DIBUTYLTIN DILAURATE-CATALYZED DIISOCYANATE COUPLING—GRAFTING OF POLY(ETHYLENE GLYCOL) ONTO NANO-SILICA SURFACE THROUGH A ONE-STEP PROCEDURE

Grafting polymer glycols onto nano-silica surface through one-step procedure was investigated. The major characteristic of this procedure is that all the materials and reagents (silica, PEG, TDI, DBTDL, solvent) required for grafting were added simultaneously into the reaction vessel. TDI and DBTDL were used as coupling agent and catalyst, respectively.The products were characterized by FTIR, TGA, elemental analyses and TEM, giving evidence for successful grafting of PEG. Possible mechanism of this grafting was studied and two grafting processes were proposed. The process through which the grafting proceeds depends on the reaction temperature. Effect of molecular weight of PEG on grafting was also investigated.     

SURFACE MODIFICATION OF POLYMERS

The principal objectives and methods of surface modification of polymers are reviewed inthis paper. The methods covered include physical, chemical, mechanical and biological.     

DIBUTYLTIN DILAURATE-CATALYZED DIISOCYANATE COUPLING- GRAFTING OF POLY(ETHYLENE GLYCOL) ONTO NANO-SILICA SURFACE THROUGH A ONE-STEP PROCEDURE

Grafting polymer glycols onto nano-silica surface through one-step procedure was investigated. The major characteristic of this procedure is that all the materials and reagents (silica, PEG, TDI, DBTDL, solvent) required for grafting were added simultaneously into the reaction vessel. TDI and DBTDL were used as coupling agent and catalyst, respectively.The products were characterized by FTIR, TGA, elemental analyses and TEM, giving evidence for successful grafting of PEG. Possible mechanism of this grafting was studied and two grafting processes were proposed. The process through which the grafting proceeds depends on the reaction temperature. Effect of molecular weight of PEG on grafting was also investigated.     

纳米微晶纤维素表面改性研究

分别对纳米微晶纤维素(NCC)的表面进行醋酸酯化、羟乙基化和羟丙基化改性,利用FT-IR、TEM、13C-NMR、TGA对改性产物进行表征,研究不同的表面改性方法对纳米微晶纤维素性能的影响.结果表明,利用这几种方法改性后的NCC,经干燥后都可以重新分散在适当的溶剂中,且颗粒粒径没有明显变化,但不同改性产物的热性能有所差异.     

SURFACE MODIFICATION OF POLYPROPYLENE MICROPOROUS MEMBRANE BY TETHERING POLYPEPTIDES

Two kinds of polypeptides were tethered onto the surface of polypropylene microporous membrane （PPMM） through a ring opening polymerization of L-glutamate N-carboxyanhydride initiated by amino groups which were introduced by ammonia plasma and y-aminopropyl triethanoxysilane treatments. X-ray photoelectron spectroscopy （XPS）, attenuated total reflectance Fourier transform infrared spectroscopy （FT-IR/ATR）, scanning electron microscopy （SEM）, together with water contact angle measurements were used to characterize the modified membranes. XPS analyses and FT-IR/ATR spectra demonstrated that polypeptides are actually grafted onto the membrane surface. The wettability of the membrane surface increases at first and then decreases with the increase in grafting degrees of polypeptide. Platelet adhesion and murine macrophage attachment experiments reveal an enhanced hemocompatibility for the polypeptide modified PPMMs. All these results give evidence that polypeptide grafting can simultaneously improve the hemocompatibility as well as reserve the hydrophobicity for the membrane, which will provide a potential approach to improve the performance of polypropylene hollow fiber microporous membrane used in artificial oxygenator.     

