthesized by condensation reaction of PDEA-OH with acryloyl chloride. The macromonomer was characterized by FTIR and ¹H NMR, and the molecular weight was determined by GPC. Thermo- and pH-sensitive comb-type grafted poly(N,N-diethylacrylamide-co-acrylic acid) (PDEA-co-AA) hydrogels (GHs) were successfully prepared by grafting PDEA chains with freely mobile ends onto the backbone of a cross-linked (PDEA-co-AA) network. The results showed that the deswelling behavior of the hydrogels was dependent on the test temperature. At 45 °C (beneath the VPTT of the hydrogels), both the normal-type hydrogels (NHs) and comb-type grafted P(DEA-co-AA) hydrogels had lower deswelling rates. While at 60 °C (far beyond the VPTT of the hydrogels), the deswelling rates of the GHs were faster than that of the NHs. Furthermore, pulsatile stimuli-responsive studies indicated that the GHs had excellent thermo-reversibility and were superior to the NHs in the magnitude of their swelling ratios to temperature changes. However, the reversibility to pH changes was poor for both the NHs and the GHs.     

Synthesis and network structure of ionic poly(N,N-dimethylacrylamide-co-acrylamide) hydrogels: Comparison of swelling degree with theory

At four different charge densities, ionic hydrogels based on N,N-dimethylacrylamide (DMAAm), acrylamide (AAm), and itaconic acid (IA) were synthesized by free-radical cross-linking copolymerization in water with N,N-methylenebis(acrylamide) (BAAm) as the cross-linker, ammonium persulfate (APS) as the initiator, and N,N,N′,N′-tetramethylenediamine (TEMED) as the activator. The swelling behaviors of these hydrogels were analyzed in buffer solutions at various pH. It was observed that the swelling behavior of cross-linked ionic poly(N,N-dimethylacrylamide-co-acrylamide) [P(DMAAm-co-AAm)] hydrogels at different pHs agreed with the modified Flory-Rehner equation based both on the phantom network and affine network models and the ideal Donnan theory. In addition, the kinetics of swelling of the hydrogels was studied in pH 2, 5 and 9 buffer solutions. The swelling curves exhibited the characteristic features of transport process, apparently the Fickian diffusion of fast rates.     

Thermosensitive poly(N-isopropylacrylamide-co-acrylamide) hydrogels: Synthesis, swelling and interaction with ionic surfactants

Thermosensitive hydrogels were prepared by free-radical polymerization in aqueous solution from N-isopropylacrylamide (NIPA) and acrylamide (AAm) monomers. N,N-Methylenebis(acrylamide) (MBAAm) was used as a crosslinker. A kinetic study of the absorption determined the transport mechanism. The diffusion coefficients of these hydrogels were calculated for the Fickian mechanism. It was shown that the swelling behavior of the P(NIPA-co-AAm) hydrogels can be controlled by changing the amount of MBAAm. The swelling equilibrium of the P(NIPA-co-AAm) hydrogels was also investigated as a function of temperature in aqueous solutions of the anionic surfactant sodium dodecyl sulfate (SDS) and the cationic surfactant dodecyltrimethylammonium bromide (DTAB). In SDS and DTAB solutions, the equilibrium swelling ratio of the hydrogels increased, this is ascribed to the conversion of non-ionic P(NIPA-co-AAm) hydrogel into polyelectrolyte hydrogels due to binding of surfactant molecules through the hydrophobic interaction. Additionally, the amount of free SDS and DTAB ions was measured at different temperatures by a conductometric method, it was found that the electric conductivity of the P(NIPA-co-AAm)—surfactant systems depended strongly on both the type and concentration of surfactant solutions.     

