聚乳酸与聚丙撑碳酸酯共混体系的性能

采用熔融共混的方法制备了聚乳酸(PLA)/聚丙撑碳酸酯(PPC)共混物。DSC测试结果表明,纯PLA和PPC的玻璃化转变温度分别为54和37℃,不同组成的PLA/PPC共混物有2个明显的玻璃化转变温度,且与纯PLA和PPC的玻璃化转变温度相对应,说明二者是不相容体系。力学测试结果表明,当PPC质量分数超过20%时,可以看到明显的屈服点。共混物在拉伸过程中也有明显的颈缩、应力发白现象,表明随着PPC含量增加,PLA/PPC共混物由典型的脆性断裂向韧性转变。随着PPC含量的增加,共混物模量降低,断裂伸长率增加,当PPC质量分数为50%时,共混物的断裂伸长率达到最大值62%。共混物的粘度可在很宽的范围内予以调控,以满足不同加工的需要。     

聚碳酸1,2-丙二酯/聚琥珀酸丁二酯/邻苯二甲酸二烯丙酯共混体系的研究

采用熔融共混的方法制备了聚碳酸1,2-丙二酯(PPC)/聚琥珀酸丁二酯(PBS)共混物和PPC/PBS/DAOP(邻苯二甲酸二烯丙酯)增塑共混物,对共混物的相容性、热性能、结晶性和物理机械性能进行了初步研究.研究结果表明PPC/PBS共混物为不相容体系,PPC对PBS的结晶度影响很小;PBS的加入提高了共混物的起始热分解温度(Td-5%),当共混物中PBS含量从10%增加到90%时,共混物的Td-5%可分别增加15℃到59℃.DAOP对PPC/PBS共混物有增塑作用,当PPC/PBS/DAOP的比例从30/70/0变化到30/70/30时,共混物玻璃化转变温度(Tg)下降了36.9℃.与PPC/PBS共混物相比,组成优化的DAOP增塑共混物PPC/PBS/DAOP(PPC/PBS/DAOP=30/70/5)的断裂伸长率和断裂能最大可提高31倍和34倍,分别达到655.1%和3.4 J/mm2,因此引入DAOP尽管使共混材料的热稳定性有所下降,但拓宽了PPC/PBS共混材料的使用温度窗口.     

接枝聚乳酸/塑化淀粉共混物的制备与性能研究

为提高聚乳酸(PLA)/淀粉共混物界面作用和降低成本,引入甲基丙烯酸缩水甘油酯(GMA)接枝聚乳酸和塑化淀粉(TPS),通过挤出和注射成型制备接枝聚乳酸/塑化淀粉共混物(PLA-g-GMA/TPS)。红外光谱分析证实,GMA成功接枝到PLA分子链上。对共混物的力学性能、热机械性能、微观形貌、热性能及亲水性等进行了系统研究,结果表明,选择GMA用量为6%(接枝率为1.51%)和TPS用量为10%时的拉伸强度、断裂伸长率及弹性模量最佳,分别为42.6MPa、8.9%及260MPa。FE-SEM观察结果表明,低含量TPS中颗粒被基体包覆或嵌入,界面平整,界面结合力强。DMA和DSC结果显示,不同质量配比的PLA-g-6%GMA/TPS共混物的Tg、储存模量、结晶度、结晶温度及熔融温度仅在小范围内发生变化。吸水率和接触角结果表明,低含量TPS的共混物吸水率和接触角变化幅度均小于高含量TPS体系。     