超临界二氧化碳体系中PVDF微孔膜的表面接枝改性

超临界二氧化碳（SCCO2）是一种T〉31．1℃,P〉7．38MPa的二氧化碳流体,不仅具有类似于气体的粘度和类似于液体的密度,而且可以通过改变温度或压力控制SCCO2的密度及溶解性．SCCO2对有机小分子具有优良的溶解、扩散和渗透性能,化学惰性,无污染,易于分离,作为一种聚合反应介质,受到学术界日益增多重视．SCCO2极低的粘度使其具有良好的流动性和扩散渗透性能,零表面张力使其对聚合物具有良好的润湿和增塑性,这将促进引发剂和聚合单体向微孔膜的外表面及内表面扩散．利用温度和压力改变SCCO2的溶解性能调整单体在聚合物相和SCCO2相之间的分布,进而控制微孔膜内外表面的接枝程度．所以SCCO2接枝聚合反应对于聚合物膜的表面改性具有极其重要的意义．     

聚苯乙烯大单体与丙烯酸酯接枝共聚物对聚苯乙烯表面的改性研究

研究了由大单体技术合成的侧链为聚苯乙烯、骨架由丙烯酸丁酯或甲基丙烯酸羟乙酯/丙烯酸丁酯组成的接枝共聚物对聚苯乙烯的表面改性效果(试样浇注于玻璃纸上成膜)。发现仅添加0.5wt％的接枝共聚物就可完全改变聚苯乙烯膜两面的临界表面张力γ-c与表面能中的色散力部份γ_s~D,少量添加的接枝共聚物在改性聚苯乙烯膜的两面呈现出明显的表面富集现象。虽然两类接枝共聚物的极性有较大的差异,但改性聚苯乙烯成膜后的自由表面均显示出与聚丙烯酸丁酯相同的低表面能(γ_s~D=37×10~(-3)牛顿·米~(-1)),而添加三元接枝共聚物的改性膜与玻璃纸接触的表面却具有高于聚苯乙烯的表面能|(γ_s~D=54×10(-3)牛顿·米~(-1))。这种改性膜的两面具有不同的表面能是由于接枝共聚物中不同的组分在膜的两面富集所致,已通过ESCA的表面测试结果证实,并与按Gibbs吸附式的计算值相符。     

硬脂酸表面改性碳酸钙粉末的热分析及其表面性质变化

硬脂酸表面改性碳酸钙粉末的热分析及其表面性质变化李新军廖景发＊瞿龙＊吕海波（中南工业大学粉末冶金研究所＊化学系长沙４１００８３）关键词表面改性热分析碳酸钙粉末表面性质硬脂酸中图分类号Ｏ６２３．６１１，Ｏ６４７．２碳酸钙粉末是一种重要的无机化工产品，广...     

SYNTHESIS OF AMPHIPHILIC COMB-SHAPED COPOLYMERS USED FOR SURFACE MODIFICATION OF PVDF MEMBRANES

The synthesis of a novel amphiphilic comb-shaped copolymer consisting of a main chain of styrene-(N-(4- hydroxyphenyl) maleimide)(SHMI) copolymer and poly(ethylene glycol) methyl ether methacrylate(PEGMA) side groups was achieved by atom transfer radical polymerization(ATRP).The amphiphilic copolymers were characterized by ~1H-NMR, Fourier transform infrared(FTIR) spectroscopy and gel permeation chromatography(GPC).From thermogravimetric analysis (TGA),the decomposition temperature of SHMI-g-PEGMA is low...     

SURFACE MODIFICATION OF POLYPROPYLENE MICROPOROUS MEMBRANES BY THE ADSORPTION OF NON-IONIC SURFACTANTS

Surface modification by physical adsorption of a series of non-ionic surfactants including Tween 20, Tween 40, Tween 60, Tween 80 and Tween 85, was accomplished on polypropylene microporous hollow fiber and flat membranes. The adsorption curve of the membrane surface was analyzed by weight measurements and the typical results showed a twoplatform character similarly. Differences in the degree and curve shape of adsorption resulting from such factors as concentration, temperature, as well as water cleaning time were observed for Tween 85 among other Tweens. Attenuated total reflection - Fourier transform infrared spectroscopy analysis and field emission scanning electron microscopy observation showed that the adsorption of Tween on polypropylene microporous membrane （PPMM） is effective and occurs mainly in the pores of PPMMs at low adsorption amount, and on the membrane surface also at high adsorption value.     