Preparation of homogeneous polyacrylamide hydrogels by free-radical crosslinking copolymerization

Network microstructures of acrylamide (AAm)-based hydrogels were investigated by static and dynamic light scattering techniques. The hydrogels were prepared by free-radical crosslinking copolymerization of the monomers acrylamide (AAm), N,N-dimethylacrylamide (DMA) and N-isopropylacrylamide (NIPA) with N,N′-methylenebis(acrylamide) as a crosslinker in aqueous solutions. It was observed that the addition of DMA or NIPA into the comonomer feed suppresses the extent of frozen concentration fluctuations in polyacrylamide (PAAm) hydrogels. The cooperative diffusion coefficient increases while both the static and dynamic correlation lengths decrease as the amount of DMA in the comonomer feed is increased. Formation of homogeneous PAAm hydrogels by introduction of hydrophobic moieties was explained as a result of the steric effect of the bulky side groups on DMA or NIPA segments.     

Effects of synthesis-solvent on swelling and elastic properties of poly(N-isopropylacrylamide) hydrogels

Thermosensitive N-isopropylacrylamide (NIPA) hydrogels were synthesized by a free radical copolymerization with N,N′-methylenebisacrylamide (MBAA) in four solvents: water, ethanol, acetone and N,N-dimethylformamide. The swelling and elastic properties of the hydrogels were affected by the synthesis-solvents; the hydrogels (e.g. NIPA/MBAA = 1000/50 mol/m³-pre-gel solution) synthesized in water have smaller swelling volume and larger shear modulus at 10 °C than those synthesized in amphiphilic solvents. The network structure of hydrogels was estimated in terms of the conversion and two sorts of effective crosslinking density based on the Flory theory and the concentration of crosslinker. The hydrogels synthesized in water can have the microscopic inhomogeneous network arising from the entanglement of polymer chains, while the hydrogels synthesized in amphiphilic solvents can have the homogeneous network arising from the polymer concentration lower than the pre-gel solution and can be similar in network structure to the lightly crosslinked hydrogel synthesized in water.     

Immobilization of insulin-like growth factor-1 onto thermosensitive hydrogels to enhance cardiac progenitor cell survival and differentiation under ischemic conditions

Stem cell therapy is a promising approach to treat myocardial infarction. However, direct delivery of stem cells into hearts experiences poor cell engraftment and differentiation, due to ischemic conditions (low nutrient and oxygen) in the infarct hearts. Development of suitable cell carriers capable of supporting cell survival and differentiation under these harsh conditions is critical for improving the efficacy of current stem cell therapy. In this work, we created a family of novel cell carriers based on thermosensitive hydrogels and insulin-like growth factor 1 (IGF-1), and investigated if these cell carriers can improve cell survival and differentiation under ischemic conditions. The thermosensitive hydrogels were synthesized from N-isopropylacrylamide, acrylic acid, acrylic acid N-hydroxysuccinicimide ester, and 2-hydroxyethyl methacrylate-oligo(hydroxybutyrate). The hydrogel solutions can be readily injected through 26G needles, and can quickly solidify at 37 °C to form highly flexible hydrogels. IGF-1 was immobilized into the hydrogels in order to support long-term cell survival and differentiation. Different amount of IGF-1 was immobilized by using hydrogels with different content of N-hydroxysuccinicimide ester groups. Cardiosphere derived cells were encapsulated in the hydrogels and cultured under ischemic conditions. The results demonstrated that a significant improvement of cell survival and differentiation was achieved after IGF-1 immobilization. These IGF-1 immobilized hydrogels have the potential to improve cell survival and differentiation in infarct hearts.     

Insulin release behavior of poly(N-isopropylacrylamide-co-N-vinyl-2-pyrrolidone) hydrogel based on modified melamine crosslinkers

