Nanostructured SnO2-ZnO heterojunction photocatalysts showing enhanced photocatalytic activity for the degradation of organic dyes

Nanoporous SnO(2)-ZnO heterojunction nanocatalyst was prepared by a straightforward two-step procedure involving, first, the synthesis of nanosized SnO(2) particles by homogeneous precipitation combined with a hydrothermal treatment and, second, the reaction of the as-prepared SnO(2) particles with zinc acetate followed by calcination at 500 °C. The resulting nanocatalysts were characterized by X-ray diffraction (XRD), FTIR, Raman, X-ray photoelectron spectroscopy (XPS), nitrogen adsorption-desorption analyses, transmission electron microscopy (TEM), and UV-vis diffuse reflectance spectroscopy. The SnO(2)-ZnO photocatalyst was made of a mesoporous network of aggregated wurtzite ZnO and cassiterite SnO(2) nanocrystallites, the size of which was estimated to be 27 and 4.5 nm, respectively, after calcination. According to UV-visible diffuse reflectance spectroscopy, the evident energy band gap value of the SnO(2)-ZnO photocatalyst was estimated to be 3.23 eV to be compared with those of pure SnO(2), that is, 3.7 eV, and ZnO, that is, 3.2 eV, analogues. The energy band diagram of the SnO(2)-ZnO heterostructure was directly determined by combining XPS and the energy band gap values. The valence band and conduction band offsets were calculated to be 0.70 ± 0.05 eV and 0.20 ± 0.05 eV, respectively, which revealed a type-II band alignment. Moreover, the heterostructure SnO(2)-ZnO photocatalyst showed much higher photocatalytic activities for the degradation of methylene blue than those of individual SnO(2) and ZnO nanomaterials. This behavior was rationalized in terms of better charge separation and the suppression of charge recombination in the SnO(2)-ZnO photocatalyst because of the energy difference between the conduction band edges of SnO(2) and ZnO as evidenced by the band alignment determination. Finally, this mesoporous SnO(2)-ZnO heterojunction nanocatalyst was stable and could be easily recycled several times opening new avenues for potential industrial applications.     

基于上转换发光共振能量转移的CRISPR/Cas12a生物传感系统用于HPV16 DNA双信号检测

传统的纯核结构的上转换纳米材料用于生物传感时, 存在表面猝灭效应或者因发光共振能量转移(LRET)效率不高导致灵敏度低等缺点, 对目标物的灵敏检测有一定的局限性. 本文通过多步高温共沉淀, 介导壳层外延成长法, 合成了NaYF₄∶Yb³⁺,Er³⁺(C-UCNPs)核层发光和NaYF₄@NaYF₄∶Yb³⁺,Er³⁺@NaYF₄(CSS-UCNPs)内壳层发光能量限域型上转换纳米材料, 并表征了材料的晶型、 形貌、 表面配体、 元素组成和发光共振能量转移效率. 结果表明, 该材料具有表面猝灭效应低、 发光共振转移效率较高的优势, 随后将其与成簇规律间隔的短回文重复序列及其相关蛋白(CRISPR/Cas)12a-纳米金系统结合, 实现了人乳头瘤病毒DNA(HPV16 DNA)的比色定性和上转换发光定量分析, 检出限为69.8 pmol/L, 双信号检测有效提高了检测结果的准确性. 此外, 本方法不仅特异性强, 还能识别单碱基错配的HPV16 DNA, 提高了DNA片段的容错率.     

Selective nucleation and discovery of organic polymorphs through epitaxy with single crystal substrates.