PVA/HDPE/HDPE-g-MAH共混物的相形貌与动态流变性能

采用熔融共混法制备了聚乙烯醇(PVA)/高密度聚乙烯(HDPE)共混物,引入马来酸酐接枝高密度聚乙烯(HDPE-g-MAH)对体系进行增容。利用SEM、小振幅震荡剪切、溶剂提取、拉伸测试考察组成和增容剂含量对共混物相形貌、动态流变性质、相连续性和力学性能的影响。结果表明,当HDPE质量分数达到20%~30%时,PVA/HDPE/HDPE-g-MAH共混物呈现接近共连续的结构;储能模量-频率图中观察到较为明显的第二平台;PVA相的连续度达到98%;共混物的断裂伸长率由5%显著提高到25%左右。另外,当HDPE-g-MAH的含量增大时,共混物的相界面变得模糊,力学性能也随之提高。     

共混方法对聚氯乙烯/聚丙撑碳酸酯相容性影响

本文分别用溶液法和熔融法制得聚氯乙烯（PVC）与聚丙撑碳酸酯（PPC）共混试样，用DSC证明PVC／PPC共混物不相容，但它们不相容的程度受分子量、共混比例等因素的影响，并根据玻璃化转变温度（Tg）计算出溶液共混试样PPC富相中PVC的重量百分含量。NBR／PPC弹性体作偶联剂对PVC／PPC共混体系具有较好的增容作用，共混物中PPC的用量及分子量对共混体系性能有一定的影响。     

CaSO_4纳米晶须对PBT-PE-液晶离聚物杂化材料形态结构与力学性能的影响

通过熔融共混法将CaSO4纳米晶须和含磺酸离子的液晶离聚物(LCI)与聚对苯二甲酸丁二醇酯-聚乙烯(PBT-PE),制成PBT-PE-LCI-CaSO4纳米晶须杂化材料。通过DSC、红外图像系统分析和拉伸试验对共混体系的热性能、形态结构和力学性能进行了研究。结果表明:在共混体系中加入LCI提高了体系中PE的结晶温度和结晶度,并且LCI包裹着CaSO4纳米晶须,分散相PE均匀地分散在PBT基体中;当基体与CaSO4纳米晶须的质量比为100∶3时,杂化材料的力学性能最好。     

线性聚酯酰胺对聚碳酸亚丙酯的改性

通过己内酯和氨基己酸开环、缩合反应制备了酯段含量为81%的线性聚酯酰胺（PEA）,并用熔融共混的方法制备了PEA/聚碳酸亚丙酯（PPC）共混物,考察了PEA的引入对共混体系相容性、热力学稳定性和机械性能的影响。 结果表明,PEA与PPC之间有较好的相容性,共混物的热力学稳定性比PPC有显著提高,当PEA质量分数为3%时,共混体系的起始分解温度（T-5%）和最大分解速率时的温度（Tmax）比PPC分别提高了52.7%和46.4%。 通过调节PEA的含量可以使共混体系同时达到增强和增韧的效果。     

氯化聚丙撑碳酸酯增容聚丙撑碳酸酯/秸秆粉复合材料的制备及性能

聚丙撑碳酸酯(PPC)是一种新型热塑性生物降解材料,但其热性能及力学性能较差,应用受到限制。以秸秆粉这种农作物副产品作为增强体改性PPC,既可以提高PPC的力学性能同时又可开发利用秸秆资源。氯化聚丙撑碳酸酯(CPPC)是聚丙撑碳酸酯(PPC)经过氯化得到的,对天然纤维表面具有良好的浸润性和粘结性。本文以CPPC为增容剂,通过熔融共混法制备了PPC/秸秆粉复合材料。采用扫描电子显微镜(SEM)、拉伸实验、动态力学性能测试(DMA)及转矩流变仪对复合材料的结构及性能进行了表征,重点考察了CPPC的添加量对复合材料力学和流变性能的影响。结果表明,当CPPC质量分数为1.8%时,可使添加质量分数为30%秸秆粉的PPC复合材料拉伸强度提高38%,模量提高30%。同时,CPPC的引入使复合材料的粘度下降,改善了PPC/秸秆粉复合材料的加工性能。因此,作为增容剂的CPPC为制备高性能PPC/天然纤维复合材料提供了新的解决办法。     