Novel hydrogels based on poly(N-isopropylacrylamide-co-N-vinyl-2-pyrrolidone) (PNIPAAm/PNVP), were synthesized by solution radical polymerization using water as solvent and different weight percentage of crosslinkers ranging from 0.5 to 4%. The monomer mol ratios of NIPAAm/VP (0.9/0.1, 0.5/0.5, and 0.1/0.9) were used in all cases. N,N′-methylenebisacrylamide (MBA) and the new synthesized N,N,N-triacrylamido melamine (MAAm) were used as crosslinkers. The swelling parameters such as the swelling ratio Q, equilibrium water content (EWC), volume fraction of polymer φ_p and volume fraction at crosslinking φ_r were calculated from swelling measurements at different temperatures. The lower critical solution temperatures (LCST) of the prepared hydrogels were measured using DSC technique. The data of LCST indicated that the NIPAAm/VP crosslinked with MAAm or MBA showed reversible swelling and shrinking with temperature changes. The temperature dependence of swelling ratio and response kinetics upon heating or cooling was also investigated to understand the smart properties, i.e., temperature sensitive properties of these smart hydrogels. The in vitro release experiments were carried out at 22 and 37°C, respectively, to investigate the effect of temperature-sensitive property of these PNIPAAm/PNVP hydrogels crosslinked with MAAm and MBA crosslinkers on insulin release profiles.     

Swelling behavior of strong polyelectrolyte poly(N-t-butylacrylamide-co-acrylamide) hydrogels

Temperature-sensitive ionic hydrogels based on N-t-butylacrylamide (TBA), acrylamide (AAm), 2-acrylamido-2-methylpropane sulfonic acid sodium salt (AMPS) and N,N^′-methylenebis(acrylamide) (BAAm) monomers were prepared. The molar ratio of TBA to the monomers AAm and AMPS was fixed at 60/40, while the AMPS content of the hydrogels was varied. The elastic modulus of the hydrogels was in the range of 347-447 Pa, much lower than the modulus of PAAm or poly(N-isopropylacrylamide) hydrogels due to the reduced crosslinking efficiency of BAAm in TBA/AAm copolymerization. The hydrogels exhibited swelling-deswelling transition in water depending on the temperature. Increasing ionic group (AMPS) content resulted in shifting of the transition temperature interval in which the deswelling takes place. The higher the ionic group content, the broader the temperature interval at the phase transition. Ionic hydrogels exhibited first-order reentrant conformational transitions in ethanol-water and in dimethylsulfoxide (DMSO)-water mixtures. The higher the ionic group content of the hydrogels the narrower the ethanol (or DMSO) range in which the reentrant phenomena occur. By taking into account the difference of the solvent mixture composition inside and outside the gel, the equilibrium swelling theory provided a satisfactory agreement to the experimental swelling data of the hydrogels immersed in the solvent mixtures.     

Synthesis and characterization of poly(methacrylic acid) hydrogels for metoclopramide delivery

Polymeric hydrogels based on biocompatible materials, methacrylic acid (MAA), were designed and synthesized. Synthesis was carried out by free-radical copolymerization using potassium persulfate as initiator and N,N^′-methylenebisacrylamide as crosslinker. Hydrogels were also characterized by Fourier transform infrared spectroscopy (FTIR), proton nuclear magnetic resonance spectroscopy (¹H NMR) and differential scanning calorimetry (DSC). DSC was used for the quantitive determination of the amounts of freezing and non-freezing water of the hydrogels with 0.5% of N,N^′-methylenebisacrylamide. Equilibrium swelling of hydrogels was studied in phosphate buffer of physiological pH (1.0, 4.0, 7.4 and 8.5) at 37 °C. The swelling kinetic of the hydrogels were studied and the kinetic characteristic constant of copolymeric systems, k, and the exponent which characterizes the mechanism of water transport at short times, n, were obtained. Metoclopramide hydrochloride was entrapped into the hydrogels by sorption and the “in vitro” release profile of this drug was established in simulated gastric fluid (SGF) and simulated intestinal fluid (SIF). It was observed that the drug release mechanism was non-Fickian.     

