Ag-Au合金/SiO2复合薄膜的制备与表征

以AgNO3,HAuCl4和正硅酸乙酯为主要原料,利用溶胶-凝胶法和旋涂技术,通过热处理和紫外光辐射还原得到了不同nAg/nAu(1∶0,2∶1,1∶2,0∶1)的Ag-Au合金/SiO2复合薄膜.从扫描电子显微镜和X射线衍射谱的结果可以看出得到的薄膜均匀性好,复合薄膜中合金颗粒的尺寸为10 nm左右.利用紫外-可见分光光谱仪研究了复合薄膜的光吸收性能,结果表明,随着nAg/nAu的降低,吸收峰的位置也由最初的Ag纳米粒子的等离子共振吸收峰430 nm附近,逐渐红移到Au纳米粒子的等离子共振吸收峰605和880 nm附近.从光吸收谱可以看出,nAg∶nAu＝2∶1和1∶2的两个样品分别在515,730 nm附近和550,730 nm附近出现表面等离子共振吸收峰.这表明Au-Ag合金固溶体的形成.     

Au/SiO2纳米多层薄膜的制备及其性质表征

利用多靶磁控溅射技术制备了Au/SiO₂纳米颗粒分散氧化物多层复合薄膜.研究了在保持Au单层颗粒膜沉积时间一定时薄膜厚度一定、变化SiO₂的沉积时间及SiO₂的沉积时间一定而改变薄膜厚度时，多层薄膜在薄膜厚度方向的微观结构对吸收光谱的影响.研究结果表明：具有纳米层状结构的Au/SiO₂多层薄膜在560 nm波长附近有明显的表面等离子共振吸收峰，吸收峰的强度随Au颗粒的浓度增加而增强，在Au颗粒浓度相同的情况下，复合薄膜 关键词： 2纳米复合薄膜')" href="#">Au/SiO₂纳米复合薄膜 多靶磁控溅射 吸收光谱 有效介质理论     

多孔TiO2/Al/SiO2纳米复合结构的紫外光吸收特性研究

在SiO₂玻璃衬底上用脉冲激光沉积(PLD)技术,分别沉积Ti和Ti/Al膜,经电化学阳极氧化成功制备了多孔TiO₂/SiO₂和TiO₂/Al/SiO₂纳米复合结构. 其中TiO₂薄膜上的微孔阵列高度有序,分布均匀. 实验研究了Al过渡层对多孔TiO₂薄膜光吸收特性的影响. 结果表明：无Al过渡层的多孔TiO₂薄膜其紫外吸收峰在27 关键词： 2薄膜')" href="#">多孔TiO₂薄膜 阳极氧化 紫外光吸收     

Al2O3薄膜/纳米Ag颗粒复合结构的光吸收谱及增强Raman散射光谱研究

Al₂O₃介质薄膜与纳米Ag颗粒构成的复合结构,被应用于表面增强Raman散射探测实验中,其中Al₂O₃介质薄膜对纳米Ag颗粒的吸收谱及增强Raman散射光谱的影响被特别关注.该复合结构的光学特性表征出纳米Ag颗粒的偶极振荡特性.从光吸收谱中可以看到,其共振吸收谱随Al₂O₃介质薄膜厚度增加而在整个谱域上发生红移,表明纳米Ag颗粒的周围介电常数随Al₂O₃介质薄膜厚度的增加而增大.采用罗丹明6G作为探针原子,6个Raman特征峰的平均增益值作为表征表面增强Raman散射衬底增益程度的量度.实验结果表明,Al₂O₃介质薄膜层的引入提高了纳米Ag颗粒的衬底介电常数,并引起了散射共振的增强,从而使表面增强Raman散射强度提高. 关键词： 纳米Ag薄膜 共振吸收 表面增强Raman散射 介电常数     