A REVIEW OF OXYGEN-CONTAINING SURFACE GROUPS AND SURFACE MODIFICATION OF ACTIVATED CARBON

This review focused on the recent reports related to the function, characterization and modification of axygen-containing surface groups of activated carbon (AC). The Oxygen-containing surface groups were briefly described, and the most frequently used techniques for characterization of the oxygen-containing surface groups on .ACs were also briefly stated .4 detailed discussion of the effects of the oxygen-containing snrface groups on the adsorptive capacity of .4C was given. The recent progresses in modification of the oxygen-containing surface groups of AC were also reviewed     

A REVIEW OF OXYGEN-CONTAINING SURFACE GROUPS AND SURFACE MODIFICATION OF ACTIVATED CARBON

1. INTRODUCTION Activated carbons (ACs) have been widely used as adsorbents in environmental protection, e.g. removing organic or inorganic pollutants from liquid effluents and voltaic organic compounds (VOCs) from polluted air. It has been well known that the adsorptive capacity of ACs is not only determined by its textural properties (e.g. specific surface area, pore size distribution, pore volume), but also related to its surface chemistry. Many studies have demonstrated that the ad…     

采用层层自组装与光化学修饰法在聚氨酯表面固定生物多糖衍生物

采用层层自组装技术与光化学修饰方法相结合在聚氨酯材料表面固定生物多糖衍生物,首先合成具有光反应活性的叠氮壳聚糖,再在聚氨酯基材表面进行叠氮壳聚糖与香菇多糖硫酸酯的层层自组装,然后通过光化学反应对自组装多层膜修饰层进行交联,制备得到生物多糖衍生物层层自组装与光化学表面修饰的聚氨酯材料.通过红外光谱、X射线光电子能谱、水接触角测量仪、抗菌活性测试、溶血试验和血小板黏附测试等方法对被修饰聚氨酯材料的表面性能和生物性能进行了分析,测试结果表明修饰后的聚氨酯材料表面的亲水性和血液相容性得到改善,并且被修饰材料对大肠杆菌具有良好的抑制效果.     

羊毛表面改性对拒水拒油整理的作用及机理研究

应用扫描电镜(SEM)、X射线光电子能谱(XPS)和衰减全反射红外光谱(FTIR-ATR)等现代表面分析技术研究不同改性处理羊毛表面的化学和物理结构特性.SEM研究结果表明,经低温等离子体表面改性或特定化学改性后的羊毛鳞片表面呈现纳米尺度的沟槽和凹凸结构,应用Wenzel公式和Cassie and Baxter公式阐述了表面粗糙度与接触角的关系,揭示了羊毛表面改性对于提高拒水拒油整理效果的原因所在.XPS和FTIR-ATR研究表明,上述物理和化学的表面改性技术使羊毛表面的二硫键氧化断裂和表面类脂物质改性/除去,促进拒水拒油整理剂的吸附和固着.表面改性和拒水拒油整理的协同效应赋予羊毛类荷叶效应,使其呈现超级拒水拒油拒污功能.     

SURFACE MODIFICATION OF CaCO_3 WITH DENDRITIC CARBOXYLIC ACIDS

Nanometer calcium carbonate was modified with Frechet type polyether dendrons bearing a COOH group at thefocal point by a wet-coating technique in dichloromethane at room temperature. The interaction between CaCO_3 and thedendritic modifier was proven by IR and mass spectroscopy of the modified CaCO_3 after thorough extraction withdichloromethane. The amount of tightly bonded organic modifier was estimated by TGA. It was shown that the amount ofbonded molecules decreased with increasing generation number due to the larger number of branches. Compared tounmodified CaCO_3, the modified CaCO_3 possess different dispersibility in water and in organic solvents.     