Radiation synthesis and characterization of poly(N,N-dimethylaminoethyl methacrylate-co-N-vinyl 2-pyrrolidone) hydrogels

In this study, radiation synthesis and characterization of swelling behavior and network structure of poly(N,N-dimethylaminoethyl methacrylate) (PDMAEMA), and poly(N,N-dimethylaminoethyl methacrylate-co-N-vinyl 2-pyrrolidone) (P(DMAEMA-co-VP)), hydrogels were investigated. PDMAEMA and P(DMAEMA-co-VP) hydrogels in the rod forms were prepared by irradiating the ternary mixtures of DMAEMA/VP/cross-linking agent, ethyleneglycol dimethacrylate (EGDMA), by gamma rays at ambient temperature. In composition ranges where the three components were completely miscible, water was also added to the ternary mixture to provide the formation of homogeneous polymerization and gelation. The influence of irradiation dose, comonomer, VP, and cross-linking agent, EGDMA, content on the total percentage gelation and monomer conversion were investigated. The effect of pH and temperature on the swelling behavior of hydrogels have also been examined. Hydrogels showed typical pH response and temperature responses, such as low-pH and low temperature swelling and high-pH and high temperature deswelling. Polymer-solvent interaction parameter (χ) and enthalpy and entropy changes appearing in the χ parameter for the P(DMAEMA-co-VP)-water system were determined by using Flory-Rehner theory of swelling equilibrium. The negative values for ΔH and ΔS indicate that prepared pure PDMAEMA and P(DMAEMA-co-VP) hydrogels have lower critical solution temperature (LCST) and Flory-Rehner theory of swelling equilibrium provides a satisfactory agreement to the experimental swelling data of the hydrogels.     

Nucleophilic addition of regioselectively lithiated indoline with aldimines for the syntheses of 2- and 7-indolinyl methanamine derivatives

Indolines bearing different N-protecting groups (N-Tbf and N-Boc) were deprotonated regioselectively at C-2 (sp³ hybridized ortho-H) and C-7 (sp² hybridized para-H) of the indoline ring, respectively. The generated organolithium intermediates reacted with aldimines to give the desired products in good yields with excellent anti-diastereoselectivities (>99:1). The produced N-Ts-(1-Tbf-indolin-2-yl)methanamine was facilely transformed to a fused heterocyclic compound.     

Comparative rheological study of ionic semi-IPN composite hydrogels based on polyacrylamide and dextran sulphate and of polyacrylamide hydrogels

Ionic semi-interpenetrating polymer networks composite hydrogels were synthesized by free-radical polymerization using dextran sulphate (DxS), acrylamide as monomer and N,N′-methylene(bis)acrylamide as cross-linking agent. The viscoelastic properties of these composite hydrogels were investigated by oscillatory shear measurements under small deformation conditions comparative with those of polyacrylamide gels. Changes of the rheological properties of composite hydrogels have been studied in terms of polymerization temperature, cross-linker ratio, initial monomer concentration and molar mass of DxS. The results showed that the stability of the composite hydrogels obtained at room temperature (22?°C) was relatively low because the storage modulus (G′) was only eight times higher than the loss modulus (G″), while for those obtained by cryopolymerization (?18?°C), the stability was improved, the G′ values being about 30 times higher than those of G″. This behaviour indicated that, by conducting the synthesis of hydrogels below the freezing point of the reaction solutions, an enhancement of the hydrogels elasticity was achieved. The network parameters, i.e. the average molecular weight between two cross-links and the cross-link density of the composite hydrogels prepared at ?18?°C, were estimated from rheological data.     

Synthesis, characterisation and evaluation of poly[lactose acrylate-N-vinyl-2-pyrrolidinone] hydrogels for drug delivery

New biodegradable polymeric hydrogels based on biocompatible materials, lactose acrylate (LA) and N-vinyl-2-pyrrolidinone were designed and synthesized. LA was synthesized and characterized by Fourier transform infrared spectroscopy and proton nuclear magnetic resonance spectroscopy. Hydrogel synthesis was carried out by free-radical polymerization of the co-monomers using azobisisobutyronitrile as initiator and N,N^′-methylenebisacrylamide as crosslinker. These hydrogels were also characterized. Equilibrium swelling of the hydrogels was studied in phosphate buffer of physiological pH, 7.4 and at 37 °C. Propranolol hydrochloride was entrapped into these hydrogels and the in vitro release profile of this drug was established in phosphate buffer. The drug release followed a near zero-order fashion in the first 6 h and thereafter slowed down releasing more than 90% of the entrapped drug at the end of 48 h.     