Crystallization of 5-methyl-2-[(2-nitrophenyl)amino]-3-thiophenecarbonitrile (1), previously found to produce six conformational polymorphs from solution, on single-crystal pimelic acid (PA) substrates results in selective and oriented growth of the metastable "YN" (yellow needle) polymorph on the (101)(PA) faces of the substrate. Though the freshly cleaved substrate crystals expose (101)(PA) and (111)(PA) faces, which are both decorated with [101](PA) ledges that could serve as nucleation sites, crystal growth of YN occurs on only (101)(PA). Goniometry measurements performed with an atomic force microscope reveal that the (001)(YN) plane contacts (101)(PA) with a crystal orientation [100](YN)//[010](PA) and [010](YN)//[101](PA). A geometric lattice analysis using a newly developed program dubbed GRACE (geometric real-space analysis of crystal epitaxy) indicates that this interfacial configuration arises from optimal two-dimensional epitaxy and that among the six polymorphs of 1, only the YN polymorph, in the observed orientation, achieves reasonable epitaxial match to (101)(PA). The geometric analysis also reveals that none of the polymorphs, including YN, can achieve comparable epitaxial match with (111)(PA), consistent with the absence of nucleation on this crystal face. In contrast, sublimation of 1 on cleaved succinic acid (SA) substrates, which expose large (010)(SA) faces decorated with steps along [101](SA), affords growth of several polymorphs, each with multiple orientations, as well as oriented crystals of a new metastable polymorph on the (010)(SA) surfaces. The lack of polymorphic selectivity on (010)(SA) can be explained by the geometric lattice analysis, which reveals low-grade epitaxial matches between (010)(SA) and several polymorphs of 1 but no inherent selectivity toward a single polymorph. These observations demonstrate the sensitivity of crystal nucleation to substrate surface structure, the potential of crystalline substrates for selective nucleation and discovery of polymorphs, and the utility of geometric lattice modeling for screening of substrate libraries for controlling polymorphism.     

Single crystal SnO2 zigzag nanobelts

Zigzag SnO2 nanobelts have been synthesized by evaporating tin grain in air. XRD, SEM, and TEM were employed to characterize the prepared samples. SEM images showed large amounts of zigzag nanobelts with periodic morphology. XRD result showed a pure tetragonal SnO2 phase. HRTEM and SAED revealed a single crystal structure with [010] zone axis on the whole zigzag zone. The zigzag structure is deduced to be formed by shifting the growth direction from [101] to [10] or vice versa. Growing nanobelts along different equivalent directions opens a new avenue for the preparation of novel nanostructured materials.     

Vapor-liquid-solid and vapor-solid growth of phase-change Sb2Te3 nanowires and Sb2Te3/GeTe nanowire heterostructures

We report the synthesis and characterization of radial heterostructures composed of an antimony telluride (Sb2Te3) core and a germanium telluride (GeTe) shell, as well as an improved synthesis of Sb2Te3 nanowires. The synthesis of the heterostructures employs Au-catalyst-assisted vapor-liquid-solid (VLS) and vapor-solid (VS) mechanisms. Energy-dispersive X-ray spectrometry indicates that Sb and Ge are localized in the Sb2Te3 and GeTe portions, respectively, confirming the alloy-free composition in the core/shell heterostructures. Transmission electron microscopy and diffraction studies show that Sb2Te3 and GeTe regions exhibit rhombohedral crystal structure. Both Sb2Te3 and GeTe grow along the [110] direction with an epitaxial interface between them. Electrical characterization of individual nanowires and nanowire heterostructures demonstrates that these nanostructures exhibit memory-switching behavior.     

Morphological and photoelectrochemical characterization of core-shell nanoparticle films for dye-sensitized solar cells: Zn-O type shell on SnO2 and TiO2 cores

Core-shell type nanoparticles with SnO2 and TiO2 cores and zinc oxide shells were prepared and characterized by surface sensitive techniques. The influence of the structure of the ZnO shell and the morphology ofnanoparticle films on the performance was evaluated. X-ray absorption near-edge structure and extended X-ray absorption fine structure studies show the presence of thin ZnO-like shells around the nanoparticles at low Zn levels. In the case of SnO2 cores, ZnO nanocrystals are formed at high Zn/Sn ratios (ca. 0.5). Scanning electron microscopy studies show that Zn modification of SnO2 nanoparticles changes the film morphology from a compact mesoporous structure to a less dense macroporous structure. In contrast, Zn modification of TiO2 nanoparticles has no apparent influence on film morphology. For SnO2 cores, adding ZnO improves the solar cell efficiency by increasing light scattering and dye uptake and decreasing recombination. In contrast, adding a ZnO shell to the TiO2 core decreases the cell efficiency, largely owing to a loss of photocurrent resulting from slow electron transport associated with the buildup of the ZnO surface layer.     

Local‐Curvature‐Controlled Non‐Epitaxial Growth of Hierarchical Nanostructures

Site‐selective growth on non‐spherical seeds provides an indispensable route to hierarchical complex nanostructures that are interesting for diverse applications. However, this has only been achieved through epitaxial growth, which is restricted to crystalline materials with similar crystal structures and physicochemical properties. A non‐epitaxial growth strategy is reported for hierarchical nanostructures, where site‐selective growth is controlled by the curvature of non‐spherical seeds. This strategy is effective for site‐selective growth of silica nanorods from non‐spherical seeds of different shapes and materials, such as α‐Fe₂O₃, NaYF₄, and ZnO. This growth strategy is not limited by the stringent requirements of epitaxy and is thus a versatile general method suitable for the preparation of hierarchical nanostructures with controlled morphologies and compositions to open up a verity of applications in self‐assembly, nanorobotics, catalysis, electronics, and biotechnology.     