MMA接枝改性PVC/CaCO3纳米复合材料的力学性能

采用熔融共混法制备PMMA接枝改性纳米CaCO3增韧PVC（PVC/CaCO3）复合材料,并研究了复合材料的力学性能.结果表明,通过表面PMMA的接枝改性,可以显著提高纳米CaCO3增韧聚氯乙烯复合材料的拉伸强度和拉伸模量,在纳米CaCO3颗粒表面PMMA包覆层厚度为2nm时,复合材料的拉伸强度和拉伸模量达到极大值.对比于未处理纳米CaCO3和钛酸酯偶联剂处理纳米CaCO3,PMMA接枝改性纳米CaCO3增韧PVC复合材料的拉伸强度得到较大幅度提高.SEM显示,经过PMMA接枝改性后的碳酸钙在PVC基体中分散均匀,与基体界面结合良好.     

相分离对聚偏氟乙烯/聚甲基丙烯酸甲酯共混物的力学与耐紫外老化性能的影响

采用熔融共混法制备聚偏氟乙烯/聚甲基丙烯酸甲酯( PVDF/PMMA)共混物,考察其力学性能、耐紫外老化性能、熔体动态流变、结晶与热分解行为.PMMA含量(wPMMA)为10 wt％时,共混物形成均相结构,力学与耐老化性能最好.wPMMA≥20 wt％时,PMMA形成球状聚集体,共混物力学性能与耐候性显著降低.PMMA的存在可提高PVDF的结晶度,降低熔融温度,但不改变PVDF晶体结构.     

Thermal,mechanical and rheological properties of biodegradable poly(propylene carbonate) and poly(butylene carbonate) blends

Poly(propylene carbonate)(PPC) was melt blended in a batch mixer with poly(butylene carbonate)(PBC) in an effort to improve the toughness of the PPC without compromising its biodegradability and biocompatibility. DMA results showed that the PPC/PBC blends were an immiscible two-phase system. With the increase in PBC content, the PPC/PBC blends showed decreased tensile strength, however, the elongation at break was increased to 230% for the 50/50 PPC/PBC blend. From the tensile strength experiments, the Pukanszky model gave credit to the modest interfacial adhesion between PPC and PBC, although PPC/PBC was immscible. The impact strength increased significantly which indicated the toughening effects of the PBC on PPC. SEM examination showed that cavitation and shear yielding were the major toughening mechanisms in the blends subjected the impact tests. TGA measurements showed that the thermal stability of PPC decreased with the incorporation of PBC. Rheological investigation demonstrated that the addition of PBC reduced the value of storage modulus, loss modulus and complex viscosity of the PPC/PBC blends to some extent. Moreover, the addition of PBC was found to increase the processability of PPC in extrusion. The introduction of PBC provided an efficient and novel toughened method to extend the application area of PPC.     

Mechanical,thermal and rheological properties and morphology of poly (lactic acid)/poly (propylene carbonate) blends prepared by vane extruder

In this study, the poly (lactic acid) (PLA) and poly (propylene carbonate) (PPC) blends with different compositions were prepared by a novel vane extruder based on elongation rheology. The mechanical properties, morphologies, crystallization behavior, thermal stability, and rheological properties of the blends were investigated. Mechanical test showed that PLA could be toughened by PPC to some extent, and the impact strength of the PLA was maximized when PPC content was about 30%. Differential scanning calorimetry analysis revealed that PPC had little effect on the melting process, the crystallization behavior of PLA component in the blend was improved, and the cold crystallizability of PLA decreased with the increase of PPC content when the PPC content was less than 50%. Thermogravimetry analysis showed that the thermal stability of the blends was improved by compounding with PLA. Scanning electron microscope showed that the dispersion of PLA droplets in PPC matrix was better than that of PPC droplets in PLA matrix. Rheological test showed that the melt viscosity of the pure PLA and the blend with 10% PPC was insensitive to shear rate, and the blends melt appeared shear thinning phenomenon with the increase of PPC content. It also showed that the blends microstructure changed with the addition of PPC and the blends with PPC content in a certain range had similar stress relaxation mechanism. Copyright © 2016 John Wiley & Sons, Ltd.     