Hydrogels synthesised through photoinitiator-free photopolymerisation technique for delivering drugs including a tumour-tracing porphyrin

Hydrogels were synthesised using the photoinitiator-free photopolymerisation technique involving interactions between donor/acceptor pairs for delivering drugs of different molecular weights including a porphyrin used as a tumour-tracing agent. N-(5-hydroxy) pentylmaleimide, an acceptor, formed hydrogels with N-vinyl-2-pyrrolidinone, 2-hydroxyethyl methacrylate and N-vinylcaprolactum. Glucosamine, an effective H-donor in enhancing polymerisation as shown by Differential Photocalorimetric results, was found unsuitable for hydrogel preparation. Drugs of different molecular weights releasing at the same rate was discussed. The hydrogels were found to have no toxic effects and were biocompatible with a human keratinocyte cell line.     

Characterisation of N-vinyl-2-pyrrolidone-based hydrogels prepared by a Diels-Alder click reaction in water

N-vinyl-2-pyrrolidone-based hydrogels were prepared by the Diels-Alder reaction in water for the first time. Copolymers of N-vinyl-2-pyrrolidone(VP) and furfuryl methacrylate(FM) were synthesised by free radical polymerisation in toluene at 70 °C by using 2,2′-azobisisobutyronltrile as an initiator. Polymeric dienophile (PEG-AMI) was prepared from N-alaninyl maleimide (AMI) and poly(ethylene glycol) (PEG) by using N,N′-dicyclohexylcarbodiimide (DCC) as a dehydrating agent. The prepared dienes and dienophile were then dissolved in water and mixed, leading to gelation via Diels-Alder reaction after some time. The gelation times of different copolymers and PEG-AMI in different solvents and at different temperatures were measured by the vial inversion method, and the swelling behaviour of dried hydrogels was studied using a general gravimetric method. The gelation time was shorter in water than in organic solvents, and the gelation time decreased with the increase of temperature and FM content in copolymers. Conversely, the swelling ratios increased with the decrease of temperature and FM content in the copolymers. Disassembly experiments suggested that N,N-dimethylformamide (DMF) could accelerate the retro-DA reaction.     

An enhanced immobilization of BSA biomolecule on anionic hydrogels: swelling and adsorption modeling

The three-dimensional structure of hydrogels plays a leading role in several areas of applications. The hydrogels are more and more used as systems of immobilized and controlled release of biomolecules in biotechnology and bio-pharmacy industries. To improve protein adsorption capacity in poly(acrylamide) hydrogels, maleic acid co-monomer was included into the reaction mixture during hydrogel synthesis. So, hydrogels of poly(acrylamide) and its copolymers with diprotic maleic acid were prepared by copolymerization and chemical crosslinking with N,N′-methylene bis-acrylamide. Swelling behavior in distilled water, in physiological saline and in bovine serum albumin (BSA) solutions was studied. Influence of initial BSA concentration on hydrogel swelling and BSA adsorption was investigated. The high amount of maleic acid present in the hydrogels has a significant effect on the swelling behavior and BSA adsorption. Results showed that the pH sensitivity of hydrogels resulted in the high amount of adsorbed BSA. The adsorption isotherms were described by Langmuir and Freundlich models. The thermodynamic parameter (ΔG _ads ⁰ ) was determined for all obtained hydrogels. We demonstrated the favorable character and reversibility of the BSA adsorption process.     

