Summary: Polystyrene nanosize particles have been synthesized by a differential microemulsion polymerization process involving the use of a small amount of poly(methyl methacrylate) as the seeds. Sodium dodecyl sulfate and ammonium persulfate were used as the surfactant and initiator, respectively. The effects of various reaction conditions on the particle size have been investigated. Particle sizes of less than 20 nm have been achieved at milder conditions than those previously reported in the literature.
An amphiphilic biodegradable polymer, poly(aspartic acid‐co‐lactic acid) (PAL), was synthesized by simply heating a mixture of aspartic acid (Asp) and L ‐lactide without additional catalysts or solvents. The unique branched architecture comprising succinimide units and lactic acid units was confirmed by IR and NMR spectroscopy. A copolymer of sodium aspartate and lactic acid (PALNa) was prepared by reacting PAL with an aqueous sodium hydroxide solution. The PAL was soluble in many organic solvents, while the PALNa was soluble in methanol and water. The hydrolytic degradation behavior of PAL varied with the copolymer composition. A higher Asp content resulted in a faster molecular weight decrease, and introducing glycolic acid units accelerated the degradation rate.
New examples for the monomer-isomerization polymerizations of some branched internal olefins, 4-methyl-2-pentene and 4-phenyl-2-butene, are presented. When these olefins are polymerized with A1(C2 H5)3-TiCl3 ([TiCl3] = 120 mmole/liter, A1/Ti = 3.0) catalyst at 80°C, considerable amounts of high polymers [27.5%/60 hr ([η] = 0.68 d1/g) and 35.6%/100hr, respectively] were obtained. From the additional fact that the isomerization from these 2-olefins to the mixture of their positional isomers including 1-olefins was observed during the polymerization, it is assumed that the polymerizations from these 2-olefins are performed with the 1-olefins which isomerized from the starting 2-olefins. 相似文献
Stereocomplexes formed in atactic poly(methyl methacrylate) (a-PMMA) films cast form different solvents were studied by means of Fourier transform infrared spectroscopy (FTIR), and differential scanning calorimetry (DSC). The growth of stereocomplex was a function of annealing temperature and annealing time, respectively. 相似文献
Poly(n-butyl acrylate-co-methyl methacrylate) particles encapsulated with chitosan were synthesized at 1:1 monomer ratio using potassium persulfate as an initiator. Effect of concentration and molecular weight of chitosan on particle encapsulation process was investigated. Chitosan concentration was varied from 0.5%, 1%, and 1.5% w/v, while molecular weights were 120, 370, and 850 kDa, respectively. The results showed that the particle diameter of the copolymer particles with chitosan encapsulation was increased when the concentration and molecular weight of chitosan were increased. The average particle size and zeta potential were obtained in a range of 144–625 nm and +27 – +47 mV, respectively. TEM micrographs suggested a presence of the chitosan encapsulation layer on the particles. 相似文献
Poly(methyl methacrylate) nanosize particles were synthesized by a differential microemulsion polymerization process. Sodium dodecylsulfate and ammonium persulfate were used as the surfactant and initiator, respectively. The effects of reaction conditions on the particle size have been investigated. A particle size of less than 20 nm in diameter has been achieved with surfactant/monomer and surfactant/water weight ratios of 1:18 and 1:120, i.e. much milder conditions than those previously reported in the literature.
TEM image of nanoparticles prepared via differential microemulsion polymerization. 相似文献
An approach to the synthesis of highly branched vinyl copolymers containing thiol and C=C crosslinking groups is proposed. This method was exemplified by the emulsion copolymerization of methyl methacrylate (MMA) and 1,6-hexanediol diacrylate (HDDA) with 2-mercaptoethyl sulfide (MES) as chain transfer agent at 70°C with 4,4′-azobis(4-cyanovaleric acid) (ACVA) as the initiator. The resulting highly branched copolymers contain both thiol and acryloyl groups. The apparent Mw (by SEC) of the resulting copolymers increased with increasing ACVA concentration, whereas the pendent acryloyl and -SH groups decreased from 6.4% to 0.8% (relative to MMA units) and 45 ×10?5 to 5 × 10?5 mol/g, respectively. The copolymers of MMA could be self-crosslinked thermally or by exposure to UV irradiation. The gel fraction of the thermally treated samples decreased from 46% to 7.2%, with the increasing of ACVA in the polymer synthesis, while the gel fraction of UV irradiated samples changed only slightly around 70%. 相似文献