金属纳米团簇复合薄膜Au/BaTiO3与Fe/BaTiO3的PLD制备及其光吸收特征

用脉冲激光沉积技术制备了掺杂纳米金属颗粒Au或Fe的BaTiO₃复合薄膜.用透射电子显微镜和x射线光电子能谱表征了金属颗粒的形态和化学态.330—800nm范围的吸收谱研究表明，掺Au颗粒的BaTiO₃薄膜在580nm附近有一个明显的共振吸收峰，而掺Fe颗粒的BaTiO₃薄膜没有这样的吸收峰.用Mie散射理论对结果进行了分析. 关键词： 复合薄膜 金属颗粒 脉冲激光沉积 吸收谱     

降低表面等离子激元寄生吸收损失的途径研究

从纳米Ag颗粒表面等离子激元光学及表面高能电场特性两方面入手,较为系统地研究了周围介质的导电特性对表面等离子激元的影响.通过对复合薄膜紫外-可见-近红外光谱及表面增强拉曼散射光谱的分析,指出绝缘性的Al₂O₃介质薄膜能够起到良好的表面电场定域效果,且不会引入附加的光吸收损失;而导电性的ITO薄膜则会引入表面价电子的溢出损失,加速了表面电场的衰逝,同时引起长波方向上显著的光吸收损失.研究还表明致密的Al₂O₃介质薄膜能够起到良好的屏蔽作用,且纳米Ag颗粒表面等离子激元特性仅受最近邻材料特性的影响.研究结果为在硅基薄膜太阳电池中实现对纳米Ag颗粒的阻挡、寄生光吸收损失的降低以及表面高能电场的利用,提供了一条有效的解决途径.     

CdSe:Nd纳米晶及CdSe:Nd@SiO2核壳结构的合成及发光性能

利用有机相法合成Nd³⁺掺杂CdSe纳米晶（CdSe∶Nd）,通过X射线粉末衍射（XRD）、透射电镜（TEM）、紫外吸收光光谱及荧光光谱表征,证明Nd³⁺已经成功掺入到CdSe的晶格中。与纯CdSe纳米晶相比,CdSe∶Nd纳米晶的结构仍为立方晶型,且形貌近似球形,均匀分散,粒径约为2~4 nm。紫外吸收峰和荧光发射峰都发生红移,而且掺杂后的CdSe∶Nd纳米晶量子产率也提高,这可能是由于掺杂Nd³⁺引入了新的杂质能级,带隙减小。为了实现CdSe∶Nd纳米晶的可加工性和功能性,通过微乳法合成SiO₂壳包覆的CdSe∶Nd纳米球（CdSe∶Nd@SiO₂纳米球）,CdSe∶Nd@SiO₂纳米球呈均匀球形,直径约为100~115 nm,并且包壳后的CdSe∶Nd@SiO₂纳米球发射峰（581 nm）与CdSe∶Nd纳米晶（598 nm）相比,发光强度提高且发射峰蓝移,蓝移约为17 nm,可能是因为SiO₂壳可以减少纳米晶表面的非辐射跃迁以及改善表面缺陷导致的。     

脉冲激光沉积Ag:BaTiO3纳米复合薄膜及其光学特性

在MgO(100)基片上利用脉冲激光沉积技术制备了掺有Ag纳米颗粒的BaTiO₃复合薄膜.通过X射线衍射对薄膜的结构进行了表征,利用透射电子显微镜对Ag纳米颗粒的尺寸、形态进行了观测,X射线光电子能谱结果表明Ag呈金属态.在410—500nm范围内观测到了Ag纳米颗粒引起的等离子振荡峰,随着后处理温度和Ag颗粒浓度的增加,吸收峰发生红移,并出现了双峰现象. 关键词： 金属纳米复合薄膜 激光沉积 光吸收     