Effect of poly(vinyl acetate) (PVAc) on thermal behavior and mechanical properties of poly(3-hydroxybutyrate)/poly(propylene carbonate) (PHB/PPC) blends

To assess the compatibility of blends of synthetic poly(propylene carbonate) (PPC), with a natural bacterial poly(3-hydroxybutyrate) (PHB), a simple casting procedure of blend was used. poly(3-hydroxybutyrate)/poly(propylene carbonate) blends are found to be incompatible according to DSC and DMA analysis. In order to improve the compatibility and mechanical properties of PHB/PPC blends, poly(vinyl acetate) (PVAc) was added as a compatibilizer. The effects of PVAc on the thermal behavior, morphology, and mechanical properties of 70PHB/30PPC blend were investigated. The results show that the melting point and the crystallization temperature of PHB in blends decrease with the increase of PVAc content in blends, the loss factor changes from two separate peaks of 70PHB/30PPC blend to one peak of 70PHB/30PPC/12PVAc blend. It is also found that adding PVAc into 70PHB/30PPC blend can decrease the size of dispersed phase from morphology analysis. The result of tensile properties shows that PVAc can increase the tensile strength and Young’s modulus of 70PHB/30PPC blend, and both the elongation at break and the tensile toughness increase significantly with PVAc added into 70PHB/30PPC.     

离子液体/乙烯-醋酸乙烯共聚物复合材料的制备与性能

分别将离子液体三正丁基甲铵(双三氟甲磺酰)亚胺盐([TBMA][NTf₂])和1-乙基-3-甲基咪唑四氟硼酸盐([EMIM][BF₄])与乙烯-醋酸乙烯共聚物弹性体(EVM)熔融共混制备复合材料,研究了离子液体与EVM的相容性及抗静电性能。 样品宏观透明性和SEM测试结果显示,[TBMA][NTf₂]与EVM具有较好的相容性,相应的EVM/[TBMA][NTf₂]复合材料的抗静电效果更好;热重分析(TGA)结果表明,[TBMA][NTf₂]促进EVM热解,而[EMIM][BF₄]对EVM的热稳定影响较小。 室温下在EVM中填加[TBMA][NTf₂]的共混物表现出较好的柔性,当[TBMA][NTf₂]质量分数为20%时,EVM/[TBMA][NTf₂]复合材料的模量为0.58 MPa,断裂伸长率可达到2997%。     

Thermal,Rheological and Mechanical Properties of Biodegradable Poly(propylene carbonate)/Epoxidized Soybean Oil Blends

Biodegradable poly(propylene carbonate)(PPC)/epoxidized soybean oil(ESO) blends with different component ratios were prepared by melt blending to improve the performance of PPC. The phase morphology, thermal properties, rheological properties and mechanical properties of the blends were investigated in detail. SEM examination revealed good interfacial adhesion between PPC matrix and ESO.According to DSC and DMA, as the content of ESO increased, the glass transition temperature of the PPC compone...     