GRAFTING OF SULFOBETAINE ONTO A POLYURETHANE SURFACE TO IMPROVE BLOOD COMPATIBILITY

On the molecular level, it is believed that polymers containing zwitterionic structures should be compatible withblood. In this work polyurethane films were grafted with sulfobetaine by a three-step procedure. In the first step, the films'surfaces were treated with hexamethylene diisocyanate (HDI) in toluene at 50℃ in the presence of di-n-butyl tin dilaurate(DBTDL) as a catalyst. The extent of the reaction was monitored by ATR-IR spectra; a maximum number of free NCOgroups was obtained after a reaction time of 90 min. In the second step, the hydroxyl groups of N,N-dimethylethylethanolamine (DMEA) were allowed to react in toluene with NCO groups bound on the surface. In the thirdstep, sulfobetaines were formed on the surface through the ring-opening reaction between tertiary amine of DMEA and 1,3-propanesultone (PS). The surfaces of the films were characterized by ATR-IR and XPS showing that the grafted surfaceswere composed of sulfobetaine. The results of the contact angle measurement show that the surface was strongly hydrophilic.The platelet adhesion test demonstrated that the films grafted with sulfobetaine have excellent blood compatibility.     

顺丁橡胶膜的卤代烷等离子体表面改性及其气体透过性能

本研究采用CF_2Cl_2、CF_2ClCF_2Cl及CF_4等离子体对顺丁橡胶膜表面进行了改性,改性后的复合膜用SEM、水的静态接触角以及XPS进行了表征,并测定了膜的气体透过性能。     

用表面处理法降低TiO2粉末光活性问题的研究

本工作采用了两种简便的方法即用不同金属盐和金属氧化物对两种晶型(锐钛矿型和金虹石型)TiO₂粉末进行表面处理来降低TiO₂的光活性并对两种表面处理方法的优缺点作了比较,在评价TiO₂光活性时采用异丙醇光氧化反应的方法。实验证明,用金属盐表面处理TiO₂,其光活性有明显降低。用金属氧化物对TiO₂进行表面处理,在氧化物/TiO₂比例适当时也可以得到与金属盐表面处理TiO₂的同样效果。此外,我们还对TiO₂表面处理后能降低其光活性的作用机制问题进行了讨论。     

STUDY ON THE SURFACE MODIFICATION OF NANO-TiO2 BY GRAFTING PMMA／PBMA AND ITS THERMAL STABILITY

The surface of nano-TiO2 was encapsulated with hydroxyl-propyl-methyl cellulose (HPMC), and then cografted with acrylates. Conditions of absorbing and grafting have been studied. Modified nano-TiO2 particles were characterized by FT-IR spectra, TEM and TG analysis. It was convinced from FT-IR studies that both methyl methacrylate (MMA) and butylmethacrylate (BMA) were co-grafted onto the surface of nano-TiO2 particles. TEM images show that the surface of nano-TiO2 particles was successfully modified by a thick layer of film-like polymer. TG results demonstrate that the decomposition temperature of HPMC-g-PMMA/PBMA, which has been grafted onto the surface of nano-TiO2, is 56.9 K higher than that of HPMC-g-PMMA/PBMA.     

种子乳胶粒表面修饰法制备核壳结构PSt/TiO_2复合微球

首先采用无皂乳液聚合法合成了表面带负电荷、粒径为360 nm的单分散聚苯乙烯(PSt)乳液,并利用聚乙烯亚胺(PEI)在25℃下对PSt乳胶粒表面进行修饰,得到了表面带有正电荷的PSt种子乳液;然后以乙醇和水的混合物为反应介质,采用种子乳液加入法,使钛酸正丁酯(TBT)在修饰后的乳胶粒表面进行水解与缩合,制备出了核壳结构PSt/TiO2复合微球,利用电镜对复合微球的结构形态进行了表征.结果表明,PSt乳液改性时体系的zeta电位随着PEI用量的增加而升高,当PEI用量为PSt聚合物重量的15%时,体系的zeta电位从原来的-40.3 mV升高到了38.3 mV,达到对PSt乳胶粒表面改性的最佳值;在制备PSt/TiO2复合微球时,TiO2包覆量随着反应时间的延长而增加,反应7 h时达到90.2%的最大值;随介质中水含量的增加,吸附到复合微球表面上的TiO2纳米颗粒逐渐减少,复合微球表面逐渐变得光滑,当EtOH/H2O质量比为100/6.0时,得到结构均一、壳层厚度为29 nm的核壳结构PSt/TiO2复合微球.