SiO2包覆对ZnS纳米材料发光的增强机制

为了明确团聚现象及表面性质对ZnS纳米材料发光性质的影响,采用SiO₂对ZnS材料进行了表面修饰,并对ZnS及ZnS/SiO₂复合材料的光学性质进行对比研究.采用吸收光谱分析了包覆前后光吸收性质的差异,发现SiO₂包覆后ZnS纳米材料的带边由333 nm红移至360 nm.为了研究ZnS纳米材料与ZnS/SiO₂纳米复合材料的光发射性质,分别对含纳米材料的水溶液样品及粉末样品的发光光谱进行了采集.对比研究的结果表明,SiO₂包覆后ZnS纳米材料在蓝紫光区的发光得到了明显增强.以氙灯作为激发光源所获得荧光光谱显示ZnS/SiO₂粉末样品发光的积分强度增大为原来的17.5倍,但相同条件下针对溶液样品的测试结果显示其发光强度只增大了1.1倍,这种增强可用SiO₂的存在抑制了ZnS纳米粒子间的团聚来解释,且这一推断由325 nm紫外激光激发下获得的光致发光数据进行了验证.     

VO$lt;sub$gt;2$lt;/sub$gt;/AZO复合薄膜的制备及其光电特性研究

采用直流磁控溅射和后退火氧化的方法在掺铝氧化锌(AZO)导电玻璃上制备了二氧化钒(VO₂)薄膜,研究了不同的退火温度、退火时间对VO₂/AZO复合薄膜制备的影响,并对复合薄膜的结构、组分、光电特性进行了测试与分析. 结果表明,导电玻璃上的AZO没有改变VO₂的取向生长,但明显改变了VO₂薄膜的表面形貌特征. 与用相同工艺和条件在普通玻璃基底上制备的VO₂薄膜相比,VO₂/AZO复合薄膜的相变温度降低约25 ℃,热滞回线宽度收窄至6 ℃,相变前后可见光透过率均在50%以上,1500 nm处红外透过率约为55%和21%,电阻率变化达3 个数量级. 该复合薄膜表面平滑致密,制备工艺简单,性能稳定,可应用于新型光电器件. 关键词： 2')" href="#">VO₂ AZO 热致相变 光电特性     

Synthesis and microstructure of metal oxide thin films containing metal nanoparticles by liquid phase deposition (LPD) method

Au nanoparticles dispersed SiO₂-TiO₂ composite films have been prepared by a novel wet process, Liquid Phase Deposition (LPD) method. The composite films were characterized by XRD, XPS, TEM, ICP, SEM and UV-VIS absorption spectroscopy. The results showed that the SiO₂-TiO₂ composite films containing Au^III and Au^I ionic species were co-deposited from a mixed solution of ammonium silicofluoride, ammonium hexafluorotitanate, boric acid and tetrachloroauric acid. The heat treatment induced the reduction of Au ions and formation of Au nanoparticles in the film. TEM observation revealed that the Au nanoparticles with 5-10 nm in diameter were found to be dispersed uniformly in the SiO₂-TiO₂ matrix. The optical absorption band due to the surface plasmon resonance of dispersed Au particles were observed at the wavelength of 550 nm and shifted toward longer wavelength with increasing heat treatment temperature. Received 28 November 2000     

Optical properties of sol-gel fabricated Ni/SiO2 glass nanocomposites

Nickel nanoparticles were grown in silica glass by annealing of the sol-gel prepared silicate matrices doped with nickel nitrate. TEM characterization of Ni/SiO₂ glass proves the formation of isolated spherical nickel nanoparticles with mean sizes 6.7 and 20 nm depending on annealing conditions. The absorption and photoluminescence spectra of Ni/SiO₂ glasses were measured. In the absorption spectra, we observed the band related to the surface plasmon resonance (SPR) in Ni nanoparticles. The broadening of SPR was observed with decrease of Ni nanoparticle size. The width of the surface plasmon band decreases 1.5 times at the lowering of temperature from 293 to 2 K because of strong electron-phonon interaction. The spectra proved the creation of nickel oxide NiO clusters and Ni²⁺ ions in silica glass as well.     