Microwave-assisted solution synthesis and photocatalytic activity of Ag nanoparticles supported on ZnO nanostructure flowers

Ag nanoparticles supported on the surface of three-dimensional (3D) flower-like ZnO nanostructure were synthesized by a microwave-assisted solution method. The obtained products were characterized by X-ray diffraction analysis, field-emission scanning electron microscopy, Fourier-transform infrared spectroscopy, Raman spectrophotometry, X-ray photoelectron spectroscopy, and photoluminescence spectroscopy. The analytical results confirmed homogeneously distributed Ag nanoparticles supported on the surface of flower-like ZnO nanostructure. The photocatalytic effect of the heterostructure Ag/ZnO nanocomposites was investigated using photodegradation under ultraviolet (UV) light of methylene blue as model dye. The heterostructure Ag/ZnO nanocomposites exhibited much higher photocatalytic activity than pure ZnO flowers. The improved photocatalytic properties are attributed to formation of a Schottky barrier at the metal–semiconductor interface of the Ag/ZnO nanocomposites.     

Facile route to Zn-based II-VI semiconductor spheres, hollow spheres, and core/shell nanocrystals and their optical properties

A convenient chemical conversion method that allows the direct preparation of nanocrystalline ZnE (E = O, S, Se) semiconductor spheres and hollow spheres as well as their core/shell structures is reported. By using monodisperse ZnO nanospheres as a starting reactant and in situ template, ZnS, ZnSe solid and hollow nanospheres, and ZnO/ZnS and ZnO/ZnSe core/shell nanostructures have been obtained through an ultrasound-assisted solution-phase conversion process. The formation mechanism of these nanocrystals is connected with the sonochemical effect of ultrasound irradiation. The photoluminescence and electrogenerated chemiluminescence properties of the as-prepared nanocrystals were investigated.     

同晶外延生长法合成MFI型核壳复合分子筛

采用二次热液结晶法,以四丙基氢氧化铵水溶液预处理过的低硅ZSM-5分子筛为晶核,通过调控p H值、水量和晶化时间等二次结晶条件,在晶核上外延生长了高硅ZSM-5壳,制备了MFI/MFI核壳型复合分子筛。通过X射线衍射、扫描电镜、能量色散谱仪、透射电子显微镜、N2吸附-脱附和NH3-程序升温脱附等手段表征了所合成的核壳分子筛的晶体结构、表面形态及核/壳界面,并对它们的结构参数以及酸性进行了初步评估。结果表明,核壳复合分子筛的壳层由多层200 nm的MFI沸石晶粒组成;高硅ZSM-5分子筛壳层的生成,引入了介孔结构,显著增大了外比表面积;同时,核壳结构的形成降低了复合分子筛酸性和外表面的酸密度,但增加了弱酸量。当二次晶化母液p H值为8.5,H2O/SO2物质的量比为30,晶化时间为24 h时,高硅分子筛壳层更易可控生长。     

Core–shell hybrid material for ZnO nanorods generation

The aim of our study consisted in obtaining ZnO nanorods using a photonic crystal (PC) structure as substrate. For obtaining of such structures, a PC presenting with electroconductive properties was chosen. Thus, the first step was represented by the synthesis of a copper nanoparticles shell composed by a maximum of seven layers of inorganic particle. This core–shell structure was subsequently used for the generation of ZnO nanorods by electrochemical deposition. The obtained materials were characterized by SEM, dynamic light scattering, UV–Vis, and X-ray powder diffraction analysis.     