MISCIBILITY, CRYSTALLIZATION AND MECHANICAL PROPERTIES OF PPC/PBS BLENDS

In this paper,melt blends of poly(propylene carbonate)(PPC)with poly(butylene succinate)(PBS)were characterized by dynamic mechanical analysis(DMA),differential scanning calorimetry(DSC),tensile testing,wide-angle X-ray diffraction(WAXD),polarized optical microscopy and thermogravimetric analysis(TGA).The results indicated that the glass transition temperature of PPC in the 90/10 PPC/PBS blend was decreased by about 11K comparing with that of pure PPC.The presence of 10% PBS was partially miscible with PPC.The 90/10 PPC/PBS blend had better impact ==========and tensile strength than those of the other PPC/PBS blends.The glass transition temperature of PPC in the 80/20,70/30,and 60/40 PPC/PBS blends was improved by about 4.9 K,4.2 K,and 13 K comparing with that of pure PPC,respectively;which indicated the immiscibility between PPC and PBS.The DSC results indicated that the crystallization of PBS became more difficult when the PPC content increased.The matrix of PPC hindered the crystallization process of PBS.While the content of PBS was above 20%,significant crystallization-induced phase separation was observed by polarized optical microscopy. It was found from the WAXD analysis that the crystal structure of PBS did not change,and the degree of crystallinity increased with increasing PBS content in the PPC/PBS blends.     

Preparation and properties of luffa fiber- and kenaf fiber-filled poly(butylene succinate-co-lactate)/starch blend-based biocomposites

Biodegradable poly(butylene succinate-co-lactate) (PBSL)/starch blends that contain various amounts of starch were prepared. In addition, luffa fiber (LF) and kenaf fiber (KF) were incorporated, individually, into PBSL/starch (70/30) blend to achieve biocomposites. The LF and KF were treated with NaOH_(aq) prior to their addition to the blend. The Young's modulus and flexural modulus of PBSL increased with the addition of starch and increased further after the formation of the biocomposites. The highest Young's modulus increment, which was found in the KF-added system, was up to a 2.2-fold increase compared with neat PBSL. The tensile/flexural/impact strength of PBSL declined after the formation of the blends. With the further addition of LF/KF, the said properties leveled off. The blends exhibited higher complex viscosity and dynamic storage modulus in the melt state than the neat PBSL, and the values further increased in the biocomposites. The crystallization temperature of PBSL slightly decreased in the blends. By contrast, the biocomposites showed an increment in PBSL crystallization temperature, from 73.0 °C (PBSL) to 75.3 °C (KF-added composite), thereby confirming the surface nucleation effect of LF/KF. The blends showed a higher degree of water absorption than PBSL. The formation of biocomposites led to an even higher degree of water absorption. The current approach of including LF/KF in the PBSL/starch blend to enhance the rigidity and biodegradability was advantageous in expanding the applications of PBSL.     

Thermal,Mechanical and Rheological Properties of Eco-friendly Poly（propylene carbonate）/Poly（1,2-propylene succinate） Blends

In order to improve the flexibility of poly（propylene carbonate） （PPC）, poly（1,2-propylene succinate） （PPSu） was used to plasticize PPC in a batch mixer. The effects of PPSu on the miscibility, thermal stability, mechanical and theological properties of the blends were investigated. PPC was partially miscible with PPSu. It was demonstrated that PPSu decreased the glass transition temperature and melt viscosity of PPC, as shown in the DSC and rheological curves. With the increase in PPSu content, the PPC/PPSu blends showed decreased tensile strength, however, the elongation at break was increased to 1100% for the 70/30 PPC/PPSu blend. The introduction of PPSu provided an efficient and novel plasticization method to extend the application area of PPC.     

脂肪族聚碳酸酯(PPC)与聚乳酸(PLA)共混型生物降解材料的热学性能、力学性能和生物降解性研究

通过溶液浇铸法制备了脂肪族聚碳酸酯与聚乳酸的共混物(PPC/PLA).采用示差热分析(DSC)和热重分析(TG)研究了材料的热性能.采用拉伸力学试验研究了共混物的力学性能.通过土壤悬浊拟环境培养降解实验法和扫描电子显微镜分析(SEM)对共混材料的生物降解性能进行了研究.实验结果表明,随着PPC含量的增加,共混物的拉伸强度和杨氏模量降低,而生物降解速率却显著提高.但是,在一定的降解时间内,某些比例共混物的降解速率比100%PPC还要快.综合分析表明,PPC/PLA是力学性能和降解性能可以互补的共混体系.