Synthesis and properties of radiopaque polymer hydrogels II: copolymers of 2,4,6-triiodophenyl- or N-(3-carboxy-2,4,6-triiodophenyl)- acrylamide and p-styrene sulfonate

In order to pursue a possibility of application of radiopaque polymer hydrogels to vascular embolization, studies were made on synthesis of iodine containing copolyanions and properties of their hydrogels with polycation via formation of polyion complexes (PIC). Acrylamide derivatives having triiodophenyl groups were synthesized and copolymerized with sodium styrene sulfonate (SS) under several conditions. It was found that N-(3-carboxy-2,4,6-triiodophenyl)-acrylamide (CIPA) and 2,4,6-triiodophenylacrylamide (TIPA) monomers are effectively copolymerized with SS, while N-allyl-2,3,5-triiodobenzamide (ATIBA) are hardly copolymerized. Hydrogels were prepared by mixing aqueous solutions of polyanions, i.e. the copolymers (PCIPA and PTIPA) and polyallylamine (PAAn). ¹³C NMR spectra of PCIPA/PAAn and PTIPA/PAAn hydrogels gave peaks for both polyanion and polycation. This means that there remained free anionic and cationic monomer units, which did not form ion pairs because of spatial hindrance. Time dependence of ¹H T₂ showed quick increment and plateau for PSS/PAAn and gradual increments for PCIPA/PAAn. Therefore, PIC containing the radiopaque copolymer retains the hydrogel state for a long time. Embolization was examined by injection of PCIPA/PAAn hydrogels into the vein of a removed porcine kidney as a preliminary test for transcatheter arterial embolization (TAE). X-ray radiograms of the embolized organ were reasonably explained based on the structure and mobility of hydrogels.     

Biodegradation of random co-polypeptide hydrogels consisting of N-hydroxypropyl l-glutamine as one component

Two component random co-polypeptide hydrogels consisting of N-hydroxypropyl l-glutamine and l-alanine (Ala) or l-phenylalanine (Phe) were prepared by performing aminolysis reactions with 3-amino-1-propanol together with crosslinking reaction with 1,8-octamethylenediamine on hydrogels of the starting co-polymers consisted of γ-benzyl l-glutamate and Ala or Phe. The relationship between their bulk structure and properties was evaluated with regard to the swelling ratio in water (q), the rate of water vapor permeability (V_f), tensile properties, and enzymatic degradation behaviors of hydrogels in a pseudo-extracellular fluid (PECF). The tensile property of the hydrogels was highly dependent on q in PECF, and on the hydrophobicity of the side chains. A relationship was obtained between the V_f and q of hydrogels in PECF regardless of the differences in the nature of the side chains. Biodegradation of the hydrogels in vitro by bromelain indicated that degradation took place in bulk rather than on the surface, and that the rate of degradation was also highly dependent on q in the samples as well as on the hydrophobicity of the side chains of the samples.     

Dual thermo‐ and pH‐sensitive network‐grafted hydrogels formed by macrocrosslinker as drug delivery system

Dual thermo‐ and pH‐sensitive network‐grafted hydrogels made of poly(N,N‐dimethylaminoethyl methacrylate) (PDMAEMA) network and poly(N‐isopropylacrylamide) (PNIPAM) grafting chains were successfully synthesized by the combination of atom transfer radical polymerization (ATRP), reversible addition‐fragmentation chain transfer (RAFT) polymerization, and click chemistry. PNIPAM having two azide groups at one chain end [PNIPAM‐(N₃)₂] was prepared with an azide‐capped ATRP initiator of N,N‐di(β‐azidoethyl) 2‐chloropropionylamide. Alkyne‐pending poly(N,N‐dimethylaminoethyl methacrylate‐co‐propargyl acrylate) [P(DMAEMA‐co‐ProA)] was obtained through RAFT copolymerization using dibenzyltrithiocarbonate as chain transfer agent. The subsequent click reaction led to the formation of the network‐grafted hydrogels. The influences of the chemical composition of P(DMAEMA‐co‐ProA) on the properties of the hydrogels were investigated in terms of morphology and swelling/deswelling kinetics. The dual stimulus‐sensitive hydrogels exhibited fast response, high swelling ratio, and reproducible swelling/deswelling cycles under different temperatures and pH values. The uptake and release of ceftriaxone sodium by these hydrogels showed both thermal and pH dependence, suggesting the feasibility of these hydrogels as thermo‐ and pH‐dependent drug release devices. © 2011 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2011