A red-emitting Ca8MgLa(PO4)7:Ce3+,Mn2+ phosphor for UV-based white LEDs application

Ca(8)MgLa(PO(4))(7):Ce(3+),Mn(2+) phosphors have been prepared by a conventional solid state reaction under a weak reductive atmosphere. The crystal structure and photoluminescent properties were investigated. It was found that the red emission at 640nm originated from the (4)T(1)((4)G)→(6)A(1)((6)S) transition of Mn(2+) increases dramatically by a factor of 6.4 with the optimum Ce(3+) co-doping. The energy transfer from Ce(3+) to Mn(2+) was proposed to be resonance-type via an electric dipole-dipole mechanism and the energy transfer efficiency was also calculated by the relative emission intensity. With the broadband ultraviolet (UV) absorption of Ce(3+) and the suitable color coordinates, Ca(8)MgLa(PO(4))(7):Ce(3+),Mn(2+) phosphors might be a promising candidate as red phosphors in the field of UV-based white light-emitting diodes.     

Novel yellow-emitting Sr8MgLn(PO4)7:Eu2+ (Ln=Y, La) phosphors for applications in white LEDs with excellent color rendering index

Eu(2+)-activated Sr(8)MgY(PO(4))(7) and Sr(8)MgLa(PO(4))(7) yellow-emitting phosphors were successfully synthesized by solid-state reactions for applications in excellent color rendering index white light-emitting diodes (LEDs). The excitation and reflectance spectra of these phosphors show broad band excitation and absorption in the 250-450 nm near-ultraviolet region, which is ascribed to the 4f(7) → 4f(6)5d(1) transitions of Eu(2+). Therefore, these phosphors meet the application requirements for near-UV LED chips. Upon excitation at 400 nm, the Sr(8)MgY(PO(4))(7):Eu(2+) and Sr(8)MgLa(PO(4))(7):Eu(2+) phosphors exhibit strong yellow emissions centered at 518, 610, and 611 nm with better thermal stability than (Ba,Sr)(2)SiO(4) (570 nm) commodity phosphors. The composition-optimized concentrations of Eu(2+) in Sr(8)MgLa(PO(4))(7):Eu(2+) and Sr(8)MgY(PO(4))(7):Eu(2+) phosphors were determined to be 0.01 and 0.03 mol, respectively. A warm white-light near-UV LED was fabricated using a near-UV 400 nm chip pumped by a phosphor blend of blue-emitting BaMgAl(10)O(17):Eu(2+) and yellow-emitting Sr(8)MgY(PO(4))(7):0.01Eu(2+) or Sr(8)MgLa(PO(4))(7):0.03Eu(2+), driven by a 350 mA current. The Sr(8)MgY(PO(4))(7):0.01Eu(2+) and Sr(8)MgLa(PO(4))(7):0.03Eu(2+) containing LEDs produced a white light with Commission International de I'Eclairage (CIE) chromaticity coordinates of (0.348, 0.357) and (0.365, 0.328), warm correlated color temperatures of 4705 and 4100 K, and excellent color rendering indices of 95.375 and 91.75, respectively.