Density functional theory study on the structural and electronic properties of low index rutile surfaces for TiO2/SnO2/TiO2 and SnO2/TiO2/SnO2 composite systems

The present study is concerned with the structural and electronic properties of the TiO2/SnO2/TiO2 and SnO2/TiO2/SnO2 composite systems. Periodic quantum mechanical method with density functional theory at the B3LYP level has been carried out. Relaxed surface energies, structural characteristics and electronic properties of the (110), (010), (101) and (00) low-index rutile surfaces for TiO2/SnO2/TiO2 and SnO2/TiO2/SnO2 models are studied. For comparison purposes, the bare rutile TiO2 and SnO2 structures are also analyzed and compared with previous theoretical and experimental data. The calculated surface energy for both rutile TiO2 and SnO2 surfaces follows the sequence (110) < (010) < (101) < (001) and the energy increases as (010) < (101) < (110) < (001) and (010) approximately = (110) < (101) < (001) for SnO2/TiO2/SnO2 and TiO2/SnO2/TiO2 composite systems, respectively. SnO2/TiO2/SnO2 presents larger values of surface energy than the individual SnO2 and TiO2 metal oxides and the TiO2/SnO2/TiO2 system renders surface energy values of the same order that the TiO2 and lower than the SnO2. An analysis of the electronic structure of the TiO2/SnO2/TiO2 and SnO2/TiO2/SnO2 systems shows that the main characteristics of the upper part of the valence bands for all the studied surfaces are dominated by the external layers, i.e., by the TiO2 and the SnO2, respectively, and the topology of the lower part of the conduction bands looks like the core layers. There is an energy stabilization of both valence band top and conduction band bottom for (110) and (010) surfaces of the SnO2/TiO2/SnO2 composite system in relation to their core TiO2, whereas an opposite trend is found for the same surfaces of the TiO2/SnO2/TiO2 composite system in relation to the bare SnO2. The present theoretical results may explain the growth of TiO2@SnO2 bimorph composite nanotape.     

ZnO@SiO_2同轴纳米电缆的静电纺丝技术制备与表征

采用同轴静电纺丝技术,以硝酸锌、正硅酸乙酯(C8H20O4Si)、无水乙醇、聚乙烯吡咯烷酮(PVP)和N,N-二甲基甲酰胺(DMF)为原料,成功制备出大量的ZnO@SiO2同轴纳米电缆。用TG-DTA,XRD,SEM,TEM,FTIR等分析技术对样品进行了表征。结果表明,得到的ZnO@SiO2同轴纳米电缆的壳层为无定型SiO2,厚度为50nm,芯轴为晶态ZnO,电缆直径为300~450nm,长度大于300μm。探讨了ZnO@SiO2同轴纳米电缆的形成机理。     

Rational synthetic strategy: From ZnO nanorods to ZnS nanotubes

We demonstrate here that ZnS nanotubes can be successfully synthesized via a facile conversion process from ZnO nanorods precursors. During the conversion process, ZnO nanorods are first prepared as sacrificial templates and then converted into tubular ZnO/ZnS core/shell naonocomposites through a hydrothermal sulfidation treatment by using thioacetamide (TAA) as sulfur source. ZnS nanotubes are finally obtained through the removal of ZnO cores of tubular ZnO/ZnS core/shell naonocomposites by KOH treatment. The photoluminescence (PL) characterization of the as-prepared products shows much enhanced PL emission of tubular ZnO/ZnS core/shell nanocomposites compared with their component counterparts. The probable mechanism of conversion process is also proposed based on the experimental results.     

Microwave-Assisted Synthesis of ZnO–rGO Core–Shell Nanorod Hybrids with Photo- and Electro-Catalytic Activity

The unique two-dimensional structure and surface chemistry of reduced graphene oxide (rGO) along with its high electrical conductivity can be exploited to modify the electrochemical properties of ZnO nanoparticles (NPs). ZnO–rGO nanohybrids can be engineered in a simple new two-step synthesis, which is both fast and energy-efficient. The resulting hybrid materials show excellent electrocatalytic and photocatalytic activity. The structure and composition of the as-prepared bare ZnO nanorods (NRs) and the ZnO–rGO hybrids have been extensively characterised and the optical properties subsequently studied by UV/Vis spectroscopy and photoluminescence (PL) spectroscopy (including decay lifetime measurements). The photocatalytic degradation of Rhodamine B (RhB) dye is enhanced using the ZnO–rGO hybrids as compared to bare ZnO NRs. Furthermore, potentiometry comparing ZnO and ZnO–rGO electrodes reveals a featureless capacitive background for an Ar-saturated solution whereas for an O₂-saturated solution a well-defined redox peak was observed using both electrodes. The change in reduction potential and significant increase in current density demonstrates that the hybrid core–shell NRs possess remarkable electrocatalytic activity for the oxygen reduction reaction (ORR) as compared to NRs of ZnO alone.     