rf reactive co-sputtered Au-Ag alloy nanoparticles in SiO2 thin films

We have studied formation of Au-Ag alloy nanoparticles in sputtered SiO₂ thin films. Silica thin films containing Au-Ag nanoparticles were deposited on quartz substrates using rf reactive magnetron co-sputtering technique. The films heat-treated in reducing Ar + H₂ atmosphere at different temperatures. They were analyzed by using UV-vis spectrophotometry, atomic force microscopy and X-ray photoelectron spectroscopy (XPS) methods for their optical, surface morphological as well as structural and chemical properties. The optical absorption of the Au-Ag alloy nanoparticles illustrated one plasmon resonance absorption peak located at 450 nm between the absorption bands of pure Au and Ag nanoparticles at 400 and 520 nm, respectively, for the thin films annealed at 800 °C. XPS results showed that the alloys were in metallic state, and they had a greater tendency to lose electrons as compared to their corresponding monometallic state. Using lateral force microscopy analysis, we have found that the alloy particles were uniformly distributed on the surface with grain size of about 20 nm.     

Optical properties of sol-gel fabricated Mn/SiO2 nanocomposites: Observation of surface plasmon resonance in Mn nanoparticles

Manganese nanoparticles were grown in silica glass and silica film on silicon substrate by annealing of the sol-gel prepared porous silicate matrices doped with manganese nitrate. Annealing of doped porous silicate matrices was performed at various conditions that allowed to obtain the nanocomposite glasses with various content of metallic Mn. TEM of Mn/SiO₂ glass indicates the bimodal size distribution of Mn nanoparticles with mean sizes of 10.5 nm and 21 nm. The absorption and photoluminescence spectra of Mn/SiO₂ glasses were measured. In the absorption spectra at 300 nm (4.13 eV) we observed the band attributed to the surface plasmon resonance in Mn nanoparticles. The spectra proved the creation of Mn²⁺ and Mn³⁺ ions in silica glass as well. The absorption spectra of Mn/SiO₂ glasses annealed in air prove the creation of manganese oxide Mn₂O₃. The measured reflection spectra of Mn/SiO₂ film manifest at 240-310 nm the peculiarity attributed to surface plasmons in Mn nanoparticles.     

Enhanced nonlinear optical absorption of Au/SiO2 nano-composite thin films

Nano metal-particle dispersed glasses are the attractive candidates for nonlinear optical material applications.Au/SiO 2 nano-composite thin films with 3 vol% to 65 vol% Au are prepared by inductively coupled plasma sputtering.Au particles as perfect spheres with diameters between 10 nm and 30 nm are uniformly dispersed in the SiO 2 matrix.Optical absorption peaks due to the surface plasmon resonance of Au particles are observed.The absorption property is enhanced with the increase of Au content,showing a maximum value in the films with 37 vol% Au.The absorption curves of the Au/SiO 2 thin films with 3 vol% to 37 vol% Au accord well with the theoretical optical absorption spectra obtained from Mie resonance theory.Increasing Au content over 37 vol% results in the partial connection of Au particles,whereby the intensity of the absorption peak is weakened and ultimately replaced by the optical absorption of the bulk.The band gap decreases with Au content increasing from 3 vol% to 37 vol % but increases as Au content further increases.     

Au/SiO2纳米复合薄膜的微结构及光吸收特性研究

用多靶磁控溅射技术制备了Au/SiO₂纳米多层薄膜.利用透射电子显微镜以及吸 收光谱对Au/SiO₂复合薄膜的微观结构、表面形貌及光学性能进行了表征和测试 .研究结果表明：单层Au/SiO₂薄膜中Au沉积时间小于10s时，分散在SiO_{2< /sub>中的Au颗粒随Au的沉积时间的延长而增大；当沉积时间超过10s后，Au颗粒的尺寸几乎 不随沉积时间变化，但Au颗粒的形状由网络状结构变为薄膜状结构.［Au(t1关键词： 尺寸效应 纳米复合薄膜 吸收光谱 有效媒质理论}     