Rotor-like ZnO by epitaxial growth under hydrothermal conditions

Rotor-like ZnO was grown from a mixture of rod-like ZnO powder and a saturated Zn(OH)(4)(2-) solution under moderate hydrothermal conditions at 100 degree C, in which the precursor rod-like ZnO crystal plane acts as a matrix core, and the branched nanorods showed fast epitaxial growth on the six directions around the prism core.     

Epitaxial growth and photochemical annealing of graded CdS/ZnS shells on colloidal CdSe nanorods

We report the preparation and structural characterization of core/shell CdSe/CdS/ZnS nanorods. A graded shell of larger band gap is grown around CdSe rods using trioctylphosphine oxide as a surfactant. Interfacial segregation is used to preferentially deposit CdS near the core, providing relaxation of the strain at the core/shell interface. The reported synthesis allows for variation of the shell thickness between one and six monolayers, on core nanorods ranging from aspect ratios of 2:1 to 10:1. After an irreversible photochemical annealing process, the core/shell nanorods have increased quantum efficiencies and are stable in air under visible or UV excitation. In addition to their robust optical properties, these samples provide an opportunity for the study of the evolution of epitaxial strain as the shape of the core varies from nearly spherical to nearly cylindrical.     

ZnO/ZnS大面积单晶异质结及其光电性能研究

ZnO和ZnS是重要的Ⅱ-Ⅵ族宽禁带半导体材料,二者之间形成的异质结具有Ⅱ型能带结构,可以促使受激载流子实现空间分离,延长受激载流子的寿命,从而提高材料的光催化和光电探测性能。本文利用物理气相沉积方法,首次在ZnO块状单晶衬底上生长了一层ZnS单晶薄膜,薄膜由厚约4nm、边长几百纳米,取向一致的等边三角形纳米片组成。X射线衍射和透射电子显微镜的表征结果显示,ZnS薄膜与ZnO衬底具有单一外延取向关系。阴极射线荧光光谱表明ZnS薄膜的制备显著提高了ZnO单晶片可见光荧光发光峰的强度。此外,对ZnO/ZnS异质结的紫外光电探测性能的研究结果显示,异质结对不同波长的紫外光均有响应,光响应的上升弛豫时间和下降弛豫时间分别为200ms和1050ms,展示了较好的光电应用潜力。     

Weak epitaxy growth and phase behavior of planar phthalocyanines on p-sexiphenyl monolayer film

We systematically investigated the weak epitaxy growth (WEG) behavior of a series of planar phthalocyanine compounds (MPc), i.e., metal-free phthalocyanine (H2Pc), nickel phthalocyanine (NiPc), copper phthalocyanine (CuPc), zinc phthalocyanine (ZnPc), iron phthalocyanine (FePc), cobalt phthalocyanine (CoPc), grown on a p-sexiphenyl ( p-6P) monolayer film by selected area electron diffraction (SAED) and atomic force microscopy (AFM). Two types of epitaxial relations, named as incommensurate epitaxy and commensurate epitaxy, were identified between phthalocyanine compounds and the substrate of the p-6P film. The tiny variation of the lattice constant of phthalocyanine compounds can result in different crystal orientations. The change rule of incommensurate and commensurate epitaxy was extracted. The tendency of commensurate epitaxy becomes weaker as the lattice constant b increases, while it gets stronger as the substrate temperature is elevated. Large size and continuous H2Pc films can be obtained by controlling the growth conditions. The WEG method is generally applicable in the whole family of planar phthalocyanine compounds and may be used to fabricate other high-quality organic films.     

Ag/ZnO/ZnSe三元异质结的合成及其可见光光催化性能

以Ag纳米线为模板,通过两步水浴法合成了Ag/ZnO/ZnSe三元异质结光催化材料。利用场发射扫描电子显微镜(FESEM)、X射线能谱仪(EDS)、X射线衍射仪(XRD)以及透射电子显微镜(FETEM)对样品的形貌和结构进行了表征。结果显示,Ag/ZnO/ZnSe三元异质结为蠕虫状的Ag/ZnO二元异质结外镶嵌着ZnSe小颗粒。在可见光下,对比纯Ag纳米线、纯ZnO纳米球、Ag/ZnO异质结对罗丹明B的可见光降解效率,结果发现Ag/ZnO/ZnSe异质结表现出了更高的光催化效率。其光催化性能的提高主要是由于Ag/ZnO/ZnSe异质结的作用促使电子空穴对的分离,降低了电子空穴对的复合机率,从而提高了材料的光催化效率。