掺Ag纳米颗粒的BaTiO3复合薄膜的非线性光学特性

通过准分子激光(XeCl, 308 nm, 20 ns)在MgO(100)单晶衬底上制备了不同掺杂浓度的Ag:BaTiO₃纳米复合薄膜,通过X射线衍射和X射线光电子能谱对薄膜的结构和组分进行了表征.在430 nm和470 nm附近观测到了不同浓度Ag纳米颗粒引起的等离子体吸收峰,通过z扫描技术对复合薄膜的三阶非线性光学特性进行了测量,并对其光学非线性的增强机制进行了讨论. 关键词： 金属纳米复合薄膜 激光沉积 非线性光学     

Te/TeO2-SiO2复合薄膜的吸收和非线性光学特性研究

应用分光光度计测量Te/TeO₂-SiO₂复合薄膜的透射光谱和吸收光谱, 在480nm附近观察到Te颗粒引起的等离子体共振吸收峰; 采用Z扫描技术研究了共振(激发波长为532 nm)和非共振情况下(激发波长1064 nm) 不同电位制备薄膜的Te颗粒状态与复合薄膜的三阶非线性极化率的关系. 基于有效介质理论对复合薄膜的三阶非线性效应进行分析, 研究Te颗粒大小对Te/TeO₂-SiO₂复合薄膜的非线性光学性质的影响及其产生机理. 结果表明薄膜制备过电位增大, Te的粒径减小, 颗粒数量多, 颗粒分布趋于均匀, 使得金属颗粒的表面等离子体共振峰红移, 吸收强度增强, 导致三阶非线性光学效应增强, χ⁽³⁾由1064 nm的5.12×10^-7 esu增大为532 nm的8.11×10^-7 esu. 关键词： 碲 二氧化碲 复合薄膜 三阶非线性     

Surface Plasmon Resonance of Au Nanoparticles Fabricated by Negative Ion Implantation and Grid Structure toward Plasmonic Applications

Optical properties of Au nanoparticle composites and a grid structure of Cu nanoparticle composite were studied. Negative ion implantation was applied to synthesize Au and Cu nanoparticles in amorphous SiO₂ and Al₂O₃. Au nanoparticles were embedded within a depth of 30 nm by 60keV Au⁻ implantation. The surface plasmon resonance (SPR) of Au:SiO₂ and Au: Al₂O₃ composites shifted to red and to blue, respectively, compared to calculated ones by the Mie theory. Optical nonlinearity was measured with pump-probe femtosecond spectroscopy and the transient spectrum of Au: Al₂O₃ composite presented a large red shift from the SPR peak. Image mapping of far-field transmitted intensity of Cu-implanted SiO₂ with a fine grid structure drawn by laser-lithography was observed by a scanning near-field optical microscopy (SNOM) system.     

不同气氛下SiOx纳米线的制备及形貌、红外、光致发光研究

以N₂/H₂、N₂或NH₃为载气,利用碳辅助化学气相沉积法,常压1140℃下在石英衬底上制备了大量直径为20—300 nm,长数百微米的非晶SiO_x纳米线.制备得到的纳米线具有高度定向生长的特性.利用透射电子显微镜、扫描电子显微镜及电子能谱对SiO_x纳米线的形貌及组分进行了分析,Si与O原子之比为1∶18.傅里叶红外吸收谱显示了非晶氧化硅的三个特征峰（482,806和1095 cm^-1）及1132 cm^-1无序氧化硅结构的强吸收峰.SiO_x纳米线光致发光光谱（PL）在440 nm（283 eV）处具有较强的荧光峰;N₂为载气生长的SiO_x纳米线的PL峰强比NH₃为载气生长的SiO_x纳米线峰强大四个数量级. 关键词： x纳米线')" href="#">SiO_x纳米线 碳辅助化学气相沉积法 傅里叶红外吸收 光致发光